Abstract: TiO2 particles have been added in molten aluminium to result in aluminium based cast Al/Al3Ti-Al2O3 composite, which has been added then to molten magnesium to synthesize magnesium based cast Mg-Al/Al3Ti-Al2O3 composite. The nominal compositions in terms of Mg, Al, and TiO2 contents in the magnesium based composites are Mg-9Al-0.6TiO2, Mg-9Al-0.8TiO2, Mg-9Al-1.0TiO2 and Mg-9Al-1.2TiO2 designated respectively as MA6T, MA8T, MA10T and MA12T. The microstructure of the cast magnesium based composite shows grayish rods of intermetallics Al3Ti, inherited from aluminium based composite but these rods, on hot forging, breaks into smaller lengths decreasing the average aspect ratio (length to diameter) from 7.5 to 3.0. There are also cavities in between the broken segments of rods. β-phase in cast microstructure, Mg17Al12, dissolves during heating prior to forging and re-precipitates as relatively finer particles on cooling. The amount of β-phase also decreases on forging as segregation is removed. In both the cast and forged composite, the Brinell hardness increases rapidly with increasing addition of TiO2 but the hardness is higher in forged composites by about 80 BHN. With addition of higher level of TiO2 in magnesium based cast composite, yield strength decreases progressively but there is marginal increase in yield strength over that of the cast Mg-9 wt. pct. Al, designated as MA alloy. But the ultimate tensile strength (UTS) in the cast composites decreases with the increasing particle content indicating possibly an early initiation of crack in the brittle inter-dendritic region and their easy propagation through the interfaces of the particles. In forged composites, there is a significant improvement in both yield strength and UTS with increasing TiO2 addition and also, over those observed in their cast counterpart, but at higher addition it decreases. It may also be noted that as in forged MA alloy, incomplete recovery of forging strain increases the strength of the matrix in the composites and the ductility decreases both in the forged alloy and the composites. Initiation fracture toughness, JIC, decreases drastically in cast composites compared to that in MA alloy due to the presence of intermetallic Al3Ti and Al2O3 particles in the composite. There is drastic reduction of JIC on forging both in the alloy and the composites, possibly due to incomplete recovery of forging strain in both as well as breaking of Al3Ti rods and the voids between the broken segments of Al3Ti rods in composites. The ratio of tearing modulus to elastic modulus in cast composites show higher ratio, which increases with the increasing TiO2 addition. The ratio decreases comparatively more on forging of cast MA alloy than those in forged composites.
Abstract: Partially lubricated sliding wear behaviour of a zinc-based alloy reinforced with 10wt% SiC particles has been studied as a function of applied load and solid lubricant particle size and has been compared with that of matrix alloy and conventionally used grey cast iron. The wear tests were conducted at the sliding velocities of 2.1m/sec in various partial lubricated conditions using pin on disc machine as per ASTM G-99-05. Base oil (SAE 20W-40) or mixture of the base oil with 5wt% graphite of particle sizes (7-10 µm) and (100 µm) were used for creating lubricated conditions. The matrix alloy revealed primary dendrites of a and eutectoid a + h and Î phases in the Inter dendritic regions. Similar microstructure has been depicted by the composite with an additional presence of the dispersoid SiC particles. In the case of cast iron, flakes of graphite were observed in the matrix; the latter comprised of (majority of) pearlite and (limited quantity of) ferrite. Results show a large improvement in wear resistance of the zinc-based alloy after reinforcement with SiC particles. The cast iron shows intermediate response between the matrix alloy and composite. The solid lubrication improved the wear resistance and friction behaviour of both the reinforced and base alloy. Moreover, minimum wear rate is obtained in oil+ 5wt % graphite (7-10 µm) lubricated environment for the matrix alloy and composite while for cast iron addition of solid lubricant increases the wear rate and minimum wear rate is obtained in case of oil lubricated environment. The cast iron experienced higher frictional heating than the matrix alloy and composite in all the cases especially at higher load condition. As far as friction coefficient is concerned, a mixed trend of behaviour was noted. The wear rate and frictional heating increased with load while friction coefficient was affected in an opposite manner. Test duration influenced the frictional heating and friction coefficient of the samples in a mixed manner.
