Abstract: This paper is aimed to the use of different types of
industrial wastes in concrete production. From examined waste
(crushed concrete waste) our tested concrete samples with dimension
150 mm were prepared. In these samples, fractions 4/8 mm and 8/16
mm by recycled concrete aggregate with a range of variation from 0
to 100% were replaced. Experiment samples were tested for
compressive strength after 2, 7, 14 and 28 days of hardening.
From obtained results it is evident that all samples prepared with
washed recycled concrete aggregates met the requirement of standard
for compressive strength of 20 MPa already after 14 days of
hardening. Sample prepared with recycled concrete aggregates (4/8
mm: 100% and 8/16 mm: 60%) reached 101% of compressive
strength value (34.7 MPa) after 28 days of hardening in comparison
with the reference sample (34.4 MPa). The lowest strength after 28
days of hardening (27.42 MPa) was obtained for sample consisting of
recycled concrete in proportion of 40% for 4/8 fraction and 100% for
8/16 fraction of recycled concrete.
Abstract: Concrete is found to undergo degradation when
subjected to elevated temperatures and loose substantial amount of its
strength. The loss of strength in concrete is mainly attributed to
decomposition of C-S-H and release of physically and chemically
bound water, which begins when the exposure temperature exceeds
100°C. When such a concrete comes in contact with moisture, the
cement paste is found rehydrate and considerable amount of strength
lost is found to recover. This paper presents results of an
experimental program carried out to investigate the effect of recuring
on strength gain of OPC concrete specimens subjected to elevated
temperatures from 200°C to 800°C, which were subjected to
retention time of two hours and four hours at the designated
temperature. Strength recoveries for concrete subjected to 7
designated elevated temperatures are compared. It is found that the
efficacy of recuring as a measure of strength recovery reduces with
increase in exposure temperature.
Abstract: In this research the effects of adding silica and
alumina nanoparticles on flow ability and compressive strength of
cementitious composites based on Portland cement were investigated.
In the first stage, the rheological behavior of different samples
containing nanosilica, nanoalumina and polypropylene, polyvinyl
alcohol and polyethylene fibers were evaluated. With increasing of
nanoparticles in fresh samples, the slump flow diameter reduced.
Fibers reduced the flow ability of the samples and viscosity
increased. With increasing of the micro silica particles to cement
ratio from 2/1 to 2/2, the slump flow diameter increased. By adding
silica and alumina nanoparticles up to 3% and 2% respectively, the
compressive strength increased and after decreased. Samples
containing silica nanoparticles and fibers had the highest compressive
strength.
Abstract: The main objective of this paper is study the influence
of carbon nano-tubes fibers and nano silica fibers on the
characteristic compressive strength and flexural strength on concrete
and cement mortar. Twelve tested specimens were tested with square
section its dimensions (4040 160) mm, divided into four groups.
The first and second group studied the effect of carbon nano-tubes
(CNTs) fibers with different percentage equal to 0.0, 0.11%, 0.22%,
and 0.33% by weight of cement and effect of nano-silica (nS) fibers
with different percentages equal to 0.0, 1.0%, 2.0%, and 3.0% by
weight of cement on the cement mortar. The third and fourth groups
studied the effect of CNTs fiber with different percentage equal to
0.0%, 0.11%, and 0.22% by weight of cement, and effect of nS fibers
with different percentages were equal to 0.0%, 1.0%, and 2.0% by
weight of cement on the concrete. The compressive strength and
flexural strength at 7, 28, and 90 days is determined. From analysis of
tested results concluded that the nano-fibers is more effective when
used with cement mortar more than used with concrete because of
increasing the surface area, decreasing the pore and the collection of
nano-fibers. And also by adding nano-fibers the improvement of
flexural strength of concrete and cement mortar is more than
improvement of compressive strength.
Abstract: Equal channel angular pressing (ECAP) of
commercial Al-Mg-Si alloy was conducted using two strain rates.
