Abstract: Application of nanoscience in biomedical field has come across as a new era. This study involves the synthesis of nano drug carrier with antibiotic loading. Based on the founding that polydopamine (PDA) nanoparticles could be formed via self-polymerization of dopamine at alkaline pH, one-step synthesis of rifampicin coupled polydopamine (PDA-R) nanoparticles was achieved by adding rifampicin into the dopamine solution. The successful yield of PDA nanoparticles with or without the presence of rifampicin during the polymerization process was characterized by scanning electron microscopy, Fourier transform infrared spectroscopy, and Raman spectroscopy. Drug loading was monitored by UV-vis spectroscopy and the loading efficiency of rifampicin was calculated to be 76%. Such highly capacious nano-reservoir was found very stable with little drug leakage at pH 3.
Abstract: Thin ZnO films are deposited on glass substrates via
sol–gel method and dip-coating. The films are prepared from zinc
acetate dehydrate as a starting reagent. After that the as-prepared
ZnO sol is aged for different periods (0, 1, 3, 5, 10, 15 and 30 days).
Nanocrystalline thin films are deposited from various sols. The
effect ZnO sols aging time on the structural and photocatalytic
properties of the films is studied. The films surface is studied by
Scanning Electron Microscopy. The effect of the aging time of the
starting solution is studied in the photocatalytic degradation of
Reactive Black 5 (RB5) by UV-vis spectroscopy. The experiments
are conducted upon UV-light illumination and in complete darkness.
The variation of the absorption spectra shows the degradation of RB5
dissolved in water, as a result of the reaction, occurring on the surface
of the films and promoted by UV irradiation. The initial
concentrations of dye (5, 10 and 20 ppm) and the effect of the aging
time are varied during the experiments. The results show, that the
increasing aging time of starting solution with respect to ZnO
generally promotes photocatalytic activity. The thin films obtained
from ZnO sol, which is aged 30 days have best photocatalytic
degradation of the dye (97,22%) in comparison with the freshly
prepared ones (65,92%). The samples and photocatalytic
experimental results are reproducible. Nevertheless, all films exhibit
a substantial activity in both UV light and darkness, which is
promising for the development of new ZnO photocatalysts by sol-gel
method.
Abstract: Bioreduction of silver nanoparticles (AgNPs) from silver ions (Ag+) using water extract of Thai basil leaf was successfully carried out. The basil leaf extract provided a reducing agent and stabilizing agent for a synthesis of metal nanoparticles. Silver nanoparticles received from cut and uncut basil leaf was compared. The resulting silver nanoparticles are characterized by UV-Vis spectroscopy. The maximum intensities of silver nanoparticle from cut and uncut basil leaf were 410 and 420, respectively. The techniques involved are simple, eco-friendly and rapid.
Abstract: Microfibrous palygorskite and tubular halloysite clay mineral combined with nanocrystalline TiO2 are incorporating in the preparation of nanocomposite films on glass substrates via sol-gel route at 450oC. The synthesis is employing nonionic surfactant molecule as pore directing agent along with acetic acid-based sol-gel route without addition of water molecules. Drying and thermal treatment of composite films ensure elimination of organic material lead to the formation of TiO2 nanoparticles homogeneously distributed on the palygorskite or halloysite surfaces. Nanocomposite films without cracks of active anatase crystal phase on palygorskite and halloysite surfaces are characterized by microscopy techniques, UV-Vis spectroscopy, and porosimetry methods in order to examine their structural properties.
The composite palygorskite-TiO2 and halloysite-TiO2 films with variable quantities of palygorskite and halloysite were tested as photocatalysts in the photo-oxidation of Basic Blue 41 azo dye in water. These nanocomposite films proved to be most promising photocatalysts and highly effective to dye’s decoloration in spite of small amount of palygorskite-TiO2 or halloysite-TiO2 catalyst immobilized onto glass substrates mainly due to the high surface area and uniform distribution of TiO2 on clay minerals avoiding aggregation.
