Abstract: Bacterial cellulose, a biopolysaccharide, is produced by the bacterium, Gluconacetobacter xylinus. Static batch fermentation for bacterial cellulose production was studied in sucrose and date syrup solutions (Bx. 10%) at 28 °C using G. xylinus (PTCC, 1734). Results showed that the maximum yields of bacterial cellulose (BC) were 4.35 and 1.69 g/l00 ml for date syrup and sucrose medium after 336 hours fermentation period, respectively. Comparison of FTIR spectrum of cellulose with BC indicated appropriate coincidence which proved that the component produced by G. xylinus was cellulose. Determination of the area under X-ray diffractometry patterns demonstrated that the crystallinity amount of cellulose (83.61%) was more than that for the BC (60.73%). The scanning electron microscopy imaging of BC and cellulose were carried out in two magnifications of 1 and 6K. Results showed that the diameter ratio of BC to cellulose was approximately 1/30 which indicated more delicacy of BC fibers relative to cellulose.
Abstract: In this study, Li4SiO4 powder was successfully
synthesized via sol gel method followed by drying at 150oC. Lithium
oxide, Li2O and silicon oxide, SiO2 were used as the starting
materials with citric acid as the chelating agent. The obtained powder
was then sintered at various temperatures. Crystallographic phase
analysis, morphology and ionic conductivity were investigated
systematically employing X-ray diffraction, Fourier Transform
Infrared, Scanning Electron Microscopy and AC impedance
spectroscopy. XRD result showed the formation of pure monoclinic
Li4SiO4 crystal structure with lattice parameters a = 5.140 Å, b =
6.094 Å, c = 5.293 Å, β = 90o in the sample sintered at 750oC. This
observation was confirmed by FTIR analysis. The bulk conductivity
of this sample at room temperature was 3.35 × 10-6 S cm-1 and the
highest bulk conductivity of 1.16 × 10-4 S cm-1 was obtained at
100°C. The results indicated that, the Li4SiO4 compound has
potential to be used as host for LISICON structured solid electrolyte
for low temperature application.
Abstract: Nowadays, butyl acetate, a pineapple flavor has been applied widely in food, beverage, cosmetic and pharmaceutical industries. In this study, Butyl acetate, a flavor ester was successfully synthesized via green synthesis of enzymatic reaction route. Commercial immobilized lipase from Rhizomucor miehei (Lipozyme RMIM) was used as biocatalyst in the esterification reaction between acetic acid and butanol. Various reaction parameters such as reaction time (RT), temperature (T) and amount of enzyme (E) were chosen to optimize the reaction synthesis in solvent-free system. The optimum condition to produce butyl acetate was at reaction time (RT), 18 hours; temperature (T), 37°C and amount of enzyme, 25 % (w/w of total substrate). Analysis of yield showed that at optimum condition, >78 % of butyl acetate was produced. The product was confirmed as butyl acetate from FTIR analysis whereby the presence of an ester group was observed at wavenumber of 1742 cm-1.
Abstract: Dispersions of casein micelles (CM) were studied at a
constant protein concentration of 5 wt % in high NaCl environment
ranging from 0% to 12% by Dynamic light scattering (DLS) and
Fourier Transform Infrared (FTIR). The rehydration profiles obtained
were interpreted in term of wetting, swelling and dispersion stages by
using a turbidity method. Two behaviours were observed depending
on the salt concentration. The first behaviour (low salt concentration)
presents a typical rehydration profile with a significant change
between 3 and 6% NaCl indicating quick wetting, swelling and long
dispersion stage. On the opposite, the dispersion stage of the second
behaviour (high salt concentration) was significantly shortened
indicating a strong modification of the protein backbone. A salt
increase result to a destabilization of the micelle and the formation of
mini-micelles more or less aggregated indicating an average micelles
size ranging from 100 to 200 nm. For the first time, the estimations
of secondary structural elements (irregular, ß-sheet, α-helix and turn)
by the Amide III assignments were correlated with results from
Amide I.
