Abstract: This paper reports the results of an experimental work
conducted to investigate the effect of curing conditions on the
compressive strength of self-compacting geopolymer concrete
prepared by using fly ash as base material and combination of sodium
hydroxide and sodium silicate as alkaline activator. The experiments
were conducted by varying the curing time and curing temperature in
the range of 24-96 hours and 60-90°C respectively. The essential
workability properties of freshly prepared Self-compacting
Geopolymer concrete such as filling ability, passing ability and
segregation resistance were evaluated by using Slump flow,
V-funnel, L-box and J-ring test methods. The fundamental
requirements of high flowability and resistance to segregation as
specified by guidelines on Self-compacting Concrete by EFNARC
were satisfied. Test results indicate that longer curing time and curing
the concrete specimens at higher temperatures result in higher
compressive strength. There was increase in compressive strength
with the increase in curing time; however increase in compressive
strength after 48 hours was not significant. Concrete specimens cured
at 70°C produced the highest compressive strength as compared to
specimens cured at 60°C, 80°C and 90°C.
Abstract: The research investigates the effects of super plasticizer and molarity of sodium hydroxide alkaline solution on the workability, microstructure and compressive strength of self compacting geopolymer concrete (SCGC). SCGC is an improved way of concreting execution that does not require compaction and is made by complete elimination of ordinary Portland cement content. The parameters studied were superplasticizer (SP) dosage and molarity of NaOH solution. SCGC were synthesized from low calcium fly ash, activated by combinations of sodium hydroxide and sodium silicate solutions, and by incorporation of superplasticizer for self compactability. The workability properties such as filling ability, passing ability and resistance to segregation were assessed using slump flow, T-50, V-funnel, L-Box and J-ring test methods. It was found that the essential workability requirements for self compactability according to EFNARC were satisfied. Results showed that the workability and compressive strength improved with the increase in superplasticizer dosage. An increase in strength and a decrease in workability of these concrete samples were observed with the increase in molarity of NaOH solution from 8M to 14M. Improvement of interfacial transition zone (ITZ) and micro structure with the increase of SP and increase of concentration from 8M to 12M were also identified.