Abstract: This research was to evaluate a technical feasibility of
making single-layer experimental particleboard panels from bamboo
waste (Dendrocalamus asper Backer) by converting bamboo into
strips, which are used to make laminated bamboo furniture. Variable
factors were density (600, 700 and 800 kg/m3) and temperature of
condition (25, 40 and 55 °C). The experimental panels were tested for
their physical and mechanical properties including modulus of
elasticity (MOE), modulus of rupture (MOR), internal bonding
strength (IB), screw holding strength (SH) and thickness swelling
values according to the procedures defined by Japanese Industrial
Standard (JIS). The test result of mechanical properties showed that
the MOR, MOE and IB values were not in the set criteria, except the
MOR values at the density of 700 kg/m3 at 25 °C and at the density
of 800 kg/m3 at 25 and 40 °C, the IB values at the density of 600
kg/m3, at 40 °C, and at the density of 800 kg/m3 at 55 °C. The SH
values had the test result according to the set standard, except with
the density of 600 kg/m3, at 40 and 55 °C. Conclusively, a valuable
renewable biomass, bamboo waste could be used to manufacture
boards.
Abstract: Nanostructured materials have attracted many
researchers due to their outstanding mechanical and physical
properties. For example, carbon nanotubes (CNTs) or carbon
nanofibres (CNFs) are considered to be attractive reinforcement
materials for light weight and high strength metal matrix composites.
These composites are being projected for use in structural
applications for their high specific strength as well as functional
materials for their exciting thermal and electrical characteristics. The
critical issues of CNT-reinforced MMCs include processing
techniques, nanotube dispersion, interface, strengthening mechanisms
and mechanical properties. One of the major obstacles to the effective
use of carbon nanotubes as reinforcements in metal matrix
composites is their agglomeration and poor distribution/dispersion
within the metallic matrix. In order to tap into the advantages of the
properties of CNTs (or CNFs) in composites, the high dispersion of
CNTs (or CNFs) and strong interfacial bonding are the key issues
which are still challenging. Processing techniques used for synthesis
of the composites have been studied with an objective to achieve
homogeneous distribution of carbon nanotubes in the matrix.
Modified mechanical alloying (ball milling) techniques have emerged
as promising routes for the fabrication of carbon nanotube (CNT)
reinforced metal matrix composites. In order to obtain a
homogeneous product, good control of the milling process, in
particular control of the ball movement, is essential. The control of
the ball motion during the milling leads to a reduction in grinding
energy and a more homogeneous product. Also, the critical inner
diameter of the milling container at a particular rotational speed can
be calculated. In the present work, we use conventional and modified
mechanical alloying to generate a homogenous distribution of 2 wt.
% CNT within Al powders. 99% purity Aluminium powder (Acros,
200mesh) was used along with two different types of multiwall
carbon nanotube (MWCNTs) having different aspect ratios to
produce Al-CNT composites. The composite powders were processed
into bulk material by compaction, and sintering using a cylindrical
compaction and tube furnace. Field Emission Scanning electron
microscopy (FESEM), X-Ray diffraction (XRD), Raman
spectroscopy and Vickers macro hardness tester were used to
evaluate CNT dispersion, powder morphology, CNT damage, phase
analysis, mechanical properties and crystal size determination.
Despite the success of ball milling in dispersing CNTs in Al powder,
it is often accompanied with considerable strain hardening of the Al
powder, which may have implications on the final properties of the
composite. The results show that particle size and morphology vary
with milling time. Also, by using the mixing process and sonication
before mechanical alloying and modified ball mill, dispersion of the
CNTs in Al matrix improves.
Abstract: Structural and UV/Visible optical properties can be
useful to describe a material for the CIGS solar cell active layer,
therefore, this work demonstrates the properties like surface
morphology, X-ray Photoelectron Spectroscopy (XPS) bonding
energy (EB) core level spectra, UV/Visible absorption spectra,
refractive index (n), optical energy band (Eg), reflection spectra for
the Cu25 (In16Ga9) Se40Te10 (CIGST-1) and Cu20 (In14Ga9) Se45Te12
(CIGST-2) chalcogenide compositions. Materials have been
exhibited homogenous surface morphologies, broading /-or diffusion
of bonding energy peaks relative elemental values and a high
UV/Visible absorption tendency in the wave length range 400 nm-
850 nm range with the optical energy band gaps 1.37 and 1.42
respectively. Subsequently, UV/Visible reflectivity property in the
wave length range 250 nm to 320 nm for these materials has also
been discussed.
