Abstract: This research was to evaluate a technical feasibility of
making single-layer experimental particleboard panels from bamboo
waste (Dendrocalamus asper Backer) by converting bamboo into
strips, which are used to make laminated bamboo furniture. Variable
factors were density (600, 700 and 800 kg/m3) and temperature of
condition (25, 40 and 55 °C). The experimental panels were tested for
their physical and mechanical properties including modulus of
elasticity (MOE), modulus of rupture (MOR), internal bonding
strength (IB), screw holding strength (SH) and thickness swelling
values according to the procedures defined by Japanese Industrial
Standard (JIS). The test result of mechanical properties showed that
the MOR, MOE and IB values were not in the set criteria, except the
MOR values at the density of 700 kg/m3 at 25 °C and at the density
of 800 kg/m3 at 25 and 40 °C, the IB values at the density of 600
kg/m3, at 40 °C, and at the density of 800 kg/m3 at 55 °C. The SH
values had the test result according to the set standard, except with
the density of 600 kg/m3, at 40 and 55 °C. Conclusively, a valuable
renewable biomass, bamboo waste could be used to manufacture
boards.
Abstract: Concerning the measurement of friction properties of
textiles and fabrics using Kawabata Evaluation System (KES), whose
output is constrained to the surface friction factor of fabric, and no
other data would be generated; this research has been conducted to
gain information about surface roughness regarding its surface
friction factor. To assess roughness properties of light nonwovens, a
3-dimensional model of a surface has been simulated with regular
sinuous waves through it as an ideal surface. A new factor was
defined, namely Surface Roughness Factor, through comparing
roughness properties of simulated surface and real specimens. The
relation between the proposed factor and friction factor of specimens
has been analyzed by regression, and results showed a meaningful
correlation between them. It can be inferred that the new presented
factor can be used as an acceptable criterion for evaluating the
roughness properties of light nonwoven fabrics.
Abstract: Optical properties of sputter-deposited ZnS thin films
were investigated as potential replacements for CBD(chemical bath
deposition) CdS buffer layers in the application of CIGS solar cells.
ZnS thin films were fabricated on glass substrates at RT, 150oC, 200oC,
and 250oC with 50 sccm Ar gas using an RF magnetron sputtering
system. The crystal structure of the thin film is found to be zinc blende
(cubic) structure. Lattice parameter of ZnS is slightly larger than CdS
on the plane and thus better matched with that of CIGS. Within a
400-800 nm wavelength region, the average transmittance was larger
than 75%. When the deposition temperature of the thin film was
increased, the blue shift phenomenon was enhanced. Band gap energy
of the ZnS thin film tended to increase as the deposition temperature
increased. ZnS thin film is a promising material system for the CIGS
buffer layer, in terms of ease of processing, low cost, environmental
friendliness, higher transparency, and electrical properties
Abstract: The composite materials were prepared by sawdust, cassava starch and natural rubber latex (NR). The mixtures of 15%w/v gelatinized cassava starch and 15%w/v PVOH were used as the binder of these composite materials. The concentrated rubber latex was added to the mixtures. They were mixed rigorously to the treated sawdust in the ratio of 70:30 until achive uniform dispersion. The batters were subjected to the hot compression moulding at the temperature of 160°C and 3,000 psi pressure for 5 min. The experimental results showed that the mechanical properties of composite materials, which contained the gelatinized cassava starch and PVOH in the ratio of 2:1, 20% NR latex by weight of the dry starch and treated sawdust with 5%NaOH or 1% BPO, were the best. It contributed the maximal compression strength (341.10 + 26.11 N), puncture resistance (8.79 + 0.98 N/mm2) and flexural strength (3.99 + 0.72N/mm2). It is also found that the physicochemical and mechanical properties of composites strongly depends on the interface quality of sawdust, cassava starch and NR latex.
