Abstract: Effect of Zn addition on the microstructure and
mechanical properties of Mg-Zn alloys with Zn contents from 6 to 10
weight percent was investigated in this study. Through calculation of
phase equilibria of Mg-Zn alloys, carried out by using FactSage® and
FTLite database, solution treatment temperature was decided as
temperatures from 300 to 400oC, where supersaturated solid solution
can be obtained. Solid solution treatment of Mg-Zn alloys was
successfully conducted at 380oC and supersaturated microstructure
with all beta phase resolved into matrix was obtained. After solution
treatment, hot rolling was successfully conducted by reduction of
60%. Compression and tension tests were carried out at room
temperature on the samples as-cast, solution treated, hot-rolled and
recrystallized after rolling. After solid solution treatment, each alloy
was annealed at temperatures of 180 and 200oC for time intervals from
1 min to 48 hrs and hardness of each condition was measured by
micro-Vickers method. Peak aging conditions were deduced as at the
temperature of 200oC for 10 hrs. By addition of Zn by 10 weight
percent, hardness and strength were enhanced.
Abstract: The tribological test with Pin-On-Disc configuration
measures friction and wear properties in dry or lubricated sliding
surfaces of a variety of materials and coatings. Polymeric matrix
composites loaded with mineral filler were used, 1%, 3%, 10%, 30%,
and 50% mass percentage of filler, to reduce the material cost by
using mineral tailings. Using a pin-on-disc tribometer to quantify
coefficient of friction and wear resistance of the specimens. The
parameters known to performing the test were 300 rpm rotation,
normal load of 16N and duration of 33.5 minutes. The composite
with 10% mineral filler performed better, considering that the wear
resistance was good when compared to the other compositions and an
average low coefficient of friction, in the order of μ ≤ 0.15.
Abstract: Among other traditional and non-traditional
additives, polymers have shown an efficient performance in the field
and improved sustainability. Polyacrylamide (PAM) is one such
additive that has demonstrated many advantages including a
reduction in permeability, an increase in durability and the provision
of strength characteristics. However, information about its effect on
the improved geotechnical characteristics is very limited to the field
performance monitoring. Therefore, a laboratory investigation was
carried out to examine the basic and engineering behaviors of three
types of soils treated with a PAM additive. The results showed an
increase in dry density and unconfined compressive strength for all
the soils. The results further demonstrated an increase in unsoaked
CBR and a reduction in permeability for all stabilized samples.
Abstract: Since the advent of the law 86/14 concerning the
exploitation of the national territory by foreign companies in
partnership with the Algerian oil and gas company, the problem of
hydrocarbons metering in the sharing production come out.
More generally, good management counting hydrocarbons can
provide data on the production wells, the field and the reservoir for
medium and long term planning, particularly in the context of the
management and field development.
In this work, we are interested in the transactional metering which
is a very delicate and crucial period in the current context of the new
hydrocarbon’s law characterized by assets system between the
various activities of Sonatrach and its foreign partners.
After a state of the art on hydrocarbons metering devices in
Algeria and elsewhere, we will decline the advantages and
disadvantages of each system, and then we describe the problem to
try to reach an optimal solution.
Abstract: The new design of heat exchangers utilizing an
annular distributor opens a new gateway for realizing higher energy
optimization. To realize this goal, graphene nanoplatelet-based water
nanofluids with promising thermophysical properties were
synthesized in the presence of covalent and noncovalent
functionalization. Thermal conductivity, density, viscosity and
specific heat capacity were investigated and employed as a raw data
for ANSYS-Fluent to be used in two-phase approach. After
validation of obtained results by analytical equations, two special
parameters of convective heat transfer coefficient and pressure drop
were investigated. The study followed by studying other heat transfer
parameters of annular pass in the presence of graphene nanopletelesbased
water nanofluids at different weight concentrations, input
powers and temperatures. As a result, heat transfer performance and
friction loss are predicted for both synthesized nanofluids.
