Abstract: The accomplished study is based on the appointment
and identification of ageing effects and according to this absorption
of moisture of aircraft cabin components over the life-cycle. In the
first step of the study ceiling panels from same age and from the
same aircraft cabin have been examined according to weight changes
depending on the position in the aircraft cabin. In the second step of
the study different aged ceiling panels have been examined
concerning deflection, weight changes and the acoustic sound
transmission loss. To prove the assumption of water absorption
within the study and with the theoretical background from literature
and scientific papers, an older test panel was exposed extreme
thermal conditions (humidity and temperature) within a climate
chamber to show that there is a general ingress of water to cabin
components and that this ingress of water leads to the change of
different mechanical properties.
Abstract: The aluminum bronze matrix alumina composites using hot press and resin infiltration were investigated to study their porosities, hardness, bending strengths, and microstructures. The experiment results show that the hardness of the sintered composites with the decrease of porosity increases. The composites without and with resin infiltration have about HRF 42-61 of about 34-40% of porosity and about HRF 62-83 of about 30-36% of porosity, respectively. Besides, the alumina composites contain a more amount of iron and nickel powders would cause a lower bending strength due to forming some weaker bonding among the iron, nickel, copper, aluminum under this hot pressing of shorter time.
Abstract: In recent five decades, textured yarns of polyester fiber produced by false twist method are the most
important and mass-produced manmade fibers. There are
many parameters of cross section which affect the physical and mechanical properties of textured yarns. These parameters
are surface area, perimeter, equivalent diameter, large
diameter, small diameter, convexity, stiffness, eccentricity, and hydraulic diameter. These parameters were evaluated by
digital image processing techniques. To find trends between production criteria and evaluated parameters of cross section, three criteria of production line have been adjusted and different types of yarns were produced. These criteria are
temperature, drafting ratio, and D/Y ratio. Finally the relations between production criteria and cross section parameters were
considered. The results showed that the presented technique can recognize and measure the parameters of fiber cross section in acceptable accuracy. Also, the optimum condition
of adjustments has been estimated from results of image analysis evaluation.
Abstract: The mechanical properties of blends consisting of
plasticized poly(vinyl butyral) (PVB) and plasticized poly(vinyl
chloride) (PVC) are studied, in order to evaluate the possibility of
using recycled PVB waste derived from windshields. PVC was
plasticized with 38% of diisononyl phthalate (DINP), while PVB was
plasticized with 28% of triethylene glycol, bis(2-ethylhexanoate)
(3GO). The optimal process conditions for the PVB/PVC blend in 1:1
ratio were determined. Entropy was used in order to theoretically
predict the blends miscibility. The PVB content of each blend
composition used was ranging from zero to 100%. Tensile strength
and strain were tested. In addition, a comparison between recycled
and original PVB, used as constituents of the blend, was performed.
Abstract: Polylactic acid-g-polyvinyl acetate (PLLA-g-PVAc)
was used as a compatibilizer for 50/50 starch/PLLA blend. PLLA-g-
PVAc with different mol% of PVAc contents were prepared by
grafting PVAc onto PLLA backbone via free radical polymerization
in solution process. Various conditions such as type and the amount
of initiator, monomer concentration, polymerization time and
temperature were studied. Results showed that the highest mol% of
PVAc grafting (16 mol%) was achieved by conducting graft
copolymerization in toluene at 110°C for 10 h using DCP as an
initiator. Chemical structure of the PVAc grafted PLLA was
confirmed by 1H NMR. Blending of modified starch and PLLA in the
presence compatibilizer with different amounts and mol% PVAc was
acquired using internal mixer at 160°C for 15 min. Effects of PVAc
content and the amount of compatibilizer on mechanical properties of
polymer blend were studied. Results revealed that tensile strength and
tensile modulus of polymer blend with higher PVAc grafting content
compatibilizer showed better properties than that of lower PVAc
grafting content compatibilizer. The amount of compatibilizer was
found optimized in the range of 0.5-1.0 Wt% depending on the mol%
PVAc.
