Effect of Adding Sawdust on Mechanical- Physical Properties of Ceramic Bricks to Obtain Lightweight Building Material

This paper studies the application of a variety of sawdust materials in the production of lightweight insulating bricks. First, the mineralogical and chemical composition of clays was determined. Next, ceramic bricks were fabricated with different quantities of materials (3–6 and 9 wt. % for sawdust, 65 wt. % for grey clay, 24–27 and 30 wt. % for yellow clay and 2 wt% of tuff). These bricks were fired at 800 and 950 °C. The effect of adding this sawdust on the technological behaviour of the brick was assessed by drying and firing shrinkage, water absorption, porosity, bulk density and compressive strength. The results have shown that the optimum sintering temperature is 950 °C. Below this temperature, at 950 °C, increased open porosity was observed, which decreased the compressive strength of the bricks. Based on the results obtained, the optimum amounts of waste were 9 wt. % sawdust of eucalyptus, 24 wt. % shaping moisture and 1.6 particle size diameter. These percentages produced bricks whose mechanical properties were suitable for use as secondary raw materials in ceramic brick production.

Authors:

• Bachir Chemani
• Halima Chemani

Keywords:

• Clay brick
• Porosity
• Sawdust.

References:

[1] A.U. Elinwa, YA Mahmood. "Ash from timber waste as cement replacement material", Cement and Concrete Composites, vol.24, n┬░. 2, pp. 219-222, 2002.
[2] F.F. Udoeyo, PU. Dashibil, "Sawdust ash as concrete material", ASCE,
0899-1561; vol.14, n┬░.2, pp. 173-176, 2002.
[3] P.Turgut, B.Yesilata, "Physico-mechanical and thermal performances of
newly developed rubber-added bricks", Energy and Buildings, vol. 40,
pp. 679-688, 2008.
[4] P.Turgut, H.M. Algin, "Limestone dust and wood sawdust as brick
material", Building and Environment, vol. 2, pp. 3399-3403, 2006.
[5] I. Demir, "An investigation on the production of construction brick with
processed waste tea", Building and Environment, vol. 41, pp. 1274-
1278, 2005.
[6] O. Kayali, "High performance bricks from fly ash", Proceedings of the
World of Coal Ash Conference, Lexinton, Kentucky, 2005.
[7] K. L. Lin, "Feasibility study of using brick made from municipal solid
waste incinerator fly ash slag". Journal of Hazardous Materials vol.137,
pp.1810-1816, 2006.
[8] S. Veiseh, A. A Yousefi, "The use of polystyrene in lightweight brick
production", Iranian Polymer Journal, vol. 12, no. 4, pp. 324-329, 2003.
[9] T. Basegio, F. Berutti, A. Bernades, C. P. Bergmann, "Environmental
and technical aspects of the utilization of tannery sludge as a raw
material for clay products", Journal of the European Ceramic Society,
vol.22, pp.2251-2259, 2002.
[10] M. Dondi, M. Marsigli, B. Fabbri, "Recycling of industrial and urban
wastes in brick production "- a review. Tile and Brick International 13
(1), 218-225. 1997.
[11] S. Horisawa, M. Sunagawa, Y. Tamai, Y. Matsuoka, T. Tohru Miura, M.
Terazawa,"Biodegradation of nonlignocellulosic substances I1: physical
and chemical properties of sawdust before and after use as artificial soil", Journal of Wood Science, vol. 45, pp. 492-497, 1999
[12] V. Ducman, T. Kopar,"Sawdust and paper-making sludge as
poreforming agents for lightweight clay bricks source." Industrial
Ceramics, vol. 21, n┬░. 2, pp. 81-86, 2001
[13] R Sheyder, Les p├ótes et les gla├ºures Céramiques. Ecole Suisse de
Céramique, 1970
[14] J. Rigaut, "La cuisson des matières premières et des p├ótes céramiques",
Industrie Céramique n┬░. 685, pp. 685-697. Juillet 1975
[15] M. Randall. " Sintering theory and practice", John Willey and Sons, Inc.
New York, 1996, pp. 209- 213.
[16] J. Peyssou, "Industries céramique ", n┬░. 661, pp. 255-261, 377-383,1973.