Abstract: Single-phase, high band gap energy Zn0.5Mg0.5O films were grown under oxygen pressure, using pulse laser deposition with a Zn0.5Mg0.5O target. Structural characterization studies revealed that the crystal structures of the ZnX-1MgXO films could be controlled via changes in the oxygen pressure. TEM analysis showed that the thickness of the deposited Zn1-xMgxO thin films was 50–75 nm. As the oxygen pressure increased, we found that one axis of the crystals did not show a very significant increase in the crystallization compared with that observed at low oxygen pressure. The X-ray diffraction peak intensity for the hexagonal-ZnMgO (002) plane increased relative to that for the cubic-ZnMgO (111) plane. The corresponding c-axis of the h-ZnMgO lattice constant increased from 5.141 to 5.148 Å, and the a-axis of the c-ZnMgO lattice constant decreased from 4.255 to 4.250 Å. EDX analysis showed that the Mg content in the mixed-phase ZnMgO films decreased significantly, from 54.25 to 46.96 at.%. As the oxygen pressure was increased from 100 to 150 mTorr, the absorption edge red-shifted from 3.96 to 3.81 eV; however, a film grown at the highest oxygen pressure tested here (200 mTorr).
Abstract: This study compared the mechanical and microstructural properties produced during friction stir welding (FSW) of S275 structural steel in air and underwater. Post weld tests assessed the tensile strength, micro-hardness, distortion, Charpy impact toughness and fatigue performance in each case. The study showed that there was no significant difference in the strength, hardness or fatigue life of the air and underwater specimens. However, Charpy impact toughness was shown to decrease for the underwater specimens and was attributed to a lower degree of recrystallization caused by the higher rate of heat loss experienced when welding underwater. Reduced angular and longitudinal distortion was observed in the underwater welded plate compared to the plate welded in air.
Abstract: Effect of 2wt% Cu addition on tensile properties and
fracture behavior of Al-6Si-0.5Mg-2Ni alloy at various strain rates
were studied. The solution treated Al-6Si-0.5Mg-2Ni (-2Cu) alloys,
were aged isochronally for 1 hour at temperatures up to 300oC. The
uniaxial tension test was carried out at strain rate ranging from 10-4s-1
to 10-2s-1 in order to investigate the strain rate dependence of tensile
properties. Tensile strengths were found to increase with ageing
temperature and the maximum being attained ageing for 1 hr at
225oC (peak aged condition). Addition of 2wt% Cu resulted in an
increase in tensile properties at all strain rates. Evaluation of tensile
properties at three different strain rates (10-4, 10-3 and 10-2 s-1)
showed that strain rates affected the tensile properties significantly.
At higher strain rates the strength was better but ductility was poor.
Microstructures of broken specimens showed that both the void
coalescence and the interface debonding affect the fracture behavior
of the alloys
Abstract: Two new metal-based anticancer chemotherapeutic
agents, [(Ph2Sn)2(HGuO)2(phen)Cl2] 1 and [(Ph3Sn)(HGuO)(phen)]-
Cl.CH3OH.H2O 2, were designed, prepared and characterized by
analytical and spectral (IR, ESI-Mass, 1H, 13C and 119Sn NMR)
techniques. The proposed geometry of Sn(IV) in 1 and 2 is distorted
octahedral and distorted trigonal-bipyramidal, respectively. Both 1
and 2 exhibit potential cytotoxicity in vitro against MCF-7, HepG-2
and DU-145 cell lines. The intrinsic binding constant (Kb) values of 1
(2.33 × 105 M-1) and 2 (2.46 × 105 M-1) evaluated from UV-Visible
absorption studies suggest non-classical electrostatic mode of
interaction via phosphate backbone of DNA double helix. The Stern-
Volmer quenching constant (Ksv) of 1 (9.74 × 105 M-1) and 2 (2.9 ×
106 M-1) determined by fluorescence studies suggests the groove
binding and intercalation mode for 1 and 2, respectively. Effective
cleavage of pBR322 DNA is induced by 1.Their interaction with
DNA of cancer cells may account for potency.