Abstract: This paper presents the experimental results of salt fog ageing test of silicone rubber housing material for outdoor polymer insulator based on IEC 61109. Four types of HTV silicone rubber sheet with different amount of ATH were tested continuously 1000
Abstract: Herein, we report the different types of surface morphology due to the interaction between the pure protein Insulin (INS) and catanionic surfactant mixture of Sodium Dodecyl Sulfate (SDS) and Cetyl Trimethyl Ammonium Bromide (CTAB) at air/water interface obtained by the Langmuir-Blodgett (LB) technique. We characterized the aggregations by Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM) and Fourier transform infrared spectroscopy (FTIR) in LB films. We found that the INS adsorption increased in presence of catanionic surfactant at air/water interface. The presence of small amount of surfactant induces two-stage growth kinetics due to the pure protein absorption and protein-catanionic surface micelle interaction. The protein remains in native state in presence of small amount of surfactant mixture. Smaller amount of surfactant mixture with INS is producing surface micelle type structure. This may be considered for drug delivery system. On the other hand, INS becomes unfolded and fibrillated in presence of higher amount of surfactant mixture. In both the cases, the protein was successfully immobilized on a glass substrate by the LB technique. These results may find applications in the fundamental science of the physical chemistry of surfactant systems, as well as in the preparation of drug-delivery system.
Abstract: The effect of extraction solvent upon properties
of carrageenan from Eucheuma cottonii was studied. The
distilled water and KOH solution (concentration 0.1- 0.5N) were
used as the solvent. Extraction process was carried out in water
bath equipped by stirrer with constant speed of 275 rpm with a
constant ratio of seaweed weight to solvent volume ( 1:50 g/mL)
at 86oC for 45 minutes. The extract was then precipitated in 3
volume of 90% ethanol, oven dried at 60oC. Based on
experimental data, alkali significantly influenced yield and
properties of extracted carrageenan. The extracted carrageenan
was found to have essentially identical FTIR spectra to the
reference samples of kappa-carrageenan. Increasing the KOH
concentration led to carrageenan containing less sulfate content
and intrinsic viscosity. The gel strength increased along with the
increasing of KOH concentration. The decreasing of intrinsic
viscosity value indicates that a polymer degradation occurs
during alkali extraction.
Abstract: The authors report a case of swine urolithiasis caused
by improper administration of sulfamonomethoxine and which was
diagnosed by examination of urinary sediments and analyzing the
composition of the uroliths. The chemical composition of urinary
calculi obtained from affected pigs with urolithiasis was further
confimed as sulfamonomethoxine by fourier transform infrared
(FTIR). It is suggested that appearance of typical fanlike or wheat
bunchy crystals in urinary sediments under observation of lightmicroscope
and determination by FTIR for the crystals are helpful in
diagnosing sulfa calculi causced swine urolithiasis.
Abstract: This paper presents the experimental results of silicone rubber housing material for 24kV lightning arrester under artificial accelerated ageing test based on IEC 61109 specifications. Specimens having inclined and alternated shed made of HTV silicone rubber with ATH content and having leakage distance 625 mm were tested continuously 1000 hrs in artificial salt fog chamber. After 1000 hrs of salt fog ageing test, obviously surface erosion was observed on trunk between the upper large shed and the lower small shed near the energized end. Decreasing in hydrophobicity and increasing in hardness were measured on tested specimen comparing with new specimen. Chemical analysis by ATR-FTIR confirmed the observation results.
Abstract: This study describes the preparation of a novel proton
conducting membranes based on bacterial cellulose (BC) modified by
grafting of 2-acrylamido-2-methyl-1 -propanesulfonic acid (AMPS)
through UV-induced graft polymerization. These AMPS-g-BC
membranes have been characterized by various techniques including
FTIR, SEM and TGA, to find their successful grafting of AMPS on
BC, surface morphology and thermal stability, respectively. Physical
properties of AMPS-g-BC membranes have been assessed in terms of
Lamda value( λ ), ion exchange capacity(IEC) and proton
conductivity. The relationship between degree of grafting and AMPS
concentration used for grafting has been determined by weight gain
method. An optimum proton conductivity equal to 2.89x10-2 S cm-1
and IEC value equal to 1.79 mmol g-1 have been obtained when 20
wt% AMPS concentration is used for grafting (i.e. the corresponding
membrane is notated as AMPS20-g-BC).
