Abstract: Titanium nitride (TiN) has been synthesized using the
sheet plasma negative ion source (SPNIS). The parameters used for
its effective synthesis has been determined from previous
experiments and studies. In this study, further enhancement of the
deposition rate of TiN synthesis and advancement of the SPNIS
operation is presented. This is primarily achieved by the addition of
Sm-Co permanent magnets and a modification of the configuration in
the TiN deposition process. The magnetic enhancement is aimed at
optimizing the sputtering rate and the sputtering yield of the process.
The Sm-Co permanent magnets are placed below the Ti target for
better sputtering by argon. The Ti target is biased from –250V to –
350V and is sputtered by Ar plasma produced at discharge current of
2.5–4A and discharge potential of 60–90V. Steel substrates of
dimensions 20x20x0.5mm3 were prepared with N2:Ar volumetric
ratios of 1:3, 1:5 and 1:10. Ocular inspection of samples exhibit
bright gold color associated with TiN. XRD characterization
confirmed the effective TiN synthesis as all samples exhibit the (200)
and (311) peaks of TiN and the non-stoichiometric Ti2N (220) facet.
Cross-sectional SEM results showed increase in the TiN deposition
rate of up to 0.35μm/min. This doubles what was previously obtained
[1]. Scanning electron micrograph results give a comparative
morphological picture of the samples. Vickers hardness results gave
the largest hardness value of 21.094GPa.
Abstract: A novel methodology has been used to design an
evaporator coil of a refrigerant. The methodology used is through a
complete Computer Aided Design /Computer Aided Engineering
approach, by means of a Computational Fluid Dynamic/Finite
Element Analysis model which is executed many times for the
thermal-fluid exploration of several designs' configuration by an
commercial optimizer. Hence the design is carried out automatically
by parallel computations, with an optimization package taking the
decisions rather than the design engineer. The engineer instead takes
decision regarding the physical settings and initializing of the
computational models to employ, the number and the extension of the
geometrical parameters of the coil fins and the optimization tools to
be employed. The final design of the coil geometry found to be better
than the initial design.
Abstract: Wheat prediction was carried out using different meteorological variables together with agro meteorological indices in Ardebil district for the years 2004-2005 & 2005–2006. On the basis of correlation coefficients, standard error of estimate as well as relative deviation of predicted yield from actual yield using different statistical models, the best subset of agro meteorological indices were selected including daily minimum temperature (Tmin), accumulated difference of maximum & minimum temperatures (TD), growing degree days (GDD), accumulated water vapor pressure deficit (VPD), sunshine hours (SH) & potential evapotranspiration (PET). Yield prediction was done two months in advance before harvesting time which was coincide with commencement of reproductive stage of wheat (5th of June). It revealed that in the final statistical models, 83% of wheat yield variability was accounted for variation in above agro meteorological indices.
Abstract: Long terms variation of solar insolation had been
widely studied. However, its parallel observations in short time scale
is rather lacking. This paper aims to investigate the short time scale
evolution of solar radiation spectrum (UV, PAR, and NIR bands) due
to atmospheric aerosols and water vapors. A total of 25 days of
global and diffused solar spectrum ranges from air mass 2 to 6 were
collected using ground-based spectrometer with shadowband
technique. The result shows that variation of solar radiation is the
least in UV fraction, followed by PAR and the most in NIR. Broader
variations in PAR and NIR are associated with the short time scale
fluctuations of aerosol and water vapors. The corresponding daily
evolution of UV, PAR, and NIR fractions implies that aerosol and
water vapors variation could also be responsible for the deviation
pattern in the Langley-plot analysis.
Abstract: This paper reports on the results of experimental
investigations of flash evaporation from superheated jet issues
vertically upward from a round straight nozzle of 81.3 mm diameter.
