Abstract: Corrugated wire mesh laminates (CWML) are a class
of engineered open cell structures that have potential for applications
in many areas including aerospace and biomedical engineering. Two
different methods of fabricating corrugated wire mesh laminates from
stainless steel, one using a high temperature Lithobraze alloy and the
other using a low temperature Eutectic solder for joining the
corrugated wire meshes are described herein. Their implementation is
demonstrated by manufacturing CWML samples of 304 and 316
stainless steel (SST). It is seen that due to the facility of employing
wire meshes of different densities and wire diameters, it is possible to
create CWML laminates with a wide range of effective densities. The
fabricated laminates are tested under uniaxial compression. The
variation of the compressive yield strength with relative density of the
CWML is compared to the theory developed by Gibson and Ashby for
open cell structures [22]. It is shown that the compressive strength of
the corrugated wire mesh laminates can be described using the same
equations by using an appropriate value for the linear coefficient in the
Gibson-Ashby model.
Abstract: Single crystals of Magnesium alloys such as Mg-1Al,
Mg-1Zn-0.5Y, Mg-3Li, and AZ31 alloys were successfully fabricated in this study by employing the modified Bridgman method. Single
crystals of pure Mg were also made in this study. To determine the exact orientation of crystals, Laue back-reflection method and pole figure measurement were carried out on each single crystal. Dimensions of single crystals were 10 mm in diameter and 120 mm in
length. Hardness and compression tests were conducted and the results
revealed that hardness and the strength strongly depended on the
orientation. The closer to basal one the orientation was, the higher hardness and compressive strength were. The effect of alloying was
not higher than that of orientation. After compressive deformation of single crystals, the orientation of the crystals was found to rotate and to be parallel to the basal orientation.
Abstract: In this paper, the effect of addition the dune sand powder (DSP) on development of compressive strength and hydration of cement pastes was investigated as a function of water/binder ratio, was varied, on the one hand, the percentage of DSP and on the other, the fineness of DSP. In order to understand better the pozzolanic effect of dune sand powder in cement pastes, we followed the mixtures hydration (50% Pure Lime + 50% DSP) by X-ray diffraction. These mixtures the pastes present a hydraulic setting which is due to the formation of a C-S-H phase (calcium silicate hydrate). The latter is semi-crystallized. This study is a simplified approach to that of the mixtures (80% ordinary Portland cement + 20% DSP), in which the main reaction is the fixing of the lime coming from the cement hydration in the presence of DSP, to form calcium silicate hydrate semi-crystallized of second generation. The results proved that up to (20% DSP) as Portland cement replacement could be used with a fineness of 4000 cm²/g without affecting adversely the compressive strength. After 28 days, the compressive strength at 5, 10 and 15% DSP is superior to Portland cement, with an optimum effect for a percentage of the order of 5% to 10% irrespective of the w/b ratio and fineness of DSP.
Abstract: This paper presents the experimental results of the
investigation of various properties related to the durability and longterm
performance of mortars made of Fly Ash blended cement, FA
and Ordinary Portland cement, OPC. The properties that were
investigated in an experimental program include; equilibration of
specimen in different relative humidity, determination of total
porosity, compressive strength, chloride permeability index, and
electrical resistivity. Fly Ash blended cement mortar specimens
exhibited 10% to 15% lower porosity when measured at equilibrium
conditions in different relative humidities as compared to the
specimens made of OPC mortar, which resulted in 6% to 8% higher
compressive strength of FA blended cement mortar specimens. The
effects of ambient relative humidity during sample equilibration on
porosity and strength development were also studied. For specimens
equilibrated in higher relative humidity conditions, such as 75%, the
total porosity of different mortar specimens was between 35% to 50%
less than the porosity of samples equilibrated in 12% relative
humidity, consequently leading to higher compressive strengths of
these specimens.A valid statistical correlation between values of
compressive strength, porosity and the degree of saturation was
obtained. Measured values of chloride permeability index of fly ash
blended cement mortar were obtained as one fourth to one sixth of
those measured for OPC mortar specimens, which indicates high
resistance against chloride ion penetration in FA blended cement
specimens, hence resulting in a highly durable mortar.
Abstract: The predictability of masonry arch bridges and their
behaviour is widely considered doubtful due to the lack of knowledge
about the conditions of a given masonry arch bridge. The assessment
methods for masonry arch bridges are MEXE, ARCHIE, RING and
Frame Analysis Method. The material properties of the masonry and
fill material are extremely difficult to determine accurately.