Abstract: Biodegradable solid waste disposal and management has been a major problem in Nigeria and indiscriminate dumping of this waste either into watercourses or drains has led to environmental hazards affecting public health. The study investigated the nutrients level of pit composting and vermicomposting. Wooden bins 60 cm × 30 cm × 30 cm3 in size were constructed and bedding materials (sawdust, egg shell, paper and grasses) and red worms (Eisenia fetida) introduced to facilitate the free movement and protection of the worms against harsh weather. A pit of 100 cm × 100 cm × 100 cm3 was dug and worms were introduced into the pit, which was turned every two weeks. Food waste was fed to the red worms in the bin and pit, respectively. The composts were harvested after 100 days and analysed. The analyses gave: nitrogen has average value 0.87 % and 1.29 %; phosphorus 0.66 % and 1.78 %; potassium 4.35 % and 6.27 % for the pit and vermicomposting, respectively. Higher nutrient status of vermicomposting over pit composting may be attributed to the secretions in the intestinal tracts of worms which are more readily available for plant growth. However, iron and aluminium were more in the pit compost than the vermin compost and this may be attributed to the iron and aluminium already present in the soil before the composting took place. Other nutrients in ppm concentrations were aluminium 4,999.50 and 3,989.33; iron 2,131.83 and 633.40 for the pit and vermicomposting, respectively. These nutrients are only needed by plants in small quantities. Hence, vermicomposting has the higher concentration of essential nutrients necessary for healthy plant growth.
Abstract: In general, it is desirable to finish the weld quickly,
before a large volume of surrounding metal heats up and expands.
The welding process used, type, welding current and speed of travel,
thus, affect the degree of shrinkage and distortion of a weldment. The
use of mechanized welding equipment reduces welding time, metal
affected zone and consequently distortion. This article helps to define
what weld distortion is and then provide a practical understanding of
the causes of distortion, effects of shrinkage in butt joint welded
assemblies using TI6AL4VA and Aluminium AA2024 alloy sheet.
The beam offset position to the joint interface towards titanium and
aluminium side. The factors affecting distortion during welding is
also given. Test results reveal that welding speed is the significant
parameter to decide the extent of distortion. Also welding from Al
side reduces the distortion while Ti side increases the distortion.
Abstract: A Friction stir welding tool is a critical component to
the success of the process. The tool typically consists of a rotating
round shoulder and a threaded cylindrical pin that heats the work
piece, mostly by friction, and moves the softened alloy around it to
form the joint. In this research work, an attempt has been made to
investigate the relationship between FSW variables mainly tool
profile, rotating speed, welding speed and the mechanical properties
(tensile strength, yield strength, percentage elongation, and micro
hardness) of friction stir welded aluminum alloy 5083 joints. From
the experimental details, it can be assessed that the joint produced by
using Triflute profile tool has contribute superior mechanical and
structural properties as compared to Tapered unthreaded & Threaded
tool for 1000rpm.
Abstract: In this work, repaired crack in 6061- T6 aluminum
plate with composite patches presented, firstly we determine the
displacement, strain and stress, also the first six mode shape of the
plate, secondly we took the same model adding central crack
initiation, which is located in the center of the plate, its seize vary
from 20 mm to 60 mm and we compare the first results with second.
Thirdly we repair various cracks with composite patch (carbon/
epoxy) and for (2 layers, 4 layers). Finally the comparison of stress,
strain, displacement and six first natural frequencies between un-cracked
specimen, crack propagation and composite patch repair.
Abstract: Ceramic obtained on the base of aluminum oxide has
wide application range, because it has unique properties, for example,
wear-resistance, dielectric characteristics, and exploitation ability at
high temperatures and in corrosive atmosphere. Low temperature
synthesis of α-Al2O3 is energo-economical process and it is topical
for developing technologies of corundum ceramics fabrication. In the present work possibilities of low temperature transformation
of oxyhydroxides in α-Al2O3, during the presence of small amount of
rare–earth elements compounds (also Th, Re), have been discussed.
