Abstract: The research study was based on an evaluation of the
ability of glued test samples to pass the criterion of sufficient
bondline adhesion under the exposure conditions defined in EN 302-
1. Additionally, an infrared spectroscopic analysis of the evaluated
adhesives (phenol-resorcinol-formaldehyde PRF and melamine-ureaformaldehyde
MUF) with different mix ratios was carried out to
evaluate the possible effects of a faulty technological process.
Abstract: A vast array of biological materials, especially algae have received increasing attention for heavy metal removal. Algae have been proven to be cheaper, more effective for the removal of metallic elements in aqueous solutions. A fresh water algal strain was isolated from Zoo Lake, Johannesburg, South Africa and identified as Desmodesmus sp. This paper investigates the efficacy of Desmodesmus sp.in removing heavy metals contaminating the Wonderfonteinspruit Catchment Area (WCA) water bodies. The biosorption data fitted the pseudo-second order and Langmuir isotherm models. The Langmuir maximum uptakes gave the sequence: Mn2+>Ni2+>Fe2+. The best results for kinetic study was obtained in concentration 120 ppm for Fe3+ and Mn2+, whilst for Ni2+ was at 20 ppm, which is about the same concentrations found in contaminated water in the WCA (Fe3+115 ppm, Mn2+ 121 ppm and Ni2+ 26.5 ppm).
Abstract: It is well known that enhancing interfacial adhesion
between inorganic filler and matrix resin in a composite lead to
favorable properties such as excellent mechanical properties, high
thermal resistance, prominent electric insulation, low expansion
coefficient, and so on. But it should be avoided that much excess of
coupling agent is reacted due to a negative impact of their final
composite-s properties. There is no report to achieve classification of
the bonding state excepting investigation of coating layer thickness.
Therefore, the analysis of the bonding state of the coupling agent
reacted with the filler surface such as BN particles with less functional
group and silica particles having much functional group was
performed by thermal gravimetric analysis and pyrolysis GC/MS. The
reacted number of functional groups on the silane-coupling agent was
classified as a result of the analysis. Thus, we succeeded in classifying
the reacted number of the functional groups as a result of this study.
Abstract: In this study, structural, mechanical, thermal and
electrical properties of poly (lactic acid) (PLA) nanocomposites with
low-loaded (0-1.5 wt%) untreated, heat and nitric acid treated multiwalled
carbon nanotubes (MWCNTs) were studied. Among the
composites, untreated 0.5 wt % MWCNTs and acid-treated 1.0 wt%
MWCNTs reinforced PLA show the tensile strength and modulus
values higher than the others. These two samples along with pure
PLA exhibit the stable orthorhombic α-form, whilst other samples
reveal the less stable orthorhombic β-form, as demonstrated by X-ray
diffraction study. Differential scanning calorimetry reveals the
evolution of the mentioned different phases by controlled cooling and
discloses an enhancement of PLA crystallization by nanotubes
incorporation. Thermogravimetric analysis shows that the MWCNTs
loaded sample degraded faster than PLA. Surface resistivity of the
nanocomposites is found to be dropped drastically by a factor of 1013
with a low loading of MWCNTs (1.5 wt%).
Abstract: Phase transformation temperature is one of the most important parameters for the shape memory alloys (SMAs). The most popular method to determine these phase transformation temperatures is the Differential Scanning Calorimeter (DSC), but due to the limitation of the DSC testing itself, it made it difficult for the finished product which is not in the powder form. A novel method which uses the Universal Testing Machine has been conducted to determine the phase transformation temperatures. The Flexinol wire was applied with force and maintained throughout the experiment and at the same time it was heated up slowly until a temperature of approximately 1000C with direct current. The direct current was then slowly decreased to cool down the temperature of the Flexinol wire. All the phase transformation temperatures for Flexinol wire were obtained. The austenite start at 52.540C and austenite finish at 60.900C, while martensite start at 44.780C and martensite finish at 32.840C.
Abstract: This study was aimed to study the probability about
the production of fiberboard made of durian rind through latex with
phenolic resin as binding agent. The durian rind underwent the
boiling process with NaOH [7], [8] and then the fiber from durian
rind was formed into fiberboard through heat press. This means that
durian rind could be used as replacement for plywood in plywood
industry by using durian fiber as composite material with adhesive
substance. This research would study the probability about the
production of fiberboard made of durian rind through latex with
phenolic resin as binding agent. At first, durian rind was split,
exposed to light, boiled and steamed in order to gain durian fiber.
