Abstract: This study investigates the effect of using carbon-free fly ash (CfFA) and ground granulated blast-furnace slag (GGBFS) on the compressive strength of mortar. The CfFA used in this investigation is high-quality fly ash and the carbon content is 1.0% or less. In this study, three types of blends with a 30% water-binder ratio (w/b) were prepared: control, binary and ternary blends. The Control blend contained only Ordinary Portland Cement (OPC), in binary and ternary blends OPC was partially replaced with CfFA and GGBFS at different substitution rates. Mortar specimens were cured for 1 day, 7 days and 28 days under two curing conditions: steam curing and water curing. The steam cured specimens were exposed to two different pre-curing times (1.5 h and 2.5 h) and one steam curing duration (6 h) at 45 °C. The test results showed that water cured specimens revealed higher compressive strength than steam cured specimens at later ages. An increase in CfFA and GGBFS contents caused a decrease in the compressive strength of mortar. Ternary mixes exhibited better compressive strength than binary mixes containing CfFA with the same replacement ratio of mineral admixtures.
Abstract: The problem of soil stabilization has been one of the important issues in geotechnical engineering. Nowadays, nanomaterials have revolutionized many industries. In this research, improvement of the Kerman fine-grained soil by nanozeolite and nanobentonite additives separately has been investigated using Atterberg Limits and unconfined compression test. In unconfined compression test, the samples were prepared with 3, 5 and 7% nano additives, with 1, 7 and 28 days curing time with strain control method. Finally, the effect of different percentages of nanozeolite and nanobentonite on the geotechnical behavior and characteristics of Kerman fine-grained soil was investigated. The results showed that with increasing the amount of nanozeolite and also nanobentonite to fine-grained soil, the soil exhibits more compression strength. So that by adding 7% nanozeolite and nanobentonite with 1 day curing, the unconfined compression strength is 1.18 and 2.1 times higher than the unstabilized soil. In addition, the failure strain decreases in samples containing nanozeolite, whereas it increases in the presence of nanobentonite. Increasing the percentage of nanozeolite and nanobentonite also increased the elasticity modulus of soil.
Abstract: Improving the geotechnical properties of soil has always been one of the issues in geotechnical engineering. Traditional materials have been used to improve and stabilize soils to date, each with its own advantages and disadvantages. Although the soil stabilization by adding materials such as cement, lime, bitumen, etc. is one of the effective methods to improve the geotechnical properties of soil, but nanoparticles are one of the newest additives which can improve the loose soils. This research is intended to study the effect of adding nanobentonite on soil engineering properties, especially the unconfined compression strength and maximum dry unit weight, using clayey soil with low liquid limit (CL) from Kerman (Iran). Nanobentonite was mixed with soil in three different percentages (i.e. 3, 5, 7% by weight of the parent soil) with different curing time (1, 7 and 28 days). The unconfined compression strength, liquid and plastic limits and plasticity index of treated specimens were measured by unconfined compression and Atterberg limits test. It was found that increase in nanobentonite content resulted in increase in the unconfined compression strength, liquid and plastic limits of the clayey soil and reduce in plasticity index.
Abstract: This paper presents studies on the development and characterization of nanocomposites based on ethylene-propylene terpolymer rubber (EPDM), chlorobutyl rubber (IIR-Cl) and organically modified montmorillonite (OMMT). Mixtures were made containing 0, 3 and 6 phr (parts per 100 parts rubber) OMMT, respectively. They were obtained by melt intercalation in an internal mixer - Plasti-Corder Brabender, in suitable blending parameters, at high temperature for 11 minutes. Curing agents were embedded on a laboratory roller at 70-100 ºC, friction 1:1.1, processing time 5 minutes. Rubber specimens were obtained by compression, using a hydraulic press at 165 ºC and a pressing force of 300 kN. Curing time, determined using the Monsanto rheometer, decreases with the increased amount of OMMT in the mixtures. At the same time, it was noticed that mixtures containing OMMT show improvement in physical-mechanical properties. These types of nanocomposites may be used to obtain rubber seals for the space application or for other areas of application.
Abstract: The process of modification of ed-20 epoxy resin synthesized by vinyl-containing compounds is considered. It is shown that the introduction of vinyl-containing compounds into the composition based on epoxy resin ED-20 allows adjusting the technological and operational characteristics of the binder. For improvement of the properties of epoxy resin, following modifiers were selected: polyvinylformalethyl, polyvinyl butyral and composition of linear and aromatic amines (Аramine) as a hardener. Now the big range of hardeners of epoxy resins exists that allows varying technological properties of compositions, and also thermophysical and strength indicators. The nature of the aramin type hardener has a significant impact on the spatial parameters of the mesh, glass transition temperature, and strength characteristics. Epoxy composite materials based on ED-20 modified with polyvinyl butyral were obtained and investigated. It is shown that the composition of resins based on derivatives of polyvinyl butyral and ED-20 allows obtaining composite materials with a higher complex of deformation-strength, adhesion and thermal properties, better water resistance, frost resistance, chemical resistance, and impact strength. The magnitude of the effect depends on the chemical structure, temperature and curing time. In the area of concentrations, where the effect of composite synergy is appearing, the values of strength and stiffness significantly exceed the similar parameters of the individual components of the mixture. The polymer-polymer compositions form their class of materials with diverse specific properties that ensure their competitive application. Coatings with high performance under cyclic loading have been obtained based on epoxy oligomers modified with vinyl-containing compounds.
