Abstract: The design, manufacture, and operation of thin-walled
pressure vessels must be based on maximum safe operating pressure
and an adequate factor of safety (FoS). This research paper first
reports experimental evaluation of longitudinal and hoops stresses
based on working pressure as well as maximum pressure; and then
includes a critical study of factor of safety (FoS) in the design of a
glass fiber pressure vessel. Experimental work involved the use of
measuring instruments and the readings from pressure gauges.
Design calculations involved the computations of design stress and
FoS; the latter was based on breaking strength of 55 MPa for the
glass fiber (pressure-vessel material). The experimentally determined
FoS value has been critically compared with the general FoS allowed
in the design of glass fiber pressure vessels.
Abstract: Rotary draw bending is a method which is being used
in tube forming. In the tube bending process, the neutral axis moves
towards the inner arc and the wall thickness distribution changes for
tube’s cross section. Thinning takes place in the outer arc of the tube
(extrados) due to the stretching of the material, whereas thickening
occurs in the inner arc of the tube (intrados) due to the comparison of
the material. The calculations of the wall thickness distribution,
neutral axis shifting, and strain distribution have not been accurate
enough, so far. The previous model (the geometrical model)
describes the neutral axis shifting and wall thickness distribution. The
geometrical of the tube, bending radius and bending angle are
considered in the geometrical model, while the influence of the
material properties of the tube forming are ignored. The advanced
model is a modification of the previous model using material
properties that depends on the correction factor. The correction factor
is a purely empirically determined factor. The advanced model was
compared with the Finite element simulation (FE simulation) using a
different bending factor (Bf =bending radius/ diameter of the tube),
wall thickness (Wf = diameter of the tube/ wall thickness), and
material properties (strain hardening exponent). Finite element model
of rotary draw bending has been performed in PAM-TUBE program
(version: 2012). Results from the advanced model resemble the FE
simulation and the experimental test.
Abstract: The contact resistance between source/drain electrodes
and semiconductor layer is an important parameter affecting electron
transporting performance in the thin film transistor (TFT). In this
work, we introduced a transparent and the solution prossable
single-walled carbon nanotube (SWCNT)/Al-doped ZnO nano particle
(AZO NP) bilayer electrodes showing low contact resistance with
indium-oxide (In2O3) sol gel thin film. By inserting low work function
AZO NPs into the interface between the SWCNTs and the In2O3 which
has a high energy barrier, we could obtain an electrical Ohmic contact
between them. Finally, with the SWCNT-AZO NP bilayer electrodes,
we successfully fabricated a TFT showing a field effect mobility of
5.38 cm2/V·s at 250°C.
Abstract: Compositions of different molar ratios of
polymethylmethacrylate-co-methacrylic acid (PMMA-co-MAA)
were synthesized via free-radical polymerization. Polymer coated
surfaces have been produced on silicon wafers. Coated samples were
analyzed by atomic force microscopy (AFM). The results have shown
that the roughness of the surfaces have increased by increasing the
molar ratio of monomer methacrylic acid (MAA). This study reveals
that the gradual increase in surface roughness is due to the fact that
carboxylic functional groups have been generated by MAA segments.
Such surfaces can be desirable platforms for fabrication of the
biosensors for detection of the viruses and diseases.
Abstract: Equal channel angular pressing (ECAP) of
commercial Al-Mg-Si alloy was conducted using two strain rates.
The ECAP processing was conducted at room temperature and at
250°C. Route A was adopted up to a total number of four passes in
the present work. Structural evolution of the aluminum alloy discs
was investigated before and after ECAP processing using optical
microscopy (OM). Following ECAP, simple compression tests and
Vicker’s hardness were performed. OM micrographs showed that, the
average grain size of the as-received Al-Mg-Si disc tends to be larger
than the size of the ECAP processed discs. Moreover, significant
difference in the grain morphologies of the as-received and processed
discs was observed. Intensity of deformation was observed via the
alignment of the Al-Mg-Si consolidated particles (grains) in the
direction of shear, which increased with increasing the number of
passes via ECAP. Increasing the number of passes up to 4 resulted in
increasing the grains aspect ratio up to ~5. It was found that the
pressing temperature has a significant influence on the
microstructure, Hv-values, and compressive strength of the processed
discs. Hardness measurements demonstrated that 1-pass resulted in
increase of Hv-value by 42% compared to that of the as-received
alloy. 4-passes of ECAP processing resulted in additional increase in
the Hv-value. A similar trend was observed for the yield and
compressive strength. Experimental data of the Hv-values
demonstrated that there is a lack of any significant dependence on the
processing strain rate.