Abstract: The analysis and design of thin shell structures is a topic of interest in a variety of engineering applications. In structural mechanics problems the analyst seeks to determine the distribution of stresses throughout the structure to be designed. It is also necessary to calculate the displacements of certain points of the structure to ensure that specified allowable values are not exceeded. In this paper a comparative study between displacement and strain based finite elements applied to the analysis of some thin shell structures is presented. The results obtained from some examples show the efficiency and the performance of the strain based approach compared to the well known displacement formulation.
Abstract: In recent years many finite elements have been
developed for plate bending analysis. The formulated elements are
based on the strain based approach. This approach leads to the
representation of the displacements by higher order polynomial terms
without the need for the introduction of additional internal and
unnecessary degrees of freedom. Good convergence can also be
obtained when the results are compared with those obtained from the
corresponding displacement based elements, having the same total
number of degrees of freedom. Furthermore, the plate bending
elements are free from any shear locking since they converge to the
Kirchhoff solution for thin plates contrarily for the corresponding
displacement based elements. In this paper the efficiency of the strain
based approach compared to well known displacement formulation is
presented. The results obtained by a new formulated plate bending
element based on the strain approach and Kirchhoff theory are
compared with some others elements. The good convergence of the
new formulated element is confirmed.
Abstract: This paper conducts a comparison study using KES-FB and PhabrOmeter to measure 58 selected warp knitted fabric hand properties. Fabric samples were selected and measured by both KES-FB and PhabrOmeter. Results show differences between these two measurement methods. Smoothness and stiffness values obtained by KES-FB were found significant correlated (p value = 0.003 and 0.022) to the PhabrOmeter results while softness values between two measurement methods did not show significant correlation (p value = 0.828). Disagreements among these two measurement methods imply limitations on different mechanism principles when facing warp knitted fabrics. Subjective measurement methods and further studies are suggested in order to ascertain deeper investigation on the mechanisms of fabric hand perceptions.
Abstract: Metal matrix composites (MMCs) have gained a
considerable interest in the last three decades. Conventional powder
metallurgy production route often involves the addition of reinforcing
phases into the metal matrix directly, which leads to poor wetting
behavior between ceramic phase and metal matrix and the
segregation of reinforcements. The commonly used elements for
ceramic phase formation in iron based MMCs are Ti, Nb, Mo, W, V
and C, B. The aim of the present paper is to investigate the effect of
sintering temperature and V-B addition on densification, phase
development, microstructure, and hardness of Fe–V-B composites
(Fe-(5-10) wt. %B – 25 wt. %V alloys) prepared by powder
metallurgy process. Metal powder mixes were pressed uniaxial and
sintered at different temperatures (ranging from 1300 to 1400ºC) for
1h. The microstructure of the (V, B) Fe composites was studied with
the help of high magnification optical microscope and XRD.
Experimental results show that (V, B) Fe composites can be produced
by conventional powder metallurgy route.
Abstract: Biometallic materials are the most important materials for use in biomedical applications especially in manufacturing a variety of biological artificial replacements in a modern worlds, e.g. hip, knee or shoulder joints, due to their advanced characteristics. Titanium (Ti) and its alloys are used extensively in biomedical applications based on their high specific strength and excellent corrosion resistance. Beta-Ti alloys containing completely biocompatible elements are exceptionally prospective materials for manufacturing of bioimplants. They have superior mechanical, chemical and electrochemical properties for use as biomaterials. These biomaterials have the ability to introduce the most important property of biochemical compatibility which is low elastic modulus. This review examines current information on the recent developments in alloying elements leading to improvements of beta Ti alloys for use as biomaterials. Moreover, this paper focuses mainly on the evolution, evaluation and development of the modulus of elasticity as an effective factor on the performance of beta alloys.
Abstract: A new algorithm based on the lattice Boltzmann method (LBM) is proposed as a potential solver for one-dimensional heat and mass transfer for isothermal carbonization of wood particles. To check the validity of this algorithm, the LBM results have been compared with the published data and a good agreement is obtained. Then, the model is used to study the effect of reactor temperature and particle size on the evolution of the local temperature and mass loss inside the wood particle.
