Abstract: Synthesis of gold nanoparticles has attracted much
attention since the pioneering discovery of the high catalytic activity
of supported gold nanoparticles in the reaction of CO oxidation at
low temperature. In this research field, we used Na-montmorillonite
for gold nanoparticles stabilization; various gold loading percentage
1, 2 and 5% were used for gold nanoparticles preparation. The gold
nanoparticles were obtained using chemical reduction method using
NaBH4 as reductant agent. The obtained gold nanoparticles stabilized
in Na-montmorillonite were used as catalysts for the reduction of 4-
nitrophenol to aminophenol with sodium borohydride at room
temperature. The UV-Vis results confirmed directly the gold
nanoparticles formation. The XRD and N2 adsorption results showed
the formation of gold nanoparticles in the pores of montmorillonite
with an average size of 5 nm obtained on samples with 2% gold
loading percentage. The gold particles size increased with the
increase of gold loading percentage. The reduction reaction of 4-
nitrophenol into 4-aminophenol with NaBH4 catalyzed by Au-Namontmorillonite
catalyst exhibits remarkably a high activity; the
reaction was completed within 9 min for 1%Au-Na-montmorillonite
and within 3 min for 2%Au-Na-montmorillonite.
Abstract: In our recent study, we have used ZnO nanoparticles assisted with UV light irradiation to investigate the photocatalytic degradation of Phenol Red (PR). The ZnO photocatalyst was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), specific surface area analysis (BET) and UVvisible spectroscopy. X-ray diffractometry result for the ZnO nanoparticles exhibit normal crystalline phase features. All observed peaks can be indexed to the pure hexagonal wurtzite crystal structures, with the space group of P63mc. There are no other impurities in the diffraction peak. In addition, TEM measurement shows that most of the nanoparticles are rod-like and spherical in shape and fairly monodispersed. A significant degradation of the PR was observed when the catalyst was added into the solution even without the UV light exposure. In addition, the photodegradation increases with the photocatalyst loading. The surface area of the ZnO nanomaterials from the BET measurement was 11.9 m2/g. Besides the photocatalyst loading, the effect of some parameters on the photodegradation efficiency such as initial PR concentration and pH were also studied.