Abstract: Electromagnetic Interference (EMI) shielded doors made from brass extruded channels need to be welded with shielded enclosures to attain optimum shielding performance. Control of welding induced distortion is a problem in welding dissimilar metals like steel and brass. In this research, soldering of the steel-brass joint has been proposed to avoid weld distortion. The material used for brass channel is UNS C36000. The thickness of brass is defined by the manufacturing process, i.e. extrusion. The thickness of shielded enclosure material (ASTM A36) can be varied to produce joint between the dissimilar metals. Steel sections of different gauges are soldered using (91% tin, 9% zinc) solder to the brass, and strength of joint is measured by standard test procedures. It is observed that thin steel sheets produce a stronger bond with brass. The steel sections further require to be welded with shielded enclosure steel sheets through TIG welding process. Stresses and deformation in the vicinity of soldered portion is calculated through FE simulation. Crack formation in soldered area is also studied through experimental work. It has been found that in thin sheets deformation produced due to applied force is localized and has no effect on soldered joint area whereas in thick sheets profound cracks have been observed in soldered joint. The shielding effectiveness of EMI shielded door is compromised due to these cracks. The shielding effectiveness of the specimens is tested and results are compared.
Abstract: Earing defect in drawing process is highly undesirable not only because it adds on an additional trimming operation but also because the uneven material flow demands extra care. The objective of this work is to study the earing problem in the Deep Drawing of circular cup and to optimize the blank shape to reduce the earing. A finite element model is developed for 3-D numerical simulation of cup forming process in ABAQUS. Extra-deep-drawing (EDD) steel sheet has been used for simulation. Properties and tool design parameters were used as input for simulation. Earing was observed in the simulated cup and it was measured at various angles with respect to rolling direction. To reduce the earing defect initial blank shape was modified with the help of anisotropy coefficient. Modified blanks showed notable reduction in earing.
Abstract: In this work, the plastic behaviour of cold-rolled zinc
coated dual-phase steel sheets DP600 and DP800 grades is firstly
investigated with the help of uniaxial, hydraulic bulge and Forming
Limit Curve (FLC) tests. The uniaxial tensile tests were performed in
three angular orientations with respect to the rolling direction to
evaluate the strain-hardening and plastic anisotropy. True stressstrain
curves at large strains were determined from hydraulic bulge
testing and fitted to a work-hardening equation. The limit strains are
defined at both localized necking and fracture conditions according to
Nakajima’s hemispherical punch procedure. Also, an elasto-plastic
localization model is proposed in order to predict strain and stress
based forming limit curves. The investigated dual-phase sheets
showed a good formability in the biaxial stretching and drawing FLC
regions. For both DP600 and DP800 sheets, the corresponding
numerical predictions overestimated and underestimated the
experimental limit strains in the biaxial stretching and drawing FLC
regions, respectively. This can be attributed to the restricted failure
necking condition adopted in the numerical model, which is not
suitable to describe the tensile and shear fracture mechanisms in
advanced high strength steels under equibiaxial and biaxial stretching
conditions.
Abstract: There is not much effective guideline on development of design parameters selection on spring back for advanced high strength steel sheet metal in U-channel process during cold forming process. This paper presents the development of predictive model for spring back in U-channel process on advanced high strength steel sheet employing Response Surface Methodology (RSM). The experimental was performed on dual phase steel sheet, DP590 in Uchannel forming process while design of experiment (DoE) approach was used to investigates the effects of four factors namely blank holder force (BHF), clearance (C) and punch travel (Tp) and rolling direction (R) were used as input parameters using two level values by applying Full Factorial design (24 ). From a statistical analysis of variant (ANOVA), result showed that blank holder force (BHF), clearance (C) and punch travel (Tp) displayed significant effect on spring back of flange angle (β2 ) and wall opening angle (β1 ), while rolling direction (R) factor is insignificant. The significant parameters are optimized in order to reduce the spring back behavior using Central Composite Design (CCD) in RSM and the optimum parameters were determined. A regression model for spring back was developed. The effect of individual parameters and their response was also evaluated. The results obtained from optimum model are in agreement with the experimental values.
Abstract: The design of multi stage deep drawing processes requires the evaluation of many process parameters such as the intermediate die geometry, the blank shape, the sheet thickness, the blank holder force, friction, lubrication etc..These process parameters have to be determined for the optimum forming conditions before the process design. In general sheet metal forming may involve stretching drawing or various combinations of these basic modes of deformation. It is important to determine the influence of the process variables in the design of sheet metal working process. Especially, the punch and die corner for deep drawing will affect the formability. At the same time the prediction of sheet metals springback after deep drawing is an important issue to solve for the control of manufacturing processes. Nowadays, the importance of this problem increases because of the use of steel sheeting with high stress and also aluminum alloys.
