Abstract: PVC foam-fly ash composites (PVC-FA) are
characterized for their structural, morphological, mechanical and
thermal properties. The tensile strength of the composites increased
modestly with higher fly ash loading, while there was a significant
increase in the elastic modulus for the same composites. On the other
hand, a decrease in elongation at UTS was observed upon increasing
fly ash content due to increased rigidity of the composites. Similarly,
the flexural modulus increased as the fly ash loading increased,
where the composites containing 25 phr fly ash showed the highest
flexural strength. Thermal properties of PVC-fly ash composites were
determined by Thermo Gravimetric Analysis (TGA). The
microstructural properties were studied by Scanning Electron
Microscopy (SEM). SEM results confirm that fly ash particles were
mechanically interlocked in PVC matrix with good interfacial
interaction with the matrix. Particle agglomeration and debonding
was observed in samples containing higher amounts of fly ash.
Abstract: Nanocrystalline powders of the lead-free piezoelectric
material, tantalum-substituted potassium sodium niobate
(K0.5Na0.5)(Nb0.9Ta0.1)O3 (KNNT), were produced using a Retsch
PM100 planetary ball mill by setting the milling time to 15h, 20h,
25h, 30h, 35h and 40h, at a fixed speed of 250rpm. The average
particle size of the milled powders was found to decrease from 12nm
to 3nm as the milling time increases from 15h to 25h, which is in
agreement with the existing theoretical model. An anomalous
increase to 98nm and then a drop to 3nm in the particle size were
observed as the milling time further increases to 30h and 40h
respectively. Various sizes of these starting KNNT powders were
used to investigate the effect of milling time on the microstructure,
dielectric properties, phase transitions and piezoelectric properties of
the resulting KNNT ceramics. The particle size of starting KNNT
was somewhat proportional to the grain size. As the milling time
increases from 15h to 25h, the resulting ceramics exhibit
enhancement in the values of relative density from 94.8% to 95.8%,
room temperature dielectric constant (εRT) from 878 to 1213, and
piezoelectric charge coefficient (d33) from 108pC/N to 128pC/N. For
this range of ceramic samples, grain size refinement suppresses the
maximum dielectric constant (εmax), shifts the Curie temperature (Tc)
to a lower temperature and the orthorhombic-tetragonal phase
transition (Tot) to a higher temperature. Further increase of milling
time from 25h to 40h produces a gradual degradation in the values of
relative density, εRT, and d33 of the resulting ceramics.
Abstract: The edge waviness in hot rolled steel is a common
defect. Variables that affect such defect include raw material and
machine. These variables are necessary to consider to understand
such defect. This research studied the defect of edge waviness for SS
400 of metal sheet manufacture. Defect of metal sheets were divided
into two groups. The specimens were investigated on chemical
composition and mechanical properties to find the difference. The
results of investigation showed that the difference was not significant.
Therefore the roll mill machine should be used to adjust to support
another location on a roller to avoide edge waviness.
Abstract: Heavy rare earth (HRE) oxalate concentrates were
prepared from the Egyptian crude monazite sand (graded about 47%).
The concentrates were specified quantitatively for their constituents
of individual rare earth elements using ion chromatograph (IC) and
qualitatively by scanning electron microscope (SEM) for the other
major constituents. The 1st concentrate was composed of 10.5%
HREE where 7.25% of them represented yttrium. The 2nd concentrate
contained about 41.7% LREE, 17.5% HREE and 13.6% Th. The
LREE involved 18.3% Ce, 10.5% La and 8% Nd while the HREE
were 8.7% Y, 3.5% Gd and 2.9% Dy. The 3rd concentrate was
containing about 8.0% LREE (3.7% Ce, 2.0% La and 1.5% Nd),
10.2% HREE (6.4% yttrium and 2.0% Dy) and 2.1% uranium. The
final concentrate comprised 0.84% uranium beside iron, chromium
and traces of REE.
Abstract: Self-compacting concrete (SCC) developed in Japan
in the late 80s has enabled the construction industry to reduce
demand on the resources, improve the work condition and also
reduce the impact of environment by elimination of the need for
compaction. Fuzzy logic (FL) approaches has recently been used to
model some of the human activities in many areas of civil
engineering applications. Especially from these systems in the model
experimental studies, very good results have been obtained. In the
present study, a model for predicting compressive strength of SCC
containing various proportions of fly ash, as partial replacement of
cement has been developed by using Fuzzy Inference System (FIS).