Abstract: Absorptive characteristics of polyaniline synthesized
in mixture of water and acetonitrile in 50/50 volume ratio was
studied. Synthesized polyaniline in powder shape is used as an
adsorbent to remove toxic hexavalent chromium from aqueous
solutions. Experiments were conducted in batch mode with different
variables such as agitation time, solution pH and initial concentration
of hexavalent chromium. Removal mechanism is the combination of
surface adsorption and reduction. The equilibrium time for removal
of Cr(T) and Cr(VI) was about 2 and 10 minutes respectively. The
optimum pH for total chromium removal occurred at pH 7 and
maximum hexavalent chromium removal took place under acidic
condition at pH 3. Investigating the isothermal characteristics showed
that the equilibrium adsorption data fitted both Freundlich-s and
Langmuir-s isotherms. The maximum adsorption of chromium was
calculated 36.1 mg/g for polyaniline
Abstract: Protective coatings that resist oxide scale growth and
decrease chromium evaporation are necessary to make stainless steel
interconnect materials for long-term durable operation of solid oxide
fuel cells (SOFCs). In this study a layer of cobalt was electroplated
on the surface of AISI 441 ferritic stainless steel which is used in
solid oxide fuel cells for interconnect applications. The oxidation
behavior of coated substrates was studied as a function of time at
operating conditions of SOFCs. Cyclic oxidation has been also tested
at 800ºC for 100 cycles. Cobalt coating during isothermal oxidation
caused to the oxide growth resistance by limiting the outward
diffusion of Cr cation and the inward diffusion of oxygen anion.
Results of cyclic oxidation exhibited that coated substrates
demonstrate an excellent resistance against the spallation and
cracking.
Abstract: Wet chemistry methods are used to prepare the
SiO2/Au nanoshells. The purpose of this research was to synthesize
gold coated SiO2 nanoshells for biomedical applications. Tunable
nanoshells were prepared by using different colloidal concentrations.
The nanoshells are characterized by FTIR, XRD, UV-Vis
spectroscopy and atomic force microscopy (AFM). The FTIR results
confirmed the functionalization of the surfaces of silica nanoparticles
with NH2 terminal groups. A tunable absorption was observed
between 470-600 nm with a maximum range of 530-560 nm. Based
on the XRD results three main peaks of Au (111), (200) and (220)
were identified. Also AFM results showed that the silica core
diameter was about 100 nm and the thickness of gold shell about 10
nm.
Abstract: In our recent study, we have used ZnO nanoparticles assisted with UV light irradiation to investigate the photocatalytic degradation of Phenol Red (PR). The ZnO photocatalyst was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), specific surface area analysis (BET) and UVvisible spectroscopy. X-ray diffractometry result for the ZnO nanoparticles exhibit normal crystalline phase features. All observed peaks can be indexed to the pure hexagonal wurtzite crystal structures, with the space group of P63mc. There are no other impurities in the diffraction peak. In addition, TEM measurement shows that most of the nanoparticles are rod-like and spherical in shape and fairly monodispersed. A significant degradation of the PR was observed when the catalyst was added into the solution even without the UV light exposure. In addition, the photodegradation increases with the photocatalyst loading. The surface area of the ZnO nanomaterials from the BET measurement was 11.9 m2/g. Besides the photocatalyst loading, the effect of some parameters on the photodegradation efficiency such as initial PR concentration and pH were also studied.
Abstract: This paper aims to fabricated high quality anodic
aluminum oxide (AAO) film by anodization method. AAO pore size,
pore density, and film thickness can be controlled in 10~500 nm,
108~1011 pore.cm-2, and 1~100 μm. AAO volume and surface area can
be computed based on structural parameters such as thickness, pore
size, pore density, and sample size. Base on the thetorical calculation,
AAO has 100 μm thickness with 15 nm, 60 nm, and 500 nm pore
diameters AAO surface areas are 1225.2 cm2, 3204.4 cm2, and 549.7
cm2, respectively. The large unit surface area which is useful for
adsorption application. When AAO adsorbed pH indictor of
bromphenol blue presented a sensitive pH detection of solution
change. This testing method can further be used for the precise
measurement of biotechnology, convenience measurement of
industrial engineering.
Abstract: Regarding previous research studies it was concluded
that thin-walled fiber-cement composites are able to conduct electric
current under specific conditions. This property is ensured by using
of various kinds of carbon materials. Though carbon fibers are less
conductive than metal fibers, composites with carbon fibers were
evaluated as better current conductors than the composites with metal
fibers. The level of electric conductivity is monitored by the means of
impedance measurement of designed samples. These composites
could be used for a range of applications such as heating of
trafficable surfaces or shielding of electro-magnetic fields.