Then, fiberboard was tested with the density of 600 Kg/m3 and 800
Kg/m3. in order to find a suitable ratio of durian fiber and latex.
Afterwards, mechanical properties were tested according to the
standards of ASTM and JIS A5905-1994. After the suitable ratio was
known, the test results would be compared with medium density
fiberboard (MDF) and other related research studies. According to
the results, fiberboard made of durian rind through latex with
phenolic resin at the density of 800 Kg/m3 at ratio of 1:1, the
moisture was measured to be 5.05% with specific gravity (ASTM D
2395-07a) of 0.81, density (JIS A 5905-1994) of 0.88 g/m3, tensile
strength, hardness (ASTM D2240), flexibility or elongation at break
yielded similar values as the ones by medium density fiberboard
(MDF).
Abstract: An electrical apparatus for measuring moisture
content was developed by our laboratory and uses dependence of
electrical properties on water content in studied material. Error
analysis of the apparatus was run by measuring different volumes of
water in a simplified specimen, i.e. hollow plexiglass block, in order
to avoid as many side-effects as possible. Obtained data were
processed using both basic and advanced statistics and results were
compared with each other. The influence of water content on
accuracy of measured data was studied as well as the influence of
variation of apparatus' proper arrangement or factual methodics of its
usage. The overall coefficient of variation was 4%. There was no
trend found in results of error dependence on water content.
Comparison with current surveys led to a conclusion, that the studied
apparatus can be used for indirect measurement of water content in
porous materials, with expectable error and under known conditions.
Factual experiments with porous materials are not involved, but are
currently under investigation.
Abstract: In this research, the main aim is to investigate the
antimicrobial effectiveness of ammonyx solutions finishing on
Sweatshirt Sport with immersion method. 60 Male healthy subjects
(football player) participated in this study. They were dressed in a
Sweatshirt for 14 days and some microbes found on them were
investigated. The antimicrobial effect of different ammonyx
solutions(1/100, 1/500, 1/1000, 1/2000 v/v solutions of Ammonyx)
on the identified microbes was studied by the zone inhabitation
method in vitro. In the next step the Sweatshirt Sports were treated
with the same different solutions of ammonyx and the antimicrobial
effectiveness was assessed by colony count method in different times
and the results were compared whit untreated ones. Some mechanical
properties of treated cotton/polyester yarn that used in Sweatshirt
Sport were measured after 30 days and were compared with
untreated one. Finally after finishing, scanning electron microscopy
(SEM) was used to compare the surfaces of the finished and
unfinished specimens. The results showed the presence of five
pathogenic microbes on Sweatshirt Sports such as Escherichia coli,
Staphylococcus aureus, Aspergillus, Mucor and Candida. The
inhalation time for treated on Sweatshirt Sports improved. The
amount of colony growth on treated clothes reduced considerably
and moreover the mechanical tests results showed no significant
deterioration effect of studies properties in comparison to the
untreated yarn. The visual examination of the SEM indicated that the
antimicrobial treatments were applied usefully to fabrics.
Abstract: Magnetic carbon nanotubes composites were obtained
by filling carbon nanotubes with paramagnetic iron oxide particles.
Detailed investigation of magnetic behaviour of resulting composites
was done at different temperatures. Measurements indicate that these
functionalized nanotubes are superparamagnetic at room temperature;
however, no superparamagnetism was observed at 125 K and 80 K.
The blocking temperature TB was estimated at 145 K. These magnetic
carbon nanotubes have the potential of being used in a wide range of
applications, in particular, the production of nanofluids, which can be
controlled and steered by appropriate magnetic fields.
Abstract: Single crystals of Magnesium alloys such as Mg-1Al,
Mg-1Zn-0.5Y, Mg-3Li, and AZ31 alloys were successfully fabricated in this study by employing the modified Bridgman method. Single
crystals of pure Mg were also made in this study. To determine the exact orientation of crystals, Laue back-reflection method and pole figure measurement were carried out on each single crystal. Dimensions of single crystals were 10 mm in diameter and 120 mm in
length. Hardness and compression tests were conducted and the results
revealed that hardness and the strength strongly depended on the
orientation. The closer to basal one the orientation was, the higher hardness and compressive strength were. The effect of alloying was
not higher than that of orientation. After compressive deformation of single crystals, the orientation of the crystals was found to rotate and to be parallel to the basal orientation.