The ECAP processing was conducted at room temperature and at
250°C. Route A was adopted up to a total number of four passes in
the present work. Structural evolution of the aluminum alloy discs
was investigated before and after ECAP processing using optical
microscopy (OM). Following ECAP, simple compression tests and
Vicker’s hardness were performed. OM micrographs showed that, the
average grain size of the as-received Al-Mg-Si disc tends to be larger
than the size of the ECAP processed discs. Moreover, significant
difference in the grain morphologies of the as-received and processed
discs was observed. Intensity of deformation was observed via the
alignment of the Al-Mg-Si consolidated particles (grains) in the
direction of shear, which increased with increasing the number of
passes via ECAP. Increasing the number of passes up to 4 resulted in
increasing the grains aspect ratio up to ~5. It was found that the
pressing temperature has a significant influence on the
microstructure, Hv-values, and compressive strength of the processed
discs. Hardness measurements demonstrated that 1-pass resulted in
increase of Hv-value by 42% compared to that of the as-received
alloy. 4-passes of ECAP processing resulted in additional increase in
the Hv-value. A similar trend was observed for the yield and
compressive strength. Experimental data of the Hv-values
demonstrated that there is a lack of any significant dependence on the
processing strain rate.
Abstract: This study investigated the improvement in concrete properties with addition of cellulose, steel, carbon and PET fibers. Each fiber was added at four percentages to the fresh concrete, which was moist-cured for 28-days and then tested for compressive, flexural and tensile strengths. Changes in strength and increases in cost were analyzed. Results showed that addition of cellulose caused a decrease between 9.8% and 16.4% in compressive strength. This range may be acceptable as cellulose fibers can significantly increase the concrete resistance to fire, and freezing and thawing cycles. Addition of steel fibers to concreteincreased the compressive strength by up to 20%. Increases 121.5% and 80.7% were reported in tensile and flexural strengths respectively. Carbon fibers increased flexural and tensile strengths by up to 11% and 45%, respectively. Concrete strength properties decreased after the addition of PET fibers. Results showed that improvement in strength after addition of steel and carbon fibers may justify the extra cost of fibers.
Abstract: The outstanding mechanical properties of Carbon
nanotubes (CNTs) have generated great interest for their potential as
reinforcements in high performance cementitious composites. The
main challenge in research is the proper dispersion of carbon
nanotubes in the cement matrix. The present work discusses the role
of dispersion of multiwalled carbon nanotubes (MWCNTs) on the
compressive strength characteristics of hydrated Portland IS 1489
cement paste. Cement-MWCNT composites with different mixing
techniques were prepared by adding 0.2% (by weight) of MWCNTs
to Portland IS 1489 cement. Rectangle specimens of size
approximately 40mm × 40mm ×160mm were prepared and curing of
samples was done for 7, 14, 28 and 35days. An appreciable increase
in compressive strength with both techniques; mixture of MWCNTs
with cement in powder form and mixture of MWCNTs with cement
in hydrated form 7 to 28 days of curing time for all the samples was
observed.
Abstract: Many synthetic additives have been using for improve cement mortar and concrete characteristics, but natural additive is a friendly environment option. The quantity of (2% and 4%) seashell powder has been replaced in cement mortar, and compared with plain cement mortar in early age of 7 days. The strain gauges have been installed on beams and cube, for monitoring fluctuation of flexural and compressive strength. Main objective of this paper is to study effect of linear static force on flexural and compressive strength of modified cement mortar. The results have been indicated that the replacement of appropriate proportion of seashell powder enhances cement mortar mechanical properties. The replacement of 2% seashell causes improvement of deflection, time to failure and maximum load to failure on concrete beam and cube, the same occurs for compressive modulus elasticity. Increase replacement of seashell to 4% reduces all flexural strength, compressive strength and strain of cement mortar.