The aim of the present research was to design an element with the
ability to monitor internal processes in building structures and
prevent them from collapsing. As a typical element for laboratory
testing there was chosen a concrete column, which was repeatedly
subjected to load by simple pressure with continual monitoring of
changes in electrical properties.
Abstract: The fabrication of porous NiTi shape memory alloys (SMAs) from elemental powder compacts was conducted by selfpropagating high temperature synthesis (SHS). Effects of the preheating temperature and the chamber pressure on the combustion characteristics as well as the final morphology and the composition of products were studied. The samples with porosity between 56.4 and 59.0% under preheating temperature in the range of 200-300°C and Ar-gas chamber pressure of 138 and 201 kPa were obtained. The pore structures were found to be dissimilar only in the samples processed with different preheating temperature. The major phase in the porous product is NiTi with small amounts of secondary phases, NiTi2 and Ni4Ti3. The preheating temperature and the chamber pressure have very little effect on the phase constituent. While the combustion temperature of the sample was notably increased by increasing the preheating temperature, they were slightly changed by varying the chamber pressure.
Abstract: Since polymerase chain reaction (PCR) has been
invented, it has emerged as a powerful tool in genetic analysis. The
PCR products are closely linked with thermal cycles. Therefore, to
reduce the reaction time and make temperature distribution uniform in
the reaction chamber, a novel oscillatory thermal cycler is designed.
The sample is placed in a fixed chamber, and three constant isothermal
zones are established and lined in the system. The sample is oscillated
and contacted with three different isothermal zones to complete
thermal cycles. This study presents the design of the geometric
characteristics of the chamber. The commercial software
CFD-ACE+TM is utilized to investigate the influences of various
materials, heating times, chamber volumes, and moving speed of the
chamber on the temperature distributions inside the chamber. The
chamber moves at a specific velocity and the boundary conditions
with time variations are related to the moving speed. Whereas the
chamber moves, the boundary is specified at the conditions of the
convection or the uniform temperature. The user subroutines compiled
by the FORTRAN language are used to make the numerical results
realistically. Results show that the reaction chamber with a rectangular
prism is heated on six faces; the effects of various moving speeds of
the chamber on the temperature distributions are examined. Regarding
to the temperature profiles and the standard deviation of the
temperature at the Y-cut cross section, the non-uniform temperature
inside chamber is found as the moving speed is larger than 0.01 m/s.
By reducing the heating faces to four, the standard deviation of the
temperature of the reaction chamber is under 1.4×10-3K with the range
of velocities between 0.0001 m/s and 1 m/s. The nature convective
boundary conditions are set at all boundaries while the chamber moves
between two heaters, the effects of various moving velocities of the
chamber on the temperature distributions are negligible at the assigned
time duration.
Abstract: In this article, using finite element analysis (FEA)
and an X-ray diffractometer (XRD), cold-sprayed titanium particles
on a steel substrate is investigated in term of cooling time and the
development of residual strains. Three cooling-down models of
sprayed particles after deposition stage are simulated and discussed:
the first model (m1) considers conduction effect to the substrate only,
the second model (m2) considers both conduction as well as
convection effect to the environment, and the third model (m3) which
is the same as the second model but with the substrate heated to a
near particle temperature before spraying. Thereafter, residual strains
developed in the third model is compared with the experimental
measurement of residual strains, which involved a Bruker D8
Advance Diffractometer using CuKa radiation (40kV, 40mA)
monochromatised with a graphite sample monochromator. For
deposition conditions of this study, a good correlation was found to
exist between the FEA results and XRD measurements of residual
strains.
Abstract: The electrolyte stirring method of anodization etching
process for manufacturing porous silicon (PS) is reported in this work.
Two experimental setups of nature air stirring (PS-ASM) and
electrolyte stirring (PS-ESM) are employed to clarify the influence of
stirring mechanisms on electrochemical etching process. Compared to
traditional fabrication without any stirring apparatus (PS-TM), a large
plateau region of PS surface structure is obtained from samples with
both stirring methods by the 3D-profiler measurement. Moreover, the
light emission response is also improved by both proposed electrolyte
stirring methods due to the cycling force in electrolyte could
effectively enhance etch-carrier distribution while the electrochemical
etching process is made. According to the analysis of statistical
calculation of photoluminescence (PL) intensity, lower standard
deviations are obtained from PS-samples with studied stirring methods,
i.e. the uniformity of PL-intensity is effectively improved. The
calculated deviations of PL-intensity are 93.2, 74.5 and 64,
respectively, for PS-TM, PS-ASM and PS-ESM.
