Abstract: This study is about the structural transformations of
aluminium examining with the Dynamic Mechanical Thermal
Analyzer (DMTA). It is a faster and simpler measuring method to
make consequence about the metal’s structural transformations. The
device measures the changing of the mechanical characteristics
depending on the heating rate, and concludes certain transformations.
This measuring method fast and shows clean-cut results comparing
the conventional ways.
Applying polymer measuring devices for metal investigations is
not widespread method. One of the adaptable ways is shown in this
study. The article compares the results of the small specimen test and
the DMTA method, considering the temperature and the forming
dependence of recrystallization temperature.
Abstract: The temperature dependence of wettability (wetting
angle, Θ (T)) for Ag-based melts on graphite and Al2O3 substrates is
compared. Typical alloying effects are found, as the Ag host metal is
gradually replaced by various metallic elements. The essence of
alloying lies in the change of the electron/atom (e/a) ratio. This ratio
is also manifested in the shift of wetting angles on the same substrate.
Nevertheless, the effects are partially smeared by other
(metallurgical) factors, like the interaction between the oxygenalloying
elements and by the graphite substrate-oxygen interaction. In
contrast, such effects are not pronounced in the case of Al2O3
substrates. As a consequence, Θ(T) exhibits an opposite trend in the
case of two substrates. Crossovers of the Θ(T) curves were often
found. The positions of crossovers depend on the chemical character
and concentration of solute atoms. Segregation and epitaxial texture
formation after solidification were also observed in certain alloy
drops, especially in high concentration range. This phenomenon is
not yet explained in every detail.