Fabrication of Single Crystal of Mg Alloys Containing Rare Earth Elements

Single crystals of Magnesium alloys such as Mg-1Al, Mg-1Zn-0.5Y, Mg-3Li, and AZ31 alloys were successfully fabricated in this study by employing the modified Bridgman method. Single crystals of pure Mg were also made in this study. To determine the exact orientation of crystals, Laue back-reflection method and pole figure measurement were carried out on each single crystal. Dimensions of single crystals were 10 mm in diameter and 120 mm in length. Hardness and compression tests were conducted and the results revealed that hardness and the strength strongly depended on the orientation. The closer to basal one the orientation was, the higher hardness and compressive strength were. The effect of alloying was not higher than that of orientation. After compressive deformation of single crystals, the orientation of the crystals was found to rotate and to be parallel to the basal orientation.

Authors:

• Joon Ho Kim
• Tae Kwon Ha

Keywords:

• Compressive strength
• Hardness
• Mg alloys
• Modified Bridgman method
• Orientation
• Pole figure
• Single crystal.

References:

1] O. W. Qiu, E-H. Han, L. Liu: Trans. Nonferrous Met. Soc. China Vol. 20 (2010), p. 481.
[2] S.M.Masoudpanah, R. Mahmudi: Mater. Sci. & Eng. A, Vol.526 (2009),p. 22.
[3] Y. Wang, S. Guan, X. Zeng, W. Ding: Mater. Sci. & Eng. A, Vol.416 (2006), 109.
[4] M.R. Barnett, M.D. Nave, C.J. Bettles: Mater. Sci. & Eng. A, Vol.386 (2004), p. 205.
[5] E. Schmid: Z. Elektrochem, Vol. 37 (1931), p.447.
[6] A. Beck: The technology of Magnesium and its Alloys, Huges, London, (1940), p. 22.
[7] N.-J. Park, S.-H. Han: Kor. J. Met. Mater. Vol.48 (2010), pp. 498-505.