Abstract: Compatibility between sulfonated acetone- formalehyde superplasticizer (SAF) and copolymer-based grinding aids (GA) were studied by fluidity, Zeta potential, setting time of cement pasts, initial slump and slump flow of concrete and compressive strength of concrete. ESEM, MIP, and XRD were used to investigate the changing of microstructure of interior concrete. The results indicated that GA could noticeably enhance the dispersion ability of SAF. It was found that better fluidity and slump-keeping ability of cement paste were obtained in the case of GA. In addition, GA together with SAF had a certain retardation effect on hydration of cement paste. With increasing of the GA dosage, the dispersion ability and retardation effect of admixture increased. The compressive strength of the sample made with SAF and GA after 28 days was higher than that of the control sample made only with SAF. The initial slump and slump flow of concrete increased by 10.0% and 22.9%, respectively, while 0.09 wt.% GA was used. XRD examination indicated that new products were not found in the case of GA. In addition, more dense arrangement of hydrates and lower porosity of the specimen were observed by ESEM and MIP, which contributed to higher compressive strength.
Abstract: In this paper, the effect of addition the dune sand powder (DSP) on development of compressive strength and hydration of cement pastes was investigated as a function of water/binder ratio, was varied, on the one hand, the percentage of DSP and on the other, the fineness of DSP. In order to understand better the pozzolanic effect of dune sand powder in cement pastes, we followed the mixtures hydration (50% Pure Lime + 50% DSP) by X-ray diffraction. These mixtures the pastes present a hydraulic setting which is due to the formation of a C-S-H phase (calcium silicate hydrate). The latter is semi-crystallized. This study is a simplified approach to that of the mixtures (80% ordinary Portland cement + 20% DSP), in which the main reaction is the fixing of the lime coming from the cement hydration in the presence of DSP, to form calcium silicate hydrate semi-crystallized of second generation. The results proved that up to (20% DSP) as Portland cement replacement could be used with a fineness of 4000 cm²/g without affecting adversely the compressive strength. After 28 days, the compressive strength at 5, 10 and 15% DSP is superior to Portland cement, with an optimum effect for a percentage of the order of 5% to 10% irrespective of the w/b ratio and fineness of DSP.
Abstract: This paper studies the application of a variety of
sawdust materials in the production of lightweight insulating bricks.
First, the mineralogical and chemical composition of clays was determined. Next, ceramic bricks were fabricated with different
quantities of materials (3–6 and 9 wt. % for sawdust, 65 wt. % for grey clay, 24–27 and 30 wt. % for yellow clay and 2 wt% of tuff).
These bricks were fired at 800 and 950 °C. The effect of adding this sawdust on the technological behaviour of the brick was assessed by
drying and firing shrinkage, water absorption, porosity, bulk density
and compressive strength. The results have shown that the optimum
sintering temperature is 950 °C. Below this temperature, at 950 °C,
increased open porosity was observed, which decreased the compressive strength of the bricks. Based on the results obtained, the
optimum amounts of waste were 9 wt. % sawdust of eucalyptus, 24 wt. % shaping moisture and 1.6 particle size diameter. These percentages produced bricks whose mechanical properties were
suitable for use as secondary raw materials in ceramic brick
production.
Abstract: In this study two series of self compacting concrete
mixtures were prepared with 100% coarse recycled concrete
aggregates and different percentages of 0%, 20%, 40%, 60%, 80%
and 100% fine recycled concrete aggregates. In series I and II the
water to binder ratios were 0.50 and 0.45, respectively. The cement
content was kept 350
3 m
kg for those mixtures that don't have any
Nano-Silica. To improve the compressive strength of samples, Nano-
Silica replaced with 10% of cement weight in concrete mixtures. By
doing the tests, the results showed that, adding Nano-silica to the
samples with less percentage of fine recycled concrete aggregates,
lead to more increase on the compressive strength.
Abstract: This paper reports the results of an experimental work
conducted to investigate the effect of curing conditions on the
compressive strength of self-compacting geopolymer concrete
prepared by using fly ash as base material and combination of sodium
hydroxide and sodium silicate as alkaline activator. The experiments
were conducted by varying the curing time and curing temperature in
the range of 24-96 hours and 60-90°C respectively. The essential
workability properties of freshly prepared Self-compacting
Geopolymer concrete such as filling ability, passing ability and
segregation resistance were evaluated by using Slump flow,
V-funnel, L-box and J-ring test methods. The fundamental
requirements of high flowability and resistance to segregation as
specified by guidelines on Self-compacting Concrete by EFNARC
were satisfied. Test results indicate that longer curing time and curing
the concrete specimens at higher temperatures result in higher
compressive strength. There was increase in compressive strength
with the increase in curing time; however increase in compressive
strength after 48 hours was not significant. Concrete specimens cured
at 70°C produced the highest compressive strength as compared to
specimens cured at 60°C, 80°C and 90°C.