Abstract: The present study was undertaken to investigate the
effect of pre-aging and aging parameters (time and temperature) on
the mechanical properties of Al-Mg-Zn (7075) alloys. Ultimate
tensile strength, 0.5% offset yield strength and % elongation
measurements were carried out on specimens prepared from cast and
heat treated 7075 alloys. Aging treatments were carried out for the as
solution treated (SHT) specimens (after quenching in warm water).
The specimens were aged at different conditions; Natural aging was
carried out at room temperature for different periods of time. Double
aging was performed for SHT conditions (pre-aged at different time
and temperature followed by high temperature aging). Ultimate
tensile strength, yield strength and % elongation as a function of
different pre-aging and aging parameters are analyzed to acquire an
understanding of the effects of these variables and their interactions
on the mechanical properties of Be-treated 7075 alloys.
Abstract: The current study investigated the influence of milling
time and ball-to-powder (BPR) weight ratio on the microstructural
constituents and mechanical properties of bulk nanocrystalline Al;
Al-10%Cu; and Al-10%Cu-5%Ti alloys. Powder consolidation was
carried out using a high frequency induction heat sintering where the
processed metal powders were sintered into a dense and strong bulk
material. The powders and the bulk samples were characterized using
XRD and FEGSEM techniques. The mechanical properties were
evaluated at various temperatures of 25°C, 100°C, 200°C, 300°C and
400°C to study the thermal stability of the processed alloys. The
processed bulk nanocrystalline alloys displayed extremely high
hardness values even at elevated temperatures. The Al-10%Cu-5%Ti
alloy displayed the highest hardness values at room and elevated
temperatures which are related to the presence of Ti-containing
phases such as Al3Ti and AlCu2Ti. These phases are thermally stable
and retain the high hardness values at elevated temperatures up to
400ºC.
Abstract: In this study, composites were fabricated from oil
palm empty fruit bunch fiber and poly(lactic) acid by extrusion
followed by injection moulding. Surface of the fiber was pre-treated
by ultrasound in an alkali medium and treatment efficiency was
investigated by scanning electron microscopy (SEM) analysis and
Fourier transforms infrared spectrometer (FTIR). Effect of fiber
treatment on composite was characterized by tensile strength (TS),
tensile modulus (TM) and impact strength (IS). Furthermore,
biostrong impact modifier was incorporated into the treated fiber
composite to improve its impact properties. Mechanical testing
showed an improvement of up to 23.5% and 33.6% respectively for
TS and TM of treated fiber composite above untreated fiber
composite. On the other hand incorporation of impact modifier led to
enhancement of about 20% above the initial IS of the treated fiber
composite.
Abstract: A parametric study on circular thin-walled pipes
subjected to pure bending is performed. Both straight and curved
pipes are considered. Ratio D/t, initial pipe curvature and internal
pressure are the parameters varying in the analyses. The study is
mainly FEA-based.
It is found that negative curvatures (opposite to bending moment)
considerably increase stiffness and buckling limit of the pipe when no
internal pressure is acting and, similarly, positive curvatures decrease
the stiffness and buckling limit. For internal pressurised pipes the
effects of initial pipe curvature are less relevant. Results show that
this phenomenon is in relationship with the cross-section deformation
due to bending moment, which undergoes relevant ovalisation for no
pressurised pipes and little ovalisation for pressurised pipes.
Abstract: In the present work, the alloy of Bismuth-lead is
prepared on the basis of percentage of molecular weight 9:1, 5:5 and
1:9 ratios and grown by Zone- Refining Technique under a vacuum
atmosphere. The EDAX of these samples are done and the results are
reported. Micro hardness test has been used as an alternative test for
measuring material’s tensile properties. The effect of temperature and
load on the hardness of the grown alloy has been studied. Further the
comparative studies of work hardening coefficients are reported.