Abstract: Sodium borosilicate glasses doped with different
content of NdF3 mol % have been prepared by rapid quenching
method. Ultrasonic velocities (both longitudinal and shear)
measurements have been carried out at room temperature and at
ultrasonic frequency of 4 MHz. Elastic moduli, Debye temperature,
softening temperature and Poisson's ratio have been obtained as a
function of NdF3 modifier content. Results showed that the elastic
moduli, Debye temperature, softening temperature and Poisson's ratio
have very slight change with the change of NdF3 mol % content.
Based on FTIR spectroscopy and theoretical (Bond compression)
model, quantitative analysis has been carried out in order to obtain
more information about the structure of these glasses. The study
indicated that the structure of these glasses is mainly composed of
SiO4 units with four bridging oxygens (Q4), and with three bridging
and one nonbridging oxygens (Q3).
Abstract: In this study, the butt welding of the commercial AZ31 magnesium alloy sheets have been carried out by using Tungsten Inert Gas (TIG) welding process with alternative and pulsed current. Welded samples were examined with regards to hardness and microstructure. Despite some recent developments in welding of magnesium alloys, they have some problems such as porosity, hot cracking, oxide formation and so on. Samples of the welded parts have undergone metallographic and mechanical examination. Porosities and homogeneous micron grain oxides were rarely observed. Orientations of the weld microstructure in terms of heat transfer also were rarely observed and equiaxed grain morphology was dominant grain structure as in the base metal. As results, fusion zone and few locations of the HAZ of the welded samples have shown twin’s grains. Hot cracking was not observed for any samples. Weld bead geometry of the welded samples were evaluated as normal according to welding parameters. In the results, conditions of alternative and pulsed current and the samples were compared to each other with regards to microstructure and hardness.
Abstract: For briquetting of metal chips are used hydraulic and
mechanical presses. The density of the briquettes in this case is about
60% - 70 % on the density of solid metal. In this work are presented
the results of experimental studies for briquetting of metal chips, by
using a new technology for impact briquetting. The used chips are by
Armco iron, steel, cast iron, copper, aluminum and brass. It has been
found that: (i) in a controlled impact the density of the briquettes can
be increases up to 30%; (ii) at the same specific impact energy Es
(J/sm3) the density of the briquettes increases with increasing of the
impact velocity; (iii), realization of the repeated impact leads to
decrease of chips density, which can be explained by distribution of
elastic waves in the briquette.
Abstract: E-glass-epoxy laminated composites having different fiber volume fractions (40, 50, 60 and 70) were fabricated with and without the addition of nanoclay. Flexural strength and tensile strength of the composite laminates were determined. It was observed that, with increasing the fiber volume fraction (Vf) of fiber from 40 to 60, the ability of nanoclay to enhance the tensile and flexural strength of E-glass-epoxy composites decreases significantly. At 70Vf, the tensile and flexural strength of the nanoclay reinforced E-glass-epoxy were found to be lowest when compared to the E-glass-epoxy composite made without the addition of nanoclay. Based on the obtained data and microstructure of the tested samples, plausible mechanism for the observed trends has been proposed. The enhanced mechanical properties for nanoclay reinforced E-glass-epoxy composites for 40-60 Vf, due to higher interface toughness coupled with strong interfilament bonding may have ensured the homogeneous load distribution across all the glass fibers. Results in the decrease in mechanical properties at 70Vf, may be due to the inability of the matrix to bind the nanoclay and glass-fibers.
Abstract: This study attempts to understand the effect of different UV irradiation methods on the intercalation of LDPE/MMT nanocomposites, and its molecular behavior at certain isothermal crystallization temperature. Three different methods of UV exposure were employed using single composition of LDPE/MMT nanocomposites. All samples were annealed for 5 hours at a crystallization temperature of 100oC. The crystallization temperature was chosen to be at large supercooling temperature to ensure quick and complete crystallization. The raw material of LDPE consisted of two stable monoclinic and orthorhombic phases according to XRD results. The thermal behavior of both phases acted differently when UV exposure method was changed. The monoclinic phase was more dependent on the method used compared to the orthorhombic phase. The intercalation of clay, as well as, the non-isothermal crystallization temperature, has also shown a clear dependency on the type of UV exposure. A third phase that is thermally less stable was also observed. Its respond to UV irradiation was greater since it contains low molecular weight entities which make it more vulnerable to any UV exposure.