For the purpose of building this model, a database of experimental
data were gathered from the literature and used for training and
testing the model. The used data as the inputs of fuzzy logic models
are arranged in a format of five parameters that cover the total binder
content, fly ash replacement percentage, water content,
superplasticizer and age of specimens. The training and testing results
in the fuzzy logic model have shown a strong potential for predicting
the compressive strength of SCC containing fly ash in the considered
range.
Abstract: To develop AZ91D magnesium alloys with improved
properties, we have applied TiN and VN/TiN multilayer coatings
using DC magnetron sputter technique. Coating structure, surface
morphology, chemical bonding and corrosion resistance of coatings
were analyzed by x-ray diffraction (XRD), scanning electron
microscope (SEM), x-ray photoelectron spectroscopy (XPS), and
tafel extrapolation method, respectively. XPS analysis reveal that VN
overlayer reacts with oxygen at the VN/TiN interface and forms more
stable TiN layer. Morphological investigations and the corrosion
results show that VN/TiN multilayer thin film coatings are quite
effective to optimize the corrosion resistance of Mg alloys.
Abstract: This study investigates how AlGaAs/GaAs thin film
solar cells perform under varying global solar spectrum due to the
changes of environmental parameters such as the air mass and the
atmospheric turbidity. The solar irradiance striking the solar cell is
simulated using the spectral irradiance model SMARTS2 (Simple
Model of the Atmospheric Radiative Transfer of Sunshine) for clear
skies on the site of Setif (Algeria). The results show a reduction in the
short circuit current due to increasing atmospheric turbidity, it is
63.09% under global radiation. However increasing air mass leads to
a reduction in the short circuit current of 81.73%. The efficiency
decreases with increasing atmospheric turbidity and air mass.
Abstract: The paper involves a chain of activities from
synthesis, establishment of the methodology for characterization and
testing of novel protective materials through the pilot production and
application on model supports.
It summarizes the results regarding the development of the pilot
production protocol for newly developed self-cleaning materials. The
optimization of the production parameters was completed in order to
improve the most important functional properties (mineralogy
characteristics, particle size, self-cleaning properties and
photocatalytic activity) of the newly designed nanocomposite
material.
Abstract: This paper investigates the viability of using carbon
fiber reinforced epoxy composites modified with carbon nanotubes to
strengthening reinforced concrete (RC) columns. Six RC columns
was designed and constructed according to ASCE standards. The
columns were wrapped using carbon fiber sheets impregnated with
either neat epoxy or CNTs modified epoxy. These columns were then
tested under concentric axial loading. Test results show that;
compared to the unwrapped specimens; wrapping concrete columns
with carbon fiber sheet embedded in CNTs modified epoxy resulted
in an increase in its axial load resistance, maximum displacement,
and toughness values by 24%, 109% and 232%, respectively. These
results reveal that adding CNTs into epoxy resin enhanced the
confinement effect, specifically, increased the axial load resistance,
maximum displacement, and toughness values by 11%, 6%, and
19%, respectively compared with columns strengthening with carbon
fiber sheet embedded in neat epoxy.
Abstract: In this research, waterglass based aerogel powder was
prepared by sol–gel process and ambient pressure drying. Inspired by
limited dust releasing, aerogel powder was introduced to the PET
electrospinning solution in an attempt to create required bulk and
surface structure for the nanofibers to improve their hydrophobic and
insulation properties. The samples evaluation was carried out by
measuring density, porosity, contact angle, heat transfer, FTIR, BET,
and SEM. According to the results, porous silica aerogel powder was
fabricated with mean pore diameter of 24 nm and contact angle of
145.9º. The results indicated the usefulness of the aerogel powder
confined into nanofibers to control surface roughness for
manipulating superhydrophobic nanowebs with water contact angle
of 147º. It can be due to a multi-scale surface roughness which was
created by nanowebs structure itself and nanofibers surface
irregularity in presence of the aerogels while a layer of fluorocarbon
created low surface energy. The wettability of a solid substrate is an
important property that is controlled by both the chemical
composition and geometry of the surface. Also, a decreasing trend in
the heat transfer was observed from 22% for the nanofibers without
any aerogel powder to 8% for the nanofibers with 4% aerogel
powder. The development of thermal insulating materials has become
increasingly more important than ever in view of the fossil energy
depletion and global warming that call for more demanding energysaving
practices.