For the investigated range of jet superheat degree and velocity, it was
shown that flash evaporation enhances with initial temperature
increase. Due to the increase of jet inertia and subsequently the delay
of jet shattering, increase of jet velocity was found to result in
increase of evaporation "delay period". An empirical equation
predicts the jet evaporation completion height was developed, this
equation is thought to be useful in designing the flash evaporation
chamber. In attempts for enhancement of flash evaporation, use of
steel wire mesh located at short distance downstream was found
effective with no consequent pressure drop.
Abstract: A good green building design project, designers should consider not only energy consumption, but also healthy and comfortable needs of inhabitants. In recent years, the Taiwan government paid attentions on both carbon reduction and indoor air quality issues, which be presented in the legislation of Building Codes and other regulations. Taiwan located in hot and humid climates, dampness in buildings leads to significant microbial pollution and building damage. This means that the high temperature and humidity present a serious indoor air quality issue. The interactions between vapor transfers and energy fluxes are essential for the whole building Heat Air and Moisture (HAM) response. However, a simulation tool with short calculation time, property accuracy and interface is needed for practical building design processes. In this research, we consider the vapor transfer phenomenon of building materials as well as temperature and humidity and energy consumption in a building space. The simulation bases on the EMPD method, which was performed by EnergyPlus, a simulation tool developed by DOE, to simulate the indoor moisture variation in a one-zone residential unit based on the Effective Moisture Penetration Depth Method, which is more suitable for practical building design processes.
Abstract: Carbon nanotubes (CNTs) possess unique structural,
mechanical, thermal and electronic properties, and have been
proposed to be used for applications in many fields. However, to
reach the full potential of the CNTs, many problems still need to be
solved, including the development of an easy and effective
purification procedure, since synthesized CNTs contain impurities,
such as amorphous carbon, carbon nanoparticles and metal particles.
Different purification methods yield different CNT characteristics
and may be suitable for the production of different types of CNTs. In
this study, the effect of different purification chemicals on carbon
nanotube quality was investigated. CNTs were firstly synthesized by
chemical vapor deposition (CVD) of acetylene (C2H2) on a
magnesium oxide (MgO) powder impregnated with an iron nitrate
(Fe(NO3)3·9H2O) solution. The synthesis parameters were selected
as: the synthesis temperature of 800°C, the iron content in the
precursor of 5% and the synthesis time of 30 min. The liquid phase
oxidation method was applied for the purification of the synthesized
CNT materials. Three different acid chemicals (HNO3, H2SO4, and
HCl) were used in the removal of the metal catalysts from the
synthesized CNT material to investigate the possible effects of each
acid solution to the purification step. Purification experiments were
carried out at two different temperatures (75 and 120 °C), two
different acid concentrations (3 and 6 M) and for three different time
intervals (6, 8 and 15 h). A 30% H2O2 : 3M HCl (1:1 v%) solution
was also used in the purification step to remove both the metal
catalysts and the amorphous carbon. The purifications using this
solution were performed at the temperature of 75°C for 8 hours.
Purification efficiencies at different conditions were evaluated by
thermogravimetric analysis. Thermal and electrical properties of
CNTs were also determined. It was found that the obtained electrical
conductivity values for the carbon nanotubes were typical for organic
semiconductor materials and thermal stabilities were changed
depending on the purification chemicals.
Abstract: Owing to the stringent environmental legislations,
CO2 capture and sequestration is one of the viable solutions to reduce
the CO2 emissions from various sources. In this context, Ionic liquids
(ILs) are being investigated as suitable absorption media for CO2
capture. Due to their non-evaporative, non-toxic, and non-corrosive
nature, these ILs have the potential to replace the existing solvents
like aqueous amine solutions for CO2 separation technologies. Thus,
the present work aims at studying the important aspects such as the
interactions of CO2 molecule with different anions (F-, Br-, Cl-, NO3
-,
BF4
-, PF6
-, Tf2N-, and CF3SO3
-) that are commonly used in ILs
through molecular modeling. In this, the minimum energy structures
have been obtained using Ab initio based calculations at MP2
(Moller-Plesset perturbation) level. Results revealed various degrees
of distortion of CO2 molecule (from its linearity) with the anions
studied, most likely due to the Lewis acid-base interactions between
CO2 and anion. Furthermore, binding energies for the anion-CO2
complexes were also calculated. The implication of anion-CO2
interactions to the solubility of CO2 in ionic liquids is also discussed.