Abstract: This paper aims at manipulating loop alignment in knitting a three-dimensional (3D) shape by its geometry. Two loop alignment methods are introduced to handle a surface with positive Gaussian curvature. As weft knitting is a two-dimensional (2D) knitting mechanism that the knitting cam carrying the feeders moves in two directions only, left and right, the knitted fabric generated grows in width and length but not in depth. Therefore, a 3D shape is required to be flattened to a 2D plane with surface area preserved for knitting. On this flattened plane, dimensional measurements are taken for loop alignment. The way these measurements being taken derived two different loop alignment methods. In this paper, only plain knitted structure was considered. Each knitted loop was taken as a basic unit for loop alignment in order to achieve the required geometric dimensions, without the inclusion of other stitches which give textural dimensions to the fabric. Two loop alignment methods were experimented and compared. Only one of these two can successfully preserve the dimensions of the shape.
Abstract: In order to predict and model wrinkling which is caused by out of plane deformation due to compressive loading in the plane of the material during composite prepregs forming, it is necessary to quantitatively understand the relative magnitude of the bending stiffness. This study aims to examine the bending properties of out-of-autoclave (OOA) thermosetting prepreg under vertical cantilever test condition. A direct method for characterizing the bending behavior of composite prepregs was developed. The results from direct measurement were compared with results derived from an image-processing procedure that analyses the captured image during the vertical bending test. A numerical simulation was performed using ABAQUS to confirm the bending stiffness value.
Abstract: The great majority of the applications of thermal isolation in the strip of drops and averages temperatures (up to 200ºC), it is made of materials aggressive nature, such an as glass wool, rock wool, polystyrene, EPS among others. Such materials, in spite of the effectiveness in the retention of the flow of heat, possess considerable cost and when discarded they are long years to be to decompose. In that context, trying to adapt the world politics the about of the preservation of the environment, a study began with intention of developing a material composite, with properties of thermal, originating from insulating industrial residues. In this research, the behavior of the composite was analyzed, as submitted the fire. For this, the reaction rehearsals were accomplished to the fire for the composites 2:1; 1:1; 1:2 and for the Latex, based in the "con" experiment in agreement with the norm ASTM - E 1334 - 90. As consequence, in function of the answers of the system was possible to be observed to the acting of each mixture proportion.
Abstract: We have incorporated the translational rotational (TR)
coupling effects in the framework of three body force shell model
(TSM) to develop an extended TSM (ETSM). The dynamical matrix
of ETSM has been applied to compute the phonon frequencies of
orientationally disordered mixed crystal (ND4Br)x(KBr)1-x in (q00),
(qq0) and (qqq) symmetry directions for compositions 0.10≤x≤0.50
at T=300K.These frequencies are plotted as a function of wave vector
k. An unusual acoustic mode softening is found along symmetry
directions (q00) and (qq0) as a result of translation-rotation coupling.
Abstract: Different knitted structures and knitted parameters play a vital role in the stretch and recovery management of compression sportswear in addition to the materials use to generate this stretch and recovery behavior of the fabric. The present work was planned to predict the different performance indicators of a compression sportswear fabric with some ground parameters i.e. base yarn stitch length (polyester as base yarn and spandex as plating yarn involve to make a compression fabric) and linear density of the spandex which is a key material of any sportswear fabric. The prediction models were generated by response surface method for performance indicators such as stretch & recovery percentage, compression generated by the garment on body, total elongation on application of high power force and load generated on certain percentage extension in fabric. Certain physical properties of the fabric were also modeled using these two parameters.