Consequently, it is necessary to examine the effect of load dispersal
angle through the fill material, the effect of variations in the stiffness
of the masonry, the tensile strength of the masonry mortar continuum
and the compressive strength of the masonry mortar continuum. It is
also important to understand the effect of fill material on load
dispersal angle to determine their influence on ratings. In this paper a
series of parametric studies, to examine the sensitivity of assessment
ratings to the various sets of input data required by the frame analysis
method, are carried out.
Abstract: The compressive strength development through
polymerization process of alkaline solution and fly ash blended with Microwave Incinerated Rice Husk Ash (MIRHA) is described in this
paper. Three curing conditions, which are hot gunny curing, ambient
curing, and external humidity curing are investigated to obtain the suitable curing condition for cast in situ provision. Fly ash was
blended with MIRHA at 3%, 5%, and 7% to identify the effect of blended mixes to the compressive strength and microstructure
properties of geopolymer concrete. Compressive strength results
indicated an improvement in the strength development with external humidity curing concrete samples compared to hot gunny curing and
ambient curing. Blended mixes also presented better performance
than control mixes. Improvement of interfacial transition zone (ITZ)
and micro structure in external humidity concrete samples were also
identified compared to hot gunny and ambient curing.
Abstract: This paper studies the application of a variety of
sawdust materials in the production of lightweight insulating bricks.
First, the mineralogical and chemical composition of clays was determined. Next, ceramic bricks were fabricated with different
quantities of materials (3–6 and 9 wt. % for sawdust, 65 wt. % for grey clay, 24–27 and 30 wt. % for yellow clay and 2 wt% of tuff).
These bricks were fired at 800 and 950 °C. The effect of adding this sawdust on the technological behaviour of the brick was assessed by
drying and firing shrinkage, water absorption, porosity, bulk density
and compressive strength. The results have shown that the optimum
sintering temperature is 950 °C. Below this temperature, at 950 °C,
increased open porosity was observed, which decreased the compressive strength of the bricks. Based on the results obtained, the
optimum amounts of waste were 9 wt. % sawdust of eucalyptus, 24 wt. % shaping moisture and 1.6 particle size diameter. These percentages produced bricks whose mechanical properties were
suitable for use as secondary raw materials in ceramic brick
production.
Abstract: The work presents a development of EN338 strength classes for Strombosia pustulata, Pterygotama crocarpa, Nauclea diderrichii and Entandrophragma cyclindricum Nigerian timber species. The specimens for experimental measurements were obtained from the timber-shed at the famous Panteka market in Kaduna in the northern part of Nigeria. Laboratory experiments were conducted to determine the physical and mechanical properties of the selected timber species in accordance with EN 13183-1 and ASTM D193. The mechanical properties were determined using three point bending test. The generated properties were used to obtain the characteristic values of the material properties in accordance with EN384. The selected timber species were then classified according to EN 338. Strombosia pustulata, Pterygotama crocarpa, Nauclea diderrichii and Entandrophragma cyclindricum were assigned to strength classes D40, C14, D40 and D24 respectively. Other properties such as tensile and compressive strengths parallel and perpendicular to grains, shear strength as well as shear modulus were obtained in accordance with EN 338.
Abstract: Climate change and environmental pressures are
major international issues nowadays. It is time when governments,
businesses and consumers have to respond through more
environmentally friendly and aware practices, products and policies.
This is the prime time to develop alternative sustainable construction
materials, reduce greenhouse gas emissions, save energy, look to
renewable energy sources and recycled materials, and reduce waste.
The utilization of waste materials (slag, fly ash, glass beads, plastic
and so on) in concrete manufacturing is significant due to its
engineering, financial, environmental and ecological benefits. Thus,
utilization of waste materials in concrete production is very much
helpful to reach the goal of the sustainable construction. Therefore,
this study intends to use glass beads in concrete production.
The paper reports on the performance of 9 different concrete
mixes containing different ratios of glass crushed to 5 mm - 20 mm
maximum size and glass marble of 20 mm size as coarse aggregate.
Ordinary Portland cement type 1 and fine sand less than 0.5 mm were
used to produce standard concrete cylinders. Compressive strength
tests were carried out on concrete specimens at various ages. Test
results indicated that the mix having the balanced ratio of glass beads
and round marbles possess maximum compressive strength which is
3889 psi, as glass beads perform better in bond formation but have
lower strength, on the other hand marbles are strong in themselves
but not good in bonding. These mixes were prepared following a
specific W/C and aggregate ratio; more strength can be expected to
achieve from different W/C, aggregate ratios, adding admixtures like
strength increasing agents, ASR inhibitor agents etc.
