Abstract: This study aims to investigate the ability of different formula of mixed bacteria as a biological treatments of wastewater after primary treatment as a bio-treatment and bio-removal and bio-adsorbent of different heavy metals in natural circumstances. The wastewater was collected from Sarpium forest site-Ismailia Governorate, Egypt. These treatments were mixture of free cells and mixture of immobilized cells of different bacteria. These different formulas of mixed bacteria were prepared under Lab. condition. The obtained data indicated that, as a result of wastewater bio-treatment, the removal rate was found to be 76.92 and 76.70% for biological oxygen demand, 79.78 and 71.07% for chemical oxygen demand, 32.45 and 36.84 % for ammonia nitrogen as well as 91.67 and 50.0% for phosphate after 24 and 28 hrs with mixed free cells and mixed immobilized cells, respectively. Moreover, the bio-removals of different heavy metals were found to reach 90.0 and 50. 0% for Cu ion, 98.0 and 98.5% for Fe ion, 97.0 and 99.3% for Mn ion, 90.0 and 90.0% Pb, 80.0% and 75.0% for Zn ion after 24 and 28 hrs with mixed free cells and mixed immobilized cells, respectively. The results indicated that 13.86 and 17.43% of removal efficiency and reduction of total dissolved solids were achieved after 24 and 28 hrs with mixed free cells and mixed immobilized cells, respectively.
Abstract: The main aim of this research is to study the possible
use of recycled fine aggregate made from waste rubble wall to
substitute partially for the natural sand used in the production of
cement and sand bricks. The bricks specimens were prepared by
using 100% natural sand; they were then replaced by recycled fine
aggregate at 25, 50, 75, and 100% by weight of natural sand. A series
of tests was carried out to study the effect of using recycled aggregate
on the physical and mechanical properties of bricks, such as density,
drying shrinkage, water absorption characteristic, compressive and
flexural strength. Test results indicate that it is possible to
manufacture bricks containing recycled fine aggregate with good
characteristics that are similar in physical and mechanical properties
to those of bricks with natural aggregate, provided that the percentage
of recycled fine aggregates is limited up to 50-75%.
Abstract: In this paper, the experimental design of using the
Taguchi method is employed to optimize the processing parameters in
the plasma arc surface hardening process. The processing parameters
evaluated are arc current, scanning velocity and carbon content of
steel. In addition, other significant effects such as the relation between
processing parameters are also investigated. An orthogonal array,
signal-to-noise (S/N) ratio and analysis of variance (ANOVA) are
employed to investigate the effects of these processing parameters.
Through this study, not only the hardened depth increased and surface
roughness improved, but also the parameters that significantly affect
the hardening performance are identified. Experimental results are
provided to verify the effectiveness of this approach.