Abstract: NiFe2O4 (nickel ferrite), ZnFe2O4 (zinc ferrite) and
Ni0.5Zn0.5Fe2O4 (nickel-zinc ferrite) were prepared by
mechanochemical route in a planetary ball mill starting from mixture
of the appropriate quantities of the Ni(OH)2/Fe(OH)3,
Zn(OH)2/Fe(OH)3 and Ni(OH)2/Zn(OH)2/Fe(OH)3 hydroxide
powders. In order to monitor the progress of chemical reaction and
confirm phase formation, powder samples obtained after 25 h, 18 h
and 10 h of milling were characterized by X-ray diffraction (XRD),
transmission electron microscopy (TEM), IR, Raman and Mössbauer
spectroscopy. It is shown that the soft mechanochemical method, i.e.
mechanochemical activation of hydroxides, produces high quality
single phase ferrite samples in much more efficient way. From the IR
spectroscopy of single phase samples it is obvious that energy of
modes depends on the ratio of cations. It is obvious that all samples
have more than 5 Raman active modes predicted by group theory in
the normal spinel structure. Deconvolution of measured spectra
allows one to conclude that all complex bands in the spectra are made
of individual peaks with the intensities that vary from spectrum to
spectrum. The deconvolution of Raman spectra allows to separate
contributions of different cations to a particular type of vibration and
to estimate the degree of inversion.
Abstract: The use of magnesium alloys is limited due to their
susceptibility to corrosion although they have many attractive
physical and mechanical properties. To increase mechanical and
corrosion properties of these alloys, many deposition method and
coating types are used. Electroless Ni–B coatings have received
considerable interest recently due to its unique properties such as
cost-effectiveness, thickness uniformity, good wear resistance,
lubricity, good ductility and corrosion resistance, excellent
solderability and electrical properties and antibacterial property. In
this study, electroless Ni-B coating could been deposited on AZ91
magnesium alloy. The obtained coating exhibited a harder and
rougher structure than the substrate.
Abstract: Novel wind-lens turbine designs can augment power
output. Vacuum-Assisted Resin Transfer Molding (VARTM) is used
to form large and complex structures from a Carbon Fiber Reinforced
Polymer (CFRP) composite. Typically, wind-lens turbine structures
are fabricated in segments, and then bonded to form the final structure.
This paper introduces five new adhesive joints, divided into two
groups: one is constructed between dry carbon and CFRP fabrics, and
the other is constructed with two dry carbon fibers. All joints and
CFRP fabrics were made in our laboratory using VARTM
manufacturing techniques. Specimens were prepared for tensile testing
to measure joint performance. The results showed that the second
group of joints achieved a higher tensile strength than the first group.
On the other hand, the tensile fracture behavior of the two groups
showed the same pattern of crack originating near the joint ends
followed by crack propagation until fracture.
Abstract: The laser-ultrasonic method is realized for
quantifying the influence of porosity on the local Young’s
modulus of isotropic composite materials. The method is based on
a laser thermooptical method of ultrasound generation combined
with measurement of the phase velocity of longitudinal and shear
acoustic waves in samples. The main advantage of this method
compared with traditional ultrasonic research methods is the
efficient generation of short and powerful probing acoustic pulses
required for reliable testing of ultrasound absorbing and
scattering heterogeneous materials. Using as an example samples
of a metal matrix composite with reinforcing microparticles of
silicon carbide in various concentrations, it is shown that to
provide an effective increase in Young’s modulus with increasing
concentration of microparticles, the porosity of the final sample
should not exceed 2%.
Abstract: Heat treatable aluminum alloys such as 7075 and
7055, because of high strength and low density, are used widely in
aircraft industry. For best mechanical properties, T6 heat treatment
has recommended for this regards, but this temper treatment is
sensitive to corrosion induced and Stress Corrosion Cracking (SCC)
damage. For improving this property, the over-aging treatment (T7)
applies to this alloy, but it decreases the mechanical properties up to
30 percent. Hence, to increase the mechanical properties, without any
remarkable decrease in SCC resistant, Retrogression and Re-Aging
(RRA) heat treatment is used. This treatment performs in a relatively
short time. In this paper, the RRA heat treatment was applied to 7055
aluminum alloy and then effect of RRA time on the mechanical
properties of 7055 has been investigated. The results show that the
40-minute time is suitable time for retrogression of 7055 aluminum
alloy and ultimate strength increases up to 625MPa.
