Abstract: The massive demolition of old buildings in recent years has generated tons of waste, especially brick waste. Thus, a concern of recent research is the use of this waste for the production of environmentally friendly concrete. At the same time, corrosion of the reinforcement steel rebar in classical concrete is a current problem. In this context, in the present paper a study was carried out on the corrosion of metal reinforcement in cement mortars with added brick waste. The corrosion process was analyzed on four compositions of mortars without and with 15%, 25% and 35% brick waste replacing the sand. The brick waste has majority content in SiO2, Al2O3, FeO3 and CaO. The grain size distribution of brick waste was close to that of the sand (dmax = 2 mm). The preparation method of the samples was similar to ordinary mortars. The corrosion action on the rebar in concrete, at different brick waste concentrations, was investigated by electrochemical measurements (polarization curves and electrochemical impedance spectroscopy (EIS)) at 1 month and 26 months. The results obtained at 26 months revealed that the addition of the brick waste in mortar improved the anticorrosion properties in the case of all samples compared with the etalon mortar. The best results were obtained in the case of the sample with 15% brick waste (the efficiency was ≈ 90%). The corrosion intermediary layer formed on the rebar surface was evidenced by SEM-EDX.
Abstract: Phenol is a hazardous material found in many industrial wastewaters. Photocatalytic degradation and furthermore catalyst doping are promising techniques in purpose of effective phenol removal, which have been studied comprehensively in this decade. In this study, Fe, Cr codoped TiO2 were prepared by sol-gel method, and its photocatalytic activity was investigated through degradation of phenol under visible light. The catalyst was characterized by XRD, SEM, FT-IR, BET, and EDX. The results showed that nanoparticles possess anatase phase, and the average size of nanoparticles was about 21 nm. Also, photocatalyst has significant surface area. Effect of experimental parameters such as pH, irradiation time, pollutant concentration, and catalyst concentration were investigated by using Design-Expert® software. 98% of phenol degradation was achieved after 6h of irradiation.
Abstract: Cytotoxic platinum compounds play a major role in the chemotherapy of a large number of human cancers. However, due to the severe side effects for the patient and other problems associated with their use, there is a need for the development of more efficient drugs and new methods for their selective delivery to the tumours. One way to achieve the latter could be in the use of nanoparticular substrates that can adsorb or chemically bind the drug. In the cell, the drug is supposed to be slowly released, either by physical desorption or by dissolution of the particle framework. Ideally, the cytotoxic properties of the platinum drug unfold only then, in the cancer cell and over a longer period of time due to the gradual release. In this paper, we report on our first steps in this direction. The binding properties of a series of cytotoxic Pt(II) oxadiazoline compounds to mesoporous silica particles has been studied by NMR and UV/vis spectroscopy. High loadings were achieved when the Pt(II) compound was relatively polar, and has been dissolved in a relatively nonpolar solvent before the silica was added. Typically, 6-10 hours were required for complete equilibration, suggesting the adsorption did not only occur to the outer surface but also to the interior of the pores. The untreated and Pt(II) loaded particles were characterised by C, H, N combustion analysis, BET/BJH nitrogen sorption, electron microscopy (REM and TEM) and EDX. With the latter methods we were able to demonstrate the homogenous distribution of the Pt(II) compound on and in the silica particles, and no Pt(II) bulk precipitate had formed. The in vitro cytotoxicity in a human cancer cell line (HeLa) has been determined for one of the new platinum compounds adsorbed to mesoporous silica particles of different size, and compared with the corresponding compound in solution. The IC50 data are similar in all cases, suggesting that the release of the Pt(II) compound was relatively fast and possibly occurred before the particles reached the cells. Overall, the platinum drug is chemically stable on silica and retained its activity upon prolonged storage.
Abstract: In the present work, the effect of load and sliding
distance on the performance tribology of commercially used
aluminium-silicon engine block and piston was evaluated at ambient
conditions with humidity of 80% under dry sliding conditions using a
pin-on-disc with two different loads of 5N and 20N yielding applied
pressure of 0.30MPa and 1.4MPa, respectively, at sliding velocity of
0.29ms-1 and with varying sliding distance ranging from 260m-
4200m. Factors and conditions that had significant effect were
identified. The results showed that the load and the sliding distance
affect the wear rate of the alloys and the wear rate increased with
increasing load for both the alloys. Wear rate also increases almost
linearly at low loads and increase to a maximum then attain a plateau
with increasing sliding distance. For both applied loads the piston
alloy showed the better performance due to higher Ni and Mg
content. The worn surface and wear debris was characterized by
optical microscope, SEM and EDX analyzer. The worn surface was
characterized by surface with shallow grooves at loads while the
groove width and depth increased as the loads increases. Oxidative
wear was found to be the predominant mechanisms in the dry sliding
of Al-Si alloys at low loads.
Abstract: Cancer becomes one of the leading cause of death in
many countries over the world. Fourier-transform infrared (FTIR)
spectra of human lung cancer cells (A549) treated with PMF (natural
product extracted from PM 701) for different time intervals were
examined. Second derivative and difference method were taken in
comparison studies. Cesium (Cs) and Rubidium (Rb) nanoparticles in
PMF were detected by Energy Dispersive X-ray attached to Scanning
Electron Microscope SEM-EDX. Characteristic changes in protein
secondary structure, lipid profile and changes in the intensities of
DNA bands were identified in treated A549 cells spectra. A
characteristic internucleosomal ladder of DNA fragmentation was
also observed after 30 min of treatment. Moreover, the pH values
were significantly increases upon treatment due to the presence of Cs
and Rb nanoparticles in the PMF fraction. These results support the
previous findings that PMF is selective anticancer agent and can
produce apoptosis to A549 cells.