Abstract: TiO2 thin films have been prepared by the sol-gel dipcoating
technique in order to elaborate antireflective thin films for
monocrystalline silicon (mono-Si). The titanium isopropoxyde was
chosen as a precursor with hydrochloric acid as a catalyser for
preparing a stable solution. The optical properties have been tailored
with varying the solution concentration, the withdrawn speed, and the
heat-treatment. We showed that using a TiO2 single layer with 64.5
nm in thickness, heat-treated at 450°C or 300°C reduces the mono-Si
reflection at a level lower than 3% over the broadband spectral
domains [669-834] nm and [786-1006] nm respectively. Those latter
performances are similar to the ones obtained with double layers of
low and high refractive index glasses respectively.
Abstract: In order to manufacture short gap single Si nanowire
(NW) field effect transistor (FET) by imprinting and transferring
method, we introduce the method using Al2O3 sacrificial layer. The
diameters of cylindrical Si NW addressed between Au electrodes by
dielectrophoretic (DEP) alignment method are controlled to 106, 128,
and 148 nm. After imprinting and transfer process, cylindrical Si NW
is embedded in PVP adhesive and dielectric layer. By curing
transferred cylindrical Si NW and Au electrodes on PVP-coated p++ Si
substrate with 200nm-thick SiO2, 3μm gap Si NW FET fabrication
was completed. As the diameter of embedded Si NW increases, the
mobility of FET increases from 80.51 to 121.24 cm2/V·s and the
threshold voltage moves from –7.17 to –2.44 V because the ratio of
surface to volume gets reduced.
Abstract: The thermal conductivity of a fluid can be
significantly enhanced by dispersing nano-sized particles in it, and
the resultant fluid is termed as "nanofluid". A theoretical model for
estimating the thermal conductivity of a nanofluid has been proposed
here. It is based on the mechanism that evenly dispersed
nanoparticles within a nanofluid undergo Brownian motion in course
of which the nanoparticles repeatedly collide with the heat source.
During each collision a rapid heat transfer occurs owing to the solidsolid
contact. Molecular dynamics (MD) simulation of the collision
of nanoparticles with the heat source has shown that there is a pulselike
pick up of heat by the nanoparticles within 20-100 ps, the extent
of which depends not only on thermal conductivity of the
nanoparticles, but also on the elastic and other physical properties of
the nanoparticle. After the collision the nanoparticles undergo
Brownian motion in the base fluid and release the excess heat to the
surrounding base fluid within 2-10 ms. The Brownian motion and
associated temperature variation of the nanoparticles have been
modeled by stochastic analysis. Repeated occurrence of these events
by the suspended nanoparticles significantly contributes to the
characteristic thermal conductivity of the nanofluids, which has been
estimated by the present model for a ethylene glycol based nanofluid
containing Cu-nanoparticles of size ranging from 8 to 20 nm, with
Gaussian size distribution. The prediction of the present model has
shown a reasonable agreement with the experimental data available
in literature.
Abstract: Carbon fiber reinforced polymersarewidely used to strengthen steel structural elements. These structural elements are normally subjected to static, dynamic and fatigue loadings during their life-time. CFRP laminate is commonly used to strengthen these structures under the subjected loads. A number of studies have focused on the characteristics of CFRP sheets bonded to steel members under static, dynamic and fatigue loadings. However, there is a gap in understanding the bonding behavior between CFRP laminates and steel members under impact loading. This paper shows the effect of high load rates on this bond. CFRP laminate CFK 150/2000 was used to strengthen steel joints using Araldite 420 epoxy. The results show that applying a high load rate significantly affects the bond strength but has little influence on the effective bond length.
Abstract: Strong anion exchange resins with QN+OH-, have the
potential to be developed and employed as heterogeneous catalyst for
transesterification, as they are chemically stable to leaching of the
functional group. Nine different SIERs (SIER1-9) with QN+OH-were
prepared by suspension polymerization of vinylbenzyl chloridedivinylbenzene
(VBC-DVB) copolymers in the presence of n-heptane
(pore-forming agent). The amine group was successfully grafted into
the polymeric resin beads through functionalization with
trimethylamine. These SIERs are then used as a catalyst for the
transesterification of triacetin with methanol. A set of differential
equations that represents the Langmuir-Hinshelwood-Hougen-
Watson (LHHW) and Eley-Rideal (ER) models for the
transesterification reaction were developed. These kinetic models of
LHHW and ER were fitted to the experimental data. Overall, the
synthesized ion exchange resin-catalyzed reaction were welldescribed
by the Eley-Rideal model compared to LHHW models,
with sum of square error (SSE) of 0.742 and 0.996, respectively.
