Abstract: Intermetallic Ni3Al – based alloys belong to a group
of advanced materials characterized by good chemical and physical
properties (such as structural stability, corrosion resistance) which
offer advenced technological applications. The paper presents the
study of catalytic properties of Ni3Al foils (thickness approximately
50 &m) in the methanol and hexane decomposition. The egzamined
material posses microcrystalline structure without any additional
catalysts on the surface. The better catalytic activity of Ni3Al foils
with respect to quartz plates in both methanol and hexane
decomposition was confirmed. On thin Ni3Al foils the methanol
conversion reaches approximately 100% above 480 oC while the
hexane conversion reaches approximately 100% (98,5%) at 500 oC.
Deposit formed during the methanol decomposition is built up of
carbon nanofibers decorated with metal-like nanoparticles.
Abstract: In this study, a synthetic pathway was created by
assembling genes from Clostridium butyricum and Escherichia coli
in different combinations. Among the genes were dhaB1 and dhaB2
from C. butyricum VPI1718 coding for glycerol dehydratase (GDHt)
and its activator (GDHtAc), respectively, involved in the conversion
of glycerol to 3-hydroxypropionaldehyde (3-HPA). The yqhD gene
from E.coli BL21 was also included which codes for an NADPHdependent
1,3-propanediol oxidoreductase isoenzyme (PDORI)
reducing 3-HPA to 1,3-propanediol (1,3-PD). Molecular modeling
analysis indicated that the conformation of fusion protein of YQHD
and DHAB1 was favorable for direct molecular channeling of the
intermediate 3-HPA. According to the simulation results, the yqhD
and dhaB1 gene were assembled in the upstream of dhaB2 to express
a fusion protein, yielding the recombinant strain E. coliBL21
(DE3)//pET22b+::yqhD-dhaB1_dhaB2 (strain BP41Y3). Strain
BP41Y3 gave 10-fold higher 1,3-PD concentration than E. coliBL21
(DE3)//pET22b+::yqhD-dhaB1_dhaB2 (strain BP31Y2) expressing
the recombinant enzymes simultaneously but in a non-fusion mode.
This is the first report using a gene fusion approach to enhance the
biological conversion of glycerol to the value added compound 1,3-
PD.
Abstract: Nanophotocatalysts such as titanium (TiO2), zinc (ZnO), and iron (Fe2O3) oxides can be used in organic pollutants oxidation, and in many other applications. But among the challenges for technological application (scale-up) of the nanotechnology scientific developments two aspects are still little explored: research on environmental risk of the nanomaterials preparation methods, and the study of nanomaterials properties and/or performance variability. The environmental analysis was performed for six different methods of ZnO nanoparticles synthesis, and showed that it is possible to identify the more environmentally compatible process even at laboratory scale research. The obtained ZnO nanoparticles were tested as photocatalysts, and increased the degradation rate of the Rhodamine B dye up to 30 times.
Abstract: Iron oxide nanoparticle was synthesized by reactive-precipitation method followed by high speed centrifuge and phase transfer in order to stabilized nanoparticles in the solvent. Particle size of SPIO was 8.2 nm by SEM, and the hydraulic radius was 17.5 nm by dynamic light scattering method. Coercivity and saturated magnetism were determined by VSM (vibrating sample magnetometer), coercivity of nanoparticle was lower than 10 Hc, and the saturated magnetism was higher than 65 emu/g. Stabilized SPIO was then transferred to aqueous phase by reacted with excess amount of poly (ethylene glycol) (PEG) silane. After filtration and dialysis, the SPIO T2 contrast agent was ready to use. The hydraulic radius of final product was about 70~100 nm, the relaxation rates R2 (1/T2) measured by magnetic resonance imaging (MRI) was larger than 200(sec-1).
Abstract: The aim of this research was to calculate the thermal
properties of Au3Ni Nanowire. The molecular dynamics (MD)
simulation technique was used to obtain the effect of radius size on
the energy, the melting temperature and the latent heat of fusion at
the isobaric-isothermal (NPT) ensemble. The Quantum Sutton-Chen
(Q-SC) many body interatomic potentials energy have been used for
Gold (Au) and Nickel (Ni) elements and a mixing rule has been
devised to obtain the parameters of these potentials for nanowire
stats. Our MD simulation results show the melting temperature and
latent heat of fusion increase upon increasing diameter of nanowire.
Moreover, the cohesive energy decreased with increasing diameter of
nanowire.