Abstract: Cold bitumen emulsion mixture (CBEM) offers a series benefits as compared with hot mix asphalt (HMA); these include environmental factors, energy saving, the resolution of logistical challenges that can characterise hot mix, and the potential to reserve funds. However, this mixture has some problems similar to any bituminous mixtures as it has low early strength, long curing time that needed to obtain the maximum performance, high air voids and considered inferior to HMA. Thus, CBEM has been used in limited applications such as lightly trafficked roads, footways and reinstatements. This laboratory study describes the development of CBEM using ordinary Portland cement (OPC) instead of the traditional mineral filler. Stiffness modulus, moisture damage and temperature sensitivity tests were used to evaluate the mechanical properties of the produced mixtures. The study concluded that there is a substantial improvement in the mechanical properties and moisture damage resistance of CBEMs containing OPC. Also, the produced cement modified CBEM shows a considerable lower thermal sensitivity than the conventional CBEM.
Abstract: Today, with developments in science and technology, there is an excessive potential for the use of nanomaterials in various fields of geotechnical project such as soil stabilization. This study investigates the effect of Nano-SiO2 solution on the unconfined compression strength and Young's elastic modulus of Kaolinite. For this purpose, nano-SiO2 was mixed with kaolinite in five different contents: 1, 2, 3, 4 and 5% by weight of the dry soil and a series of the unconfined compression test with curing time of one-day was selected as laboratory test. Analyses of the tests results show that stabilization of kaolinite with Nano-SiO2 solution can improve effectively the unconfined compression strength of modified soil up to 1.43 times compared to the pure soil.
Abstract: In this research, effect of curing time (TC), curing temperature (CT), sodium concentration (SC) and silicate modules (SM) on the compressive strength, chloride ion permeability, and water absorption capacity of alkali activated slag (AAS) concretes were investigated. For maximization of compressive strength while for minimization of chloride ion permeability and water absorption capacity of AAS concretes, best possible combination of CT, CTime, SC and SM were determined. An experimental program was conducted by using the central composite design method. Alkali solution-slag ratio was kept constant at 0.53 in all mixture. The effects of the independent parameters were characterized and analyzed by using statistically significant quadratic regression models on the measured properties (dependent parameters). The proposed regression models are valid for AAS concretes with the SC from 0.1% to 7.5%, SM from 0.4 to 3.2, CT from 20 °C to 94 °C and TC from 1.2 hours to 25 hours. The results of test and analysis indicate that the most effective parameter for the compressive strength, chloride ion permeability and water absorption capacity is the sodium concentration.
Abstract: During the interim storage or final disposal of low level waste, migration/diffusion of radionuclides can occur when the waste comes in contact with water. The long-term leaching behaviour into surrounding fluid (demineralized water) of 137Cs, 60Co and 152Eu radionuclides, artificially incorporated in mortar matrices made from natural aggregates (river sand) and recycled radioactive concrete was studied. Results presented in this work are obtained in two years of mortar testing and will be used for the safety increasing in the storage of low level radioactive waste. The study involved the influence of curing time, type and size distribution of the aggregates on leaching behaviour. The mortar samples were immersed in distilled water for 30 days. The leached activity of the mortar samples was measured on samples from the immersing water and analyzed through a gamma-ray spectrometry method using an HPGe detector with a GESPECOR code for efficiency evaluation. The long-term leaching behaviour of the radionuclides was evaluated from the leaching data calculating the apparent diffusion coefficient.
Abstract: Cement utilization to improve the properties of soil is a well-known method applied in field. However, its addition in large quantity must be controlled. This study presents utilization of natural and environmental-friendly material mixed with small amount of cement content in soil improvement, i.e. bamboo chips. Absorbability, elongation, and flatness ratio of bamboo chips were examined to investigate and understand the influence of its characteristics in the mixture. Improvement of dilation behavior as a problem of loose and poorly graded sand soil is discussed. Bamboo chips are able to improve the permeability value that affects the dilation behavior of cemented sand soil. It is proved by the stress path as the result of triaxial compression test in the undrained condition. The effect of size and content variation of bamboo chips, as well as the curing time variation are presented and discussed.
