Abstract: Fiber cross sectional area value is a crucial factor in determining the strength properties of natural fiber. Furthermore, unlike synthetic fiber, a diameter and cross sectional area of natural fiber has a large variation along and between the fibers. This study aims to determine the main and interaction effects of alkali treatment conditions which influence kenaf bast fiber mean cross sectional area. Three alkali treatment conditions at two different levels were selected. The conditions setting were alkali concentrations at 2 and 10 w/v %; fiber immersed temperature at room temperature and 1000C; and fiber immersed duration for 30 and 480 minutes. Untreated kenaf fiber was used as a control unit. Kenaf bast fiber bundle mounting tab was prepared according to ASTM C1557-03. Cross sectional area was measured using a Leica video analyzer. The study result showed that kenaf fiber bundle mean cross sectional area was reduced 6.77% to 29.88% after alkali treatment. From analysis of variance, it shows that interaction of alkali concentration and immersed time has a higher magnitude at 0.1619 compared to alkali concentration and immersed temperature interaction which was 0.0896. For the main effect, alkali concentration factor contributes to the higher magnitude at 0.1372 which indicated are decrease pattern of variability when the level was change from lower to higher level. Then, it was followed by immersed temperature at 0.1261 and immersed time at 0.0696 magnitudes.
Abstract: Environmental awareness and depletion of the
petroleum resources are among vital factors that motivate a number
of researchers to explore the potential of reusing natural fiber as an
alternative composite material in industries such as packaging,
automotive and building constructions. Natural fibers are available in
abundance, low cost, lightweight polymer composite and most
importance its biodegradability features, which often called “ecofriendly"
materials. However, their applications are still limited due
to several factors like moisture absorption, poor wettability and large
scattering in mechanical properties. Among the main challenges on
natural fibers reinforced matrices composite is their inclination to
entangle and form fibers agglomerates during processing due to
fiber-fiber interaction. This tends to prevent better dispersion of the
fibers into the matrix, resulting in poor interfacial adhesion between
the hydrophobic matrix and the hydrophilic reinforced natural fiber.
Therefore, to overcome this challenge, fiber treatment process is one
common alternative that can be use to modify the fiber surface
topology by chemically, physically or mechanically technique.
Nevertheless, this paper attempt to focus on the effect of
mercerization treatment on mechanical properties enhancement of
natural fiber reinforced composite or so-called bio composite. It
specifically discussed on mercerization parameters, and natural fiber
reinforced composite mechanical properties enhancement.