Abstract: The primary objective of this research is to improve the flexural capacity of FRP strengthened RC Beam structures with Aluminum and Titanium laminates. FRP rupture of flexural strengthened RC beams using FRP plates generally occurs at the interface between FRP plate and the beam. Therefore, in order to prevent brittle rupture and improve the ductility of the system, this research was performed by using Aluminum and Titanium materials between the two different structural systems. The research also aims to provide various strengthening/retrofitting methods for RC beam structures and to conduct a preliminary analysis of the demands on the structural systems. This was achieved by estimation using the experimental data from this research to identify a flexural capacity for the systems. Ultimately, the preliminary analysis of current study showed that the flexural capacity and system demand ductility was significantly improved by the systems inserted with Aluminum and Titanium anchor plates. Further verification of the experimental research is currently on its way to develop a new or reliable design guideline to retrofit/strengthen the concrete-FRP structural system can be evaluated.
Abstract: The techniques for estimating the adhesive and cohesive strength in high velocity oxy fuel (HVOF) thermal spray coatings have been discussed and compared. The development trend and the last investigation have been studied. We will focus on benefits and limitations of these methods in different process and materials.
Abstract: The role of neighborhood center as semi public (the
balance space) is disappeared in bonding between private and public
in new urbanism. In this way, a hierarchical principle in the
traditional neighborhood center appears to create or develop the
conditions for residents` relationships and belonging. This paper
evaluates significant of hierarchical principles of the neighborhood
center in residents` territoriality and its factors. In this way Miandeh
neighborhood center from Boshrooyeh city was determined as a case
study area. Results indicated that a hierarchical principle is the best
instrument to improve the territoriality as the subcomponent of place
belonging in residents. The findings help the urban designer to
revitalization the neighborhoods and proceedings in organization of
physical space.
Abstract: An active RC filters with a 880 / 1760 MHz dual bandwidth tuning ability is present for 60 GHz unlicensed band applications. A third order Butterworth low-pass filter utilizes two Cherry-Hooper amplifiers to satisfy the very high bandwidth requirements of an amplifier. The low-pass filter is fabricated in 90nm standard CMOS process. Drawing 6.7 mW from 1.2 V power supply, the low frequency gains of the filter are -2.5 and -4.1 dB, and the output third order intercept points (OIP3) are +2.2 and +1.9 dBm for the single channel and channel bonding conditions, respectively.
Abstract: Ciprofloxacin (CIP) and Carbamazepine (CBZ), nonbiodegradable pharmaceutical residues, were become emerging pollutants in several aquatic environments. The objectives of this research were to study the possibility to recover these pharmaceuticals residues from pharmaceutical wastewater by increasing the selective adsorption on synthesized functionalized porous silicate, comparing with powdered activated carbon (PAC). Hexagonal mesoporous silicate (HMS), functionalized HMSs (3- aminopropyltriethoxy, 3- mercaptopropyltrimethoxy and noctyldimethyl) were synthesized and characterized physico-chemical characteristics. Obtained adsorption kinetics and isotherms showed that 3-mercaptopropyltrimethoxy functional groups grafted on HMS provided highest CIP and CBZ adsorption capacities; however, it was still lower than that of PAC. The kinetic results were compatible with pseudo-second order. The hydrophobicity and hydrogen bonding might play a key role on the adsorption. Furthermore, the capacities were affected by varying pH values due to the strength of hydrogen bonding between targeted compounds and adsorbents. Electrostatic interaction might not affect the adsorption capacities.
Abstract: In this study, Friction Stir Processing (FSP) a recent grain refinement technique was employed to disperse micron-sized (2 *m) SiCp particles into aluminum alloy AA6063. The feasibility to fabricate bulk composites through FSP was analyzed and experiments were conducted at different traverse speeds and wider volumes of the specimens. Micro structural observation were carried out by employing optical microscopy test of the cross sections in both parallel and perpendicular to the tool traverse direction. Mechanical property including micro hardness was evaluated in detail at various regions on the specimen. The composites had an excellent bonding with aluminum alloy substrate and a significant increase of 30% in the micro hardness value of metal matrix composite (MMC) as to that of the base metal has observed. The observations clearly indicate that SiC particles were uniformly distributed within the aluminum matrix.
Abstract: The aluminum bronze matrix alumina composites using hot press and resin infiltration were investigated to study their porosities, hardness, bending strengths, and microstructures. The experiment results show that the hardness of the sintered composites with the decrease of porosity increases. The composites without and with resin infiltration have about HRF 42-61 of about 34-40% of porosity and about HRF 62-83 of about 30-36% of porosity, respectively. Besides, the alumina composites contain a more amount of iron and nickel powders would cause a lower bending strength due to forming some weaker bonding among the iron, nickel, copper, aluminum under this hot pressing of shorter time.