Abstract: Martensitic stainless steels have been extensively used for their good corrosion resistance and better mechanical properties. Heat treatment was suggested as one of the most excellent ways to this regard; hence, it affects the microstructure, mechanical and corrosion properties of the steel. In the current research work the microstructural changes and corrosion behavior in an AISI 420A stainless steel exposed to temperatures in the 980-1035oC range were investigated. The heat treatment is carried out in vacuum furnace within the said temperature range. The quenching of the samples was carried out in oil, brine and water media. The formation and stability of passive film was studied by Open Circuit Potential, Potentiodynamic polarization and Electrochemical Scratch Tests. The Electrochemical Impedance Spectroscopy results simulated with Equivalent Electrical Circuit suggested bilayer structure of outer porous and inner barrier oxide films. The quantitative data showed thick inner barrier oxide film retarded electrochemical reactions. Micrographs of the quenched samples showed sigma and chromium carbide phases which prove the corrosion resistance of steel alloy.
Abstract: The nanofiber sheet of Multiwall Cabon Nanotube
(MWCNTs)/Polyacylonitile (PAN) composites was fabricated from
electrospun nanofiber. Firstly the surface of MWCNTs was
chemically modified, comparing two different techniques consisting
of admicellar polymerization and functionalization to improve the
dispersion and prevent the aggregation in the PAN matrix. The
modified MWCNTs were characterized by the dispersion in
dimethylformamide (DMF) solvent, Laser particle size, and FTRaman.
Lastly, DSC, SEM and mechanical properties of the
nanofiber sheet were examined. The results show that the mechanical
properties of the nanofiber sheet prepared from admicellar
polymerization-modified MWCNTs were higher than those of the
others.
Abstract: The mechanical properties including flexural and
tensile of neat vinyl ester and polymer based on layered silicate
nanocomposite materials are discussed. The addition of layered
silicate into the polymer matrix increased the tensile and flexural
modulus up to 1 wt.% clay loading. The incorporation of more clay
resulted in decreasing the mechanical properties which was traced to
the existence of aggregation layers. Likewise, up to 1 wt.% clay
loading, the thermal behaviour showed significant improvements and
at higher clay loading the thermal pattern was reduced. The
aggregation layers imparted a negative impact on the overall
mechanical and thermal properties. Wide Angle X-ray Diffraction,
Scanning Electron Microscopy and Transmission Electron
Microscopy were utilised in order to characterise the interlamellar
structure of nanocomposites.
Abstract: Nowadays, engineering ceramics have significant
applications in different industries such as; automotive, aerospace,
electrical, electronics and even martial industries due to their
attractive physical and mechanical properties like very high hardness
and strength at elevated temperatures, chemical stability, low friction
and high wear resistance. However, these interesting properties plus
low heat conductivity make their machining processes too hard,
costly and time consuming. Many attempts have been made in order
to make the grinding process of engineering ceramics easier and
many scientists have tried to find proper techniques to economize
ceramics' machining processes. This paper proposes a new diamond
plunge grinding technique using ultrasonic vibration for grinding
Alumina ceramic (Al2O3). For this purpose, a set of laboratory
equipments have been designed and simulated using Finite Element
Method (FEM) and constructed in order to be used in various
measurements. The results obtained have been compared with the
conventional plunge grinding process without ultrasonic vibration
and indicated that the surface roughness and fracture strength
improved and the grinding forces decreased.
Abstract: The main aim of this research is to study the possible
use of recycled fine aggregate made from waste rubble wall to
substitute partially for the natural sand used in the production of
cement and sand bricks. The bricks specimens were prepared by
using 100% natural sand; they were then replaced by recycled fine
aggregate at 25, 50, 75, and 100% by weight of natural sand. A series
of tests was carried out to study the effect of using recycled aggregate
on the physical and mechanical properties of bricks, such as density,
drying shrinkage, water absorption characteristic, compressive and
flexural strength. Test results indicate that it is possible to
manufacture bricks containing recycled fine aggregate with good
characteristics that are similar in physical and mechanical properties
to those of bricks with natural aggregate, provided that the percentage
of recycled fine aggregates is limited up to 50-75%.
Abstract: Multifunctional structures are a potentially disruptive
technology that allows for significant mass savings on spacecraft.
The specific concept addressed herein is that of a multifunctional
power structure. In this paper, a parametric optimisation of the
design of such a structure that uses commercially available battery
cells is presented. Using numerical modelling, it was found that there
exists several trade-offs aboutthe conflict between the capacity of the
panel and its mechanical properties. It was found that there is no
universal optimal location for the cells. Placing them close to the
mechanical interfaces increases loading in the mechanically weak
cells whereas placing them at the centre of the panel increases the
stress inthe panel and reduces the stiffness of the structure.