Abstract: This article experimentally investigates various physical properties of special fire retardant sewing threads under different sewing speeds. The aramid threads are common for sewing the fire-fighter clothing due to high strength and high melting temperature. 3 types of aramid threads with different linear densities are used for sewing at different speed of 2000 to 4000 r/min. The needle temperature is measured at different speeds of sewing and tensile properties of threads are measured before and after the sewing process respectively. The results shows that the friction and abrasion during the sewing process causes a significant loss to the tensile properties of the threads and needle temperature rises to nearly 300oC at 4000 r/min of machine speed. The Scanning electron microscope images are taken before and after the sewing process and shows no melting spots but significant damage to the yarn. It is also found that machine speed of 2000r/min is ideal for sewing firefighter clothing for higher tensile properties and production.
Abstract: Composites materials of Poly (vinyl alcohol) (PVA)/Chitosan (CS) have been synthesized and characterized successfully. HNTs have been added to composites to enhance the mechanical and degradation properties by hydrogen bonding interactions, compatibility, and chemical crosslink between HNTs and PVA. PVA/CS/HNTs composites prepared with different concentration ratio. SEM micrographs of composites surface showed that more agglomeration with more chitosan ratio. Mechanical and degradation properties were characterized and the result indicates that Mechanical and degradation of 80%PVA/5%Chitosan/15%HNTs higher than the others PVA/CS/HNTs composites.
Abstract: Space Radiation has become one of the major factors in successful long duration space exploration. Exposure to space radiation not only can affect the health of astronauts but also can disrupt or damage materials and electronics. Hazards to materials include degradation of properties, such as, modulus, strength, or glass transition temperature. Electronics may experience single event effects, gate rupture, burnout of field effect transistors and noise. Presently aluminum is the major component in most of the space structures due to its lightweight and good structural properties. However, aluminum is ineffective at blocking space radiation. Therefore, most of the past research involved studying at polymers which contain large amounts of hydrogen. Again, these materials are not structural materials and would require large amounts of material to achieve the structural properties needed. One of the materials to alleviate this problem is polymeric composite materials, which has good structural properties and use polymers that contained large amounts of hydrogen. This paper presents steps involved in fabrication of multi-functional hybrid sandwich panels that can provide beneficial radiation shielding as well as structural strength. Multifunctional hybrid sandwich panels were manufactured using vacuum assisted resin transfer molding process and were subjected to radiation treatment. Study indicates that various nanoparticles including Boron Nano powder, Boron Carbide and Gadolinium nanoparticles can be successfully used to block the space radiation without sacrificing the structural integrity.
Abstract: The microstructure, mechanical properties and metalgraphic characteristics of Ni plated AlN-Astaloy Cr-M powders were investigated using specimens produced by tube furnace sintering at 1000-1400 °C temperature. A uniform nickel layer on AlN powders was deposited prior to sintering using electroless plating technique. A composite consisting of ternary additions, metallic phase, Ni and ceramic phase AlN within a matrix of Astaloy Cr-M had been prepared under Ar shroud and then tube furnace sintered. The experimental results carried out by using XRD (X-Ray Diffraction) and SEM (Scanning Electron Microscope) for composition (10% AlN-Astaloy Cr-M) 10% Ni at 1400 °C suggest that the best properties as 132.45HB and permittivity were obtained at 1400 °C.
Abstract: Proper selection of welding parameters for getting
excellent weld is a challenge. HAZ simulation helps in identifying
suitable welding parameters like heating rate, cooling rate, peak
temperature, and energy input. In this study, the influence of weld
thermal cycle of heat affected zone (HAZ) is simulated for
Submerged Arc Welding (SAW) using Gleeble ® 3800 thermomechanical
simulator. A (Micro-alloyed) MA steel plate of thickness
18 mm having yield strength 450MPa is used for making test
specimens. Determination of the mechanical properties of weld
simulated specimens including Charpy V-notch toughness and
hardness is performed. Peak temperatures of 1300°C, 1150°C,
1000°C, 900°C, 800°C, heat energy input of 22KJ/cm and preheat
temperatures of 30°C have been used with Rykalin-3D simulation
model. It is found that the impact toughness (75J) is the best for the
simulated HAZ specimen at the peak temperature 900ºC. For parent
steel, impact toughness value is 26.8J at -50°C in transverse
direction.