Abstract: In the present work homogeneous silica film on
silicon was fabricated by colloidal silica sol. The silica sol precursor
with uniformly granular particle was derived by the alkaline
hydrolysis of tetraethoxyorthosilicate (TEOS) in presence of glycerol
template. The film was prepared by dip coating process. The
templated hetero-structured silica film was annealed at elevated
temperatures to generate nano- and meso porosity in the film. The
film was subsequently annealed at different temperatures to make it
defect free and abrasion resistant. The sol and the film were
characterized by the measurement of particle size distribution,
scanning electron microscopy, XRD, FTIR spectroscopy,
transmission electron microscopy, atomic force microscopy,
measurement of the refractive index, thermal conductivity and
abrasion resistance. The porosity of the films decreased whereas
refractive index and dielectric constant of it `increased with the
increase in the annealing temperature. The thermal conductivity of
the films increased with the increase in the film thickness. The
developed porous silica film holds strong potential for use in
different areas.
Abstract: This paper presents the experimental results of silicone rubber outdoor polymer insulators in salt fog ageing test based on IEC 61109. Specimens made ofHTV silicone rubber with ATH content having three different configurations, straight shedsalternated sheds, and incline and alternate sheds, were tested continuously 1000 hrs.in artificial salt fog chamber. Contamination level, reduction of hydrophobicity and hardness measurement were used as physical damaged inspection techniques to evaluate degree of surface deterioration. In addition, chemical changing of tested specimen surface was evaluated by ATR-FTIRto confirm physical damaged inspection. After 1000 hrs.of salt fog test, differences in degree of surface deterioration were observed on all tested specimens. Physical damaged inspection and chemical analysis results confirmed the experimental results as well.
Abstract: The complex structure of lignocellulose leads to great
difficulties in converting it to fermentable sugars for the ethanol
production. The major hydrolysis impediments are the crystallinity of
cellulose and the lignin content. To improve the efficiency of
enzymatic hydrolysis, microbial pretreatment of corncob was
investigated using two bacterial strains of Bacillus subtilis A 002 and
Cellulomonas sp. TISTR 784 (expected to break open the crystalline
part of cellulose) and lignin-degrading fungus, Phanerochaete
sordida SK7 (expected to remove lignin from lignocellulose). The
microbial pretreatment was carried out with each strain under its
optimum conditions. The pretreated corncob samples were further
hydrolyzed to produce reducing glucose with low amounts of
commercial cellulase (25 U·g-1 corncob) from Aspergillus niger. The
corncob samples were determined for composition change by X-ray
diffraction (XRD), Fourier transform infrared spectroscopy (FTIR),
and scanning electron microscope (SEM). According to the results,
the microbial pretreatment with fungus, P. sordida SK7 was the most
effective for enhancing enzymatic hydrolysis, approximately, 40%
improvement.
Abstract: The hybrid membranes containing inorganic materials in polymer matrix are identified as a remarkable family of proton conducting hybrid electrolytes. In this work, the proton conducting inorganic/organic hybrid membranes for proton exchange membrane fuel cells (PEMFCs) were prepared using polyvinyl alcohol (PVA), tetraethoxyorthosilane (TEOS) and heteropolyacid (HPA). The synthesized hybrid membranes were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction spectroscopy (XRD), Scanning electron microscopy (SEM) and Thermogravimetry analysis (TGA). The effects of heteropolyacid incorporation on membrane properties, including morphology and thermal stability were extensively investigated.
Abstract: In this study, multiwall carbon nanotubes (MWNTs)
were modified with nitric acid chemically and by dielectric barrier
discharge (DBD) plasma in an oxygen-based atmosphere. Used
carbon nanotubes (CNTs) were prepared by chemical vapour
deposition (CVD) floating catalyst method. For removing amorphous
carbon and metal catalyst, MWNTs were exposed to dry air and
washed with hydrochloric acid. Heating purified CNTs under helium
atmosphere caused elimination of acidic functional groups. Fourier
transformed infrared spectroscopy (FTIR) shows formation of
oxygen containing groups such as C=O and COOH. Brunauer,
Emmett, Teller (BET) analysis revealed that functionalization causes
generation of defects on the sidewalls and opening of the ends of
CNTs. Results of temperature-programmed desorption (TPD) and gas
chromatography(GC) indicate that nitric acid treatment create more
acidic groups than plasma treatment.