Aluminum unstable oxyhydroxides have been obtained by hydrolysis
of aluminium isopropoxide, nitrates, sulphate, and chloride in
alkaline environment at 80-90ºC temperatures. β-Al(OH)3 has been
received from aluminum powder by ultrasonic development. Drying
of oxyhydroxide sol has been conducted with presence of various
types seeds, which amount reaches 0,1-0,2% (mas). Neodymium,
holmium, thorium, lanthanum, cerium, gadolinium, disprosium
nitrates and rhenium carbonyls have been used as seeds and they
have been added to the sol specimens in amount of 0.1-0.2% (mas)
calculated on metals. Annealing of obtained gels is carried out at 70–
1100ºC for 2 hrs. The same specimen transforms in α-Al2O3 at
1100ºC. At this temperature in case of presence of lanthanum and
gadolinium transformation takes place by 70-85%. In case of
presence of thorium stabilization of γ-and θ-phases takes place. It is
established, that thorium causes inhibition of α-phase generation at
1100ºC, and at the time when in all other doped specimens α-phase is
generated at lower temperatures (1000-1050ºC). Synthesis of various
type compounds and simultaneous consolidation has developed in the
furnace of OXY-GON. Composite materials containing oxide and
non-oxide components close to theoretical data have been obtained in
this furnace respectively. During the work the following devices have
been used: X-ray diffractometer DRON-3M (Cu-Kα, Ni filter,
2º/min), High temperature vacuum furnace OXY-GON, electronic
scanning microscopes Nikon ECLIPSE LV 150, NMM-800TRF,
planetary mill Pulverisette 7 premium line, SHIMADZU Dynamic
Ultra Micro Hardness Tester, DUH-211S, Analysette 12 Dyna sizer.
Abstract: This paper presents a fully Lagrangian coupled
Fluid-Structure Interaction (FSI) solver for simulations of
fluid-structure interactions, which is based on the Moving Particle
Semi-implicit (MPS) method to solve the governing equations
corresponding to incompressible flows as well as elastic structures.
The developed solver is verified by reproducing the high velocity
impact loads of deformable thin wedges with three different materials
such as mild steel, aluminium and tin during water entry. The present
simulation results for aluminium are compared with analytical solution
derived from the hydrodynamic Wagner model and linear Wan’s
theory. And also, the impact pressure and strain on the water entry
wedge with three different materials, such as mild steel, aluminium
and tin, are simulated and the effects of hydro-elasticity are discussed.
Abstract: Aluminium matrix composites with alumina
reinforcements give superior mechanical & physical properties. Their
applications in several fields like automobile, aerospace, defense,
sports, electronics, bio-medical and other industrial purposes are
becoming essential for the last several decades. In the present work,
fabrication of hybrid composite was done by Stir casting technique
using Al 6061 as a matrix with alumina and silicon carbide (SiC) as
reinforcement materials. The weight percentage of alumina is varied
from 2 to 4% and the silicon carbide weight percentage is maintained
constant at 2%. Hardness and wear tests are performed in the as cast
and heat treated conditions. Age hardening treatment was performed
on the specimen with solutionizing at 550°C, aging at two
temperatures (150 and 200°C) for different time durations. Hardness
distribution curves are drawn and peak hardness values are recorded.
Hardness increase was very sensitive with respect to the decrease in
aging temperature. There was an improvement in wear resistance of
the peak aged material when aged at lower temperature. Also
increase in weight percent of alumina, increases wear resistance at
lower temperature but opposite behavior was seen when aged at
higher temperature.
Abstract: The secondary alloy A226 is used for many
automotive casting produced by mould casting and high pressure die
casting. This alloy has excellent castability, good mechanical
properties and cost-effectiveness. Production of primary aluminium
alloys belong to heavy source fouling of life environs. The European
Union calls for the emission reduction and reduction in energy
consumption therefore increase production of recycled (secondary)
aluminium cast alloys. The contribution is deal with influence of
recycling on the quality of the casting made from A226 in automotive
industry. The properties of the casting made from secondary
aluminium alloys were compared with the required properties of
primary aluminium alloys. The effect of recycling on microstructure
was observed using combination different analytical techniques (light
microscopy upon black-white etching, scanning electron microscopy
- SEM upon deep etching and energy dispersive X-ray analysis -
EDX). These techniques were used for the identification of the
various structure parameters, which was used to compare secondary
alloy microstructure with primary alloy microstructure.
Abstract: This study is about the structural transformations of
aluminium examining with the Dynamic Mechanical Thermal
Analyzer (DMTA). It is a faster and simpler measuring method to
make consequence about the metal’s structural transformations. The
device measures the changing of the mechanical characteristics
depending on the heating rate, and concludes certain transformations.