Abstract: This research paper portrays a comparative analysis of
thermomechanical behaviour of Shielded Metal Arc Welding
(SMAW) and Gas Tungsten Arc Welding (GTAW) of low carbon
steel of AISI 1020 grade butt joints. The thermal history has been
obtained by experimental work. We have focused on temperature
dependent cooling rate as depicted by Adam’s two-dimensional
model. The effect of moving point heat source of SMAW and GTAW
on mechanical properties has been judged by optical and scanning
electron micrographs of different regions in weld joints. The
microhardness study has been carried to visualize the joint strength
due to formation of different phases.
Abstract: Chatter vibrations, occurring during cutting process,
cause vibration between the cutting tool and workpiece, which
deteriorates surface roughness and reduces tool life. The purpose of
this study is to investigate the influence of cutting parameters and
tool construction on surface roughness and vibration in turning of
aluminum alloy AA2024. A new design of cutting tool is proposed,
which is filled up with epoxy granite in order to improve damping
capacity of the tool. Experiments were performed at the lathe using
carbide cutting insert coated with TiC and two different cutting tools
made of AISI 5140 steel. Taguchi L9 orthogonal array was applied to
design of experiment and to optimize cutting conditions. By the help
of signal-to-noise ratio and analysis of variance the optimal cutting
condition and the effect of the cutting parameters on surface
roughness and vibration were determined. Effectiveness of Taguchi
method was verified by confirmation test. It was revealed that new
cutting tool with epoxy granite has reduced vibration and surface
roughness due to high damping properties of epoxy granite in
toolholder.
Abstract: Within Rapid Prototyping technologies are used many
types of materials. Many of them are recyclable but there are still as
plastic like, so practically they do not degrade in the landfill.
Polylactic acid (PLA) is one of the special plastic materials, which
are biodegradable and available for 3D printing within Fused
Deposition Modeling (FDM) technology. The question is, if the
mechanical properties of produced models are comparable to similar
technical plastic materials which are usual for prototype production.
Presented paper shows the experiments results for tensile strength
measurements for specimens prepared with different 3D printer
settings and model orientation. Paper contains also the comparison of
tensile strength values with values measured on specimens produced
by conventional technologies as injection moulding.
Abstract: In this article was evaluated the protective effect of
the alternative concrete obtained from the binary mixture of fly ash,
and iron and steel slag. After mixing the cement with aggregates,
structural steel was inserted in the matrix cementitious. The study
was conducted comparatively with specimens exposed to natural
conditions free of chloride ion. The chloride ion effect on the
specimens accelerated under controlled conditions (3.5% NaCl and
25°C temperature). The impedance data were acquired in a range of 1
mHz to 100 kHz.
Abstract: Within this paper, latest results on processing of energetic nanomaterials by means of the Spray Flash Evaporation technique are presented. This technology constitutes a highly effective and continuous way to prepare fascinating materials on the nano- and micro-scale. Within the process, a solution is set under high pressure and sprayed into an evacuated atomization chamber. Subsequent ultrafast evaporation of the solvent leads to an aerosol stream, which is separated by cyclones or filters. No drying gas is required, so the present technique should not be confused with spray dying. Resulting nanothermites, insensitive explosives or propellants and compositions are foreseen to replace toxic (according to REACH) and very sensitive matter in military and civil applications. Diverse examples are given in detail: nano-RDX (n-Cyclotrimethylentrinitramin) and nano-aluminum based systems, mixtures (n-RDX/n-TNT - trinitrotoluene) or even cocrystalline matter like n-CL-20/HMX (Hexanitrohexaazaisowurtzitane/ Cyclotetra-methylentetranitramin). These nanomaterials show reduced sensitivity by trend without losing effectiveness and performance. An analytical study for material characterization was performed by using Atomic Force Microscopy, X-Ray Diffraction, and combined techniques as well as spectroscopic methods. As a matter of course, sensitivity tests regarding electrostatic discharge, impact, and friction are provided.