The aim of this paper is to give a better understanding of the springback and its effect in various sheet metals forming process such as expansion and restreint deep drawing in the cup drawing process, by varying radius die, lubricant for two commercially available materials e.g. galvanized steel and Aluminum sheet. To achieve these goals experiments were carried out and compared with other results. The original of our purpose consist on tests which are ensured by adapting a U-type stretching-bending device on a tensile testing machine, where we studied and quantified the variation of the springback.
Abstract: Spheroidization heat treatment was conducted on the SK85 high carbon steel sheets with various initial microstructures obtained after cold rolling by various reduction ratios at a couple of annealing temperatures. On the high carbon steel sheet with fine pearlite microstructure, obtained by soaking at 800oC for 2hr in a box furnace and then annealing at 570oC for 5min in a salt bath furnace followed by water quenching, cold rolling was conducted by reduction ratios of 20, 30, and 40%. Heat treatment for spheroidization was carried out at 600 and 720oC for the various time intervals from 0.1 to 32 hrs. Area fraction of spheroidized cementite was measured with an image analyzer as a function of cold reduction ratios and duration times. Tensile tests were carried out at room temperature on the spheoidized high carbon steel.
Abstract: Resistance spot welding (RSW) has been used widely to join sheet metals. It has been a challenge to get required weld quality in spot welding of dissimilar thickness materials. Weld parameters are not generally available in standards for thickness beyond 4mm. This paper presents the welding process design and parameter optimization of RSW used in joining of low carbon steel sheet of thickness 0.8 mm and metal strips of cross section 10 x 5mm for electrical motor applications. Taguchi quality design was adopted for weld current and time optimization using L9 orthogonal array. Optimum process parameters (current- 3.5kA and time- 10 cycles) were obtained from the Taguchi analysis and shear test results. Confirmation experiment result revealed that the weld quality was within acceptable interval. Further, numerical simulation of RSW process was carried out with selected weld parameters to quantify the temperature at faying surface and check for formation of appropriate nugget. The nugget geometry measured after peel test and predicted from numerical validation method were similar and in accordance with the standards.
Abstract: A solar powered air heating system using parabolic trough collector was experimentally investigated. In this experimental setup, the reflected solar radiations were focused on absorber tube which was placed at focal length of the parabolic trough. In this setup, air was used as working fluid which collects the heat from absorber tube. To enhance the performance of parabolic trough, collector with different type of reflectors were used. It was observed For Aluminum sheet maximum temperature is 52.3ºC, which 24.22% more than steel sheet as reflector and 8.5% more than Aluminum foil as reflector, also efficiency by using Aluminum sheet as reflector compared to steel sheet as reflector is 61.18% more. Efficiency by using Aluminum sheet as reflector compared to Aluminum foil as reflector is 18.98% more.
Abstract: Composite steel-concrete slabs using thin-walled
corrugated steel sheets with embossments represent a modern and
effective combination of steel and concrete. However, the design
of new types of sheeting is conditional on the execution of expensive
and time-consuming laboratory testing. The effort to develop
a cheaper and faster method has lead to many investigations all over
the world. In our paper we compare the results from our experiments
involving vacuum loading, four-point bending and small-scale shear
tests.
Abstract: Low carbon deep drawing steel DC 01 according to EN 10130-91 was nitrooxidized in dissociated ammonia at 580°C/45 min and consequently oxidised at 380°C/5 min in vapour of distilled water. Material after nitrooxidation had 54 % increase of yield point, 34 % increase of strength and 10-times increased resistance to atmospheric corrosion in comparison to the material before nitrooxidation. The microstructure of treated material consisted of thin ε-phase layer connected to layer containing precipitated massive needle shaped Fe4N - γ' nitrides. This layer passed to a diffusion layer consisting of fine irregular shaped Fe16N2 - α'' nitrides regularly dispersed in ferritic matrix. Fatigue properties were examined under bending load with frequency of 20 kHz and sinusoidal symmetric cycle. The results confirmed positive influence of nitrooxidation on fatigue properties as fatigue limit of treated material was double in comparison to untreated material.