Abstract: Al-Si-Mg-Ni(-Cu) alloys are widely used in the automotive industry. They have the advantage of low weight associated with low coefficient of thermal expansion and excellent mechanical properties – mainly at high temperatures. The corrosion resistance of these alloys in coastal area, particularly sea water, however is not yet known. In this investigation, electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization have been used to evaluate the corrosion resistance of Al-6Si-0.5Mg-2Ni (-2Cu) alloys in simulated sea water environments. The potentiodynamic polarization curves reveal that 2 wt% Cu content alloy (Alloy-2) is more prone to corrosion than the Cu free alloy (Alloy-1). But the EIS test results showed that corrosion resistance or charge transfer resistance (Rct) increases with the addition of Cu. Due to addition of Cu and thermal treatment, the magnitude of open circuit potential (OCP), corrosion potential (Ecorr) and pitting corrosion potential (Epit) of Al-6Si-0.5Mg-2Ni alloy in NaCl solution were shifted to the more noble direction.
Abstract: Strontium hexaferrite (SrFe12O19; Sr-ferrite) is one of
the well-known materials for permanent magnets. In this study, Mtype
strontium ferrite was prepared by following the conventional
ceramic method from steelmaking by-product. Initial materials;
SrCO3 and by-product, were mixed together in the composition of
SrFe12O19 in different Sr/Fe ratios. The mixtures of these raw
materials were dry-milled for 6h. The blended powder was presintered
(i.e. calcination) at 1000°C for different times periods, then
cooled down to room temperature. These pre-sintered samples were
re-milled in a dry atmosphere for 1h and then fired at different
temperatures in atmospheric conditions, and cooled down to room
temperature. The produced magnetic powder has a dense hexagonal
grain shape structure. The calculated energy product values for the
produced samples ranged from 0.3 to 2.4 MGOe.
Abstract: This study investigates the effect of moisture
conditioning on the Indirect Tensile Strength (ITS) of asphalt
concrete. As a first step, cylindrical samples of 100 mm diameter and
50 mm thick were prepared using a Superpave gyratory compactor.
Next, the samples were conditioned using Moisture Induced
Susceptibility Test (MIST) device at different numbers of moisture
conditioning cycles. In the MIST device, samples are subjected water
pressure through the sample pores cyclically. The MIST conditioned
samples were tested for ITS. Results show that the ITS does not
change significantly with MIST conditioning at the specific pressure
and cycles adopted in this study.
Abstract: Three dimensional non-Interlaced carbon fibre
reinforced silicon carbide (3-D-Cf/SiC) composites with pyrocarbon
interphase were fabricated using isothermal chemical vapor
infiltration (ICVI) combined with polymer impregnation pyrolysis
(PIP) process. Polysilazane (PSZ) is used as a preceramic polymer to
obtain silicon carbide matrix. Thermo gravimetric analysis (TGA),
Infrared spectroscopic analysis (IR) and X-ray diffraction (XRD)
analysis were carried out on PSZ pyrolysed at different temperatures
to understand the pyrolysis and obtaining the optimum pyrolysing
condition to yield β-SiC phase. The density of the composites was
1.94 g cm-3 after the 3-D carbon preform was SiC infiltrated for 280 h
with one intermediate polysilazane pre-ceramic PIP process.
Mechanical properties of the composite materials were investigated
under tensile, flexural, shear and impact loading. The values of
tensile strength were 200 MPa at room temperature (RT) and 195
MPa at 500°C in air. The average RT flexural strength was 243 MPa.
The lower flexural strength of these composites is because of the
porosity. The fracture toughness obtained from single edge notched
beam (SENB) technique was 39 MPa.m1/2. The work of fracture
obtained from the load-displacement curve of SENB test was 22.8
kJ.m-2. The composites exhibited excellent impact resistance and the
dynamic fracture toughness of 44.8 kJ.m-2 is achieved as determined
from instrumented Charpy impact test. The shear strength of the
composite was 93 MPa, which is significantly higher compared 2-D
Cf/SiC composites. Microstructure evaluation of fracture surfaces
revealed the signatures of fracture processes and showed good
support for the higher toughness obtained.
Abstract: In this paper, strontium ferrite (SrO.6Fe2O3) was
synthesized by the sol-gel auto-combustion process. The thermal
behavior of powder obtained from self-propagating combustion of
initial gel was evaluated by simultaneous differential thermal analysis
(DTA) and thermo gravimetric (TG), from room temperature to
1200°C. The as-burnt powder was calcined at various temperatures
from 700-900°C to achieve the single-phase Sr-ferrite. Phase
composition, morphology and magnetic properties were investigated
using X-ray diffraction (XRD), transmission electron microscopy
(TEM) and vibrating sample magnetometry (VSM) techniques.
