Abstract: Biomass is renewable and sustainable. As an energy source, it will not release extra carbon dioxide into the atmosphere. Hence, tremendous efforts have been made to develop technologies capable of transforming biomass into suitable forms of bio-fuel. One of the viable technologies is gasifying biomass in supercritical water (SCW), a green medium for reactions. While previous studies overwhelmingly selected glucose as a model compound for biomass, the present study adopted fructose for the sake of comparison. The gasification of fructose in SCW was investigated experimentally to evaluate the applicability of supercritical water processes to biomass gasification. Experiments were conducted with an autoclave reactor. Gaseous product mainly consists of H2, CO, CO2, CH4 and C2H6. The effect of two major operating parameters, the reaction temperature (673-873 K) and the dosage of oxidizing agent (0-0.5 stoichiometric oxygen), on the product gas composition, yield and heating value was also examined, with the reaction pressure fixed at 25 MPa.
Abstract: Polymer composite nano-fibers including (1, 3 wt %)
silver nano-particles have been produced by electrospinning method.
Polyacrylonitrile/N,N-dimethylformamide (PAN/DMF) solution have
been prepared and the amount of silver nitrate have been adjusted to
PAN weight. Silver nano-particles were obtained from reduction of
silver ions into silver nano-particles by chemical reduction by
hydrazine hydroxide (N2H5OH). The different amount of silver salt
was loaded into polymer matrix to obtain polyacrylonitrile composite
nano-fiber containing silver nano-particles. The effect of the amount
of silver nano-particles on the properties of composite nano-fiber web
was investigated. Electrical conductivity, mechanical properties,
thermal properties were examined by Microtest LCR Meter 6370
(0.01 mΩ-100 MΩ), Tensile tester, Differential scanning calorimeter
DSC (Q10) and SEM respectively. Also antimicrobial efficiency test
(ASTM E2149-10) was done against to Staphylococcus aureus
bacteria. It has been seen that breaking strength, conductivity,
antimicrobial effect, enthalpy during cyclization increase by use of
silver nano-particles while the diameter of nano-fiber decreases.
Abstract: Nanoscale thermites such as the composite mixture of
nano-sized aluminum and molybdenum trioxide powders possess
several technical advantages such as much higher reaction rate and
shorter ignition delay, when compared to the conventional energetic
formulations made of micron-sized metal and oxidizer particles. In this
study, the self-propagation of combustion wave in compacted pellets
of nanoscale thermite composites is modeled and computationally
investigated by utilizing the activation energy reduction of aluminum
particles due to nanoscale particle sizes. The present computational
model predicts the speed of combustion wave propagation which is
good agreement with the corresponding experiments of thermite
reaction. Also, several characteristics of thermite reaction in nanoscale
composites are discussed including the ignition delay and combustion
wave structures.
Abstract: The protective effect of hesperidin was investigated in
rats exposed to liver injury induced by a single intraperitoneal
injection of cyclophosphamide (CYP) at a dose of 150 mg kg-1.
Hesperidin treatment (100 mg kg-1/day, orally) was applied for seven
days, starting five days before CYP administration. Hesperidin
significantly decreased the CYP-induced elevations of serum alanine
aminotransferase, and hepatic malondialdehyde and myeloperoxidase
activity, significantly prevented the depletion of hepatic glutathione
peroxidase activity resulted from CYP administration. Also,
hesperidin ameliorated the CYP-induced liver tissue injury observed
by histopathological examination. In addition, hesperidin decreased
the CYP-induced expression of inducible nitric oxide synthase, tumor
necrosis factor-α, cyclooxygenase-2, Fas ligand, and caspase-9 in
liver tissue. It was concluded that hesperidin may represent a
potential candidate to protect against CYP-induced hepatotoxicity.