Abstract: Fly ash is a significant waste that is released of
thermal power plants and defined as very fine particles that are drifted upward with up taken by the flue gases due to the burning of
used coal [1]. The fly-ash is capable of removing organic
contaminants in consequence of high carbon content, a large surface area per unit volume and contained heavy metals. Therefore, fly ash
is used as an effective coagulant and adsorbent by pelletization [2, 3].
In this study, the possibility of use of fly ash taken from Turkey like low-cost adsorbent for adsorption of zinc ions found in waste
water was investigated. The fly ash taken from Turkey was pelletized with bentonite and molass to evaluate the adsorption capaticity. For
this purpose; analyses such as sieve analysis, XRD, XRF, FTIR and SEM were performed. As a result, it was seen that pellets prepared
from fly ash, bentonite and molass would be used for zinc adsorption.
Abstract: This paper presents the experimental results of silicone rubber polymer insulators for 22 kV systems under salt water dip wheel test based on IEC 62217. Straight shed silicone rubber polymer insulators having leakage distance 685 mm were tested continuously 30,000 cycles. One test cycle includes 4 positions, energized, de-energized, salt water dip and deenergized, respectively. For one test cycle, each test specimen remains stationary for about 40 second in each position and takes 8 second for rotate to next position. By visual observation, sever surface erosion was observed on the trunk near the energized end of tested specimen. Puncture was observed on the upper shed near the energized end. In addition, decreasing in hydrophobicity and increasing in hardness were measured on tested specimen comparing with new specimen. Furthermore, chemical analysis by ATR-FTIR was conducted in order to elucidate the chemical change of tested specimens comparing with new specimen.
Abstract: This current research focused on development of degradable starch based packaging film with enhanced mechanical properties. A series of low density polyethylene (LDPE)/tapioca starch compounds with various tapioca starch contents were prepared by twin screw extrusion with the addition of maleic anhydride grafted polyethylene as compatibilizer. Palm cooking oil was used as processing aid to ease the blown film process, thus, degradable film can be processed via conventional blown film machine. Studies on their characteristics, mechanical properties and biodegradation were carried out by Fourier Transform Infrared (FTIR) spectroscopy and optical properties, tensile test and exposure to fungi environment respectively. The presence of high starch contents had an adverse effect on the tensile properties of LDPE/tapioca starch blends. However, the addition of compatibilizer to the blends improved the interfacial adhesion between the two materials, hence, improved the tensile properties of the films. High content of starch amount also was found to increase the rate of biodegradability of LDPE/tapioca starch films. It can be proved by exposure of the film to fungi environment. A growth of microbes colony can be seen on the surface of LDPE/tapioca starch film indicates that the granular starch present on the surface of the polymer film is attacked by microorganisms, until most of it is assimilated as a carbon source.
Abstract: Solid dispersions (SD) of curcuminpolyvinylpyrrolidone
in the ratio of 1:2, 1:4, 1:5, 1:6, and 1:8 were
prepared in an attempt to increase the solubility and dissolution.
Solubility, dissolution, powder X-ray diffraction (XRD), differential
scanning calorimetry (DSC) and Fourier transform infrared
spectroscopy (FTIR) of solid dispersions, physical mixtures (PM)
and curcumin were evaluated. Both solubility and dissolution of
curcumin solid dispersions were significantly greater than those
observed for physical mixtures and intact curcumin. The powder
X-ray diffractograms indicated that the amorphous curcumin was
obtained from all solid dispersions. It was found that the optimum
weight ratio for curcumin:PVP K-30 is 1:6. The 1:6 solid dispersion
still in the amorphous from after storage at ambient temperature for 2
years and the dissolution profile did not significantly different from
freshly prepared.
Abstract: This report shows the performance of composite
biodegradable film from chitosan, starch and sawdust fiber. The main
objectives of this research are to fabricate and characterize composite
biodegradable film in terms of morphology and physical properties.
The film was prepared by casting method. Sawdust fiber was used as
reinforcing agent and starch as polymer matrix in the casting
solution. The morphology of the film was characterized using atomic
force microscope (AFM). The result showed that the film has
smooth structure. Chemical composition of the film was investigated
using Fourier transform infrared (FTIR) where the result revealed
present of starch in the film. The thermal properties were
characterized using thermal gravimetric analyzer (TGA) and
differential scanning calorimetric (DSC) where the results showed
that the film has small difference in melting and degradation
temperature.