Abstract: The production of devices in nanoscale with specific
molecular rectifying function is one of the most significant goals in
state-of-art technology. In this work we show by ab initio quantum
mechanics calculations coupled with non-equilibrium Green
function, the design of an organic two-terminal device. These
molecular structures have molecular source and drain with several
bridge length (from five up to 11 double bonds). Our results are
consistent with significant features as a molecular rectifier and can be
raised up as: (a) it can be used as bi-directional symmetrical rectifier;
(b) two devices integrated in one (FET with one operational region,
and Thyristor thiristor); (c) Inherent stability due small intrinsic
capacitance under forward/reverse bias. We utilize a scheme for the
transport mechanism based on previous properties of ¤Ç bonds type
that can be successfully utilized to construct organic nanodevices.
Abstract: This paper present some preliminary work on the
preparation and physicochemical caracterization of nanocomposite
MFI-alumina structures based on alumina hollow fibres. The fibers
are manufactured by a wet spinning process. α-alumina particles were
dispersed in a solution of polysulfone in NMP. The resulting slurry is
pressed through the annular gap of a spinneret into a precipitation
bath. The resulting green fibres are sintered. The mechanical strength
of the alumina hollow fibres is determined by a three-point-bending
test while the pore size is characterized by bubble-point testing. The
bending strength is in the range of 110 MPa while the average pore
size is 450 nm for an internal diameter of 1 mm and external diameter
of 1.7 mm. To characterize the MFI membranes various techniques
were used for physicochemical characterization of MFI–ceramic
hollow fibres membranes: The nitrogen adsorption, X-ray
diffractometry, scanning electron microscopy combined with X
emission microanalysis. Scanning Electron Microscopy (SEM) and
Energy Dispersive Microanalysis by the X-ray were used to observe
the morphology of the hollow fibre membranes (thickness,
infiltration into the carrier, defects, homogeneity). No surface film,
has been obtained, as observed by SEM and EDX analysis and
confirmed by high temperature variation of N2 and CO2 gas
permeances before cation exchange. Local analysis and characterise
(SEM and EDX) and overall (by ICP elemental analysis) were
conducted on two samples exchanged to determine the quantity and
distribution of the cation of cesium on the cross section fibre of the
zeolite between the cavities.
Abstract: Renewable natural fibres such as oil palm, flax, and
pineapple leaf can be utilized to obtain new high performance
polymer materials. The reuse of waste natural fibres as reinforcement
for polymer is a sustainable option to the environment. However, due
to its high hydroxyl content of cellulose, natural fibres are
susceptible to absorb water that affects the composite mechanical
properties adversely. Research found that Nano materials such as
Nano Silica Carbide (n-SiC) and Nano Clay can be added into the
polymer composite to overcome this problem by enhancing its
mechanical properties in wet condition. The addition of Nano
material improves the tensile and wear properties, flexural stressstrain
behaviour, fracture toughness, and fracture strength of polymer
natural composites in wet and dry conditions.
Abstract: Research results and optimal parameters investigation
of laser cut and profiling of diamond and quartz substrates by
femtosecond laser pulses are presented. Profiles 10 μm in width, ~25
μm in depth and several millimeters long were made. Investigation of
boundaries quality has been carried out with the use of AFM
«Vecco». Possibility of technological formation of profiles and
micro-holes in diamond and quartz substrates with nanometer-scale
boundaries is shown. Experimental results of multilayer dielectric
cover treatment are also presented. Possibility of precise upper layer
(thickness of 70–140 nm) removal is demonstrated. Processes of thin
metal film (60 nm and 350 nm thick) treatment are considered.
Isolation tracks (conductance ~ 10-11 S) 1.6–2.5 μm in width in
conductive metal layers are formed.
Abstract: ZnO-SnO2 i.e. Zinc-Tin-Oxide (ZTO) thin films were
deposited on glass substrate with varying concentrations (ZnO:SnO2
- 100:0, 90:10, 70:30 and 50:50 wt.%) at room temperature by flash
evaporation technique. These deposited ZTO film were annealed at
450 0C in vacuum. These films were characterized to study the effect
of annealing on the structural, electrical, and optical properties.
Atomic force microscopy (AFM) and Scanning electron microscopy
(SEM) images manifest the surface morphology of these ZTO thin
films. The apparent growth of surface features revealed the formation
of nanostructure ZTO thin films. The small value of surface
roughness (root mean square RRMS) ensures the usefulness in
optical coatings. The sheet resistance was also found to be decreased
for both types of films with increasing concentration of SnO2. The
optical transmittance found to be decreased however blue shift has
been observed after annealing.