Abstract: We used 24 Ile de France lambs, weighing between 15 and 32 kg (BW). Treatments were supplemented with concentrate: “in nature” sugarcane (IN), sugarcane hydrolyzed using 0.6% calcium oxide (CaO) under aerobic condition (AER), and sugarcane hydrolyzed using 0.6% CaO under anaerobic condition (ANA), constituting a completely randomized design with eight repetitions per treatment. Lambs were housed in individual stalls and fed into the through, allowing 10% of leftovers. Lambs were slaughtered when body weight reached 32 kg. The following parameters were determined on Longissimu lumborum muscle of hot and cold carcasses: pH and color, 45 minutes and 24 hours after slaughtering. Qualitative analysis of the meat were performed in the loins, water-holding capacity (WHC), cooking loss (CL), and shear force (SF). We used a completely randomized design with three treatments and eight repetitions. Means were compared by Tukey test at 5% significance. A higher value for redness (a*) 45 minutes after slaughter (10.48) were found for lambs fed hydrolyzed under anaerobic conditions sugarcane. The other qualitative characteristics of meat were not affected by treatments (P >0.05). The comparison of meat quality resulting from the treatments shows that it is possible to feed in nature sugarcane to lambs, thus waiving hydrolyses process and the spending with alkalizing agent.
Abstract: Ni-based catalysts with different amounts of Na as
promoter from 2 to 6 wt % were prepared by solution combustion
method. The catalytic activity was investigated in syngas methanation
reaction. Carbon oxides conversion and methane selectivity are greatly
influenced by sodium loading. Adding 2 wt% Na remarkably improves
catalytic activity and long-term stability, attributed to its smaller mean
NiO particle size, better distribution, and milder metal-support
interaction. However, excess addition of Na results in deactivation
distinctly due to the blockage of active sites.
Abstract: Zinc borate is an important boron compound that can be used as multi-functional flame retardant additive due to its high dehydration temperature property. In this study, theraw materials of ZnSO4.7H2O, NaOH and H3BO3werecharacterized by X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) and used in the synthesis of zinc borates.The synthesis parameters were set to 100°C reaction temperature and 120 minutes of reaction time, with different molar ratio of starting materials (ZnSO4.7H2O:NaOH:H3BO3). After the zinc borate synthesis, the identifications of the products were conducted by XRD and FT-IR. As a result,Zinc Oxide Borate Hydrate [Zn3B6O12.3.5H2O], were synthesized at the molar ratios of 1:1:3, 1:1:4, 1:2:5 and 1:2:6. Among these ratios 1:2:6 had the best results.
Abstract: Utilizing solar energy in producing electricity can minimize environmental pollution generated by fossil fuel in producing electricity. Our research was base on the extraction of dye from Roystonea regia fruit by using methanol as solvent. The dye extracts were used as sensitizers in Dye-sensitized solar cell (DSSCs). Study was done on the electrical properties from the extracts of Roystonea regia fruit as Dye-sensitized solar cell (DSSCs). The absorptions of the extracts and extracts with dye were determined at different wavelengths (350-1000nm). Absorption peak was observed at 1.339 at wavelength 400nm. The obtained values for methanol extract Roystonea regia extract are, Imp = 0.015mA, Vmp = 12.0mV, fill factor = 0.763, Isc= 0.018 mA and Voc = 13.1 mV and efficiency of 0.32%. .The phytochemical screening was taken and it was observed that Roystonea regia extract contained less of anthocyanin compared to flavonoids. The nanostructured dye sensitized solar cell (DSSC) will provide economically credible alternative to present day silicon p–n junction photovoltaic.
Abstract: This work details the generation of thin films of
structured zeolite catalysts (ZSM–5 and Y) onto the surface of a
metal substrate (FeCrAlloy) using in-situ hydrothermal synthesis. In
addition, the zeolite Y is post-synthetically modified by acidified
ammonium ion exchange to generate US-Y. Finally the catalytic
activity of the structured ZSM-5 catalyst films (Si/Al = 11, thickness
146 0m) and structured US–Y catalyst film (Si/Al = 8, thickness
230m) were compared with the pelleted powder form of ZSM–5 and
USY catalysts of similar Si/Al ratios.