Abstract: Extraction of Fe(III) from aqueous solution using Trin-
butyl Phosphate (TBP) as carrier needs a highly acidic medium
(>6N) as it favours formation of chelating complex FeCl3.TBP.
Similarly, stripping of Iron(III) from loaded organic solvents requires
neutral pH or alkaline medium to dissociate the same complex. It is
observed that TBP co-extracts acids along with metal, which causes
reversal of driving force of extraction and iron(III) is re-extracted
back from the strip phase into the feed phase during Liquid Emulsion
Membrane (LEM) pertraction. Therefore, rate of extraction of
different mineral acids (HCl, HNO3, H2SO4) using TBP with and
without presence of metal Fe(III) was examined. It is revealed that in
presence of metal acid extraction is enhanced. Determination of mass
transfer coefficient of both acid and metal extraction was performed
by using Bulk Liquid Membrane (BLM). The average mass transfer
coefficient was obtained by fitting the derived model equation with
experimentally obtained data. The mass transfer coefficient of the
mineral acid extraction is in the order of kHNO3 = 3.3x10-6m/s > kHCl =
6.05x10-7m/s > kH2SO4 = 1.85x10-7m/s. The distribution equilibria of
the above mentioned acids between aqueous feed solution and a
solution of tri-n-butyl-phosphate (TBP) in organic solvents have been
investigated. The stoichiometry of acid extraction reveals the
formation of TBP.2HCl, HNO3.2TBP, and TBP.H2SO4 complexes.
Moreover, extraction of Iron(III) by TBP in HCl aqueous solution
forms complex FeCl3.TBP.2HCl while in HNO3 medium forms
complex 3FeCl3.TBP.2HNO3
Abstract: In the Fe-3%Si sheets, grade Hi-B, with AlN and MnS
as inhibitors, the Goss grains which abnormally grow do not have a
size greater than the average size of the primary matrix. In this
heterogeneous microstructure, the size factor is not a required
condition for the secondary recrystallization. The onset of the small
Goss grain abnormal growth appears to be related to a particular
behavior of their grain boundaries, to the local texture and to the
distribution of the inhibitors. The presence and the evolution of
oriented clusters ensure to the small Goss grains a favorable
neighborhood to grow. The modified Monte-Carlo approach, which
is applied, considers the local environment of each grain. The grain
growth is dependent of its real spatial position; the matrix
heterogeneity is then taken into account. The grain growth conditions
are considered in the global matrix and in different matrixes
corresponding to A component clusters. The grain growth behaviour
is considered with introduction of energy only, energy and mobility,
energy and mobility and precipitates.
Abstract: The objective of this study is to investigate the effect of adding coal to obtain insulating ceramic product. The preparation of mixtures is achieved with 04 types of different masse compositions, consisting of gray and yellow clay, and coal. Analyses are performed on local raw materials by adding coal as additive. The coal content varies from 5 to 20 % in weight by varying the size of coal particles ranging from 0.25mm to 1.60mm.
Initially, each natural moisture content of a raw material has been determined at the temperature of 105°C in a laboratory oven. The Influence of low-coal content on absorption, the apparent density, the contraction and the resistance during compression have been evaluated. The experimental results showed that the optimized composition could be obtained by adding 10% by weight of coal leading thus to insulating ceramic products with water absorption, a density and resistance to compression of 9.40 %, 1.88 g/cm3, 35.46 MPa, respectively. The results show that coal, when mixed with traditional raw materials, offers the conditions to be used as an additive in the production of lightweight ceramic products.
Abstract: Calculations of energy efficiency of several AACbased
building envelopes under different climatic conditions are
presented. As thermal insulating materials, expanded polystyrene and
hydrophobic and hydrophilic mineral wools are assumed. The
computations are accomplished using computer code HEMOT
developed at Department of Materials Engineering, Faculty of Civil
Engineering at the Czech Technical University in Prague. The
climatic data of Athens, Kazan, Oslo, Prague and Reykjavík are
obtained using METEONORM software.