Abstract: This paper presents the stabilization potential of Class
F pond ash (PA) from a coal fired thermal power station on tropical
peat soil. Peat or highly organic soils are well known for their high
compressibility, natural moisture content, low shear strength and
long-term settlement. This study investigates the effect of different
amount (i.e., 5, 10, 15 and 20%) of PA on peat soil, collected from
Sarawak, Malaysia, mainly compaction and unconfined compressive
strength (UCS) properties. The amounts of PA added to the peat soil
sample as percentage of the dry peat soil mass. With the increase in
PA content, the maximum dry density (MDD) of peat soil increases,
while the optimum moisture content (OMC) decreases. The UCS
value of the peat soils increases significantly with the increase of PA
content and also with curing periods. This improvement on
compressive strength of tropical peat soils indicates that PA has the
potential to be used as a stabilizer for tropical peat soil. Also, the use
of PA in soil stabilization helps in reducing the pond volume and
achieving environment friendly as well as a sustainable development
of natural resources.
Abstract: In this study two series of self compacting concrete
mixtures were prepared with 100% coarse recycled concrete
aggregates and different percentages of 0%, 20%, 40%, 60%, 80%
and 100% fine recycled concrete aggregates. In series I and II the
water to binder ratios were 0.50 and 0.45, respectively. The cement
content was kept 350
3 m
kg for those mixtures that don't have any
Nano-Silica. To improve the compressive strength of samples, Nano-
Silica replaced with 10% of cement weight in concrete mixtures. By
doing the tests, the results showed that, adding Nano-silica to the
samples with less percentage of fine recycled concrete aggregates,
lead to more increase on the compressive strength.
Abstract: Limited infrastructure development on peats and
organic soils is a serious geotechnical issues common to many
countries of the world especially Malaysia which distributed 1.5 mill
ha of those problematic soil. These soils have high water content and
organic content which exhibit different mechanical properties and
may also change chemically and biologically with time. Constructing
structures on peaty ground involves the risk of ground failure and
extreme settlement. Nowdays, much efforts need to be done in
making peatlands usable for construction due to increased landuse.
Deep mixing method employing cement as binders, is generally used
as measure again peaty/ organic ground failure problem. Where the
technique is widely adopted because it can improved ground
considerably in a short period of time. An understanding of
geotechnical properties as shear strength, stiffness and compressibility
behavior of these soils was requires before continues construction on
it. Therefore, 1- 1.5 meter peat soil sample from states of Johor and
an organic soil from Melaka, Malaysia were investigated. Cement
were added to the soil in the pre-mixing stage with water cement ratio
at range 3.5,7,14,140 for peats and 5,10,30 for organic soils,
essentially to modify the original soil textures and properties. The
mixtures which in slurry form will pour to polyvinyl chloride (pvc)
tube and cured at room temperature 250C for 7,14 and 28 days.
Laboratory experiments were conducted including unconfined
compressive strength and bender element , to monitor the improved
strength and stiffness of the 'stabilised mixed soils'. In between,
scanning electron miscroscopic (SEM) were observations to
investigate changes in microstructures of stabilised soils and to
evaluated hardening effect of a peat and organic soils stabilised
cement. This preliminary effort indicated that pre-mixing peat and
organic soils contributes in gaining soil strength while help the
engineers to establish a new method for those problematic ground
improvement in further practical and long term applications.
Abstract: In this work, the primary compressive strength
components of human femur trabecular bone are qualitatively
assessed using image processing and wavelet analysis. The Primary
Compressive (PC) component in planar radiographic femur trabecular
images (N=50) is delineated by semi-automatic image processing
procedure. Auto threshold binarization algorithm is employed to
recognize the presence of mineralization in the digitized images. The
qualitative parameters such as apparent mineralization and total area
associated with the PC region are derived for normal and abnormal
images.The two-dimensional discrete wavelet transforms are utilized
to obtain appropriate features that quantify texture changes in medical
images .The normal and abnormal samples of the human femur are
comprehensively analyzed using Harr wavelet.The six statistical
parameters such as mean, median, mode, standard deviation, mean
absolute deviation and median absolute deviation are derived at level
4 decomposition for both approximation and horizontal wavelet
coefficients. The correlation coefficient of various wavelet derived
parameters with normal and abnormal for both approximated and
horizontal coefficients are estimated. It is seen that in almost all cases
the abnormal show higher degree of correlation than normals. Further
the parameters derived from approximation coefficient show more
correlation than those derived from the horizontal coefficients. The
parameters mean and median computed at the output of level 4 Harr
wavelet channel was found to be a useful predictor to delineate the
normal and the abnormal groups.
