Abstract: The commercially available titanium alloy, Ti-6Al-4V, was oxynitrided in the deoxygenated nitrogen gas at high temperatures followed by cooling in oxygen-containing nitrogen in order to analyze the influence of oxynitriding parameters on the phase modification, hardness, and the microstructural evolution of the oxynitrided coating. The surface microhardness of the oxynitrided alloy increased due to the strengthening effect of the formed titanium oxynitrides, TiNxOy. The maximum microhardness was obtained, when TiNxOy had near equiatomic composition of nitrogen and oxygen. It could be attained under the optimum oxygen partial pressure and temperature-time condition.
Abstract: Micro-alloyed steel components are used in
automotive industry for the necessity to make the manufacturing
process cycles shorter when compared to conventional steel by
eliminating heat treatment cycles, so an important saving of costs and
energy can be reached by reducing the number of operations. Microalloying
elements like vanadium, niobium or titanium have been
added to medium carbon steels to achieve grain refinement with or
without precipitation strengthening along with uniform
microstructure throughout the matrix. Present study reports the
applicability of medium carbon vanadium micro-alloyed steel in hot
forging. Forgeability has been determined with respect to different
cooling rates, after forging in a hydraulic press at 50% diameter
reduction in temperature range of 900-11000C. Final microstructures,
hardness, tensile strength, and impact strength have been evaluated.
The friction coefficients of different lubricating conditions, viz.,
graphite in hydraulic oil, graphite in furnace oil, DF 150 (Graphite,
Water-Based) die lubricant and dry or without any lubrication were
obtained from the ring compression test for the above micro-alloyed
steel. Results of ring compression tests indicate that graphite in
hydraulic oil lubricant is preferred for free forging and dry lubricant
is preferred for die forging operation. Exceptionally good forgeability
and high resistance to fracture, especially for faster cooling rate has
been observed for fine equiaxed ferrite-pearlite grains, some amount
of bainite and fine precipitates of vanadium carbides and
carbonitrides. The results indicated that the cooling rate has a
remarkable effect on the microstructure and mechanical properties at
room temperature.
Abstract: Quaternary InxAlyGa1-x-yN semiconductors have
attracted much research interest because the use of this quaternary
offer the great flexibility in tailoring their band gap profile while
maintaining their lattice-matching and structural integrity. The
structural and optical properties of InxAlyGa1-x-yN alloys grown by
molecular beam epitaxy (MBE) is presented. The structural quality of
InxAlyGa1-x-yN layers was characterized using high-resolution X-ray
diffraction (HRXRD). The results confirm that the InxAlyGa1-x-yN
films had wurtzite structure and without phase separation. As the In
composition increases, the Bragg angle of the (0002) InxAlyGa1-x-yN
peak gradually decreases, indicating the increase in the lattice constant
c of the alloys. FWHM of (0002) InxAlyGa1-x-yN decreases with
increasing In composition from 0 to 0.04, that could indicate the
decrease of quality of the samples due to point defects leading to
non-uniformity of the epilayers. UV-VIS spectroscopy have been used
to study the energy band gap of InxAlyGa1-x-yN. As the indium (In)
compositions increases, the energy band gap decreases. However, for
InxAlyGa1-x-yN with In composition of 0.1, the band gap shows a
sudden increase in energy. This is probably due to local alloy
compositional fluctuations in the epilayer. The bowing parameter
which appears also to be very sensitive on In content is investigated
and obtained b = 50.08 for quaternary InxAlyGa1-x-yN alloys. From
photoluminescence (PL) measurement, green luminescence (GL)
appears at PL spectrum of InxAlyGa1-x-yN, emitted for all x at ~530 nm
and it become more pronounced as the In composition (x) increased,
which is believed cause by gallium vacancies and related to isolated
native defects.
Abstract: Low carbon deep drawing steel DC 01 according to EN 10130-91 was nitrooxidized in dissociated ammonia at 580°C/45 min and consequently oxidised at 380°C/5 min in vapour of distilled water. Material after nitrooxidation had 54 % increase of yield point, 34 % increase of strength and 10-times increased resistance to atmospheric corrosion in comparison to the material before nitrooxidation. The microstructure of treated material consisted of thin ε-phase layer connected to layer containing precipitated massive needle shaped Fe4N - γ' nitrides. This layer passed to a diffusion layer consisting of fine irregular shaped Fe16N2 - α'' nitrides regularly dispersed in ferritic matrix. Fatigue properties were examined under bending load with frequency of 20 kHz and sinusoidal symmetric cycle. The results confirmed positive influence of nitrooxidation on fatigue properties as fatigue limit of treated material was double in comparison to untreated material.
Abstract: We have investigated the effect of piezoelectric (PZ)
polarization property in binary as well as in ternary wurtzite nitrides.
It is found that with the presence of PZ polarization property, the
phonon group velocity is modified. The change in phonon group
velocity due to PZ polarization effect directly depends on
piezoelectric tensor value. Using different piezoelectric tensor values
recommended by different workers in the literature, percent change in
group velocities of phonons has been estimated. The Debye
temperatures and frequencies of binary nitrides GaN, AlN and InN
are also calculated using the modified group velocities. For ternary
nitrides AlxGa(1-x)N, InxGa(1-x)N and InxAl(1-x)N, the phonon group
velocities have been calculated as a functions of composition. A
small positive bowing is observed in phonon group velocities of
ternary alloys. Percent variations in phonon group velocities are also
calculated for a straightforward comparison among ternary nitrides.
The results are expected to show a change in phonon relaxation rates
and thermal conductivity of III-nitrides when piezoelectric
polarization property is taken into consideration.