Abstract: The purpose of this study is to propose an effective method to improve frictional coefficient between shoe rubber soles with added glass fibers and the surfaces of icy and snowy road in order to prevent slip-and-fall accidents by the users. The additional fibers into the rubber were uniformly tilted to the perpendicular direction of the frictional surface, where tilting angles were -60, -30, +30, +60, 90 degrees and 0 (as normal specimen), respectively. It was found that parallel arraignment was effective to improve the frictional coefficient when glass fibers were embedded in the shoe rubber, while perpendicular to normal direction of the embedded glass fibers on the shoe surface was also effective to do that once after they were exposed from the shoe rubber with its abrasion. These improvements were explained by the increase of stiffness against the shear deformation of the rubber at critical frictional state and adequate scratching of fibers when fibers were protruded in perpendicular to frictional direction, respectively. Most effective angle of tilting of frictional coefficient between rubber specimens and a stone was perpendicular (= 0 degree) to frictional direction. Combinative modified rubber specimen having 2 layers was fabricated where tilting angle of protruded fibers was 0 degree near the contact surface and tilting angle of embedded fibers was 90 degrees near back surface in thickness direction to further improve the frictional coefficient. Current study suggested that effective arraignments in tilting angle of the added fibers should be applied in designing rubber shoe soles to keep the safeties for users in regions of cold climates.
Abstract: A model to predict the plastic zone size for material
under plane stress condition has been developed and verified
experimentally. The developed model is a function of crack size,
crack angle and material property (dislocation density). Simulation
and validation results show that the model developed show good
agreement with experimental results. Samples of low carbon steel
(0.035%C) with included surface crack angles of 45o, 50o, 60o, 70o
and 90o and crack depths of 2mm and 4mm were subjected to low
strain rate between 0.48 x 10-3 s-1 – 2.38 x 10-3 s-1. The mechanical
properties studied were ductility, tensile strength, modulus of
elasticity, yield strength, yield strain, stress at fracture and fracture
toughness. The experimental study shows that strain rate has no
appreciable effect on the size of plastic zone while crack depth and
crack angle plays an imperative role in determining the size of the
plastic zone of mild steel materials.
Abstract: Durian skin is a newly explores natural fibre
potentially reinforced polyolefin for diverse applications. In this
work, investigation on the effect of coupling agent, maleic anhydride
polypropylene (MAPP) on the mechanical, morphological, and
thermal properties of polypropylene (PP) reinforced with durian skin
fibre (DSF) was conducted. The presence of 30 wt% DSF
significantly reduced the tensile strength of PP-DSF composite.
Interestingly, even though the same trend goes to PP-DSF with the
presence of MAPP, the reduction is only about 4% relative to
unreinforced PP and 18% higher than PP-DSF without MAPP
(untreated composite or UTC). The used of MAPP in treated
composite (TC) also increased the tensile modulus, flexural
properties and degradation temperature. The enhanced mechanical
properties are consistent with good interfacial interaction as
evidenced under scanning electron microscopy.
Abstract: In this work, our goal is to optimize the nitriding treatment at a low-temperature of the steel 32CrMoV13 using gas mixtures of ammonia, nitrogen and hydrogen to improve the mechanical properties of the surface (good wear resistance, friction and corrosion), and of the diffusion layer of the nitrogen (good resistance to fatigue and good tenacity with heart). By limiting our work to the pure iron and to the alloys iron-chromium and iron-chromium-carbon, we have studied the various parameters which manage the nitriding: flow rate and composition of the gaseous phase, the interaction chromium-nitrogen and chromium-carbon by the help of experiments of nitriding realized in the laboratory by thermogravimetry. The acquired knowledge has been applied by the mastery of the growth of the γ' combination layer on the α diffusion layer in the case of the industrial steel 32CrMoV13.
Abstract: Mechanical behavior of 6082T6 aluminum is
investigated at different temperatures. The strain rate sensitivity is
investigated at different temperatures on the grain size variants. The
sensitivity of the measured grain size variants on 3-D grain is
discussed. It is shown that the strain rate sensitivities are negative for
the grain size variants during the deformation of nanostructured
materials. It is also observed that the strain rate sensitivities vary in
different ways with the equivalent radius, semi minor axis radius,
semi major axis radius and major axis radius. From the obtained
results, it is shown that the variation of strain rate sensitivity with
temperature suggests that the strain rate sensitivity at the low and the
high temperature ends of the 6082T6 aluminum range is different.