Abstract: Reinforced Concrete (RC) structures strengthened
with fiber reinforced polymer (FRP) lack in thermal resistance under
elevated temperatures in the event of fire. This phenomenon led to
the lining of strengthened concrete with thin high performance
cementitious composites (THPCC) to protect the substrate against
elevated temperature. Elevated temperature effects on THPCC, based
on different cementitious materials have been studied in the past but
high-alumina cement (HAC)-based THPCC have not been well
characterized. This research study will focus on the THPCC based on
HAC replaced by 60%, 70%, 80% and 85% of ground granulated
blast furnace slag (GGBS). Samples were evaluated by the
measurement of their mechanical strength (28 & 56 days of curing)
after exposed to 400°C, 600°C and 28°C of room temperature for
comparison and corroborated by their microstructure study. Results
showed that among all mixtures, the mix containing only HAC
showed the highest compressive strength after exposed to 600°C as
compared to other mixtures. However, the tensile strength of THPCC
made of HAC and 60% GGBS content was comparable to the
THPCC with HAC only after exposed to 600°C. Field emission
scanning electron microscopy (FESEM) images of THPCC
accompanying Energy Dispersive X-ray (EDX) microanalysis
revealed that the microstructure deteriorated considerably after
exposure to elevated temperatures which led to the decrease in
mechanical strength.
Abstract: A laboratory study on the influence of compactive
effort on expansive black cotton specimens treated with up to 8%
ordinary Portland cement (OPC) admixed with up to 8% bagasse ash
(BA) by dry weight of soil and compacted using the energies of the
standard Proctor (SP), West African Standard (WAS) or
“intermediate” and modified Proctor (MP) were undertaken. The
expansive black cotton soil was classified as A-7-6 (16) or CL using
the American Association of Highway and Transportation Officials
(AASHTO) and Unified Soil Classification System (USCS),
respectively. The 7day unconfined compressive strength (UCS)
values of the natural soil for SP, WAS and MP compactive efforts are
286, 401 and 515kN/m2 respectively, while peak values of 1019,
1328 and 1420kN/m2 recorded at 8% OPC/ 6% BA, 8% OPC/ 2% BA
and 6% OPC/ 4% BA treatments, respectively were less than the
UCS value of 1710kN/m2 conventionally used as criterion for
adequate cement stabilization. The soaked California bearing ratio
(CBR) values of the OPC/BA stabilized soil increased with higher
energy level from 2, 4 and 10% for the natural soil to Peak values of
55, 18 and 8% were recorded at 8% OPC/4% BA 8% OPC/2% BA
and 8% OPC/4% BA, treatments when SP, WAS and MP compactive
effort were used, respectively. The durability of specimens was
determined by immersion in water. Soils treatment at 8% OPC/ 4%
BA blend gave a value of 50% resistance to loss in strength value
which is acceptable because of the harsh test condition of 7 days
soaking period specimens were subjected instead of the 4 days
soaking period that specified a minimum resistance to loss in strength
of 80%. Finally An optimal blend of is 8% OPC/ 4% BA is
recommended for treatment of expansive black cotton soil for use as
a sub-base material.
Abstract: In recent years demolished concrete waste handling and management is the new primary challenging issue faced by the countries all over the world. It is very challenging and hectic problem that has to be tackled in an indigenous manner, it is desirable to completely recycle demolished concrete waste in order to protect natural resources and reduce environmental pollution. In this research paper an experimental study is carried out to investigate the feasibility and recycling of demolished waste concrete for new construction. The present investigation to be focused on recycling demolished waste materials in order to reduce construction cost and resolving housing problems faced by the low income communities of the world. The crushed demolished concrete wastes is segregated by sieving to obtain required sizes of aggregate, several tests were conducted to determine the aggregate properties before recycling it into new concrete. This research shows that the recycled aggregate that are obtained from site make good quality concrete. The compressive strength test results of partial replacement and full recycled aggregate concrete and are found to be higher than the compressive strength of normal concrete with new aggregate.