Abstract: In this research the effects of adding silica and
alumina nanoparticles on flow ability and compressive strength of
cementitious composites based on Portland cement were investigated.
In the first stage, the rheological behavior of different samples
containing nanosilica, nanoalumina and polypropylene, polyvinyl
alcohol and polyethylene fibers were evaluated. With increasing of
nanoparticles in fresh samples, the slump flow diameter reduced.
Fibers reduced the flow ability of the samples and viscosity
increased. With increasing of the micro silica particles to cement
ratio from 2/1 to 2/2, the slump flow diameter increased. By adding
silica and alumina nanoparticles up to 3% and 2% respectively, the
compressive strength increased and after decreased. Samples
containing silica nanoparticles and fibers had the highest compressive
strength.
Abstract: Physical properties of uranium dinitride (UN2) were
investigated in detail using first principle calculations based on
density functional theory (DFT). To study the strong correlation
effects due to 5f uranium valence electrons, the on-site coulomb
interaction correction U via the Hubbard-like term (DFT+U) was
employed. The UN2 structural, mechanical and thermodynamic
properties were calculated within DFT and Various U of DFT+U
approach.
The Perdew–Burke–Ernzerhof (PBE.5.2) version of the
generalized gradient approximation (GGA) is used to describe the
exchange-correlation with the projector-augmented wave (PAW)
pseudo potentials.
A comparative study shows that results are improved by using the
Hubbard formalism for a certain U value correction like the structural
parameter. For some physical properties the variation versus
Hubbard-U is strong like Young modulus but for others it is weakly
noticeable such as bulk modulus.
We noticed also that from U=7.5 eV, elastic results don’t agree
with the cubic cell because of the C44 values which turn out to be
negative.
Abstract: The present study was undertaken to investigate the
effect of aging parameters (time and temperature) on the mechanical
properties of Be-and/or Zr- treated Al-Mg-Zn (7075) alloys. Ultimate
tensile strength, 0.5% offset yield strength and % elongation
measurements were carried out on specimens prepared from cast and
heat treated 7075 alloys containing Be and/or Zr. Different aging
treatment were carried out for the as solution treated (SHT)
specimens (after quenching in warm water). The specimens were
aged at different conditions; Natural and artificial aging was carried
out at room temperature, 120C, 150C, 180C and 220C for different
periods of time. Duplex aging was performed for SHT conditions
(pre-aged at different time and temperature followed by high
temperature aging). Ultimate tensile strength, yield strength and %
elongation data results as a function of different aging parameters are
analysed. A statistical design of experiments (DOE) approach using
fractional factorial design is applied to acquire an understanding of
the effects of these variables and their interactions on the mechanical
properties of Be- and/or Zr- treated 7075 alloys. Mathematical
models are developed to relate the alloy mechanical properties with
the different aging parameters.
Abstract: Fiber Bragg optic sensor is embedded in composite
material to detect and monitor the damage that occurs in composite
structures. In this paper, we deal with the mode-Ι delamination to
determine the material strength to crack propagation, using the
coupling mode theory and T-matrix method to simulate the FBGs
spectrum for both uniform and non-uniform strain distribution. The
double cantilever beam test is modeled in FEM to determine the
longitudinal strain. Two models are implemented, the first is the
global half model, and the second is the sub-model to represent the
FBGs with higher refined mesh. This method can simulate damage in
composite structures and converting strain to a wavelength shifting in
the FBG spectrum.
Abstract: Sandwich structure composites produced by epoxy
core and aluminium skin were developed as potential building
materials. Interface bonding between core and skin was controlled by
varying kenaf content. Five different weight percentage of kenaf
loading ranging from 10 wt% to 50 wt% were employed in the core
manufacturing in order to study the mechanical properties of the
sandwich composite. Properties of skin aluminium with epoxy were
found to be affected by drying time of the adhesive. Mechanical
behavior of manufactured sandwich composites in relation with
properties of constituent materials was studied. It was found that 30
wt% of kenaf loading contributed to increase the flexural strength and
flexural modulus up to 102 MPa and 32 GPa, respectively. Analysis
were done on the flatwise and edgewise compression test. For
flatwise test, it was found that 30 wt% of fiber loading could
withstand maximum force until 250 kN, with compressive strength
results at 96.94 MPa. However, at edgewise compression test, the
sandwich composite with same fiber loading only can withstand 31
kN of the maximum load with 62 MPa of compressive strength
results.