This measuring method fast and shows clean-cut results comparing
the conventional ways.
Applying polymer measuring devices for metal investigations is
not widespread method. One of the adaptable ways is shown in this
study. The article compares the results of the small specimen test and
the DMTA method, considering the temperature and the forming
dependence of recrystallization temperature.
Abstract: The wear measuring and wear modelling are
fundamental issues in the industrial field, mainly correlated to the
economy and safety. Therefore, there is a need to study the wear
measurements and wear estimation. Pin-on-disc test is the most
common test which is used to study the wear behaviour. In this paper,
the pin-on-disc (AEROTECH UNIDEX 11) is used for the
investigation of the effects of normal load and hardness of material on
the wear under dry and sliding conditions. In the pin-on-disc rig, two
specimens were used; one, a pin is made of steel with a tip, positioned
perpendicular to the disc, where the disc is made of aluminium. The
pin wear and disc wear were measured by using the following
instruments: The Talysurf instrument, a digital microscope, and the
alicona instrument. The Talysurf profilometer was used to measure
the pin/disc wear scar depth, digital microscope was used to measure
the diameter and width of wear scar, and the alicona was used to
measure the pin wear and disc wear. After that, the Archard model,
American Society for Testing and Materials model (ASTM), and
neural network model were used for pin/disc wear modelling.
Simulation results were implemented by using the Matlab program.
This paper focuses on how the alicona can be used for wear
measurements and how the neural network can be used for wear
estimation.
Abstract: To achieve reliable welds with minimum distortion for
the fabrication of components in aerospace industry laser beam
welding is attempted. Laser welding can provide a significant benefit
for the welding of Titanium and Aluminium thin sheet alloys of its
precision and rapid processing capability. For laser welding, pulse
shape, energy, duration, repetition rate and peak power are the most
important parameters that influence directly the quality of welds. In
this experimental work for joining 1mm thick TI6AL4V and AA2024
alloy and JK600 Nd:YAG pulsed laser units used. The distortions at
different welding power and speed of titanium and aluminium thin
sheet alloys are investigated. Test results reveal that increase in
welding speed increases distortion in weldment
Abstract: Sandwich structure composites produced by epoxy
core and aluminium skin were developed as potential building
materials. Interface bonding between core and skin was controlled by
varying kenaf content. Five different weight percentage of kenaf
loading ranging from 10 wt% to 50 wt% were employed in the core
manufacturing in order to study the mechanical properties of the
sandwich composite. Properties of skin aluminium with epoxy were
found to be affected by drying time of the adhesive. Mechanical
behavior of manufactured sandwich composites in relation with
properties of constituent materials was studied. It was found that 30
wt% of kenaf loading contributed to increase the flexural strength and
flexural modulus up to 102 MPa and 32 GPa, respectively. Analysis
were done on the flatwise and edgewise compression test. For
flatwise test, it was found that 30 wt% of fiber loading could
withstand maximum force until 250 kN, with compressive strength
results at 96.94 MPa. However, at edgewise compression test, the
sandwich composite with same fiber loading only can withstand 31
kN of the maximum load with 62 MPa of compressive strength
results.
Abstract: Metal matrix composites (MMCs) attract considerable
attention as a result from its ability in providing a high strength, high
modulus, high toughness, high impact properties, improving wear
resistance and providing good corrosion resistance compared to
unreinforced alloy. Aluminium Silicon (Al/Si) alloy MMC has been
widely used in various industrial sectors such as in transportation,
domestic equipment, aerospace, military, construction, etc.
