Abstract: A series of tests on cold-formed steel foamed concrete (CSFC) composite walls subjected to axial load were proposed. The primary purpose of the experiments was to study the mechanical behavior and identify the failure modes of CSFC composite walls. Two main factors were considered in this study: 1) specimen with pouring foamed concrete or without and 2) different foamed concrete density ranks (corresponding to different foamed concrete strength). The interior space between two pieces of straw board of the specimen W-2 and W-3 were poured foamed concrete, and the specimen W-1 does not have foamed concrete core. The foamed concrete density rank of the specimen W-2 was A05 grade, and that of the specimen W-3 was A07 grade. Results showed that the failure mode of CSFC composite wall without foamed concrete was distortional buckling of cold-formed steel (CFS) column, and that poured foamed concrete includes the local crushing of foamed concrete and local buckling of CFS column, but the former prior to the later. Compared with CSFC composite wall without foamed concrete, the ultimate bearing capacity of spec imens poured A05 grade and A07 grade foamed concrete increased 1.6 times and 2.2 times respectively, and specimen poured foamed concrete had a low vertical deformation. According to these results, the simplified calculation formula for the CSFC wall subjected to axial load was proposed, and the calculated results from this formula are in very good agreement with the test results.
Abstract: Chemical vapor deposition (CVD) diamond coated
cutting tool has excellent cutting performance, it is the most ideal tool
for the processing of nonferrous metals and alloys, composites,
nonmetallic materials and other difficult-to-machine materials
efficiently and accurately. Depositing CVD diamond coating on the
cemented carbide with high cobalt content can improve its toughness
and strength, therefore, it is very important to research on the
preparation technology and cutting properties of CVD diamond coated
cemented carbide cutting tool with high cobalt content. The
preparation technology of boron-doped diamond (BDD) coating has
been studied and the coated drills were prepared. BDD coating were
deposited on the drills by using the optimized parameters and the SEM
results show that there are no cracks or collapses in the coating.
Cutting tests with the prepared drills against the silumin and aluminum
base printed circuit board (PCB) have been studied. The results show
that the wear amount of the coated drill is small and the machined
surface has a better precision. The coating does not come off during
the test, which shows good adhesion and cutting performance of the
drill.
Abstract: A closed-loop controlled wireless power transmission circuit block for implantable biomedical applications is described in this paper. The circuit consists of one front-end rectifier, power management sub-block including bandgap reference and low drop-out regulators (LDOs) as well as transmission power detection / feedback circuits. Simulation result shows that the front-end rectifier achieves 80% power efficiency with 750-mV single-end peak-to-peak input voltage and 1.28-V output voltage under load current of 4 mA. The power management block can supply 1.8mA average load current under 1V consuming only 12μW power, which is equivalent to 99.3% power efficiency. The wireless power transmission block described in this paper achieves a maximum power efficiency of 80%. The wireless power transmission circuit block is designed and implemented using UMC 65-nm CMOS/RF process. It occupies 1 mm × 1.2 mm silicon area.