Abstract: This paper is aimed to the use of different types of
industrial wastes in concrete production. From examined waste
(crushed concrete waste) our tested concrete samples with dimension
150 mm were prepared. In these samples, fractions 4/8 mm and 8/16
mm by recycled concrete aggregate with a range of variation from 0
to 100% were replaced. Experiment samples were tested for
compressive strength after 2, 7, 14 and 28 days of hardening.
From obtained results it is evident that all samples prepared with
washed recycled concrete aggregates met the requirement of standard
for compressive strength of 20 MPa already after 14 days of
hardening. Sample prepared with recycled concrete aggregates (4/8
mm: 100% and 8/16 mm: 60%) reached 101% of compressive
strength value (34.7 MPa) after 28 days of hardening in comparison
with the reference sample (34.4 MPa). The lowest strength after 28
days of hardening (27.42 MPa) was obtained for sample consisting of
recycled concrete in proportion of 40% for 4/8 fraction and 100% for
8/16 fraction of recycled concrete.
Abstract: In recent years demolished concrete waste handling and management is the new primary challenging issue faced by the countries all over the world. It is very challenging and hectic problem that has to be tackled in an indigenous manner, it is desirable to completely recycle demolished concrete waste in order to protect natural resources and reduce environmental pollution. In this research paper an experimental study is carried out to investigate the feasibility and recycling of demolished waste concrete for new construction. The present investigation to be focused on recycling demolished waste materials in order to reduce construction cost and resolving housing problems faced by the low income communities of the world. The crushed demolished concrete wastes is segregated by sieving to obtain required sizes of aggregate, several tests were conducted to determine the aggregate properties before recycling it into new concrete. This research shows that the recycled aggregate that are obtained from site make good quality concrete. The compressive strength test results of partial replacement and full recycled aggregate concrete and are found to be higher than the compressive strength of normal concrete with new aggregate.