Abstract: Two different superhydrophobic surfaces were
elaborated and their oil repellency behavior was evaluated using
several liquid with different surface tension. A silicone rubber/SiO2
nanocomposite coated (A) on aluminum substrate by “spin-coating"
and the sample B was an anodized aluminum surface covered by
Teflon-like coating. A high static contact angle about ∼162° was
measured for two prepared surfaces on which the water droplet rolloff.
Scanning electron microscopy (SEM) showed the presence of
micro/nanostructures for both sample A and B similar to that of lotus
leaf.
However the sample A presented significantly different behaviour
of wettability against the low surface tension liquid. Sample A has
been wetted totally by oil (dodecan) droplet while sample B showed
oleophobic behaviour. Oleophobic property of Teflon like coating
can be contributed to the presence of CF2 and CF3 functional group
which was shown by XPS analysis.
Abstract: Although silicon photonic devices provide a significantly larger bandwidth and dissipate a substantially less power than the electronic devices, they suffer from a large size due to the fundamental diffraction limit and the weak optical response of Si. A potential solution is to exploit Si plasmonics, which may not only miniaturize the photonic device far beyond the diffraction limit, but also enhance the optical response in Si due to the electromagnetic field confinement. In this paper, we discuss and summarize the recently developed metal-insulator-Si-insulator-metal nanoplasmonic waveguide as well as various passive and active plasmonic components based on this waveguide, including coupler, bend, power splitter, ring resonator, MZI, modulator, detector, etc. All these plasmonic components are CMOS compatible and could be integrated with electronic and conventional dielectric photonic devices on the same SOI chip. More potential plasmonic devices as well as plasmonic nanocircuits with complex functionalities are also addressed.
Abstract: The nickel and gold nanoclusters as supported
catalysts were analyzed by XAS, XRD and XPS in order to
determine their local, global and electronic structure. The present
study has pointed out a strong deformation of the local structure of
the metal, due to its interaction with oxide supports. The average
particle size, the mean squares of the microstrain, the particle size
distribution and microstrain functions of the supported Ni and Au
catalysts were determined by XRD method using Generalized Fermi
Function for the X-ray line profiles approximation. Based on EXAFS
analysis we consider that the local structure of the investigated
systems is strongly distorted concerning the atomic number pairs.
Metal-support interaction is confirmed by the shape changes of the
probability densities of electron transitions: Ni K edge (1s →
continuum and 2p), Au LIII-edge (2p3/2 → continuum, 6s, 6d5/2 and
6d3/2). XPS investigations confirm the metal-support interaction at
their interface.
Abstract: In the present work homogeneous silica film on
silicon was fabricated by colloidal silica sol. The silica sol precursor
with uniformly granular particle was derived by the alkaline
hydrolysis of tetraethoxyorthosilicate (TEOS) in presence of glycerol
template. The film was prepared by dip coating process. The
templated hetero-structured silica film was annealed at elevated
temperatures to generate nano- and meso porosity in the film. The
film was subsequently annealed at different temperatures to make it
defect free and abrasion resistant. The sol and the film were
characterized by the measurement of particle size distribution,
scanning electron microscopy, XRD, FTIR spectroscopy,
transmission electron microscopy, atomic force microscopy,
measurement of the refractive index, thermal conductivity and
abrasion resistance. The porosity of the films decreased whereas
refractive index and dielectric constant of it `increased with the
increase in the annealing temperature. The thermal conductivity of
the films increased with the increase in the film thickness. The
developed porous silica film holds strong potential for use in
different areas.
Abstract: Water, soil and sediment contaminated with
metolachlor poses a threat to the environment and human health.
We determined the effectiveness of nano-zerovalent iron (NZVI) to
dechlorinate metolachlor [2-chloro-n-(2-ethyl-6-methyl-phenyl)-n-
(1-methoxypropan-2-yl)acetamide] in pH solution and the presence
of aluminium salt. The optimum dosage of degradation of 100 mlL-1
metolachlor was 1% (w/v) NZVI. The degradation kinetic rate (kobs)
was 0.218×10-3 min-1 and specific first-order rates (kSA) was
8.72×10-7 L m-2min-1. By treating aqueous solutions of metolachlor
with NZVI, metolachlor destruction rate were increased as the pH
decrease from 10 to 4. Lowering solution pH removes Fe (III)
passivating layers from the NZVI and makes it free for reductive
transformations. Destruction kinetic rates were 20.8×10-3 min-1 for
pH4, 18.9×10-3 min-1 for pH7, 13.8×10-3 min-1 for pH10. In addition,
destruction kinetic of metolachlor by NZVI was enhanced when
aluminium sulfate was added. The destruction kinetic rate were
20.4×10-3 min-1 for 0.05% Al(SO4)3 and 60×10-3 min-1 for 0.1%
Al(SO4)3.
