Abstract: Protective coatings that resist oxide scale growth and
decrease chromium evaporation are necessary to make stainless steel
interconnect materials for long-term durable operation of solid oxide
fuel cells (SOFCs). In this study a layer of cobalt was electroplated
on the surface of AISI 441 ferritic stainless steel which is used in
solid oxide fuel cells for interconnect applications. The oxidation
behavior of coated substrates was studied as a function of time at
operating conditions of SOFCs. Cyclic oxidation has been also tested
at 800ÂșC for 100 cycles. Cobalt coating during isothermal oxidation
caused to the oxide growth resistance by limiting the outward
diffusion of Cr cation and the inward diffusion of oxygen anion.
Results of cyclic oxidation exhibited that coated substrates
demonstrate an excellent resistance against the spallation and
cracking.
Abstract: Manganese steel (Hadfield) is one of the important
alloys in industry due to its special properties. High work hardening
ability with appropriate toughness and ductility are the properties that
caused this alloy to be used in wear resistance parts and in high
strength condition. Heat treatment is the main process through which
the desired mechanical properties and microstructures are obtained in
Hadfield steel. In this study various heat treatment cycles, differing in
austenising temperature, time and quenching solution are applied. For
this purpose, the same samples of manganese steel was heat treated in
9 different cycles, and then the mechanical properties and
microstructures were investigated. Based on the results of the study,
the optimum heat treatment cycle was obtained.