Abstract: The aim of this study is to moderate the dependence of counter frictional coefficient on temperature between counter surfaces and to reduce the wear of C/C composites at low temperature. To modify the C/C composites, Silica (SiO2) powders were added into phenolic resin for carbon precursor. The preform plate of the precursor of C/C composites was prepared by conventional filament winding method. The C/C composites plates were obtained by carbonizing preform plate at 2200 °C under an argon atmosphere. At that time, the silicon carbides (SiC) were synthesized around the surfaces and the internal vacancies of the C/C composites. The frictional coefficient on the counter surfaces and specific wear volumes of the C/C composites were measured by our developed frictional test machine like pin-on disk type. The XRD indicated that SiC was synthesized in the body of C/C composite fabricated by current method. The results of friction test showed that coefficient of friction of unmodified C/C composites have temperature dependence when the test condition was changed. In contrast, frictional coefficient of the C/C composite modified with SiO2 powders was almost constant at about 0.27 when the temperature condition was changed from Room Temperature (RT) to 300 °C. The specific wear rate decreased from 25×10-6 mm2/N to 0.1×10-6 mm2/N. The observations of the surfaces after friction tests showed that the frictional surface of the modified C/C composites was covered with a film produced by the friction. This study found that synthesizing SiC around surface and internal vacancies of C/C composites was effective to moderate the dependence on the frictional coefficient and reduce to the abrasion of C/C composites.
Abstract: This research aimed to produce offset printing inks from Samut Songkram’s coconut oil and to test properties of the printing inks comparing with commercial offset printing inks. One of the ingredients in the process of mixing varnish is coconut oil – used to produce black offset printing inks which were the subject of testing issues in order to compare with commercial offset printing inks. Based on the results of research, the best formula for mixing varnish was 50% of coconut oil, 36% of phenolic resin, and 14% of solvent oil. At the same time, the best formula in producing black offset inks was mixing varnish with 20% of coconut oil 20%. Consequently, the result of testing of properties of coconut oil based solvent offset printing inks regarding viscosity, tack and ink flow, showed that offset printing inks with oil based solvent had the properties less than commercial offset printing ink. Additionally, the result of testing also indicate that the rate of properties in aspects of ink spread and setting time of coconut oil based solvent offset printing were higher than that of commercial offset printing inks.
Abstract: Influences of the amount of phenolic, curing temperature and curing time on the Mechanical Properties of phenolic/fiber composite were investigated by using two-level factorial design. The latter was used to determine the affects of those factors on mechanical properties. The purpose of this study was to investigate the affects of amount of phenolic, curing temperature and curing time of the composite to determine the best condition for mechanical properties according to MIL-I-24768 by the tensile strength is more than 103 MPa.
Abstract: In this paper, taking Chinese Nanjing Metro ALSTOM vehicle synthesis brake as an example, the subway with synthetic brake shoe formula components of final product performance, has done a lot of research and performance test, final is drawn with hybrid fiber as reinforcing material, modified phenolic resin as matrix material, and then filling friction modifier performance, by the hot pressing process made a new type of domestic subway brake shoe. The product of the test performance indicators that can replace the similar foreign products.
Abstract: This study was aimed to study the probability about
the production of fiberboard made of durian rind through latex with
phenolic resin as binding agent. The durian rind underwent the
boiling process with NaOH [7], [8] and then the fiber from durian
rind was formed into fiberboard through heat press. This means that
durian rind could be used as replacement for plywood in plywood
industry by using durian fiber as composite material with adhesive
substance. This research would study the probability about the
production of fiberboard made of durian rind through latex with
phenolic resin as binding agent. At first, durian rind was split,
exposed to light, boiled and steamed in order to gain durian fiber.
Then, fiberboard was tested with the density of 600 Kg/m3 and 800
Kg/m3. in order to find a suitable ratio of durian fiber and latex.
Afterwards, mechanical properties were tested according to the
standards of ASTM and JIS A5905-1994. After the suitable ratio was
known, the test results would be compared with medium density
fiberboard (MDF) and other related research studies. According to
the results, fiberboard made of durian rind through latex with
phenolic resin at the density of 800 Kg/m3 at ratio of 1:1, the
moisture was measured to be 5.05% with specific gravity (ASTM D
2395-07a) of 0.81, density (JIS A 5905-1994) of 0.88 g/m3, tensile
strength, hardness (ASTM D2240), flexibility or elongation at break
yielded similar values as the ones by medium density fiberboard
(MDF).
Abstract: The objectives of this research are to produce
prototype coconut oil based solvent offset printing inks and to
analyze a basic quality of printing work derived from coconut oil
based solvent offset printing inks, by mean of bringing coconut oil
for producing varnish and bringing such varnish to produce black
offset printing inks. Then, analysis of qualities i.e. CIELAB value,
density value, and dot gain value of printing work from coconut oil
based solvent offset printing inks which printed on gloss-coated
woodfree paper weighs 130 grams were done. The research result of
coconut oil based solvent offset printing inks indicated that the
suitable varnish formulation is using 51% of coconut oil, 36% of
phenolic resin, and 14% of solvent oil 14%, while the result of
producing black offset ink displayed that the suitable formula of
printing ink is using varnish mixed with 20% of coconut oil, and the
analyzing printing work of coconut oil based solvent offset printing
inks which printed on paper, the results were as follows: CIELAB
value of black offset printing ink is at L* = 31.90, a* = 0.27, and b* =
1.86, density value is at 1.27 and dot gain value was high at mid tone
area of image area.
Abstract: In this study, an ablation, mechanical and thermal properties of a rocket motor insulation from phenolic/ fiber matrix composites forming a laminate with different fiber between fiberglass and locally available synthetic fibers. The phenolic/ fiber matrix composites was mechanics and thermal properties by means of tensile strength, ablation, TGA and DSC. The design of thermal insulation involves several factors.Determined the mechanical properties according to MIL-I-24768: Density >1.3 g/cm3, Tensile strength >103 MPa and Ablation