Abstract: Environmental awareness and depletion of the
petroleum resources are among vital factors that motivate a number
of researchers to explore the potential of reusing natural fiber as an
alternative composite material in industries such as packaging,
automotive and building constructions. Natural fibers are available in
abundance, low cost, lightweight polymer composite and most
importance its biodegradability features, which often called “ecofriendly"
materials. However, their applications are still limited due
to several factors like moisture absorption, poor wettability and large
scattering in mechanical properties. Among the main challenges on
natural fibers reinforced matrices composite is their inclination to
entangle and form fibers agglomerates during processing due to
fiber-fiber interaction. This tends to prevent better dispersion of the
fibers into the matrix, resulting in poor interfacial adhesion between
the hydrophobic matrix and the hydrophilic reinforced natural fiber.
Therefore, to overcome this challenge, fiber treatment process is one
common alternative that can be use to modify the fiber surface
topology by chemically, physically or mechanically technique.
Nevertheless, this paper attempt to focus on the effect of
mercerization treatment on mechanical properties enhancement of
natural fiber reinforced composite or so-called bio composite. It
specifically discussed on mercerization parameters, and natural fiber
reinforced composite mechanical properties enhancement.
Abstract: This current research focused on development of degradable starch based packaging film with enhanced mechanical properties. A series of low density polyethylene (LDPE)/tapioca starch compounds with various tapioca starch contents were prepared by twin screw extrusion with the addition of maleic anhydride grafted polyethylene as compatibilizer. Palm cooking oil was used as processing aid to ease the blown film process, thus, degradable film can be processed via conventional blown film machine. Studies on their characteristics, mechanical properties and biodegradation were carried out by Fourier Transform Infrared (FTIR) spectroscopy and optical properties, tensile test and exposure to fungi environment respectively. The presence of high starch contents had an adverse effect on the tensile properties of LDPE/tapioca starch blends. However, the addition of compatibilizer to the blends improved the interfacial adhesion between the two materials, hence, improved the tensile properties of the films. High content of starch amount also was found to increase the rate of biodegradability of LDPE/tapioca starch films. It can be proved by exposure of the film to fungi environment. A growth of microbes colony can be seen on the surface of LDPE/tapioca starch film indicates that the granular starch present on the surface of the polymer film is attacked by microorganisms, until most of it is assimilated as a carbon source.
Abstract: Properties of cement pastes with fine-ground ceramics
used as an alternative binder replacing Portland cement up to 20% of
its mass are investigated. At first, the particle size distribution of
cement and fine-ground ceramics is measured using laser analyser.
Then, the material properties are studied in the early hardening
period up to 28 days. The hydration process of studied materials is
monitored by electrical conductivity measurement using TDR
sensors. The changes of materials- structures within the hardening are
observed using pore size distribution measurement. The compressive
strength measurements are done as well. Experimental results show
that the replacement of Portland cement by fine-ground ceramics in
the amount of up to 20% by mass is acceptable solution from the
mechanical point of view. One can also assume similar physical
properties of designed materials to the reference material with only
Portland cement as binder.
Abstract: In spite of the advent of new materials, clay bricks
remain, arguably, the most popular construction materials today.
Nevertheless the low cost and versatility of clay bricks cannot always
be associated with high environmental and sustainable values,
especially in terms of raw material sources and manufacturing
processes. At the same time, the worldwide agricultural footprint is
fast growing, with vast agricultural land cultivation and active
expansion of the agro-based industry. The resulting large quantities of
agricultural wastes, unfortunately, are not always well managed or
utilised. These wastes can be recycled, such as by retrieving fibres
from disposed leaves and fruit bunches, and then incorporated in
brick-making. This way the clay bricks are made a 'greener' building
material and the discarded natural wastes can be reutilised, avoiding
otherwise wasteful landfill and harmful open incineration. This study
examined the physical and mechanical properties of clay bricks made
by adding two natural fibres to a clay-water mixture, with baked and
non-baked conditions. The fibres were sourced from pineapple leaves
(PF) and oil palm fruit bunch (OF), and added within the range of
0.25-0.75 %. Cement was added as a binder to the mixture at 5-15 %.