The structured catalyst films have been characterised using a range
of techniques, including X-ray diffraction (XRD), Electron
microscopy (SEM), Energy Dispersive X–ray analysis (EDX) and
Thermogravimetric Analysis (TGA). The transition from oxide-onalloy
wires to hydrothermally synthesised uniformly zeolite coated
surfaces was followed using SEM and XRD. In addition, the
robustness of the prepared coating was confirmed by subjecting these
to thermal cycling (ambient to 550oC).
The cracking of n–heptane over the pellets and structured catalysts
for both ZSM–5 and Y zeolite showed very similar product
selectivities for similar amounts of catalyst with an apparent
activation energy of around 60 kJ mol-1. This paper demonstrates that
structured catalysts can be manufactured with excellent zeolite
adherence and when suitably activated/modified give comparable
cracking results to the pelleted powder forms. These structured
catalysts will improve temperature distribution in highly exothermic
and endothermic catalysed processes.
Abstract: Due to their strong mechanical and thermal properties magnesium borates have a wide usage area such as ceramic industry, detergent production, friction reducing additive and grease production. In this study, microwave synthesis of magnesium borates from MgCl2.6H2O (Magnesium chloride hexahydrate), MgO (Magnesium oxide) and H3BO3 (Boric acid) for different reaction times is researched. X-ray Diffraction (XRD) and Fourier Transform Infrared (FT-IR) Spectroscopy are used to find out how the reaction time sways on the products. The superficial properties are investigated with Scanning Electron Microscopy (SEM). According to XRD analysis, the synthesized compounds are 00-041-1407 pdf coded Shabinite (Mg5(BO3)4Cl2(OH)5.4(H2O)) and 01-073-2158 pdf coded Karlite (Mg7(BO3)3(OH,Cl)5).
Abstract: The research work covered in this study includes the morphological structure and optical properties of TiO2-coated silk fibroin (SF) filters at 2.5% wt. TiO2/vol. PVA solution. SEM micrographs revealed the fibrous morphology of the TiO2-coated SF filters. An average diameter of the SF fiber was estimated to be approximately 10µm. Also, it was confirmed that TiO2 can be adhered more on SF filter surface at higher TiO2 dosages. The activity of semiconductor materials was studied by UV-VIS spectrophotometer method. The spectral data recorded shows the strong cut off at 390 nm. The calculated band-gap energy was about 3.19 eV. The photocatalytic activity of the filter was tested for gaseous formaldehyde removal in a modeling room with the total volume of 2.66 m3. The highest removal efficiency (54.72 ± 1.75%) was obtained at the initial formaldehyde concentration of about 5.00 ± 0.50ppm.
Abstract: Stoneware clay, fired clay (as a grog), calcite waste and class C fly ash in various mixing rations were the basic raw materials for the mixture for production of dry pressed ceramic tiles. Mechanical properties (water absorption, bulk density, apparent porosity, flexural strength) as well as mineralogical composition were studied on samples with different source of calcium oxide after firing at 900, 1000, 1100 and 1200°C. It was found that samples with addition of calcite waste contain dmisteinbergit and anorthite. This minerals help to improve the strength of the body and reduce porosity fired at lower temperatures. Class C fly ash has not significantly influence on properties of the fired body as calcite waste.
Abstract: RF magnetron sputtering is used on the ceramic targets, each of which contains zinc oxide (ZnO), zinc oxide doped with aluminum (AZO) and zinc oxide doped with gallium (GZO). The electric conduction mechanism of the AZO and GZO films came mainly from the Al and Ga, the oxygen vacancies, Zn interstitial atoms, and Al and/or Ga interstitial atoms. AZO and GZO films achieved higher conduction than did ZnO film, it being ion vacant and nonstoichiometric. The XRD analysis showed a preferred orientation along the (002) plane for ZnO, AZO, and GZO films.
