Abstract: This quantitative research is aimed to identify the level of leadership quality and emotional intelligence for members of Students' Representatives Council (SRC) of Malaysian Public Universities (MPU). The variables include the leadership quality and emotional quotient (EQ). 238 SRC members in MPU were selected as subjects of the study. Data were collected using two instruments i.e. Malaysian Emotional Quotient Inventory (MEQI) and Ayu-Noriah Leadership Audit Trail Inventory (Ayu-Noriah, LATI). Data were analyzed using descriptive (mean and percentage). Research findings showed that the subjects scored highly in four out of five EQ domains (Self-Regulations, Self-Motivation, Empathy and Social Skills). However, the subjects scored medium to low in Self-Awareness. Analysis on the sub domains (a total of 28 sub domains) showed that the subjects scored high in 17 sub domains for EQ, whilst another 11 were at medium level. The overall analysis indicates that the subjects have high level of EQ. Findings on their leadership qualities showed that they obtained high scores in all seven factors that were measured i.e. Strategy and Leadership Model, Recruit, Review Performance and Honor, Deploy Strategically, Developing, Engage and Retain and Built HR Capabilities/Line Ownership. The overall score for leadership qualities was found to be high.
Abstract: This study focuses on the effect of pin taper tool ratio on friction stir welding of magnesium alloy AZ31. Two pieces of AZ31 alloy with thickness of 6 mm were friction stir welded by using the conventional milling machine. The shoulder diameter used in this experiment is fixed at 18 mm. The taper pin ratio used are varied at 6:6, 6:5, 6:4, 6:3, 6:2 and 6:1. The rotational speeds that were used in this study were 500 rpm, 1000 rpm and 1500 rpm, respectively. The welding speeds used are 150 mm/min, 200 mm/min and 250 mm/min. Microstructure observation of welded area was studied by using optical microscope. Equiaxed grains were observed at the TMAZ and stir zone indicating fully plastic deformation. Tool pin diameter ratio 6/1 causes low heat input to the material because of small contact surface between tool surface and stirred materials compared to other tool pin diameter ratio. The grain size of stir zone increased with increasing of ratio of rotational speed to transverse speed due to higher heat input. It is observed that worm hole is produced when excessive heat input is applied. To evaluate the mechanical properties of this specimen, tensile test was used in this study. Welded specimens using taper pin ratio 6:1 shows higher tensile strength compared to other taper pin ratio up to 204 MPa. Moreover, specimens using taper pin ratio 6:1 showed better tensile strength with 500 rpm of rotational speed and 150mm/min welding speed.
Abstract: The changes of the optical and structural properties of
Bismuth-Boro-Tellurite glasses pre and post gamma irradiation were
studied. Six glass samples, with different composition [(TeO2)0.7
(B2O3)0.3]1-x (Bi2O3)x prepared by melt quenching method were
irradiated with 25kGy gamma radiation at room temperature. The
Fourier Transform Infrared Spectroscopy (FTIR) was used to explore
the structural bonding in the prepared glass samples due to exposure,
while UV-VIS Spectrophotometer was used to evaluate the changes
in the optical properties before and after irradiation. Gamma
irradiation causes profound changes in the peak intensity as shown by
FTIR spectra which is due to the breaking of the network bonding.
Before gamma irradiation, the optical band gap, Eg value decreased
from 2.44 eV to 2.15 eV with the addition of Bismuth content. The
value kept decreasing (from 2.18 eV to 2.00 eV) following exposure
to gamma radiation due to the increase of non-bridging oxygen
(NBO) and the increase of defect in the glass. In conclusion, the glass
with high content of Bi2O3 (0.30Bi) give smallest Eg and show less
changes in FTIR spectra after gamma irradiation which indicate that
this glass is more resistant to gamma radiation compared to other
glasses.
Abstract: Powder of La0.6Sr0.4CoO3-α (LSCO) was synthesized
by a combined citrate-EDTA method. The as-synthesized LSCO
powder was calcined, respectively at temperatures of 800, 900 and
1000 °C with different heating/cooling rates which are 2, 5, 10 and
15 °C min-1. The effects of heat treatments on the phase formation of
perovskite phase of LSCO were investigated by powder X-ray
diffraction (XRD). The XRD patterns revealed that the rate of
5 °C min-1 is the optimum heating/cooling rate to obtain a single
perovskite phase of LSCO with calcination temperature of 800 °C.
This result was confirmed by a thermogravimetric analysis (TGA) as
it showed a complete decomposition of intermediate compounds to
form oxide material was also observed at 800 °C.
Abstract: Magnesium alloys have gained increased attention in recent years in automotive, electronics, and medical industry. This because of magnesium alloys have better properties than aluminum alloys and steels in respects of their low density and high strength to weight ratio. However, the main problems of magnesium alloy welding are the crack formation and the appearance of porosity during the solidification. This paper proposes a unique technique to weld two thin sheets of AZ31B magnesium alloy using a paste containing Ag nanoparticles. The paste containing Ag nanoparticles of 5 nm in average diameter and an organic solvent was used to coat the surface of AZ31B thin sheet. The coated sheet was heated at 100 °C for 60 s to evaporate the solvent. The dried sheet was set as a lower AZ31B sheet on the jig, and then lap fillet welding was carried out by using a pulsed Nd:YAG laser in a closed box filled with argon gas. The characteristics of the microstructure and the corrosion behavior of the joints were analyzed by opticalmicroscopy (OM), energy dispersive spectrometry (EDS), electron probe micro-analyzer (EPMA), scanning electron microscopy (SEM), and immersion corrosion test. The experimental results show that the wrought AZ31B magnesium alloy can be joined successfully using Ag nanoparticles. Ag nanoparticles insert promote grain refinement, narrower the HAZ width and wider bond width compared to weld without and insert. Corrosion rate of welded AZ31B with Ag nanoparticles reduced up to 44 % compared to base metal. The improvement of corrosion resistance of welded AZ31B with Ag nanoparticles due to finer grains and large grain boundaries area which consist of high Al content. β-phase Mg17Al12 could serve as effective barrier and suppressed further propagation of corrosion. Furthermore, Ag distribution in fusion zone provide much more finer grains and may stabilize the magnesium solid solution making it less soluble or less anodic in aqueous