Abstract: A satured liquid is warmed until boiling in a parallelepipedic boiler. The heat is supplied in a liquid through the horizontal bottom of the boiler, the other walls being adiabatic. During the process of boiling, the liquid evaporates through its free surface by deforming it. This surface which subdivides the boiler into two regions occupied on both sides by the boiled liquid (broth) and its vapor which surmounts it. The broth occupying the region and its vapor the superior region. A two- fluids model is used to describe the dynamics of the broth, its vapor and their interface. In this model, the broth is treated as a monophasic fluid (homogeneous model) and form with its vapor adiphasic pseudo fluid (two-fluid model). Furthermore, the interface is treated as a zone of mixture characterized by superficial void fraction noted α* . The aim of this article is to describe the dynamics of the interface between the boiled fluid and its vapor within a boiler. The resolution of the problem allowed us to show the evolution of the broth and the level of the liquid.
Abstract: Results are presented from a combined experimental
and modeling study undertaken to understand the effect of fuel spray
angle on soot production in turbulent liquid spray flames. The
experimental work was conducted in a cylindrical laboratory furnace
at fuel spray cone angle of 30º, 45º and 60º. Soot concentrations
inside the combustor are measured by filter paper technique. The soot
concentration is modeled by using the soot particle number density
and the mass density based acetylene concentrations. Soot oxidation
occurred by both hydroxide radicals and oxygen molecules. The
comparison of calculated results against experimental measurements
shows good agreement. Both the numerical and experimental results
show that the peak value of soot and its location in the furnace
depend on fuel spray cone angle. An increase in spray angle enhances
the evaporating rate and peak temperature near the nozzle. Although
peak soot concentration increase with enhance of fuel spray angle but
soot emission from the furnace decreases.
Abstract: The atmospheric pressure plasma torch with a direct
current arc discharge stabilized by water vapor vortex was
experimentally investigated. Overheated up to 450K water vapor was
used as plasma forming gas. Plasma torch design is one of the most
important factors leading to a stable operation of the device. The
electrical and thermal characteristics of the plasma torch were
determined during the experimental investigations. The design and
the basic characteristics of the water vapor plasma torch are presented
in the paper.
Plasma torches with the electric arc stabilized by water vapor
vortex provide special performance characteristics in some plasma
processing applications such as thermal plasma neutralization and
destruction of organic wastes enabling to extract high caloric value
synthesis gas as by-product of the process. Syngas could be used as a
surrogate fuel partly replacing the dependence on the fossil fuels or
used as a feedstock for hydrogen, methanol production.
Abstract: Isobaric vapor-liquid equilibrium measurements are reported for the binary mixtures of Mesitylene + 1-Heptanol and Mesitylene + 1-Octanol at 97.3 kPa. The measurements have been performed using a vapor recirculating type (modified Othmer's) equilibrium still. Both the mixtures show positive deviation from ideality. The Mesitylene + 1-Heptanol mixture forms an azeotrope whereas Mesitylene + 1- Octanol form a non – azeotropic mixture. The activity coefficients have been calculated taking into consideration the vapor phase nonideality. The data satisfy the thermodynamic consistency tests of Herington, and Hirata. The activity coefficients have been satisfactorily correlated by means of the Margules, Redlich-Kister, Wilson, Black, and NRTL equations. The activity coefficient values have also been obtained by UNIFAC method.
Abstract: In this paper we present modeling and simulation for
physical vapor deposition for metallic bipolar plates. In the models
we discuss the application of different models to simulate the
transport of chemical reactions of the gas species in the gas chamber.