Abstract: Depletion and hazardous gas emissions associated
with fossil fuels have caused scientists and global attention to focus
on the use of “alternative, eco-friendly substitutes for use in
Compression Ignition Engines. In this work, biodiesel was produced
by trans-esterification of soybean obtained from a Nigerian market
using Sodium Hydroxide (NaOH) as a catalyst.” After the
production, the physical properties (specific gravity to kinematic
viscosity and net calorific value) of the Soybean-biodiesel produced
and petrol diesel obtained from a filling station in Nigeria were
determined, and these properties conform to conventional standards
(ASTM). A cummins-6V-92TA DDEC diesel (Compression ignition,
CI) engine was run on various biodiesel-petrol diesel blends (0/100,
10/90, 20/80, 30/70 and 40/60), the B20 (blend 20/80) was found to
be the most satisfactory.
Abstract: Construction industry in Greece consumes annually
more than 25 million tons of natural aggregates originating mainly
from quarries. At the same time, more than 2 million tons of
construction and demolition waste are deposited every year, usually
without control, therefore increasing the environmental impact of this
sector. A potential alternative for saving natural resources and
minimize landfilling, could be the recycling and re-use of Concrete
and Demolition Waste (CDW) in concrete production. Moreover, in
order to conform to the European legislation, Greece is obliged to
recycle non-hazardous construction and demolition waste to a
minimum of 70% by 2020. In this paper characterization of recycled
materials - commercially and laboratory produced, coarse and fine,
Recycled Concrete Aggregates (RCA) - has been performed. Namely,
X-Ray Fluorescence and X-ray diffraction (XRD) analysis were used
for chemical and mineralogical analysis respectively. Physical
properties such as particle density, water absorption, sand equivalent
and resistance to fragmentation were also determined. This study,
first time made in Greece, aims at outlining the differences between
RCA and natural aggregates and evaluating their possible influence
in concrete performance. Results indicate that RCA’s chemical
composition is enriched in Si, Al, and alkali oxides compared to
natural aggregates. X-ray diffraction (XRD) analyses results
indicated the presence of calcite, quartz and minor peaks of mica and
feldspars. From all the evaluated physical properties of coarse RCA,
only water absorption and resistance to fragmentation seem to have a
direct influence on the properties of concrete. Low Sand Equivalent
and significantly high water absorption values indicate that fine
fractions of RCA cannot be used for concrete production unless
further processed. Chemical properties of RCA in terms of water
soluble ions are similar to those of natural aggregates. Four different
concrete mixtures were produced and examined, replacing natural
coarse aggregates with RCA by a ratio of 0%, 25%, 50% and 75%
respectively. Results indicate that concrete mixtures containing
recycled concrete aggregates have a minor deterioration of their
properties (3-9% lower compression strength at 28 days) compared to
conventional concrete containing the same cement quantity.
Abstract: In the era of sustainability, utilization of livestock wastes as soil amendment to provide micronutrients for crops is very economical and sustainable. It is well understood that livestock wastes are comparable, if not better, nutrient sources for crops as chemical fertilizers. However, the large concentrated volumes of animal manure produced from livestock operations and the limited amount of available nearby agricultural land areas necessitated the need for volume reduction of these animal wastes. Composting of these animal manures is a viable option for biomass and pathogenic reduction in the environment. Nevertheless, composting also increases the potential loss of available nutrients for crop production as well as unwanted emission of anthropogenic air pollutants due to the loss of ammonia and other compounds via volatilization. In this study, we examine the emission of ammonia and nitrous oxide from swine manure windrows to evaluate the benefit of biomass reduction in conjunction with the potential loss of available nutrients. The feedstock for the windrows was obtained from swine farm in Kentucky where swine manure was mixed with wood shaving as absorbent material. Static flux chambers along with photoacoustic gas analyzer were used to monitor ammonia and nitrous oxide concentrations during the composting process. The results show that ammonia and nitrous oxide fluxes were quite high during the initial composting process and after the turning of each compost pile. Over the period of roughly three months of composting, the biochemical oxygen demand (BOD) decreased by about 90%. Although composting of animal waste is quite beneficial for biomass reduction, composting may not be economically feasible from an agronomical point of view due to time, nutrient loss (N loss), and potential environmental pollution (ammonia and greenhouse gas emissions). Therefore, additional studies are needed to assess and validate the economics and environmental impact of animal (swine) manure composting (e.g., crop yield or impact on climate change).
