Abstract: Carbon nanotubes (CNTs) possess unique structural,
mechanical, thermal and electronic properties, and have been
proposed to be used for applications in many fields. However, to
reach the full potential of the CNTs, many problems still need to be
solved, including the development of an easy and effective
purification procedure, since synthesized CNTs contain impurities,
such as amorphous carbon, carbon nanoparticles and metal particles.
Different purification methods yield different CNT characteristics
and may be suitable for the production of different types of CNTs. In
this study, the effect of different purification chemicals on carbon
nanotube quality was investigated. CNTs were firstly synthesized by
chemical vapor deposition (CVD) of acetylene (C2H2) on a
magnesium oxide (MgO) powder impregnated with an iron nitrate
(Fe(NO3)3·9H2O) solution. The synthesis parameters were selected
as: the synthesis temperature of 800°C, the iron content in the
precursor of 5% and the synthesis time of 30 min. The liquid phase
oxidation method was applied for the purification of the synthesized
CNT materials. Three different acid chemicals (HNO3, H2SO4, and
HCl) were used in the removal of the metal catalysts from the
synthesized CNT material to investigate the possible effects of each
acid solution to the purification step. Purification experiments were
carried out at two different temperatures (75 and 120 °C), two
different acid concentrations (3 and 6 M) and for three different time
intervals (6, 8 and 15 h). A 30% H2O2 : 3M HCl (1:1 v%) solution
was also used in the purification step to remove both the metal
catalysts and the amorphous carbon. The purifications using this
solution were performed at the temperature of 75°C for 8 hours.
Purification efficiencies at different conditions were evaluated by
thermogravimetric analysis. Thermal and electrical properties of
CNTs were also determined. It was found that the obtained electrical
conductivity values for the carbon nanotubes were typical for organic
semiconductor materials and thermal stabilities were changed
depending on the purification chemicals.
Abstract: The aim of this study was to synthesize the single
walled carbon nanotubes (SWCNTs) and determine their hydrogen
storage capacities. SWCNTs were firstly synthesized by chemical
vapor deposition (CVD) of acetylene (C2H2) on a magnesium oxide
(MgO) powder impregnated with an iron nitrate (Fe(NO3)3·9H2O)
solution. The synthesis parameters were selected as: the synthesis
temperature of 800°C, the iron content in the precursor of 5% and the
synthesis time of 30 min. Purification process of SWCNTs was
fulfilled by microwave digestion at three different temperatures (120,
150 and 200 °C), three different acid concentrations (0.5, 1 and 1.5
M) and for three different time intervals (15, 30 and 60 min). Nitric
acid (HNO3) was used in the removal of the metal catalysts. The
hydrogen storage capacities of the purified materials were measured
using volumetric method at the liquid nitrogen temperature and gas
pressure up to 100 bar. The effects of the purification conditions such
as temperature, time and acid concentration on hydrogen adsorption
were investigated.