Abstract: Solar-light activated titanium dioxide photocatalysts were prepared by hydrolysis of titanium (IV) isopropoxide with thiourea, followed by calcinations at 450 °C. The experiments demonstrated that methyl orange in aqueous solutions were successfully degraded under solar light using doped TiO2. The photocatalytic oxidation of a mono azo methyl-orange dye has been investigated in multi ion doped TiO2 and solar light. Solutions were irradiated by solar-light until high removal was achieved. It was found that there was no degradation of methyl orange in the dark and in the absence of TiO2. Varieties of laboratory prepared TiO2 catalysts both un-doped and doped using titanium (IV) isopropoxide and thiourea as a dopant were tested in order to compare their photoreactivity. As a result, it was found that the efficiency of the process strongly depends on the working conditions. The highest degradation rate of methyl orange was obtained at optimum dosage using commercially produced TiO2. Our work focused on laboratory synthesized catalyst and the maximum methyl orange removal was achieved at 81% with catalyst loading of 0.04 g/L, initial pH of 3 and methyl orange concentration of 0.005 g/L using multi-ion doped catalyst. The kinetics of photocatalytic methyl orange dye stuff degradation was found to follow a pseudo-first-order rate law. The presence of the multi-ion dopant (thiourea) enhanced the photoefficiency of the titanium dioxide catalyst.
Abstract: Nanofibers of PVA /nickel nitrate/silica/alumina
izopropoxide/boric acid composite were prepared by using sol-gel
processing and electrospinning technique. By high temperature
calcinations of the above precursor fibers, nanofibers of
NiO/Al2O3/B2O3/SiO2 composite with diameters about 500 nm
could be successfully obtained. The fibers were characterized by
XRD and SEM analyses.
Abstract: In this study, fish bone waste was used as a new
catalyst for biodiesel production. Instead of discarding the fish bone
waste, it will be utilized as a source for catalyst that can provide
significant benefit to the environment. Also, it can be substitute as a
calcium oxide source instead of using eggshell, crab shell and snail
shell. The XRD and SEM analysis proved that calcined fish bone
contains calcium oxide, calcium phosphate and hydroxyapatite. The
catalyst was characterized using Scanning Electron Microscope
(SEM) and X-ray Diffraction (XRD).
Abstract: In this study, ZnO nano rods and ZnO ultrafine particles were synthesized by Gel-casting method. The synthesized ZnO powder has a hexagonal zincite structure. The ZnO aggregates with rod-like morphology are typically 1.4 μm in length and 120 nm in diameter, which consist of many small nanocrystals with diameters of 10 nm. Longer wires connected by many hexahedral ZnO nanocrystals were obtained after calcinations at the temperature over 600° C.The crystalline structures and morphologies of the powder have been characterized by X-ray diffraction(XRD) and Scaning electron microscopy (SEM).The result shows that the different preparation conditions such as concentration H2O, calcinations time and calcinations temperature have a lot of influences upon the properties of nano ZnO powders, an increase in the temperature of the calcinations results in an increase of the grain size and also the increase of the calcinations time in high temperature makes the size of the grains bigger. The existences of extra watter prevent nano grains from improving like rod morphology. We have obtained the smallest grain size of ZnO powder by controlling the process conditions. Finally In a suitable condition, a novel nanostructure, namely bi-rod-like ZnO nano rods was found which is different from known ZnO nanostructures.
Abstract: This work presents the hydrogen production from
steam gasification of palm kernel shell (PKS) at 700 oC in the
presence of 5% Ni/BEA and 5% Fe/BEA as catalysts. The steam
gasification was performed in two-staged reactors to evaluate the
effect of calcinations temperature and the steam to biomass ratio on
the product gas composition. The catalytic activity of Ni/BEA
catalyst decreases with increasing calcinations temperatures from 500
to 700 oC. The highest H2 concentration is produced by Fe/BEA
(600) with more than 71 vol%. The catalytic activity of the catalysts
tested is found to correspond to its physicochemical properties. The
optimum range for steam to biomass ratio if found to be between 2 to
4. Excess steam content results in temperature drop in the gasifier
which is undesirable for the gasification reactions.
Abstract: The principal objective of this study is to be able to
extract niobium oxide from columbite-tantalite concentrate of Thayet
Kon Area in Nay Phi Taw. It is recovered from columbite-tantalite
concentrate which contains 19.29 % Nb2O5.The recovery of niobium
oxide from columbite-tantalite concentrate can be divided into three
main sections, namely, digestion of the concentrate, recovery from
the leached solution and precipitation and calcinations. The
concentrate was digested with hydrofluoric acid and sulfuric acid. Of
the various parameters that effect acidity and time were studied. In
the recovery section solvent extraction process using methyl isobutyl
ketone was investigated. Ammonium hydroxide was used as a
precipitating agent and the precipitate was later calcined. The
percentage of niobium oxide is 74%.