Abstract: This article considers the problems of economic growth
and Russian energy strategy. Also in this paper, the issues related to
the economic growth prospects of Russian were discussed. Russian
energy strategy without standing Russia`s stature in global energy
markets, at the current production and extraction rates, will not be able
to sustain its own production as well as fulfil its energy strategy.
Indeed, Russia’s energy sector suffers from a chronic lack of
investments which are necessary to modernize its energy supply
system. In recent years, especially since the international financial
crisis, Russia-EU energy cooperation has made substantive progress.
Recently the break-through progress has been made, resulting mainly
from long-term contributing factors between the countries and recent
international economic and political situation changes. Analytical
material presented in the article is intended for a more detailed or
substantive analysis related to foreign economic relations of the
countries and Russia as well.
Abstract: Effect of Zn addition on the microstructure and
mechanical properties of Mg-Zn alloys with Zn contents from 6 to 10
weight percent was investigated in this study. Through calculation of
phase equilibria of Mg-Zn alloys, carried out by using FactSage® and
FTLite database, solution treatment temperature was decided as
temperatures from 300 to 400oC, where supersaturated solid solution
can be obtained. Solid solution treatment of Mg-Zn alloys was
successfully conducted at 380oC and supersaturated microstructure
with all beta phase resolved into matrix was obtained. After solution
treatment, hot rolling was successfully conducted by reduction of
60%. Compression and tension tests were carried out at room
temperature on the samples as-cast, solution treated, hot-rolled and
recrystallized after rolling. After solid solution treatment, each alloy
was annealed at temperatures of 180 and 200oC for time intervals from
1 min to 48 hrs and hardness of each condition was measured by
micro-Vickers method. Peak aging conditions were deduced as at the
temperature of 200oC for 10 hrs. By addition of Zn by 10 weight
percent, hardness and strength were enhanced.