Abstract: In this paper, taking Chinese Nanjing Metro ALSTOM vehicle synthesis brake as an example, the subway with synthetic brake shoe formula components of final product performance, has done a lot of research and performance test, final is drawn with hybrid fiber as reinforcing material, modified phenolic resin as matrix material, and then filling friction modifier performance, by the hot pressing process made a new type of domestic subway brake shoe. The product of the test performance indicators that can replace the similar foreign products.
Abstract: Nylon 6-clay hybrid/neat nylon 6, sheath/core
bicomponent nanocomposite fibers containing 4 wt% of clay in
sheath section were melt spun at different take-up speeds. Their
orientation and crystalline structure were compared to those of neat
nylon 6 fibers. Birefringence measurements showed that the
orientation development in sheath and core parts of bicomponent
fibers was different. Crystallinity results showed that clay did not act
as a nucleating agent for bicomponent fibers. The neat nylon 6 fiber
had a smooth surface while striped pattern was appeared on the
surface of bicomponent fiber containing clay due to thermal
shrinkage of the core part.
Abstract: Mechanical and water transport properties of high
performance concrete (HPC) containing natural zeolite as partial
replacement of Portland cement are studied. Experimental results
show that in the investigated mixes the use of natural zeolite leads to
an increase of porosity, decrease of compressive strength and
increase of moisture diffusivity and water vapor diffusion coefficient,
as compared with the reference HPC. However, for the replacement
level up to 20% of the mass of Portland cement the concretes still
maintain their high performance character and exhibit acceptable
water transport properties. Therefore, natural zeolite can be
considered an environmental friendly binder with a potential to
replace a part of Portland cement in concrete in building industry.
Abstract: In this paper a novel method was presented for
evaluating the fabric pills using digital image processing techniques. This work provides a novel technique for
detecting pills and also measuring their heights, surfaces and
volumes. Surely, measuring the intensity of defects by human vision is an inaccurate method for quality control; as a result, this problem became a motivation for employing digital image processing techniques for detection of defects of fabric
surface. In the former works, the systems were just limited to measuring of the surface of defects, but in the presented
method the height and the volume of defects were also
measured, which leads to a more accurate quality control. An algorithm was developed to first, find pills and then measure their average intensity by using three criteria of height, surface
and volume. The results showed a meaningful relation
between the number of rotations and the quality of pilled fabrics.
Abstract: This research focuses on the effect of weight
percentage variation and size variation of MgFeSi added,
gating system design and reaction chamber design on inmold
process. By using inmold process, well-known problem of
fading is avoided because the liquid iron reacts with
magnesium in the mold and not, as usual, in the ladle. During
the pouring operation, liquid metal passes through the
chamber containing the magnesium, where the reaction of the
metal with magnesium proceeds in the absence of atmospheric
oxygen [1].In this paper, the results of microstructural
characteristic of ductile iron on this parameters are mentioned.
The mechanisms of the inmold process are also described [2].
The data obtained from this research will assist in producing
the vehicle parts and other machinery parts for different
industrial zones and government industries and in transferring
the technology to all industrial zones in Myanmar. Therefore,
the inmold technology offers many advantages over traditional
treatment methods both from a technical and environmental,
as well as an economical point of view. The main objective of
this research is to produce ductile iron castings in all industrial
sectors in Myanmar more easily with lower costs. It will also
assist the sharing of knowledge and experience related to the
ductile iron production.
Abstract: The carbon based coils with the nanometer scale have
the 3 dimension helix geometry. We synthesized the carbon nano-coils
by the use of chemical vapor deposition technique with iron and tin as
the catalysts. The fabricated coils have the external diameter of
ranging few hundred nm to few thousand nm. The Scanning
Electro-Microscope (SEM) and Tunneling Electro-Microscope has
shown detail images of the coil-s structure. The fabrication of the
carbon nano-coils can be grown on the metal and non-metal substrates,
such as the stainless steel and silicon substrates. Besides growth on the
flat substrate; they also can be grown on the stainless steel wires. After
the synthesis of the coils, the mechanical and electro-mechanical
property is measured. The experimental results were reported.