Abstract: In this study, the effects and interactions of reaction
time and capping agent assistance during sol-gel synthesis of
magnesium substituted hydroxyapatite nanopowder (MgHA) on
hydroxyapatite (HA) to β-tricalcium phosphate (β-TCP) ratio, Ca/P
ratio and mean crystallite size was examined experimentally as well
as through statistical analysis. MgHA nanopowders were synthesized
by sol-gel technique at room temperature using aqueous solution of
calcium nitrate tetrahydrate, magnesium nitrate hexahydrate and
potassium dihydrogen phosphate as starting materials. The reaction
time for sol-gel synthesis was varied between 15 to 60 minutes. Two
process routes were followed with and without addition of
triethanolamine (TEA) in the solutions. The elemental compositions
of as-synthesized powders were determined using X-ray fluorescence
(XRF) spectroscopy. The functional groups present in the assynthesized
MgHA nanopowders were established through Fourier
Transform Infrared Spectroscopy (FTIR). The amounts of phases
present, Ca/P ratio and mean crystallite sizes of MgHA nanopowders
were determined using X-ray diffraction (XRD). The HA content in
biphasic mixture of HA and β-TCP and Ca/P ratio in as-synthesized
MgHA nanopowders increased effectively with reaction time of sols
(p0.15, two way ANOVA). The MgHA nanopowders
synthesized with TEA assistance exhibited 14 nm lower crystallite
size (p
Abstract: A group of Stellite alloys are studied in consideration
of temperature effects on their hardness and wear resistance. The
hardness test is conducted on a micro-hardness tester with a hot stage
equipped that allows heating the specimen up to 650°C. The wear
resistance of each alloy is evaluated using a pin-on-disc tribometer
with a heating furnace built-in that provides the temperature capacity
up to 450°C. The experimental results demonstrate that the hardness
and wear resistance of Stellite alloys behave differently at room
temperature and at high temperatures. The wear resistance of Stellite
alloys at room temperature mainly depends on their carbon content and
also influenced by the tungsten content in the alloys. However, at high
temperatures the wear mechanisms of Stellite alloys become more
complex, involving multiple factors. The relationships between
chemical composition, microstructure, hardness and wear resistance of
these alloys are studied, with focus on temperature effect on these
relations.