Abstract: An ecofriendly Citrus paradisipeel extract mediated synthesis of TiO2 nanoparticles is reported under sonication. U.V.-vis, Transmission electron microscopy, Dynamic light scattering, and X-ray analyses are performed to characterize the formation of TiO2 nanoparticles. It is almost spherical in shape, having a size of 60–140 nm and the XRD peaks at 2θ = 25.363° confirm the characteristic facets for anatase form. The synthesized nanocatalyst is highly active in the decomposition of methyl orange (64 mg/L) in sunlight (~73%) for 2.5h.
Abstract: Gold coated silica core nanoparticles have an optical
response dictated by the plasmon resonance. The wavelength at
which the resonance occurs depends on the core and shell sizes,
allowing nanoshells to be tailored for particular applications. The
purposes of this study was to synthesize and use different
concentration of gold nanoshells as exogenous material for skin
tissue soldering and also to examine the effect of laser soldering
parameters on the properties of repaired skin. Two mixtures of
albumin solder and different concentration of gold nanoshells were
prepared. A full thickness incision of 2×20 mm2 was made on the
surface and after addition of mixtures it was irradiated by an 810nm
diode laser at different power densities. The changes of tensile
strength σt due to temperature rise, number of scan (Ns), and scan
velocity (Vs) were investigated. The results showed at constant laser
power density (I), σt of repaired incisions increases by increasing the
concentration of gold nanoshells, Ns and decreasing Vs. It is therefore
important to consider the trade off between the scan velocity and the
surface temperature for achieving an optimum operating condition. In
our case this corresponds to σt =1610 gr/cm2 at I~ 60 Wcm-2, T ~
65ºC, Ns =10 and Vs=0.2mms-1.
Abstract: Oxidative stress makes up common incidents in
eukaryotic metabolism. The presence of diverse components
disturbing the equilibrium during oxygen metabolism increases
oxidative damage unspecifically in living cells. Body´s own
ubiquinone (Q10) seems to be a promising drug in defending the
heightened appearance of reactive oxygen species (ROS). Though, its
lipophilic properties require a new strategy in drug formulation to
overcome their low bioavailability. Consequently, the manufacture of
heterogeneous nanodispersions is in focus for medical applications.
The composition of conventional nanodispersions is made up of a
drug-consisting core and a surfactive agent, also named as surfactant.
Long-termed encapsulation of the surfactive components into tissues
might be the consequence of the use during medical therapeutics. The
potential of provoking side-effects is given by their nonbiodegradable
properties. Further improvements during fabrication
process use the incorporation of biodegradable components such as
modified γ-polyglutamic acid which decreases the potential of
prospective side-effects.
Abstract: Lanthanide-doped upconversion nanoparticles which can convert near-infrared lights to visible lights have attracted growing interest because of their great potentials in fluorescence imaging. Upconversion fluorescence imaging technique with excitation in the near-infrared (NIR) region has been used for imaging of biological cells and tissues. However, improving the detection sensitivity and decreasing the absorption and scattering in biological tissues are as yet unresolved problems. In this present study, a novel NIR-reflected multispectral imaging system was developed for upconversion fluorescent imaging in small animals. Based on this system, we have obtained the high contrast images without the autofluorescence when biocompatible UCPs were injected near the body surface or deeply into the tissue. Furthermore, we have extracted respective spectra of the upconversion fluorescence and relatively quantify the fluorescence intensity with the multispectral analysis. To our knowledge, this is the first time to analyze and quantify the upconversion fluorescence in the small animal imaging.
Abstract: In this study, a nickel film with nano-crystalline grains,
high hardness and smooth surface was electrodeposited using a post
supercritical carbon dioxide (CO2) mixed Watts electrolyte. Although
the hardness was not as high as its Sc-CO2 counterpart, the thin coating
contained significantly less number of nano-sized pinholes. By
measuring the escape concentration of the dissolved CO2 in post
Sc-CO2 mixed electrolyte with the elapsed time, it was believed that
the residue of dissolved CO2 bubbles should closely relate to the
improvement in hardness and surface roughness over its conventional
plating counterpart. Therefore, shortening the duration of
electroplating with the raise of current density up to 0.5 A/cm2 could
effectively retain more post Sc-CO2 mixing effect. This study not only
confirms the roles of dissolved CO2 bubbles in electrolyte but also
provides a potential process to overcome most issues associated with
the cost in building high-pressure chamber for large size products and
continuous plating using supercritical method.