Abstract: Water spray cooling is a technique typically used in
heat treatment and other metallurgical processes where controlled
temperature regimes are required. Water spray cooling is used in
static (without movement) or dynamic (with movement of the steel
plate) regimes. The static regime is notable for the fixed position of
the hot steel plate and fixed spray nozzle. This regime is typical for
quenching systems focused on heat treatment of the steel plate. The
second application of spray cooling is the dynamic regime. The
dynamic regime is notable for its static section cooling system and
moving steel plate. This regime is used in rolling and finishing mills.
The fixed position of cooling sections with nozzles and the
movement of the steel plate produce nonhomogeneous water
distribution on the steel plate. The length of cooling sections and
placement of water nozzles in combination with the nonhomogeneity
of water distribution lead to discontinued or interrupted cooling
conditions. The impact of static and dynamic regimes on cooling
intensity and the heat transfer coefficient during the cooling process
of steel plates is an important issue.
Heat treatment of steel is accompanied by oxide scale growth. The
oxide scale layers can significantly modify the cooling properties and
intensity during the cooling. The combination of static and dynamic
(section) regimes with the variable thickness of the oxide scale layer
on the steel surface impact the final cooling intensity. The study of
the influence of the oxide scale layers with different cooling regimes
was carried out using experimental measurements and numerical
analysis. The experimental measurements compared both types of
cooling regimes and the cooling of scale-free surfaces and oxidized
surfaces. A numerical analysis was prepared to simulate the cooling
process with different conditions of the section and samples with
different oxide scale layers.
Abstract: In the scope of application of technical textiles, Non-
Crimp Fabrics are increasingly used. In general, NCF exhibit
excellent load bearing properties, but caused by the manufacturing
process, there are some remaining disadvantages which have to be
reduced. Regarding to this, a novel technique of processing NCF was
developed substituting the binding-thread by an adhesive. This stitchfree
method requires new manufacturing concept as well as new basic
methods to prove adhesion of glue at fibres and textiles. To improve
adhesion properties and the wettability of carbon-fibres by the
adhesive, oxy-fluorination was used. The modification of carbonfibres
by oxy-fluorination was investigated via scanning electron
microscope, X-ray photoelectron spectroscopy and single fibre
tensiometry. Special tensile tests were developed to determine the
maximum force required for detachment.
Abstract: In view of a possible application in optical data
storage devices, diffraction grating efficiency of an organic dye, Acid
Fuchsin doped in PMMA matrix was studied under excitation with
CW diode pumped Nd: YAG laser at 532 nm. The open aperture Zscan
of dye doped polymer displayed saturable absorption and the
closed aperture Z-scan of the samples exhibited negative
nonlinearity. The diffraction efficiency of the grating is the ratio of
the intensity of the first order diffracted power to the incident read
beam power. The dye doped polymer films were found to be good
media for recording. It is observed that the formation of gratings
strongly depend on the concentration of dye in the polymer film, the
intensity ratios of the writing beams and the angle between the
writing beams. It has been found that efficient writing can be made at
an angle of 20o and when the intensity ratio of the writing beams is
unity.
Abstract: Lightweight design represents an important key to
successful implementation of energy-saving, fuel-efficient and
environmentally friendly means of transport in the aerospace and
automotive industry. In this context the use of carbon fibre reinforced
plastics (CFRP) which are distinguished by their outstanding
mechanical properties at relatively low weight, promise significant
improvements. Due to the reduction of the total mass, with the
resulting lowered fuel or energy consumption and CO2 emissions
during the operational phase, commercial aircraft will increasingly be
made of CFRP. An auspicious technology for the efficient and
economic production of high performance thermoset composites and
hybrid structures for future lightweight applications is the
combination of carbon fibre sheet moulding compound, tailored
continuous carbon fibre reinforcements and metallic components in a
one-shot pressing and curing process. This paper deals with a hybrid
composite technology for aerospace industries, which was developed
with the help of a special innovation and development system.
Abstract: A Silver (Ag) thin film is introduced as a template and
doping source for vertically aligned p–type ZnO nanorods. ZnO
nanorods were grown using an ammonium hydroxide based
hydrothermal process. During the hydrothermal process, the Ag thin
film was dissolved to generate Ag ions in the solution. The Ag ions can
contribute to doping in the wurzite structure of ZnO and the (111)
grain of Ag thin film can be the epitaxial temporal template for the
(0001) plane of ZnO. Hence, Ag–doped p–type ZnO nanorods were
successfully grown on the substrate, which can be an electrode or
semiconductor for the device application. To demonstrate the
potentials of this idea, p–n diode was fabricated and its electrical
characteristics were demonstrated.