Abstract: In this study, to clarify the effectiveness of an
aluminum/chromium/tungsten-based-coated tool for cutting sintered
steel, tool wear was experimentally investigated. The sintered steel
was turned with the (Al60,Cr25,W15)N-, (Al60,Cr25,W15)(C,N)- and
(Al64,Cr28,W8)(C,N)-coated cemented carbide tools according to the
physical vapor deposition (PVD) method. Moreover, the tool wear of
the aluminum/chromium/tungsten-based-coated item was compared
with that of the (Al,Cr)N coated tool. Furthermore, to clarify the tool
wear mechanism of the aluminum/chromium/tungsten-coating film for
cutting sintered steel, Scanning Electron Microscope observation and
Energy Dispersive x-ray Spectroscopy mapping analysis were
conducted on the abraded surface. The following results were
obtained: (1) The wear progress of the (Al64,Cr28,W8)(C,N)-coated
tool was the slowest among that of the five coated tools. (2) Adding
carbon (C) to the aluminum/chromium/tungsten-based-coating film
was effective for improving the wear-resistance. (3) The main wear
mechanism of the (Al60,Cr25,W15)N-, the (Al60,Cr25,W15)(C,N)-
and the (Al64,Cr28,W8)(C,N)-coating films was abrasive wear.
Abstract: In present global scenario, aluminum alloys are
coining the attention of many innovators as competing structural
materials for automotive and space applications. Comparing to other
challenging alloys, especially, 7xxx series aluminum alloys have
been studied seriously because of benefits such as moderate strength;
better deforming characteristics and affordable cost. It is expected
that substitution of aluminum alloys for steels will result in great
improvements in energy economy, durability and recyclability.
However, it is necessary to improve the strength and the formability
levels at low temperatures in aluminum alloys for still better
applications. Aluminum–Zinc–Magnesium with or without other
wetting agent denoted as 7XXX series alloys are medium strength
heat treatable alloys. In addition to Zn, Mg as major alloying
additions, Cu, Mn and Si are the other solute elements which
contribute for the improvement in mechanical properties by suitable
heat treatment process. Subjecting to suitable treatments like age
hardening or cold deformation assisted heat treatments; known as low
temperature thermomechanical treatments (LTMT) the challenging
properties might be incorporated. T6 is the age hardening or
precipitation hardening process with artificial aging cycle whereas T8
comprises of LTMT treatment aged artificially with X% cold
deformation. When the cold deformation is provided after solution
treatment, there is increase in hardness related properties such as
wear resistance, yield and ultimate strength, toughness with the
expense of ductility. During precipitation hardening both hardness
and strength of the samples are increasing. The hardness value may
further improve when room temperature deformation is positively
supported with age hardening known as thermomechanical treatment.
It is intended to perform heat treatment and evaluate hardness, tensile
strength, wear resistance and distribution pattern of reinforcement in
the matrix. 2 to 2.5 and 3 to 3.5 times increase in hardness is reported
in age hardening and LTMT treatments respectively as compared to
as-cast composite. There was better distribution of reinforcements in
the matrix, nearly two fold increase in strength levels and up to 5
times increase in wear resistance are also observed in the present
study.
Abstract: The reduction of phosphorus and sulfur in engine oil
are the main topics of this paper. Very reproducible boundary
lubrication tests were conducted as part of Design of Experiment
software (DOE) to study the behavior of fluorinated catalyst iron
fluoride (FeF3), and polutetrafluoroethylene or Teflon (PTFE) in
developing environmentally friendly (reduced P and S) anti-wear
additives for future engine oil formulations. Multi-component
Chevron fully formulated oil (GF3) and Chevron plain oil were used
with the addition of PTFE and catalyst to characterize and analyze
their performance. Lower phosphorus blends were the goal of the
model solution. Experiments indicated that new sub-micron FeF3
catalyst played an important role in preventing breakdown of the
tribofilm.