The obtained results revealed transition at different temperature from
negative strain rate sensitivity as temperature increased on the grain
size variants.
Abstract: In this study, the effects and interactions of reaction
time and capping agent assistance during sol-gel synthesis of
magnesium substituted hydroxyapatite nanopowder (MgHA) on
hydroxyapatite (HA) to β-tricalcium phosphate (β-TCP) ratio, Ca/P
ratio and mean crystallite size was examined experimentally as well
as through statistical analysis. MgHA nanopowders were synthesized
by sol-gel technique at room temperature using aqueous solution of
calcium nitrate tetrahydrate, magnesium nitrate hexahydrate and
potassium dihydrogen phosphate as starting materials. The reaction
time for sol-gel synthesis was varied between 15 to 60 minutes. Two
process routes were followed with and without addition of
triethanolamine (TEA) in the solutions. The elemental compositions
of as-synthesized powders were determined using X-ray fluorescence
(XRF) spectroscopy. The functional groups present in the assynthesized
MgHA nanopowders were established through Fourier
Transform Infrared Spectroscopy (FTIR). The amounts of phases
present, Ca/P ratio and mean crystallite sizes of MgHA nanopowders
were determined using X-ray diffraction (XRD). The HA content in
biphasic mixture of HA and β-TCP and Ca/P ratio in as-synthesized
MgHA nanopowders increased effectively with reaction time of sols
(p0.15, two way ANOVA). The MgHA nanopowders
synthesized with TEA assistance exhibited 14 nm lower crystallite
size (p
Abstract: Geopolymer composites reinforced with flax fabrics
and nanoclay are fabricated and studied for physical and mechanical
properties using X-Ray Diffraction (XRD), Fourier Transform
Infrared Spectroscopy (FTIR), and Scanning Electron Microscope
(SEM). Nanoclay platelets at a weight of 1.0%, 2.0%, and 3.0% were
added to geopolymer pastes. Nanoclay at 2.0 wt.% was found to
improve density and decrease porosity while improving flexural
strength and post-peak toughness. A microstructural analysis
indicated that nanoclay behaves as filler and as an activator
supporting geopolymeric reaction while producing a higher content
geopolymer gel improving the microstructure of binders. The process
enhances adhesion between the geopolymer matrix and flax fibres.
Abstract: This paper focuses on the mathematical modeling for
solidification of Al alloy in a cube mold cavity to study the
solidification behavior of casting process. The parametric
investigation of solidification process inside the cavity was
performed by using computational solidification/melting model
coupled with Volume of fluid (VOF) model. The implicit filling
algorithm is used in this study to understand the overall process from
the filling stage to solidification in a model metal casting process.
The model is validated with past studied at same conditions. The
solidification process is analyzed by including the effect of pouring
velocity as well as natural convection from the wall and geometry of
the cavity. These studies show the possibility of various defects
during solidification process.
Abstract: The strain intensity and redundant strains, dependent
in multistage TRIP wire drawing processes from values used single
partial reductions, should influence on the intensity of transformation
the retained austenite into martensite and thereby on mechanical
properties of drawn wires. The numerical analysis of drawing
processes with use of Drawing 2D programme, for steel wires made
from TRIP steel with 0,29% has been shown in the work. The change
of strain intensity εc and the values of redundant strain εxy, has been
determined for particular draws in dependence of used single partial
reductions.
Abstract: This paper describes the development of new class of
epoxy based rice husk filled jute reinforced composites. Rice husk
flour is added in 0%, 1%, 3%, 5% by weight. Epoxy resin and
triethylenetetramine (T.E.T.A) is used as matrix and hardener
respectively. It investigates the mechanical properties of the
composites and a comparison is done for monolithic jute composite
and the filled ones. The specimens are prepared according to the
ASTM standards and experimentation is carried out using INSTRON
8801. The result shows that with the increase of filler percentage the
tensile properties increases but compressive and flexural properties
decreases.