Abstract: During the past two decades, photoinitiated polymerization has been attracting a great interest in terms of scientific and industrial activity. The wide recognition of UV treatment in the polymer industry results not only from its many practical applications but also from its advantage for low-cost processes. Unlike most thermal curing systems, radiation-curable systems can polymerize at room temperature without additional heat, and the curing is completed in a very short time. The advantage of cationic UV technology is that post-cure can continue in the ‘dark’ after radiation. In this study, bio-based acrylated epoxidized soybean oil (AESO) was cured with UV radiation using radicalic photoinitiator Irgacure 184. Triarylsulphonium hexafluoroantimonate was used as cationic photoinitiator for curing of 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate. The effect of curing time and the amount of initiators on the curing degree and thermal properties were investigated. The thermal properties of the coating were analyzed after crosslinking UV irradiation. The level of crosslinking in the coating was evaluated by FTIR analysis. Cationic UV-cured coatings demonstrated excellent adhesion and corrosion resistance properties. Therefore, our study holds a great potential with its simple and low-cost applications.
Abstract: Concrete is strong in compression however weak in
tension. The tensile strength as well as ductile property of concrete
could be improved by addition of short dispersed fibers. Polyethylene
terephthalate (PET) fiber obtained from hand cutting or mechanical
slitting of plastic sheets generally used as discrete reinforcement in
substitution of steel fiber. PET fiber obtained from the former process
is in the form of straight slit sheet pattern that impart weaker
mechanical bonding behavior in the concrete matrix. To improve the
limitation of straight slit sheet fiber the present study considered two
additional geometry of fiber namely (a) flattened end slit sheet and
(b) deformed slit sheet. The mix for plain concrete was design for a
compressive strength of 25 MPa at 28 days curing time with a watercement
ratio of 0.5. Cylindrical and beam specimens with 0.5% fibers
volume fraction and without fibers were cast to investigate the
influence of geometry on the mechanical properties of concrete. The
performance parameters mainly studied include flexural strength,
splitting tensile strength, compressive strength and ultrasonic pulse
velocity (UPV). Test results show that geometry of fiber has a
marginal effect on the workability of concrete. However, it plays a
significant role in achieving a good compressive and tensile strength
of concrete. Further, significant improvement in term of flexural and
energy dissipation capacity were observed from other fibers as
compared to the straight slit sheet pattern. Also, the inclusion of PET
fiber improved the ability in absorbing energy in the post-cracking
state of the specimen as well as no significant porous structures.
Abstract: The outstanding mechanical properties of Carbon
nanotubes (CNTs) have generated great interest for their potential as
reinforcements in high performance cementitious composites. The
main challenge in research is the proper dispersion of carbon
nanotubes in the cement matrix. The present work discusses the role
of dispersion of multiwalled carbon nanotubes (MWCNTs) on the
compressive strength characteristics of hydrated Portland IS 1489
cement paste. Cement-MWCNT composites with different mixing
techniques were prepared by adding 0.2% (by weight) of MWCNTs
to Portland IS 1489 cement. Rectangle specimens of size
approximately 40mm × 40mm ×160mm were prepared and curing of
samples was done for 7, 14, 28 and 35days. An appreciable increase
in compressive strength with both techniques; mixture of MWCNTs
with cement in powder form and mixture of MWCNTs with cement
in hydrated form 7 to 28 days of curing time for all the samples was
observed.
Abstract: Many studies have been conducted on DC transmission. Of power apparatus for DC transmission, high voltage direct current (HVDC) cable systems are being evaluated because of the increase in power demand and transmission distance. Therefore, dc insulation characteristics of liquid silicone rubber (LSR), which has various advantages such as short curing time and the ease of maintenance, were investigated to assess its performance as a HVDC insulation material for cable joints. The electrical performance of LSR added to nano-aluminum trihydrate (ATH) were confirmed by measurements of the breakdown strength and electrical conductivity. In addition, field emission scanning electron microscope (FE-SEM) was used as a means of confirmation of nanofiller dispersion state. The LSR nanocomposite was prepared by compounding LSR filled nano-sized ATH filler. The dc insulation properties of LSR added to nano-sized ATH fillers were found to be superior to those of the LSR without a filler.
Abstract: Influences of the amount of phenolic, curing temperature and curing time on the Mechanical Properties of phenolic/fiber composite were investigated by using two-level factorial design. The latter was used to determine the affects of those factors on mechanical properties. The purpose of this study was to investigate the affects of amount of phenolic, curing temperature and curing time of the composite to determine the best condition for mechanical properties according to MIL-I-24768 by the tensile strength is more than 103 MPa.