Abstract: Haynes 25 alloy (also known as L-605 alloy) is cobalt
based super alloy which has widely applications such as aerospace
industry, turbine and furnace parts, power generators and heat
exchangers and petroleum refining components due to its excellent
characteristics. However, the workability of this alloy is more
difficult compared to normal steels or even stainless. In present work,
an experimental investigation was performed under cryogenic
cooling to determine cutting tool wear patterns and obtain optimal
cutting parameters in turning of cobalt based superalloy Haynes 25.
In experiments, uncoated carbide tool was used and cutting speed (V)
and feed rate (f) were considered as test parameters. Tool wear
(VBmax) were measured for process performance indicators.
Analysis of variance (ANOVA) was performed to determine the
importance of machining parameters.
Abstract: Aluminium matrix composites with alumina
reinforcements give superior mechanical & physical properties. Their
applications in several fields like automobile, aerospace, defense,
sports, electronics, bio-medical and other industrial purposes are
becoming essential for the last several decades. In the present work,
fabrication of hybrid composite was done by Stir casting technique
using Al 6061 as a matrix with alumina and silicon carbide (SiC) as
reinforcement materials. The weight percentage of alumina is varied
from 2 to 4% and the silicon carbide weight percentage is maintained
constant at 2%. Hardness and wear tests are performed in the as cast
and heat treated conditions. Age hardening treatment was performed
on the specimen with solutionizing at 550°C, aging at two
temperatures (150 and 200°C) for different time durations. Hardness
distribution curves are drawn and peak hardness values are recorded.
Hardness increase was very sensitive with respect to the decrease in
aging temperature. There was an improvement in wear resistance of
the peak aged material when aged at lower temperature. Also
increase in weight percent of alumina, increases wear resistance at
lower temperature but opposite behavior was seen when aged at
higher temperature.
Abstract: Electrodeposition is a simple and economic technique
for precision coating of different shaped substrates with pure metal,
alloy or composite films. Dc electrodeposition was used to produce
Cr, Co-Cr and Co-Cr/TiO2 nano-composite coatings from Cr(III)
based electrolytes onto 316L SS substrates. The effects of TiO2 nanoparticles
concentration on co-deposition of these particles along with
Cr content and microhardness of the coatings were investigated.
Morphology of the Cr, Co-Cr and Co-Cr/TiO2 coatings besides their
tribological behavior were studied. The results showed that increment
of TiO2 nanoparticles concentration from 0 to 30 g L-1 in the bath
increased their co-deposition and Cr content of the coatings from 0 to
3.5 wt.% and from 23.7 to 31.2 wt.%, respectively. Microhardness of
Cr coating was about 920 Hv which was higher than Co-Cr and even
Co-Cr/TiO2 films. Microhardness of Co-Cr and Co-Cr/TiO2 coatings
were improved by increasing their Cr and TiO2 content. All the
coatings had nodular morphology and contained microcracks.
Nodules sizes and the number of microcracks in the alloy and
composite coatings were lower than the Cr film. Wear results
revealed that the Co-Cr/TiO2 coating had the lowest wear loss
between all the samples, while the Cr film had the worst wear
resistance.
Abstract: Water miscible cutting fluids are conventionally used to lubricate and cool the machining zone. But issues related to health hazards, maintenance and disposal costs have limited their usage, leading to application of Minimum Quantity Lubrication (MQL). To increase the effectiveness of MQL, nanocutting fluids are proposed. In the present work, water miscible nanographite cutting fluids of varying concentration are applied at cutting zone by two systems A and B. System A utilizes high pressure air and supplies cutting fluid at a flow rate of 1ml/min. System B uses low pressure air and supplies cutting fluid at a flow rate of 5ml/min. Their performance in machining is evaluated by measuring cutting temperatures, tool wear, cutting forces and surface roughness and compared with dry machining and flood machining. Application of nanocutting fluid using both systems showed better performance than dry machining. Cutting temperatures and cutting forces obtained by both techniques are more than flood machining. But tool wear and surface roughness showed improvement compared to flood machining. Economic analysis has been carried out in all the cases to decide the applicability of the techniques.