Results showed that the single-phase and nano-sized hexagonal
strontium ferrite particles were formed at calcination temperature of
800°C with crystallite size of 27 nm and coercivity of 6238 Oe.
Abstract: The paper a summary of the results of concretes with
partial substitution of natural aggregates with recycled concrete is
solved. Design formulas of the concretes were characterised with 20,
40 and 60% substitution of natural 8-16mm fraction aggregates with
a selected recycled concrete of analogous coarse fractions. With the
product samples an evaluation of coarse fraction aggregates influence
on fresh concrete consistency and concrete strength in time was
carried out. The results of concretes with aggregates substitution will
be compared to reference formula containing only the fractions of
natural aggregates.
Abstract: In this study, a three dimensional numerical heat
transfer model has been used to simulate the laser structuring of
polymer substrate material in the Three-Dimensional Molded
Interconnect Device (3D MID) which is used in the advanced multifunctional
applications. A finite element method (FEM) transient
thermal analysis is performed using APDL (ANSYS Parametric
Design Language) provided by ANSYS. In this model, the effect of
surface heat source was modeled with Gaussian distribution, also the
effect of the mixed boundary conditions which consist of convection
and radiation heat transfers have been considered in this analysis. The
model provides a full description of the temperature distribution, as
well as calculates the depth and the width of the groove upon material
removal at different set of laser parameters such as laser power and
laser speed. This study also includes the experimental procedure to
study the effect of laser parameters on the depth and width of the
removal groove metal as verification to the modeled results. Good
agreement between the experimental and the model results is
achieved for a wide range of laser powers. It is found that the quality
of the laser structure process is affected by the laser scan speed and
laser power. For a high laser structured quality, it is suggested to use
laser with high speed and moderate to high laser power.
Abstract: Chloride resistance in Ultra High Performance
Concrete (UHPC) is determined in this paper. This work deals with
the one dimension chloride transport, which can be potentially
dangerous particularly for the durability of concrete structures. Risk
of reinforcement corrosion due to exposure to the concrete surface to
direct the action of chloride ions (mainly in the form de-icing salts or
groundwater) is dangerously increases. The measured data are
investigated depending on the depth of penetration of chloride ions
into the concrete structure. Comparative measurements with normal
strength concrete are done as well. The experimental results showed
that UHCP have improved resistance of chlorides penetration than
NSC and also chloride diffusion depth is significantly lower in
UHCP.
Abstract: In the present work, the effect of load and sliding
distance on the performance tribology of commercially used
aluminium-silicon engine block and piston was evaluated at ambient
conditions with humidity of 80% under dry sliding conditions using a
pin-on-disc with two different loads of 5N and 20N yielding applied
pressure of 0.30MPa and 1.4MPa, respectively, at sliding velocity of
0.29ms-1 and with varying sliding distance ranging from 260m-
4200m. Factors and conditions that had significant effect were
identified. The results showed that the load and the sliding distance
affect the wear rate of the alloys and the wear rate increased with
increasing load for both the alloys. Wear rate also increases almost
linearly at low loads and increase to a maximum then attain a plateau
with increasing sliding distance. For both applied loads the piston
alloy showed the better performance due to higher Ni and Mg
content. The worn surface and wear debris was characterized by
optical microscope, SEM and EDX analyzer. The worn surface was
characterized by surface with shallow grooves at loads while the
groove width and depth increased as the loads increases. Oxidative
wear was found to be the predominant mechanisms in the dry sliding
of Al-Si alloys at low loads.
Abstract: Fritillaria oranensis (Liliaceae) was described in 1874
by pomel from Algeria. Plant samples have been collected from the
mount of Tessala (Sidi-Bel-Abbes). The morphological features of
various organs of the plant are described in detail. In the
morphological part of the study, features of various organs of the
plants such as stem and leaf were determined and illustrated.
Ecological studies provide information about the physical and
chemical structure of soil types in Tessala Mountain. The aim of this
original investigation is to put forth ecological and anatomical
features of these species for the first time, but at the same time given
detailed account of the morphological characteristics of the stem and
leaf of Fritillaria oranensis.