Abstract: Arenga pinnata is an abundantly natural fiber that can be used for sound proof material. However, the scientific data of acoustics properties of Arenga pinnata was not available yet. In this study the sound absorption of pure arenga pinnata was measured. The thickness of Arenga pinnata was varied in 10 mm, 20 mm, 30mm, and 40mm. This work was carried out to investigate the potential of using Arenga pinnata fiber as raw material for sound absorbing material. Impedance Tube Method was used to measure sound absorption coefficient (α). The Measurements was done in accordance with ASTM E1050-98, that is the standard test method for impedance and absorption of acoustical materials using a tube, two microphones and a digital frequency analysis system . The results showed that sound absorption coefficients of Arenga pinnata were good from 2000 Hz to 5000 Hz within the range of 0.75 – 0.90. The optimum sound absorption coefficient was obtained from the thickness of 40 mm. These results indicated that Arenga pinnata fiber is promising to be used as raw material of sound absorbing material with low cost, light, and biodegradable.
Abstract: Environmental awareness and depletion of the
petroleum resources are among vital factors that motivate a number
of researchers to explore the potential of reusing natural fiber as an
alternative composite material in industries such as packaging,
automotive and building constructions. Natural fibers are available in
abundance, low cost, lightweight polymer composite and most
importance its biodegradability features, which often called “ecofriendly"
materials. However, their applications are still limited due
to several factors like moisture absorption, poor wettability and large
scattering in mechanical properties. Among the main challenges on
natural fibers reinforced matrices composite is their inclination to
entangle and form fibers agglomerates during processing due to
fiber-fiber interaction. This tends to prevent better dispersion of the
fibers into the matrix, resulting in poor interfacial adhesion between
the hydrophobic matrix and the hydrophilic reinforced natural fiber.
Therefore, to overcome this challenge, fiber treatment process is one
common alternative that can be use to modify the fiber surface
topology by chemically, physically or mechanically technique.
Nevertheless, this paper attempt to focus on the effect of
mercerization treatment on mechanical properties enhancement of
natural fiber reinforced composite or so-called bio composite. It
specifically discussed on mercerization parameters, and natural fiber
reinforced composite mechanical properties enhancement.