The so called sputter process is an extremely sensitive process to
deposit thin layers to metallic plates. We have taken into account
lower order models to obtain first results with respect to the gas
fluxes and the kinetics in the chamber.
The model equations can be treated analytically in some
circumstances and complicated multi-dimensional models are solved
numerically with a software-package (UG unstructed grids, see [1]).
Because of multi-scaling and multi-physical behavior of the models,
we discuss adapted schemes to solve more accurate in the different
domains and scales. The results are discussed with physical
experiments to give a valid model for the assumed growth of thin
layers.
Abstract: Isobaric vapor-liquid equilibrium measurements are
reported for binary mixture of 2-Methyltetrahydrofuran and Cumene
at 97.3 kPa. The data were obtained using a vapor recirculating type
(modified Othmer's) equilibrium still. The mixture shows slight
negative deviation from ideality. The system does not form an
azeotrope. The experimental data obtained in this study are
thermodynamically consistent according to the Herington test. The
activity coefficients have been satisfactorily correlated by means of
the Margules, and NRTL equations. Excess Gibbs free energy has
been calculated from the experimental data. The values of activity
coefficients have also been obtained by the UNIFAC group
contribution method.
Abstract: The combustion of liquid fuel in the porous burner
(PB) was experimented to investigate evaporation mechanism and
combustion behavior. The diesel oil was used as fuel and the pebbles
carefully chosen in the same size like the solid sphere homogeneously
was adopted as the porous media. Two structures of the liquid porous
burner, i.e. the PB without and with installation of porous emitter
(PE), were performed. PE was installed by lower than PB with
distance of 20 cm. The pebbles having porosity (φ) of 0.45 and 0.52
were, respectively, used in PB and PE. The fuel was supplied dropwise
from the top through the PB and the combustion was occurred between
PB and PE. Axial profiles of temperature along the burner length were
measured to clarify the evaporation and combustion phenomena. The
pollutant emission characteristics were monitored at the burner exit.
From the experiment, it was found that the temperature profiles of both
structures decreased with the three ways swirling air flows (QA)
increasing. On the other hand, the temperature profiles increased with
fuel heat input (QF). Obviously, the profile of the porous burner
installed with PE was higher than that of the porous burner without
PE
Abstract: Water recycling represents an important challenge for many countries, in particular in countries where this natural resource is rare. On the other hand, in many operations, water is used as a cooling medium, as a high proportion of water consumed in industry is used for cooling purposes. Generally this water is rejected directly to the nature. This reject will cause serious environment damages as well as an important waste of this precious element.. On way to solve these problems is to reuse and recycle this warm water, through the use of natural cooling medium, such as air in a heat exchanger unit, known as a cooling tower. A poor performance, design or reliability of cooling towers will result in lower flow rate of cooling water an increase in the evaporation of water, an hence losses of water and energy. This paper which presents an experimental investigate of thermal and hydraulic performances of a mechanical cooling tower, enables to show that the water evaporation rate, Mev, increases with an increase in the air and water flow rates, as well as inlet water temperature and for fixed air flow rates, the pressure drop (ΔPw/Z) increases with increasing , L, due to the hydrodynamic behavior of the air/water flow.
