Abstract: This paper presents the experimental results on
ageing deterioration of silicone rubber outdoor polymer insulator
under salt water dip wheel test based on IEC 62217. In order to comparison effect of chemical contents, silicone rubber outdoor
polymer insulators having same configuration and leakage distant
from two manufactures were tested together continuously 30,000 test cycles. Many discharge activities were observed in during the test.
After 30,000 test cycles, in spite of same configuration, differences in
degree of surface aging were observed. Physical analysis such as
decreasing in hydrophobicity and increasing in hardness
measurement were measured on two-type tested specimen surface in order to confirm degree of surface ageing. Furthermore, chemical
analysis by ATR-FTIR to diagnose the chemical change of tested
specimen surface was conducted to confirm the physical analysis results.
Abstract: This paper presents the simulation the results of
electric field and potential distributions along surface of silicone
rubber polymer insulators. Near the same leakage distance subjected
to 15 kV in 50 cycle salt fog ageing test, alternate sheds silicone
rubber polymer insulator showed better contamination performance
than straight sheds silicone rubber polymer insulator. Severe surface
ageing was observed on the straight sheds insulator. The objective of
this work is to elucidate that electric field distribution along straight
sheds insulator higher than alternate shed insulator in salt fog ageing
test. Finite element method (FEM) is adopted for this work. The
simulation results confirmed the experimental data, as well.
Abstract: This paper presents the simulation results of electric field and potential distributions along surface of silicone rubber polymer insulators under clean and various contamination conditions with/without water droplets. Straight sheds insulator having leakage distance 290 mm was used in this study. Two type of contaminants, playwood dust and cement dust, have been studied the effect of contamination on the insulator surface. The objective of this work is to comparison the effect of contamination on potential and electric field distributions along the insulator surface when water droplets exist on the insulator surface. Finite element method (FEM) is adopted for this work. The simulation results show that contaminations have no effect on potential distribution along the insulator surface while electric field distributions are obviously depended on contamination conditions.
Abstract: This paper presents the experimental results of silicone rubber polymer insulators for 22 kV systems under salt water dip wheel test based on IEC 62217. Straight shed silicone rubber polymer insulators having leakage distance 685 mm were tested continuously 30,000 cycles. One test cycle includes 4 positions, energized, de-energized, salt water dip and deenergized, respectively. For one test cycle, each test specimen remains stationary for about 40 second in each position and takes 8 second for rotate to next position. By visual observation, sever surface erosion was observed on the trunk near the energized end of tested specimen. Puncture was observed on the upper shed near the energized end. In addition, decreasing in hydrophobicity and increasing in hardness were measured on tested specimen comparing with new specimen. Furthermore, chemical analysis by ATR-FTIR was conducted in order to elucidate the chemical change of tested specimens comparing with new specimen.