Abstract: This paper presents the experimental results on
ageing deterioration of silicone rubber outdoor polymer insulator
under salt water dip wheel test based on IEC 62217. In order to comparison effect of chemical contents, silicone rubber outdoor
polymer insulators having same configuration and leakage distant
from two manufactures were tested together continuously 30,000 test cycles. Many discharge activities were observed in during the test.
After 30,000 test cycles, in spite of same configuration, differences in
degree of surface aging were observed. Physical analysis such as
decreasing in hydrophobicity and increasing in hardness
measurement were measured on two-type tested specimen surface in order to confirm degree of surface ageing. Furthermore, chemical
analysis by ATR-FTIR to diagnose the chemical change of tested
specimen surface was conducted to confirm the physical analysis results.
Abstract: This paper presents the experimental results of salt fog ageing test of silicone rubber housing material for outdoor polymer insulator based on IEC 61109. Four types of HTV silicone rubber sheet with different amount of ATH were tested continuously 1000
Abstract: This paper presents the experimental results of silicone rubber housing material for 24kV lightning arrester under artificial accelerated ageing test based on IEC 61109 specifications. Specimens having inclined and alternated shed made of HTV silicone rubber with ATH content and having leakage distance 625 mm were tested continuously 1000 hrs in artificial salt fog chamber. After 1000 hrs of salt fog ageing test, obviously surface erosion was observed on trunk between the upper large shed and the lower small shed near the energized end. Decreasing in hydrophobicity and increasing in hardness were measured on tested specimen comparing with new specimen. Chemical analysis by ATR-FTIR confirmed the observation results.