Abstract: Magnesium alloys have gained increased attention in recent years in automotive, electronics, and medical industry. This because of magnesium alloys have better properties than aluminum alloys and steels in respects of their low density and high strength to weight ratio. However, the main problems of magnesium alloy welding are the crack formation and the appearance of porosity during the solidification. This paper proposes a unique technique to weld two thin sheets of AZ31B magnesium alloy using a paste containing Ag nanoparticles. The paste containing Ag nanoparticles of 5 nm in average diameter and an organic solvent was used to coat the surface of AZ31B thin sheet. The coated sheet was heated at 100 °C for 60 s to evaporate the solvent. The dried sheet was set as a lower AZ31B sheet on the jig, and then lap fillet welding was carried out by using a pulsed Nd:YAG laser in a closed box filled with argon gas. The characteristics of the microstructure and the corrosion behavior of the joints were analyzed by opticalmicroscopy (OM), energy dispersive spectrometry (EDS), electron probe micro-analyzer (EPMA), scanning electron microscopy (SEM), and immersion corrosion test. The experimental results show that the wrought AZ31B magnesium alloy can be joined successfully using Ag nanoparticles. Ag nanoparticles insert promote grain refinement, narrower the HAZ width and wider bond width compared to weld without and insert. Corrosion rate of welded AZ31B with Ag nanoparticles reduced up to 44 % compared to base metal. The improvement of corrosion resistance of welded AZ31B with Ag nanoparticles due to finer grains and large grain boundaries area which consist of high Al content. β-phase Mg17Al12 could serve as effective barrier and suppressed further propagation of corrosion. Furthermore, Ag distribution in fusion zone provide much more finer grains and may stabilize the magnesium solid solution making it less soluble or less anodic in aqueous
Abstract: In the present work an investigation of the effects of
the air frontal velocity, relative humidity and dry air temperature on
the heat transfer characteristics of plain finned tube evaporator has
been conducted. Using an appropriate correlation for the air side heat
transfer coefficient the temperature distribution along the fin surface
was calculated using a dimensionless temperature distribution. For a
constant relative humidity and bulb temperature, it is found that the
temperature distribution decreases with increasing air frontal
velocity. Apparently, it is attributed to the condensate water film
flowing over the fin surface. When dry air temperature and face
velocity are being kept constant, the temperature distribution
decreases with the increase of inlet relative humidity. An increase in
the inlet relative humidity is accompanied by a higher amount of
moisture on the fin surface. This results in a higher amount of latent
heat transfer which involves higher fin surface temperature. For the
influence of dry air temperature, the results here show an increase in
the dimensionless temperature parameter with a decrease in bulb
temperature. Increasing bulb temperature leads to higher amount of
sensible and latent heat transfer when other conditions remain
constant.
Abstract: Prediction of benzene transport in soil and volatilization from soil to the atmosphere is important for the preservation of human health and management of contaminated soils. The adequacy of a simple numerical model, assuming two-phase diffusion and equilibrium of liquid/solid adsorption, was investigated by experimental data of benzene concentration in a flux chamber (with headspace) where Andosol and sand were filled. Adsorption experiment for liquid phase was performed to determine an adsorption coefficient. Furthermore, adequacy of vapor phase adsorption was also studied through two runs of experiment using sand with different water content. The results show that the model adequately predicted benzene transport and volatilization from Andosol and sand with water content of 14.0%. In addition, the experiment additionally revealed that vapor phase adsorption should be considered in diffusion model for sand with very low water content.
Abstract: In the present study, a steady-state simulation model
has been developed to evaluate the system performance of a
transcritical carbon dioxide heat pump system for simultaneous water
cooling and heating. Both the evaporator (including both two-phase
and superheated zone) and gas cooler models consider the highly
variable heat transfer characteristics of CO2 and pressure drop. The
numerical simulation model of transcritical CO2 heat pump has been
validated by test data obtained from experiments on the heat pump
prototype. Comparison between the test results and the model
prediction for system COP variation with compressor discharge
pressure shows a modest agreement with a maximum deviation of
15% and the trends are fairly similar. Comparison for other operating
parameters also shows fairly similar deviation between the test
results and the model prediction. Finally, the simulation results are
presented to study the effects of operating parameters such as,
temperature of heat exchanger fluid at the inlet, discharge pressure,
compressor speed on system performance of CO2 heat pump, suitable
in a dairy plant where simultaneous cooling at 4oC and heating at
73oC are required. Results show that good heat transfer properties of
CO2 for both two-phase and supercritical region and efficient
compression process contribute a lot for high system COPs.