Abstract: Cerium oxide is to be recovered from monazite,
which contains about 27.35% CeO2. The principal objective
of this study is to be able to extract cerium oxide from
monazite of Moemeik Myitsone Area. The treatment of
monazite in this study involves three main steps; extraction
of cerium hydroxide from monazite, solvent extraction of
cerium hydroxide, and precipitation with oxalic acid and
calcination of cerium oxalate.
Abstract: Low carbon deep drawing steel DC 01 according to EN 10130-91 was nitrooxidized in dissociated ammonia at 580°C/45 min and consequently oxidised at 380°C/5 min in vapour of distilled water. Material after nitrooxidation had 54 % increase of yield point, 34 % increase of strength and 10-times increased resistance to atmospheric corrosion in comparison to the material before nitrooxidation. The microstructure of treated material consisted of thin ε-phase layer connected to layer containing precipitated massive needle shaped Fe4N - γ' nitrides. This layer passed to a diffusion layer consisting of fine irregular shaped Fe16N2 - α'' nitrides regularly dispersed in ferritic matrix. Fatigue properties were examined under bending load with frequency of 20 kHz and sinusoidal symmetric cycle. The results confirmed positive influence of nitrooxidation on fatigue properties as fatigue limit of treated material was double in comparison to untreated material.
Abstract: The current study has investigated the ageing
phenomena of silica optical fibres in relation to water activity which might be accelerated when exposed to a supplementary energy, such as microwaves. A controlled stress by winding fibres onto accurate
diameter mandrel was applied. Taking into account that normally a
decrease in fibre strength is induced in time by chemical action of water, the effects of cumulative reagents such as: water, applied stress and supplementary energy (microwave) in some cases acted in
the opposite manner. The microwave effect as a structural relaxation
catalyst appears unexpected, even if the overall gain in fibre strength is not high, but the stress corrosion factor revealed significant
increase in certain simulation conditions.
Abstract: In the present work, an attempt has been made to
understand the feasibility of using UHF technique for identification
of any corona discharges/ arcing in insulating material due to water
droplets. The sensors of broadband type are useful for identification
of such discharges. It is realised that arcing initiated by liquid droplet
radiates UHF signals in the entire bandwidth up to 2 GHz. The
frequency content of the UHF signal generated due to corona/arcing
is not much varied in epoxy nanocomposites with different weight
percentage of clay content. The exfoliated/intercalated properties
were analysed through TEM studies. It is realized that corona
initiated discharges are of intermittent process. The hydrophobicity
of the material characterized through contact angle measurement. It
is realized that low Wt % of nanoclay content in epoxy resin reduces
the surface carbonization due to arcing/corona discharges. The results
of the study with gamma irradiated specimen indicates that contact
angle, discharge inception time and evaporation time of the liquid are
much lower than the virgin epoxy nanocomposite material.
Abstract: This paper investigates the influence of various
parameters on the behaviour of water droplets on polymeric surfaces
under high electric fields. An inclined plane test was carried out to
understand the droplet behaviour in strong electric field. Parameters
such as water droplet conductivity, droplet volume, polymeric
surface roughness and droplet positioning with respect to the
electrodes were studied. The flashover voltage is affected by all
aforementioned parameters. The droplet positioning is in some cases
more vital than the droplet volume. Surface damages were analysed
using Scanning Electron Microscopy (SEM) studies and by Energy
dispersive X-ray Analysis (EDAX). It is observes that magnitude of
discharge have direct influence on amount of surface da
Abstract: In this work we report on preliminary analysis of a novel optoelectronic gas sensor based on an optical fiber integrated with a tetrakis(4-sulfonatophenyl)porphyrin (TPPS) thin film. The sensitive materials are selectively deposited on the core region of a fiber tip by UV light induced deposition technique. A simple and cheap process which can be easily extended to different porphyrin derivatives. When the TPPS film on the fiber tip is exposed to acid and/or base vapors, dramatic changes occur in the aggregation structure of the dye molecules in the film, from J- to H-type, resulting in a profound modification of their corresponding reflectance spectra. From the achieved experimental results it is evident that the presence of intense and narrow band peaks in the reflected spectra could be monitored to detect hazardous vapors.