Abstract: The compressive strength development through
polymerization process of alkaline solution and fly ash blended with Microwave Incinerated Rice Husk Ash (MIRHA) is described in this
paper. Three curing conditions, which are hot gunny curing, ambient
curing, and external humidity curing are investigated to obtain the suitable curing condition for cast in situ provision. Fly ash was
blended with MIRHA at 3%, 5%, and 7% to identify the effect of blended mixes to the compressive strength and microstructure
properties of geopolymer concrete. Compressive strength results
indicated an improvement in the strength development with external humidity curing concrete samples compared to hot gunny curing and
ambient curing. Blended mixes also presented better performance
than control mixes. Improvement of interfacial transition zone (ITZ)
and micro structure in external humidity concrete samples were also
identified compared to hot gunny and ambient curing.
Abstract: This paper reports the results of an experimental work
conducted to investigate the effect of curing conditions on the
compressive strength of self-compacting geopolymer concrete
prepared by using fly ash as base material and combination of sodium
hydroxide and sodium silicate as alkaline activator. The experiments
were conducted by varying the curing time and curing temperature in
the range of 24-96 hours and 60-90°C respectively. The essential
workability properties of freshly prepared Self-compacting
Geopolymer concrete such as filling ability, passing ability and
segregation resistance were evaluated by using Slump flow,
V-funnel, L-box and J-ring test methods. The fundamental
requirements of high flowability and resistance to segregation as
specified by guidelines on Self-compacting Concrete by EFNARC
were satisfied. Test results indicate that longer curing time and curing
the concrete specimens at higher temperatures result in higher
compressive strength. There was increase in compressive strength
with the increase in curing time; however increase in compressive
strength after 48 hours was not significant. Concrete specimens cured
at 70°C produced the highest compressive strength as compared to
specimens cured at 60°C, 80°C and 90°C.