Abstract: Electrical resistivity is a fundamental parameter of metals or electrical conductors. Since resistivity is a function of temperature, in order to completely understand the behavior of metals, a temperature dependent theoretical model is needed. A model based on physics principles has recently been developed to obtain an equation that relates electrical resistivity to temperature. This equation is dependent upon a parameter associated with the electron travel time before being scattered, and a parameter that relates the energy of the atoms and their separation distance. Analysis of the energy parameter reveals that the equation is optimized if the proportionality term in the equation is not constant but varies over the temperature range. Additional analysis reveals that the theoretical equation can be used to determine the mean free path of conduction electrons, the number of defects in the atomic lattice, and the ‘equivalent’ charge associated with the metallic bonding of the atoms. All of this analysis provides validation for the theoretical model and provides insight into the behavior of metals where performance is affected by temperatures (e.g., integrated circuits and temperature sensors).
Abstract: One of the most common practices for strengthening
the reinforced concrete structures is the application of FRP (Fiber
Reinforce Plastic) sheets to increase the flexural and shear strengths
of the member. The elastic modulus of FRP is considerably higher
than that of concrete. This will result in debonding between the FRP
sheets and concrete surface. With conventional surface preparation of
concrete, the ultimate capacity of the FRP sheets can hardly be
achieved. New methods for preparation of the bonding surface have
shown improvements in reducing the premature debonding of FRP
sheets from concrete surface. The present experimental study focuses
on the application of grooving method to postpone debonding of the
FRP sheets attached to the side faces of concrete beams for shear
strengthening. Comparison has also been made with conventional
surface preparation method. This study clearly shows the efficiency
of grooving method compared to surface preparation method, in
preventing the debonding phenomenon and in increasing the load
carrying capacity of FRP.
Abstract: Bonding has become a routine procedure in several
dental specialties – from prosthodontics to conservative dentistry and
even orthodontics. In many of these fields it is important to be able to
investigate the bonded interfaces to assess their quality. All currently
employed investigative methods are invasive, meaning that samples
are destroyed in the testing procedure and cannot be used again. We
have investigated the interface between human enamel and bonded
ceramic brackets non-invasively, introducing a combination of new
investigative methods – optical coherence tomography (OCT),
fluorescence OCT and confocal microscopy (CM). Brackets were
conventionally bonded on conditioned buccal surfaces of teeth. The
bonding was assessed using these methods. Three dimensional
reconstructions of the detected material defects were developed using
manual and semi-automatic segmentation. The results clearly prove
that OCT, fluorescence OCT and CM are useful in orthodontic
bonding investigations.
Abstract: The scope of this paper is to describe a real electrical
installation of renewable energy using photovoltaic cells. The
displayed power grid connected network was established in 2007 at
area of Northern Greece. The photovoltaic park is composed of 6120
photovoltaic cells able to deliver a total power of 1.101.600 Wp. For
the transformation of DC voltage to AC voltage have been used 25
stand alone three phases inverters and for the connection at the
medium voltage network of Greek Power Authority have been
installed two oil immersed transformer of 630 kVA each one. Due to
the wide space area of installation a specific external lightning
protection system has been designed. Additionally, due to the
sensitive electronics of the control and protection systems of park,
surge protection, equipotent bonding and shielding were also of
major importance.
Abstract: This paper features the modeling and design of a Fast
Output Sampling (FOS) Feedback control technique for the Active
Vibration Control (AVC) of a smart flexible aluminium cantilever
beam for a Single Input Single Output (SISO) case. Controllers are
designed for the beam by bonding patches of piezoelectric layer as
sensor / actuator to the master structure at different locations along
the length of the beam by retaining the first 2 dominant vibratory
modes. The entire structure is modeled in state space form using the
concept of piezoelectric theory, Euler-Bernoulli beam theory, Finite
Element Method (FEM) and the state space techniques by dividing
the structure into 3, 4, 5 finite elements, thus giving rise to three
types of systems, viz., system 1 (beam divided into 3 finite
elements), system 2 (4 finite elements), system 3 (5 finite elements).
The effect of placing the sensor / actuator at various locations along
the length of the beam for all the 3 types of systems considered is
observed and the conclusions are drawn for the best performance and
for the smallest magnitude of the control input required to control the
vibrations of the beam. Simulations are performed in MATLAB. The
open loop responses, closed loop responses and the tip displacements
with and without the controller are obtained and the performance of
the proposed smart system is evaluated for vibration control.