Abstract: In spite of the advent of new materials, clay bricks
remain, arguably, the most popular construction materials today.
Nevertheless the low cost and versatility of clay bricks cannot always
be associated with high environmental and sustainable values,
especially in terms of raw material sources and manufacturing
processes. At the same time, the worldwide agricultural footprint is
fast growing, with vast agricultural land cultivation and active
expansion of the agro-based industry. The resulting large quantities of
agricultural wastes, unfortunately, are not always well managed or
utilised. These wastes can be recycled, such as by retrieving fibres
from disposed leaves and fruit bunches, and then incorporated in
brick-making. This way the clay bricks are made a 'greener' building
material and the discarded natural wastes can be reutilised, avoiding
otherwise wasteful landfill and harmful open incineration. This study
examined the physical and mechanical properties of clay bricks made
by adding two natural fibres to a clay-water mixture, with baked and
non-baked conditions. The fibres were sourced from pineapple leaves
(PF) and oil palm fruit bunch (OF), and added within the range of
0.25-0.75 %. Cement was added as a binder to the mixture at 5-15 %.
Although the two fibres had different effects on the bricks produced,
cement appeared to dominate the compressive strength. The
non-baked bricks disintegrated when submerged in water, while the
baked ones displayed cement-dependent characteristics in
water-absorption and density changes. Interestingly, further increase
in fibre content did not cause significant density decrease in both the
baked and non-baked bricks.
Abstract: Due to growing environmental concerns of the cement
industry, alternative cement technologies have become an area of
increasing interest. It is now believed that new binders are
indispensable for enhanced environmental and durability
performance. Self-compacting Geopolymer concrete is an innovative
method and improved way of concreting operation that does not
require vibration for placing it and is produced by complete
elimination of ordinary Portland cement.
This paper documents the assessment of the compressive strength
and workability characteristics of low-calcium fly ash based selfcompacting
geopolymer concrete. The essential workability
properties of the freshly prepared Self-compacting Geopolymer
concrete such as filling ability, passing ability and segregation
resistance were evaluated by using Slump flow, V-funnel, L-box and
J-ring test methods. The fundamental requirements of high
flowability and segregation resistance as specified by guidelines on
Self Compacting Concrete by EFNARC were satisfied. In addition,
compressive strength was determined and the test results are included
here. This paper also reports the effect of extra water, curing time and
curing temperature on the compressive strength of self-compacting
geopolymer concrete. The test results show that extra water in the
concrete mix plays a significant role. Also, longer curing time and
curing the concrete specimens at higher temperatures will result in
higher compressive strength.
Abstract: Cement stabilization has been widely used for
improving the strength and stiffness of soft clayey soils. Cement
treated soil specimens used to investigate the stress-strain behaviour in
the laboratory study are usually cured for 7 days. This paper examines
the effects of curing time on the strength and stress strain behaviour of
cement treated marine clay under triaxial loading condition.
Laboratory-prepared cement treated Singapore marine clay with
different mix proportion S-C-W (soil solid-cement solid-water) and
curing time (7 days to 180 days) was investigated through conducting
unconfined compressive strength test and triaxial test. The results
show that the curing time has a significant effect on the unconfined
compressive strength u q , isotropic compression behaviour and stress
strain behaviour. Although the primary yield loci of the cement treated
soil specimens with the same mix proportion expand with curing time,
they are very narrowly banded and have nearly the same shape after
being normalized by isotropic compression primary stress '
py p . The
isotropic compression primary yield stress '
py p was shown to be
linearly related to unconfined compressive strength u q for specimens
with different curing time and mix proportion. The effect of curing
time on the hardening behaviour will diminish with consolidation
stress higher than isotropic compression primary yield stress but its
damping rate is dependent on the cement content.