Abstract: The commercially available titanium alloy, Ti-6Al-4V, was oxynitrided in the deoxygenated nitrogen gas at high temperatures followed by cooling in oxygen-containing nitrogen in order to analyze the influence of oxynitriding parameters on the phase modification, hardness, and the microstructural evolution of the oxynitrided coating. The surface microhardness of the oxynitrided alloy increased due to the strengthening effect of the formed titanium oxynitrides, TiNxOy. The maximum microhardness was obtained, when TiNxOy had near equiatomic composition of nitrogen and oxygen. It could be attained under the optimum oxygen partial pressure and temperature-time condition.
Abstract: Fe-2%Mn-0.5%Si-0.2C steel was welded and corroded
at 600, 700 and 800oC for 20 h in 1 atm of N2/H2S/H2O-mixed gas in
order to characterize the high-temperature corrosion behavior of the
welded joint. Corrosion proceeded fast and almost linearly. It
increased with an increase in the corrosion temperature. H2S formed
FeS owing to sulfur released from H2S. The scales were fragile and
nonadherent.