Abstract: The effect of the modification of ZnO powders by ZrO2, Al2O3, TiO2, SiO2, CeO2 and Y2O3 nanoparticles with a concentration of 1-30 wt % is investigated by diffuse reflectance spectra within the wavelength range 200 to 2500 nm before and after 100 keV proton and electron irradiation. It has been established that the introduction of nanoparticles ZrO2, Al2O3 enhances the optical stability of the pigments under proton irradiation, but reduces it under electron irradiation. Modifying with TiO2, SiO2, CeO2, Y2O3 nanopowders leads to decrease radiation stability in both types of irradiation. Samples modified by 5 wt. % of ZrO2 nanoparticles have the highest stability of optical properties after proton exposure. The degradation of optical properties under electron irradiation is not high for this concentration of nanoparticles. A decrease in the absorption of pigments modified with nanoparticles proton exposure is determined by a decrease in the intensity of bands located in the UV and visible regions. After electron exposure the absorption bands have in the whole spectrum range.
Abstract: Cesiumiodide with Na doping (CsI(Na)) solution or melt is easily forming three- dimension dendrites on the free surface. The defects or bobbles form inside the CsI(Na) during the solution or melt solidification. The defects or bobbles can further effect the x-ray path in the CsI(Na) crystal and decrease the scintillation characteristics of CsI(Na). In order to enhance the CsI(Na) scintillated property we made single crystal of CsI(Na) column in the anodic aluminum oxide (AAO) template by hydraulic pressure injection method. It is interesting that when CsI(Na) melt is confined in the small AAO channels, the column grow as stable single column without any dendrites. The high aspect ratio (100~10000) of AAO and nano to sub-micron channel structure which is a suitable template for single of crystal CsI(Na) formation. In this work, a new low-cost approach to fabricate scintillator crystals using anodic aluminum oxide (AAO) rather than Si is reported, which can produce scintillator crystals with a wide range of controllable size to optimize their performance in X-ray detection.
Abstract: A mathematical heat transfer model for the prediction of transient heating of the slab in a direct-fired walking beam type reheating furnace has been developed by considering the nongray thermal radiation with given furnace environments. The furnace is modeled as radiating nongray medium with carbon dioxide and water with five-zoned gas temperature and the furnace wall is considered as a constant temperature lower than furnace gas one. The slabs are moving with constant velocity depending on the residence time through the non-firing, charging, preheating, heating, and final soaking zones. Radiative heat flux obtained by considering the radiative heat exchange inside the furnace as well as convective one from the surrounding hot gases are introduced as boundary condition of the transient heat conduction within the slab. After validating thermal radiation model adopted in this work, thermal fields in both model and real reheating furnace are investigated in terms of radiative heat flux in the furnace and temperature inside the slab. The results show that the slab in the furnace can be more heated with higher slab emissivity and residence time.
Abstract: In this study, fish bone waste was used as a new
catalyst for biodiesel production. Instead of discarding the fish bone
waste, it will be utilized as a source for catalyst that can provide
significant benefit to the environment. Also, it can be substitute as a
calcium oxide source instead of using eggshell, crab shell and snail
shell. The XRD and SEM analysis proved that calcined fish bone
contains calcium oxide, calcium phosphate and hydroxyapatite. The
catalyst was characterized using Scanning Electron Microscope
(SEM) and X-ray Diffraction (XRD).