Effect of Curing Conditions on Strength of Fly ash-based Self-Compacting Geopolymer Concrete

This paper reports the results of an experimental work conducted to investigate the effect of curing conditions on the compressive strength of self-compacting geopolymer concrete prepared by using fly ash as base material and combination of sodium hydroxide and sodium silicate as alkaline activator. The experiments were conducted by varying the curing time and curing temperature in the range of 24-96 hours and 60-90°C respectively. The essential workability properties of freshly prepared Self-compacting Geopolymer concrete such as filling ability, passing ability and segregation resistance were evaluated by using Slump flow, V-funnel, L-box and J-ring test methods. The fundamental requirements of high flowability and resistance to segregation as specified by guidelines on Self-compacting Concrete by EFNARC were satisfied. Test results indicate that longer curing time and curing the concrete specimens at higher temperatures result in higher compressive strength. There was increase in compressive strength with the increase in curing time; however increase in compressive strength after 48 hours was not significant. Concrete specimens cured at 70°C produced the highest compressive strength as compared to specimens cured at 60°C, 80°C and 90°C.

Authors:

• Fareed Ahmed Memon
• Muhd Fadhil Nuruddin
• Samuel Demie
• Nasir Shafiq

Keywords:

• Geopolymer Concrete
• Self-compacting Geopolymerconcrete
• Compressive strength
• Curing time
• Curing temperature

References:

[1] D. Hardjito, and B. V. Rangan, "Development and Properties of Low-
Calcium Fly ash based Geopolymer Concrete", Research report GC-1,
Faculty of Engineering, Curtin University of Technology, Perth,
Australia, 2005.
[2] B. V. Rangan, D. Hardjito, S. E. Wallah, and D. M. J. Sumajouw,
"Studies on fly ash-based geopolymer concrete, Geopolymer: green
chemistry and sustainable development solutions", Faculty of
Engineering and Computing, Curtin University of Technology, GPO
Box U 1987, Perth 6845, Australia, pp. 133-138.
[3] F. Puertas, S. Martinez-Ramirez, A. Alonso, T. Vasquez, "Alkaliactivated
fly ash/slag cements: strength behaviour and hydration
products", Cement and Concrete Research, 30 (10): 2000, pp. 1625-
1632.
[4] A. Palomo, M. W. Grutzeck, M. T. Blanco, "Alkali-activated fly ashes
- A cement for the future", Cement and Concrete Research, 29 (8):
1999, pp. 1323-1329.
[5] J. C. Swanepoel, C. A. Strydom, "Utilisation of fly ash in a
geopolymeric material", Applied Geochemistry, 17 (8): 2002, pp. 1143-
1148.
[6] T. Bakharev, "Geopolymeric materials prepared using Class F fly ash
and elevated temperature curing", Cement and Concrete Research, 35
(6): 2005, pp. 1224-1232.
[7] J. G. S. van Jaarsveld, J. S. J. van Deventer, and G. C. Lukey, "The
Effect of Composition and Temperature on the Properties of Fly Ash
and Kaolinite-based Geopolymers", Chemical Engineering Journal, 89
(1-3): 2002, pp. 63-73.
[8] P. Chindaprasirt, T. Chareerat, V. Sirivivatnanon, "Workability and
strength of coarse high calcium fly ash geopolymer", Cement &
Concrete Composites, 29 (3): 2007, pp. 224-229.
[9] Xiaolu Guo, Huisheng Shi, Warren A. Dick, "Compressive strength and
microstructural characteristics of class C fly ash geopolymer", Cement
& Concrete Composites, 32 (2010), pp. 142-147.
[10] P. Rovnanik, "Effect of curing temperature on the development of hard
structure of metakaolin-based geopolymer", Construction and Building
Materials, 24 (2010), pp. 1176-1183.
[11] EFNARC, "Specification and Guidelines for Self-Compacting
Concrete", February 2002.
[12] K. Komnitas, D. Zaharaki, "Geopolymerisation: a review and prospects
for the minerals industry", Mineral Engineering, 20 (2007), pp. 1261-
1277.
[13] D. Hardjito, S. E. Wallah, D. M. J. Sumajouw, and B. V. Rangan,
"Factors Influencing the Compressive Strength of Fly ash-Based
Geopolymer Concrete", Civil Engineering Dimension, Vol. 6, No. 2,
88-93, September 2004, ISSN 1410-9530.
[14] Djwantoro Hardjito, Chua Chung Cheak, and Carrie Ho Lee Ing,
"Strength and Setting Times of Low Calcium Fly Ash-based
Geopolymer Mortar", Modern Applied Science, 2 (4): 2008, pp. 3-11.
[15] D. Hardjito, S. E. Wallah, D. M. J. Sumajouw, and B. V. Rangan, "Fly
ash-based geopolymer concrete", Australian Journal of Structural
Engineering, Vol 6, No.1, 2005, pp. 1-9.