Abstract: This paper reports the results of an experimental work
conducted to investigate the effect of curing conditions on the
compressive strength of self-compacting geopolymer concrete
prepared by using fly ash as base material and combination of sodium
hydroxide and sodium silicate as alkaline activator. The experiments
were conducted by varying the curing time and curing temperature in
the range of 24-96 hours and 60-90°C respectively. The essential
workability properties of freshly prepared Self-compacting
Geopolymer concrete such as filling ability, passing ability and
segregation resistance were evaluated by using Slump flow,
V-funnel, L-box and J-ring test methods. The fundamental
requirements of high flowability and resistance to segregation as
specified by guidelines on Self-compacting Concrete by EFNARC
were satisfied. Test results indicate that longer curing time and curing
the concrete specimens at higher temperatures result in higher
compressive strength. There was increase in compressive strength
with the increase in curing time; however increase in compressive
strength after 48 hours was not significant. Concrete specimens cured
at 70°C produced the highest compressive strength as compared to
specimens cured at 60°C, 80°C and 90°C.
Abstract: A self-compacting concrete (SCC) is the one that can
be placed in the form and can go through obstructions by its own
weight and without the need of vibration. Since its first development
in Japan in 1988, SCC has gained wider acceptance in Japan, Europe
and USA due to its inherent distinct advantages. Although there are
visible signs of its gradual acceptance in the North Africa through its
limited use in construction, Libya has yet to explore the feasibility
and applicability of SCC in new construction. The contributing
factors to this reluctance appear to be lack of any supportive
evidence of its suitability with local aggregates and the harsh
environmental conditions. The primary aim of this study is to explore
the feasibility of using SCC made with local aggregates of Eastern
Province of Libya by examining its basic properties characteristics.
This research consists of: (i) Development of a suitable mix for SCC
such as the effect of water to cement ratio, limestone and silica fume
that would satisfy the requirements of the plastic state; (ii) Casting of
concrete samples and testing them for compressive strength and unit
weight. Local aggregates, cement, admixtures and industrial waste
materials were used in this research.
The significance of this research lies in its attempt to provide
some performance data of SCC made in the Eastern Province of
Libya so as to draw attention to the possible use of SCC.
Abstract: In this study, a new procedure for inspecting damages on LNG storage tanks was proposed with the use of structural diagnostic techniques: i.e., nondestructive inspection techniques such as macrography, the hammer sounding test, the Schmidt hammer test, and the ultrasonic pulse velocity test, and destructive inspection techniques such as the compressive strength test, the chloride penetration test, and the carbonation test. From the analysis of all the test results, it was concluded that the LNG storage tank cover was in good condition. Such results were also compared with the Korean concrete standard specifications and design values. In addition, the remaining life of the LNG storage tank was estimated by using existing models. Based on the results, an LNG storage tank cover performance evaluation procedure was suggested.
Abstract: Self-compacting concrete (SCC), a new kind of high
performance concrete (HPC) have been first developed in Japan in
1986. The development of SCC has made casting of dense
reinforcement and mass concrete convenient, has minimized noise.
Fresh self-compacting concrete (SCC) flows into formwork and
around obstructions under its own weight to fill it completely and
self-compact (without any need for vibration), without any
segregation and blocking. The elimination of the need for
compaction leads to better quality concrete and substantial
improvement of working conditions. SCC mixes generally have a
much higher content of fine fillers, including cement, and produce
excessively high compressive strength concrete, which restricts its
field of application to special concrete only. To use SCC mixes in
general concrete construction practice, requires low cost materials to
make inexpensive concrete.
Rice husk ash (RHA) has been used as a highly reactive
pozzolanic material to improve the microstructure of the interfacial
transition zone (ITZ) between the cement paste and the aggregate in
self compacting concrete. Mechanical experiments of RHA blended
Portland cement concretes revealed that in addition to the pozzolanic
reactivity of RHA (chemical aspect), the particle grading (physical
aspect) of cement and RHA mixtures also exerted significant
influences on the blending efficiency.
The scope of this research was to determine the usefulness of Rice
husk ash (RHA) in the development of economical self compacting
concrete (SCC). The cost of materials will be decreased by reducing
the cement content by using waste material like rice husk ash instead
of.
This paper presents a study on the development of Mechanical
properties up to 180 days of self compacting and ordinary concretes
with rice-husk ash (RHA), from a rice paddy milling industry in
Rasht (Iran). Two different replacement percentages of cement by
RHA, 10%, and 20%, and two different water/cementicious material
ratios (0.40 and 0.35), were used for both of self compacting and
normal concrete specimens. The results are compared with those of
the self compacting concrete without RHA, with compressive,
flexural strength and modulus of elasticity. It is concluded that RHA
provides a positive effect on the Mechanical properties at age after
60 days.
Base of the result self compacting concrete specimens have higher
value than normal concrete specimens in all test except modulus of
elasticity. Also specimens with 20% replacement of cement by RHA
have the best performance.