Abstract: This study was aimed to explain the influence of surface roughness of the drawbead on non-symmetry deep drawing cold rolled steel sheet to improve the drawability of cold rolled steel sheet. The variables used in this study included semi-circle drawbead with 3 levels of surface roughness which are 6.127 mm Ra, 0.963 mm Ra and 0.152 mm Ra and cold rolled steel sheet according to 3 grades of the JIS standards which are SPCC, SPCE and SPCD with the thickness of 1.0 mm and the blankholder force which is 50% of the drawing force and the depth of 50 mm. According to the test results, when there was the increase in the surface roughness of drawbead, there would be the increase in deep drawing force, especially the SPCC cold rolled steel sheet. This is similar to the increase in the equivalent strain and the wall thickness distribution when the surface roughness of the drawbead increased. It could be concluded that the surface roughness of drawbead has an influence on deep drawing cold rolled steel sheet, especially the drawing force, the equivalent strain and the wall thickness distribution.
Abstract: In this research work, investigations are carried out on
Continuous Wave (CW) Nd:YAG laser welding system after
preliminary experimentation to understand the influencing parameters
associated with laser welding of AISI 304. The experimental
procedure involves a series of laser welding trials on AISI 304
stainless steel sheets with various combinations of process parameters
like beam power, beam incident angle and beam incident angle. An
industrial 2 kW CW Nd:YAG laser system, available at Welding
Research Institute (WRI), BHEL Tiruchirappalli, is used for
conducting the welding trials for this research. After proper tuning of
laser beam, laser welding experiments are conducted on AISI 304
grade sheets to evaluate the influence of various input parameters on
weld bead geometry i.e. bead width (BW) and depth of penetration
(DOP). From the laser welding results, it is noticed that the beam
power and welding speed are the two influencing parameters on
depth and width of the bead. Three dimensional finite element
simulation of high density heat source have been performed for laser
welding technique using finite element code ANSYS for predicting
the temperature profile of laser beam heat source on AISI 304
stainless steel sheets. The temperature dependent material properties
for AISI 304 stainless steel are taken into account in the simulation,
which has a great influence in computing the temperature profiles.
The latent heat of fusion is considered by the thermal enthalpy of
material for calculation of phase transition problem. A Gaussian
distribution of heat flux using a moving heat source with a conical
shape is used for analyzing the temperature profiles. Experimental
and simulated values for weld bead profiles are analyzed for stainless
steel material for different beam power, welding speed and beam
incident angle. The results obtained from the simulation are
compared with those from the experimental data and it is observed
that the results of numerical analysis (FEM) are in good agreement
with experimental results, with an overall percentage of error
estimated to be within ±6%.
Abstract: The purpose of this research study is to investigate the manner in which various loads affect the mechanical properties of the formed mild steel plates. The investigation focuses on examining the cross-sectional area of the metal plate at the centre of the formed mild steel plate. Six mild steel plates were deformed with different loads. The loads applied on the plates had a magnitude of 5 kg, 10 kg, 15 kg, 20 kg, 25 kg and 30 kg. The radius of the punching die was 120 mm and the loads were applied at room temperature. The investigations established that the applied load causes the Vickers microhardness at the cross-sectional area of the plate to increase due to strain hardening. Hence, the percentage increase of the hardness due to the load was found to be directly proportional to the increase in the load. Furthermore, the tensile test results for the parent material showed that the average Ultimate Tensile Strength (UTS) for the three samples was 308 MPa while the average Yield Strength and Percentage Elongation were 227 MPa and 38 % respectively. Similarly, the UTS of the formed components increased after the deformation of the plate, as such it can be concluded that the forming loads alter the mechanical properties of the materials by improving and strengthening the material properties.
Abstract: We present the development of a new underwater laser
cutting process in which a water-jet has been used along with the
laser beam to remove the molten material through kerf. The
conventional underwater laser cutting usually utilizes a high pressure
gas jet along with laser beam to create a dry condition in the cutting
zone and also to eject out the molten material. This causes a lot of gas
bubbles and turbulence in water, and produces aerosols and waste
gas. This may cause contamination in the surrounding atmosphere
while cutting radioactive components like burnt nuclear fuel. The
water-jet assisted underwater laser cutting process produces much
less turbulence and aerosols in the atmosphere. Some amount of
water vapor bubbles is formed at the laser-metal-water interface;
however, they tend to condense as they rise up through the
surrounding water. We present the design and development of a
water-jet assisted underwater laser cutting head and the parametric
study of the cutting of AISI 304 stainless steel sheets with a 2 kW
CW fiber laser. The cutting performance is similar to that of the gas
assist laser cutting; however, the process efficiency is reduced due to
heat convection by water-jet and laser beam scattering by vapor. This
process may be attractive for underwater cutting of nuclear reactor
components.