Abstract: This paper reports the results of an experimental work
conducted to investigate the effect of curing conditions on the
compressive strength of self-compacting geopolymer concrete
prepared by using fly ash as base material and combination of sodium
hydroxide and sodium silicate as alkaline activator. The experiments
were conducted by varying the curing time and curing temperature in
the range of 24-96 hours and 60-90°C respectively. The essential
workability properties of freshly prepared Self-compacting
Geopolymer concrete such as filling ability, passing ability and
segregation resistance were evaluated by using Slump flow,
V-funnel, L-box and J-ring test methods. The fundamental
requirements of high flowability and resistance to segregation as
specified by guidelines on Self-compacting Concrete by EFNARC
were satisfied. Test results indicate that longer curing time and curing
the concrete specimens at higher temperatures result in higher
compressive strength. There was increase in compressive strength
with the increase in curing time; however increase in compressive
strength after 48 hours was not significant. Concrete specimens cured
at 70°C produced the highest compressive strength as compared to
specimens cured at 60°C, 80°C and 90°C.
Abstract: Due to growing environmental concerns of the cement
industry, alternative cement technologies have become an area of
increasing interest. It is now believed that new binders are
indispensable for enhanced environmental and durability
performance. Self-compacting Geopolymer concrete is an innovative
method and improved way of concreting operation that does not
require vibration for placing it and is produced by complete
elimination of ordinary Portland cement.
This paper documents the assessment of the compressive strength
and workability characteristics of low-calcium fly ash based selfcompacting
geopolymer concrete. The essential workability
properties of the freshly prepared Self-compacting Geopolymer
concrete such as filling ability, passing ability and segregation
resistance were evaluated by using Slump flow, V-funnel, L-box and
J-ring test methods. The fundamental requirements of high
flowability and segregation resistance as specified by guidelines on
Self Compacting Concrete by EFNARC were satisfied. In addition,
compressive strength was determined and the test results are included
here. This paper also reports the effect of extra water, curing time and
curing temperature on the compressive strength of self-compacting
geopolymer concrete. The test results show that extra water in the
concrete mix plays a significant role. Also, longer curing time and
curing the concrete specimens at higher temperatures will result in
higher compressive strength.
Abstract: Cement stabilization has been widely used for
improving the strength and stiffness of soft clayey soils. Cement
treated soil specimens used to investigate the stress-strain behaviour in
the laboratory study are usually cured for 7 days. This paper examines
the effects of curing time on the strength and stress strain behaviour of
cement treated marine clay under triaxial loading condition.
Laboratory-prepared cement treated Singapore marine clay with
different mix proportion S-C-W (soil solid-cement solid-water) and
curing time (7 days to 180 days) was investigated through conducting
unconfined compressive strength test and triaxial test. The results
show that the curing time has a significant effect on the unconfined
compressive strength u q , isotropic compression behaviour and stress
strain behaviour. Although the primary yield loci of the cement treated
soil specimens with the same mix proportion expand with curing time,
they are very narrowly banded and have nearly the same shape after
being normalized by isotropic compression primary stress '
py p . The
isotropic compression primary yield stress '
py p was shown to be
linearly related to unconfined compressive strength u q for specimens
with different curing time and mix proportion. The effect of curing
time on the hardening behaviour will diminish with consolidation
stress higher than isotropic compression primary yield stress but its
damping rate is dependent on the cement content.
Abstract: This study demonstrates the use of Class F fly ash in
combination with lime or lime kiln dust in the full depth reclamation
(FDR) of asphalt pavements. FDR, in the context of this paper, is a
process of pulverizing a predetermined amount of flexible pavement
that is structurally deficient, blending it with chemical additives and
water, and compacting it in place to construct a new stabilized base
course. Test sections of two structurally deficient asphalt pavements
were reclaimed using Class F fly ash in combination with lime and
lime kiln dust. In addition, control sections were constructed using
cement, cement and emulsion, lime kiln dust and emulsion, and mill
and fill. The service performance and structural behavior of the FDR
pavement test sections were monitored to determine how the fly ash
sections compared to other more traditional pavement rehabilitation
techniques. Service performance and structural behavior were
determined with the use of sensors embedded in the road and Falling
Weight Deflectometer (FWD) tests. Monitoring results of the FWD
tests conducted up to 2 years after reclamation show that the cement,
fly ash+LKD, and fly ash+lime sections exhibited two year resilient
modulus values comparable to open graded cement stabilized
aggregates (more than 750 ksi). The cement treatment resulted in a
significant increase in resilient modulus within 3 weeks of
construction and beyond this curing time, the stiffness increase was
slow. On the other hand, the fly ash+LKD and fly ash+lime test
sections indicated slower shorter-term increase in stiffness. The fly
ash+LKD and fly ash+lime section average resilient modulus values
at two years after construction were in excess of 800 ksi. Additional
longer-term testing data will be available from ongoing pavement
performance and environmental condition data collection at the two
pavement sites.