Abstract: Sol-enhanced Zn-Ni-Al2O3 nanocomposite coatings
were electroplated on mild steel by our newly developed solenhanced
electroplating method. In this method, transparent Al2O3 sol
was added into the acidic Zn-Ni bath to produced Zn-Ni-Al2O3nanocomposite
coatings. The chemical composition, microstructure and
mechanical properties of the composite and alloy coatings deposited
at two different agitation speed were investigated. The structure of all
coatings was single γ-Ni5Zn21 phase. The composite coatings possess
refined crystals with higher microhardness compared to Zn-Ni alloy
coatings. The wear resistance of Zn-Ni coatings was improved
significantly by incorporation of alumina nano particles into the
coatings. Higher agitation speed provided more uniform coatings
with smaller grain sized and slightly higher microhardness.
Considering composite coatings, high agitation speeds may facilitate
co-deposition of alumina in the coatings.
Abstract: Al6061 alloy base matrix, reinforced with particles of
silicon carbide (10 wt %) and Graphite powder (1wt%), known as
hybrid composites have been fabricated by liquid metallurgy route
(stir casting technique) and optimized at different parameters like
applied load, sliding speed and sliding distance by taguchi method. A
plan of experiment generated through taguchi technique was used to
perform experiments based on L27 orthogonal array. The developed
ANOVA and regression equations are used to find the optimum
coefficient of friction and wear under the influence of applied load,
sliding speed and sliding distance. On the basis of “smaller the best”
the dry sliding wear resistance was analysed and finally confirmation
tests were carried out to verify the experimental results.
Abstract: This paper is aimed at proposing a rhombus shaped
wearable fractal antenna for wireless communication systems. The
geometrical descriptors of the antenna have been obtained using
bacterial foraging optimization (BFO) for wide band operation. The
method of moment based IE3D software has been used to simulate
the antenna and observed that miniaturization of 13.08% has been
achieved without degrading the resonating properties of the proposed
antenna. An analysis with different substrates has also been done in
order to evaluate the effectiveness of electrical permittivity on the
presented structure. The proposed antenna has low profile, light
weight and has successfully demonstrated wideband and multiband
characteristics for wearable electronic applications.
Abstract: In this study, ultrasonic assisted machining (UAM) technique is applied in side-surface milling experiment for glass-ceramic workpiece material. The tungsten carbide cutting-tool with diamond coating is used in conjunction with two kinds of cooling/lubrication mediums such as water-soluble (WS) cutting fluid and minimum quantity lubricant (MQL). Full factorial process parameter combinations on the milling experiments are planned to investigate the effect of process parameters on cutting performance. From the experimental results, it tries to search for the better process parameter combination which the edge-indentation and the surface roughness are acceptable. In the machining experiments, ultrasonic oscillator was used to excite a cutting-tool along the radial direction producing a very small amplitude of vibration frequency of 20KHz to assist the machining process. After processing, toolmaker microscope was used to detect the side-surface morphology, edge-indentation and cutting tool wear under different combination of cutting parameters, and analysis and discussion were also conducted for experimental results. The results show that the main leading parameters to edge-indentation of glass ceramic are cutting depth and feed rate. In order to reduce edge-indentation, it needs to use lower cutting depth and feed rate. Water-soluble cutting fluid provides a better cooling effect in the primary cutting area; it may effectively reduce the edge-indentation and improve the surface morphology of the glass ceramic. The use of ultrasonic assisted technique can effectively enhance the surface finish cleanness and reduce cutting tool wear and edge-indentation.