Abstract: In this paper, two options of anodic alumina barrier
layer thinning have been demonstrated. The approaches varied with
the duration of the voltage step. It was found that too long step of the
barrier layer thinning process leads to chemical etching of the
nanopores on their top. At the bottoms pores are not fully opened
what is disadvantageous for further applications in nanofabrication.
On the other hand, while the duration of the voltage step is controlled
by the current density (value of the current density cannot exceed
75% of the value recorded during previous voltage step) the pores are
fully opened. However, pores at the bottom obtained with this
procedure have smaller diameter, nevertheless this procedure
provides electric contact between the bare aluminum (substrate) and
electrolyte, what is suitable for template assisted electrodeposition,
one of the most cost-efficient synthesis method in nanotechnology.
Abstract: The dielectric properties and ionic conductivity of
novel "ceramic state" polymer electrolytes for high capacity lithium
battery are characterized by Radio frequency and Microwave
methods in two broad frequency ranges from 50 Hz to 20 KHz and 4
GHz to 40 GHz. This innovative solid polymer electrolyte which is
highly ionic conductive (10-3 S/cm at room temperature) from -40oC
to +150oC can be used in any battery application. Such polymer
exhibits properties more like a ceramic rather than polymer. The
various applied measurement methods produced accurate dielectric
results for comprehensive analysis of electrochemical properties and
ion transportation mechanism of this newly invented polymer
electrolyte. Two techniques and instruments employing air gap
measurement by Capacitance Bridge and in-waveguide measurement
by vector network analyzer are applied to measure the complex
dielectric spectra. The complex dielectric spectra are used to
determine the complex alternating current electrical conductivity and
thus the ionic conductivity.
Abstract: Waste silicon carbide (waste SiC) filled high-density
polyethylene (HDPE) with and without surface modifiers were
studied. Two types of surface modifiers namely; high-density
polyethylene-grafted-maleic anhydride (HDPE-g-MA) and 3-aminopropyltriethoxysilane have been used in this study. The
composites were produced using a two roll mill, extruder and shaped
in a hydraulic compression molding machine. The mechanical
properties of polymer composites such as flexural strength and
modulus, impact strength, tensile strength, stiffness and hardness
were investigated over a range of compositions. It was found that,
flexural strength and modulus, tensile modulus and hardness
increased, whereas impact strength and tensile strength decreased
with the increasing in filler contents, compared to the neat HDPE. At
similar filler content, the effect of both surface modifiers increased
flexural modulus, impact strength, tensile strength and stiffness but
reduced the flexural strength. Morphological investigation using
SEM revealed that the improvement in mechanical properties was
due to enhancement of the interfacial adhesion between waste SiC
and HDPE.
Abstract: An investigation into Cahn-Hilliard equation was
carried out through numerical simulation to identify a possible phase
separation for one and two dimensional domains. It was observed that
this equation can reproduce important mass fluxes necessary for
phase separation within the miscibility gap and for coalescence of
particles.
Abstract: The objective of this study was to identify the optimal
level of partial replacement of Portland cement by the ashes
originating from burning straw and bagasse from sugar cane (ASB).
Order to this end, were made five series of flat plates and cylindrical
bodies: control and others with the partial replacement in 20, 30, 40
and 50% of ASB in relation to the mass of the Ordinary Portland
cement, and conducted a mechanical testing of simple axial
compression (cylindrical bodies) and the four-point bending (flat
plates) and determined water absorption (WA), bulk density (BD)
and apparent void volume (AVV) on both types of specimens. Based
on the data obtained, it may be noted that the control treatment
containing only Portland cement, obtained the best results. However,
the cylindrical bodies with 20% ashes showed better results
compared to the other treatments. And in the formulations plates, the
treatment which showed the best results was 30% cement
replacement by ashes.