Abstract: Quaternary InxAlyGa1-x-yN semiconductors have
attracted much research interest because the use of this quaternary
offer the great flexibility in tailoring their band gap profile while
maintaining their lattice-matching and structural integrity. The
structural and optical properties of InxAlyGa1-x-yN alloys grown by
molecular beam epitaxy (MBE) is presented. The structural quality of
InxAlyGa1-x-yN layers was characterized using high-resolution X-ray
diffraction (HRXRD). The results confirm that the InxAlyGa1-x-yN
films had wurtzite structure and without phase separation. As the In
composition increases, the Bragg angle of the (0002) InxAlyGa1-x-yN
peak gradually decreases, indicating the increase in the lattice constant
c of the alloys. FWHM of (0002) InxAlyGa1-x-yN decreases with
increasing In composition from 0 to 0.04, that could indicate the
decrease of quality of the samples due to point defects leading to
non-uniformity of the epilayers. UV-VIS spectroscopy have been used
to study the energy band gap of InxAlyGa1-x-yN. As the indium (In)
compositions increases, the energy band gap decreases. However, for
InxAlyGa1-x-yN with In composition of 0.1, the band gap shows a
sudden increase in energy. This is probably due to local alloy
compositional fluctuations in the epilayer. The bowing parameter
which appears also to be very sensitive on In content is investigated
and obtained b = 50.08 for quaternary InxAlyGa1-x-yN alloys. From
photoluminescence (PL) measurement, green luminescence (GL)
appears at PL spectrum of InxAlyGa1-x-yN, emitted for all x at ~530 nm
and it become more pronounced as the In composition (x) increased,
which is believed cause by gallium vacancies and related to isolated
native defects.
Abstract: Wet chemistry methods are used to prepare the
SiO2/Au nanoshells. The purpose of this research was to synthesize
gold coated SiO2 nanoshells for biomedical applications. Tunable
nanoshells were prepared by using different colloidal concentrations.
The nanoshells are characterized by FTIR, XRD, UV-Vis
spectroscopy and atomic force microscopy (AFM). The FTIR results
confirmed the functionalization of the surfaces of silica nanoparticles
with NH2 terminal groups. A tunable absorption was observed
between 470-600 nm with a maximum range of 530-560 nm. Based
on the XRD results three main peaks of Au (111), (200) and (220)
were identified. Also AFM results showed that the silica core
diameter was about 100 nm and the thickness of gold shell about 10
nm.
Abstract: This work relates the development of an optical fiber
(OF) sensor for the detection and quantification of single walled
carbon nanotubes in aqueous solutions. The developed OF displays a
compact design, it requires less expensive materials and equipment
as well as low volume of sample (0.2 mL). This methodology was
also validated by the comparison of its analytical performance with
that of a standard methodology based on ultraviolet-visible
spectroscopy. The developed OF sensor follows the general SDS
calibration proposed for OF sensors as a more suitable calibration
fitting compared with classical calibrations.
Abstract: Nano sized zirconium dioxide in monoclinic phase (m-ZrO2) has been synthesized in pure form through co-precipitation processing at different calcination temperatures and has been characterized by several techniques such as XRD, FT-IR, UV-Vis Spectroscopy and SEM. The dielectric and capacitance values of the pelletized samples have been examined at room temperature as the functions of frequency. The higher dielectric constant value of the sample having larger grain size proves the strong influence of grain size on the dielectric constant.
Abstract: Silver nanoparticles were prepared by chemical reduction method. Silver nitrate was taken as the metal precursor and hydrazine hydrate as a reducing agent. The formation of the silver nanoparticles was monitored using UV-Vis absorption spectroscopy. The UV-Vis spectroscopy revealed the formation of silver nanopart├¡cles by exhibing the typical surface plasmon absorption maxima at 418-420 nm from the UV–Vis spectrum. Comparison of theoretical (Mie light scattering theory) and experimental results showed that diameter of silver nanoparticles in colloidal solution is about 60 nm. We have used energy-dispersive spectroscopy (EDX), X-ray diffraction (XRD), transmission electron microscopy (TEM) and, UV–Vis spectroscopy to characterize the nanoparticles obtained. The energy-dispersive spectroscopy (EDX) of the nanoparticles dispersion confirmed the presence of elemental silver signal no peaks of other impurity were detected. The average size and morphology of silver nanoparticles were determined by transmission electron microscopy (TEM). TEM photographs indicate that the nanopowders consist of well dispersed agglomerates of grains with a narrow size distribution (40 and 60 nm), whereas the radius of the individual particles are between 10 and 20 nm. The synthesized nanoparticles have been structurally characterized by X-ray diffraction and transmission high-energy electron diffraction (HEED). The peaks in the XRD pattern are in good agreement with the standard values of the face-centered-cubic form of metallic silver (ICCD-JCPDS card no. 4-0787) and no peaks of other impurity crystalline phases were detected. Additionally, the antibacterial activity of the nanopart├¡culas dispersion was measured by Kirby-Bauer method. The nanoparticles of silver showed high antimicrobial and bactericidal activity against gram positive bacteria such as Escherichia Coli, Pseudimonas aureginosa and staphylococcus aureus which is a highly methicillin resistant strain.