Abstract: Synthesis of gold nanoparticles has attracted much
attention since the pioneering discovery of the high catalytic activity
of supported gold nanoparticles in the reaction of CO oxidation at
low temperature. In this research field, we used Na-montmorillonite
for gold nanoparticles stabilization; various gold loading percentage
1, 2 and 5% were used for gold nanoparticles preparation. The gold
nanoparticles were obtained using chemical reduction method using
NaBH4 as reductant agent. The obtained gold nanoparticles stabilized
in Na-montmorillonite were used as catalysts for the reduction of 4-
nitrophenol to aminophenol with sodium borohydride at room
temperature. The UV-Vis results confirmed directly the gold
nanoparticles formation. The XRD and N2 adsorption results showed
the formation of gold nanoparticles in the pores of montmorillonite
with an average size of 5 nm obtained on samples with 2% gold
loading percentage. The gold particles size increased with the
increase of gold loading percentage. The reduction reaction of 4-
nitrophenol into 4-aminophenol with NaBH4 catalyzed by Au-Namontmorillonite
catalyst exhibits remarkably a high activity; the
reaction was completed within 9 min for 1%Au-Na-montmorillonite
and within 3 min for 2%Au-Na-montmorillonite.
Abstract: The preparation of Cu nanoparticles (NPs) through the reduction of copper ions by sodium borohydride in the presence of sodium polyacrylate with a molecular weight of 1200 is reported. Cu NPs were synthesized at a concentration of copper salt equal to 2.5, 5, and 10 mM, and at a molar ratio of copper ions and monomeric unit of polyacrylate equal to 1:2. The as-prepared Cu NPs have diameters of about 2.5–3 nm for copper concentrations of 2.5 and 5 mM, and 6 nm for copper concentration of 10 mM. Depending on the copper salt concentration and concentration of additionally added polyacrylate to Cu particle dispersion, primarily formed NPs grow through the process of aggregation and/or coalescence into clusters and/or particles with a diameter between 20–100 nm. The amount of additionally added sodium polyacrylate influences the stability of Cu particles against air oxidation. The catalytic efficiency of the prepared Cu particles for the reduction of 4-nitrophenol is discussed.