Aluminium silicon alloy is an MMC that had been reinforced with
aluminium nitrate (AlN) particle and become a new generation
material use in automotive and aerospace sector. The AlN is one of
the advance material that have a bright prospect in future since it has
features such as lightweight, high strength, high hardness and
stiffness quality. However, the high degree of ceramic particle
reinforcement and the irregular nature of the particles along the
matrix material that contribute to its low density is the main problem
which leads to difficulties in machining process. This paper examined
the tool wear when milling AlSi/AlN Metal Matrix Composite using
a TiB2 (Titanium diboride) coated carbide cutting tool. The volume
of the AlN reinforced particle was 10% and milling process was
carried out under dry cutting condition. The TiB2 coated carbide
insert parameters used were at the cutting speed of (230, 300 and
370m/min, feed rate of 0.8, Depth of Cut (DoC) at 0.4m). The
Sometech SV-35 video microscope system used to quantify of the
tool wear. The result shown that tool life span increasing with the
cutting speeds at (370m/min, feed rate of 0.8mm/tooth and DoC at
0.4mm) which constituted an optimum condition for longer tool life
lasted until 123.2 mins. Meanwhile, at medium cutting speed which
at 300m/m, feed rate of 0.8mm/tooth and depth of cut at 0.4mm we
found that tool life span lasted until 119.86 mins while at low cutting
speed it lasted in 119.66 mins. High cutting speed will give the best
parameter in cutting AlSi/AlN MMCs material. The result will help
manufacturers in machining process of AlSi/AlN MMCs materials.
Abstract: Dissimilar joining of Titanium and Aluminum thin
sheets has potential applications in aerospace and automobile
industry which can reduce weight and cost and improve strength,
corrosion resistance and high temperature properties. However
successful welding of Titanium/Aluminium sheets is of challenge due
to differences in physical, chemical and metallurgical properties
between the two. This paper describes research results of Laser Beam
Welding (LBW) of Ti/Al thin sheets in which many researchers have
recently performed and critically reviewed from different
perspectives. Also some of notable works in the field of laser welding
with changes in mechanical properties, crack propagation, diffusion
behavior, chemical potential, interfacial reaction and the
microstructure are reported.
Abstract: Laser beam welding is an important joining technique
for Titanium/Aluminum thin sheet alloys with their increasing
applications in aerospace, aircraft, automotive, electronics and other
industries. In this paper the research and progress in laser welding of
Ti/Al thin sheets are critically reviewed from different perspectives.
Some important aspects such as microstructure, metallurgical defects
and mechanical properties in weldments are discussed. Also the
recent progress in laser welding of Ti/Al dissimilar thin sheets to
provide a basis for further research work is reported.
Abstract: Laser beam welding for the dissimilar Titanium and
Aluminium thin sheets is an emerging area which is having wider
applications in aerospace, aircraft, automotive, electronics and in
other industries due to its high speed, non-contact, precision with low
heat effects, least welding distortion, low labor costs and convenient
operation. Laser beam welding of dissimilar metal combinations are
increasingly demanded due to high energy densities with small fusion
and heat affected zones. Furthermore, no filler or electrode material is
required and contamination of weld is also very small. The present
study is to reviews the influence of different parameters like laser
power, welding speed, power density, beam diameter, focusing
distance and type of shielding gas on the mechanical properties of
dissimilar metal combinations like SS/Al, Cu/Al and Ti/Al focusing
on aluminum to other materials. Research findings reveal that Ti/Al
combination gives better metallurgical and mechanical properties
than other combinations such as SS/Al and Cu/Al.
Abstract: Aluminium and its alloys have excellent corrosion
resistant properties, ease of fabrication and high specific strength to
weight ratio. In this investigation an attempt has been made to study
the effect of different post weld heat treatment methods on the
mechanical and metallurgical properties of TIG welded joints of the
commercial aluminium alloy. Three different methods of post weld
heat treatments are solution heat treatment, artificial ageing and
combination of solution heat treatment and artificial aging are given
to TIG welded aluminium joints. Mechanical and metallurgical
properties of As welded joints of the aluminium alloys and post weld
heat treated joints of the aluminium alloys were examined.
Abstract: Metallic foams have good potential for lightweight
structures for impact and blast mitigation. Therefore it is important to
find out the optimized foam structure (i.e. cell size, shape, relative
density, and distribution) to maximise energy absorption. In this
paper, quasistatic compression and microstructural characterization
of closed-cell aluminium foams of different pore size and cell
distributions have been carried out. We present results for two
different aluminium metal foams of density 0.49-0.51 g/cc and 0.31-
0.34 g/cc respectively that have been tested in quasi-static
compression. The influence of cell geometry and cell topology on
quasistatic compression behaviour has been investigated using optical
microscope and computed tomography (micro-CT) analysis. It is
shown that the deformation is not uniform in the structure and
collapse begins at the weakest point.