Although the two fibres had different effects on the bricks produced,
cement appeared to dominate the compressive strength. The
non-baked bricks disintegrated when submerged in water, while the
baked ones displayed cement-dependent characteristics in
water-absorption and density changes. Interestingly, further increase
in fibre content did not cause significant density decrease in both the
baked and non-baked bricks.
Abstract: The use of additions in cement in manufacturing,
mortar and concrete offers economic and ecological advantages. Cements with additions such as limestone, slag and natural
pouzzolana are produced in cement factories in Algeria. Several studies analyzed the effect of these additions on the physical and
mechanical properties as well as the durability of concrete. However,
few studies were conducted on the effect of local metakaolin on
mechanical properties and durability of concrete. The main purpose
of this paper is to analyze the performance of mortar and concrete with local metakaolin. The preparation of the metakaolin was carried
out by calcination of kaolin at a temperature of 850 °C for a period of 3 hours. The experimental results have shown that the rates of
substitutions of 10 and 15% metakaolin increases the compressive
strength and flexural strength at both early age and long term. The durability and the permeability were also improved by reducing the
coefficient of sorptivity.
Abstract: Physical and mechanical properties of Russian olive
fruits were measured at moisture content of 14.43% w.b. The results
revealed that the mean length, width and thickness of Russian olive
fruits were 20.72, 15.73 and 14.69mm, respectively. Mean mass and
volume of Russian olive fruits were measured as 1.45 g and 2.55 cm3,
respectively. The sphericity, aspect ratio and surface area were
calculated as 0.81, 0.72 and 8.96 cm2, respectively, while arithmetic
mean diameter, geometric mean diameter and equivalent diameter of
Russian olive fruits were 17.05, 16.83 and 16.84 mm, respectively.
Whole fruit density, bulk density and porosity of jujube fruits were
measured and found to be 1.01 g/cm3, 0.29 g/cm3 and 69.5%,
respectively. The values of static coefficient of friction on three
surfaces of glass, galvanized iron and plywood were 0.35, 0.36 and
0.43, respectively. The skin color (L*, a*, b*) varied from 9.92 to
16.08; 2.04 to 3.91 and 1.12 to 3.83, respectively. The values of
rupture force, deformation, energy absorbed and hardness were found
to be between 12.14-16.85 N, 2.16-4.25 mm, 3.42-6.99 N mm and
17.1-23.85 N/mm.
Abstract: Brick is one of the most common masonry units used as building material. Due to the demand, different types of waste have been investigated to be incorporated into the bricks. Many types of sludge have been incorporated in fired clay brick for example marble sludge, stone sludge, water sludge, sewage sludge, and ceramic sludge. The utilization of these waste materials in fired clay bricks usually has positive effects on the properties such as lightweight bricks with improved shrinkage, porosity, and strength. This paper reviews on utilization of different types of sludge wastes into fired clay bricks. Previous investigations have demonstrated positive effects on the physical and mechanical properties as well as less impact towards the environment. Thus, the utilizations of sludge waste could produce a good quality of brick and could be one of alternative disposal methods for the sludge wastes.
Abstract: Base on extenics theory, the statistical physical and mechanical properties from laboratory experiments are used to evaluate the bearing capacity of lateritic soil foundation. The properties include water content, bulk density, liquid limit, cohesion, and so on. The matter-element and the dependent function are defined. Then the synthesis dependent degree and the final grade index are calculated. The results show that predicted outcomes can be matched with the in-situ test data, and a evaluate grade associate with bearing capacity can be deduced. The results provide guidance to assess and determine the bearing capacity grade of lateritic soil foundation.
Abstract: A diamond-like carbon (DLC) based solid-lubricant
film was designed and DLC films were successfully prepared using a
microwave plasma enhanced magnetron sputtering deposition
technology. Post-test characterizations including Raman
spectrometry, X-ray diffraction, nano-indentation test, adhesion test,
friction coefficient test were performed to study the influence of
substrate bias voltage on the mechanical properties of the W- and
S-doped DLC films. The results indicated that the W- and S-doped
DLC films also had the typical structure of DLC films and a better
mechanical performance achieved by the application of a substrate
bias of -200V.