Abstract: Dental porcelain composites reinforced and toughened
by 20 wt.% tetragonal zirconia (3Y-TZP) were processed by hot
pressing at 1000°C. Two types of particles were tested: yttriastabilized
zirconia (ZrO2–3%Y2O3) agglomerates and pre-sintered
yttria-stabilized zirconia (ZrO2–3%Y2O3) particles. The composites
as well as the reinforcing particles were analyzed by the means of
optical and Scanning Electron Microscopy (SEM), Energy Dispersion
Spectroscopy (EDS) and X-Ray Diffraction (XRD). The mechanical
properties were obtained by the transverse rupture strength test. Wear
tests were also performed on the composites and monolithic
porcelain. The best mechanical results were displayed by the
porcelain reinforced with the pre-sintered ZrO2–3%Y2O3
agglomerates.
Abstract: This article presents modeling studies of NiAl alloy
under solid-particle erosion and liquid-drop erosion. In the
solid-particle erosion simulation, attention is paid to the oxide scale
thickness variation on the alloy in high-temperature erosion
environments. The erosion damage is assumed to be deformation wear
and cutting wear mechanisms, incorporating the influence of the oxide
scale on the eroded surface; thus the instantaneous oxide thickness is
the result of synergetic effect of erosion and oxidation. For liquid-drop
erosion, special interest is in investigating the effects of drop velocity
and drop size on the damage of the target surface. The models of
impact stress wave, mean depth of penetration, and maximum depth of
erosion rate (Max DER) are employed to develop various maps for
NiAl alloy, including target thickness vs. drop size (diameter), rate of
mean depth of penetration (MDRP) vs. drop impact velocity, and
damage threshold velocity (DTV) vs. drop size.
Abstract: We have been grouping and developing various kinds
of practical, promising sensing applied systems concerning
agricultural advancement and technical tradition (guidance). These
include advanced devices to secure real-time data related to worker
motion, and we analyze by methods of various advanced statistics and
human dynamics (e.g. primary component analysis, Ward system
based cluster analysis, and mapping). What is more, we have been
considering worker daily health and safety issues. Targeted fields are
mainly common farms, meadows, and gardens. After then, we
observed and discussed time-line style, changing data. And, we made
some suggestions. The entire plan makes it possible to improve both
the aforementioned applied systems and farms.
Abstract: Machining of hard materials is a recent technology for
direct production of work-pieces. The primary challenge in
machining these materials is selection of cutting tool inserts which
facilitates an extended tool life and high-precision machining of the
component. These materials are widely for making precision parts for
the aerospace industry. Nickel-based alloys are typically used in
extreme environment applications where a combination of strength,
corrosion resistance and oxidation resistance material characteristics
are required. The present paper reports the theoretical and
experimental investigations carried out to understand the influence of
machining parameters on the response parameters. Considering the
basic machining parameters (speed, feed and depth of cut) a study has
been conducted to observe their influence on material removal rate,
surface roughness, cutting forces and corresponding tool wear.
Experiments are designed and conducted with the help of Central
Composite Rotatable Design technique. The results reveals that for a
given range of process parameters, material removal rate is favorable
for higher depths of cut and low feed rate for cutting forces. Low feed
rates and high values of rotational speeds are suitable for better finish
and higher tool life.
Abstract: Chemical vapor deposition (CVD) diamond coated
cutting tool has excellent cutting performance, it is the most ideal tool
for the processing of nonferrous metals and alloys, composites,
nonmetallic materials and other difficult-to-machine materials
efficiently and accurately. Depositing CVD diamond coating on the
cemented carbide with high cobalt content can improve its toughness
and strength, therefore, it is very important to research on the
preparation technology and cutting properties of CVD diamond coated
cemented carbide cutting tool with high cobalt content. The
preparation technology of boron-doped diamond (BDD) coating has
been studied and the coated drills were prepared. BDD coating were
deposited on the drills by using the optimized parameters and the SEM
results show that there are no cracks or collapses in the coating.
Cutting tests with the prepared drills against the silumin and aluminum
base printed circuit board (PCB) have been studied. The results show
that the wear amount of the coated drill is small and the machined
surface has a better precision. The coating does not come off during
the test, which shows good adhesion and cutting performance of the
drill.
Abstract: In this research (using induction furnace process)
nodular iron with three different percentages of copper (residual,
0.5% and 1,2%) was obtained. Chemical analysis was performed by
mass spectrometry and microstructures were characterized by Optical
Microscopy (ASTM E3) and Scanning Electron Microscopy (SEM).
The study of mechanical behavior was carried out in a mechanical
test machine (ASTM E8) and a Pin on disk tribometer (ASTM G99)
was used to assess wear resistance. It is observed that the dissolution
of copper in crystal lattice increases the pearlite structure improving
the wear and hardness behavior, but producing a contrary effect on
the energy absorption.
Abstract: The wear measuring and wear modelling are
fundamental issues in the industrial field, mainly correlated to the
economy and safety. Therefore, there is a need to study the wear
measurements and wear estimation. Pin-on-disc test is the most
common test which is used to study the wear behaviour. In this paper,
the pin-on-disc (AEROTECH UNIDEX 11) is used for the
investigation of the effects of normal load and hardness of material on
the wear under dry and sliding conditions. In the pin-on-disc rig, two
specimens were used; one, a pin is made of steel with a tip, positioned
perpendicular to the disc, where the disc is made of aluminium. The
pin wear and disc wear were measured by using the following
instruments: The Talysurf instrument, a digital microscope, and the
alicona instrument. The Talysurf profilometer was used to measure
the pin/disc wear scar depth, digital microscope was used to measure
the diameter and width of wear scar, and the alicona was used to
measure the pin wear and disc wear. After that, the Archard model,
American Society for Testing and Materials model (ASTM), and
neural network model were used for pin/disc wear modelling.
Simulation results were implemented by using the Matlab program.
This paper focuses on how the alicona can be used for wear
measurements and how the neural network can be used for wear
estimation.
Abstract: Vancron 40, a nitrided powder metallurgical tool
Steel, is used in cold work applications where the predominant failure
mechanisms are adhesive wear or galling. Typical applications of
Vancron 40 are among others fine blanking, cold extrusion, deep
drawing and cold work rolls for cluster mills. Vancron 40 positive
results for cold work rolls for cluster mills and as a tool for some
severe metal forming process makes it competitive compared to other
type of work rolls that require higher precision, among others in cold
rolling of thin stainless steel, which required high surface finish
quality. In this project, three roll materials for cold rolling of stainless
steel strip was examined, Vancron 40, Narva 12B (a high-carbon,
high-chromium tool steel alloyed with tungsten) and Supra 3 (a
Chromium-molybdenum tungsten-vanadium alloyed high speed
steel). The purpose of this project was to study the depth profiles of
the ironed stainless steel strips, emergence of galling and to study the
lubrication performance used by steel industries. Laboratory
experiments were conducted to examine scratch of the strip, galling
and surface roughness of the roll materials under severe tribological
conditions. The critical sliding length for onset of galling was
estimated for stainless steel with four different lubricants. Laboratory
experiments result of performance evaluation of resistance capability
of rolls toward adhesive wear under severe conditions for low and
high reductions. Vancron 40 in combination with cold rolling
lubricant gave good surface quality, prevents galling of
metal surfaces and good bearing capacity.
Abstract: In order to better understand the long term
implications of the grout wear failure mode in large-diameter plainsided
grouted connections, a numerical model has been developed
and calibrated that can take advantage of existing operational plant
data to predict the wear accumulation for the actual load conditions
experienced over a given period, thus limiting the requirement for
expensive monitoring systems. This model has been derived and
calibrated based on site structural condition monitoring (SCM) data
and supervisory control and data acquisition systems (SCADA) data
for two operational wind turbine generator substructures afflicted
with this challenge, along with experimentally derived wear rates.