Abstract: In this study, the precipitation conditions of Chevreul’s salt were evaluated. The structure of Chevreul’s salt was examined by considering the previous studies. Thermodynamically, the most important precipitation parameters were pH, temperature, and sulphite-copper(II) ratio. The amount of Chevreul’s salt increased with increasing the temperature and sulphite-copper(II) ratio at the certain range, while it increased with decreasing the pH value at the chosen range. The best solution medium for recovery of Chevreul’s salt is sulphur dioxide gas-water system. Moreover, the soluble sulphite salts are used as efficient precipitating reagents. Chevreul’s salt is generally used to produce the highly pure copper powders from synthetic copper sulphate solutions and impure leach solutions. When the pH of the initial ammoniacal solution is greater than 8.5, ammonia in the medium is not free, and Chevreul’s salt from solution does not precipitate. In contrast, copper ammonium sulphide is precipitated. The pH of the initial solution containing ammonia for precipitating of Chevreul’s salt must be less than 8.5.
Abstract: In this study, Pb2+ uptake by the hydroxyapatite nanopowders (n-Hap) from aqueous solutions was investigated by using batch adsorption techniques. The adsorption equilibrium studies were carried out as a function of contact time, adsorbent dosage, pH, temperature, and initial Pb2+ concentration. The results showed that the equilibrium time of adsorption was achieved within 60 min, and the effective pH was selected to be 5 (natural pH). The maximum adsorption capacity of Pb2+ on n-Hap was found as 565 mg.g-1. It is believed that the results obtained for adsorption may provide a background for the detailed mechanism investigations and the pilot and industrial scale applications.
Abstract: In this study, Chevreul’s salt was dissolved in ammonium chloride solutions. All experiments were performed in a batch reactor. The obtained results were optimized. Parameters used in the experiments were the reaction temperature, the ammonium chloride concentration, the reaction time and the solid-to-liquid ratio. The optimum conditions were determined by 24 factorial experimental design method. The best values of four parameters were determined as based on the experiment results. After the evaluation of experiment results, all parameters were found as effective in experiment conditions selected. The optimum conditions on the maximum Chevreul’s salt dissolution were the ammonium chloride concentration 4.5 M, the reaction time 13.2 min., the reaction temperature 25 oC, and the solid-to-liquid ratio 9/80 g.mL-1. The best dissolution yield in these conditions was 96.20%.
Abstract: The aim of the present study was to investigate the dissolution kinetics of ulexite in sodium dihydrogen phosphate in a mechanical agitation system and also to declare an alternative reactant to produce the boric acid. Reaction temperature, concentration of sodium dihydrogen phosphate, stirring speed, solid-liquid ratio, and ulexite particle size were selected as parameters. The experimental results were successfully correlated by using linear regression and a statistical program. Dissolution curves were evaluated in order to test the shrinking core models for solid-fluid systems. It was observed that increase in the reaction temperature and decrease in the solid/liquid ratio causes an increase in the dissolution rate of ulexite. The activation energy was found to be 36.4 kJ/mol. The leaching of ulexite was controlled by diffusion through the ash (or product) layer.
Abstract: Ulexite (Na2O.2CaO.5B2O3.16H2O) is boron mineral
that is found in large quantities in the Turkey and world. In this
study, the dissolution of this mineral in the disodium hydrogen
phosphate solutions has been studied. Temperature, concentration,
stirring speed, solid liquid ratio and particle size were selected as
parameters. The experimental results were successfully correlated by
linear regression using Statistica program. Dissolution curves were
evaluated shrinking core models for solid-fluid systems. It was
observed that increase in the reaction temperature and decrease in the
solid/liquid ratio causes an increase the dissolution rate of ulexite.
The activation energy was found to be 63.4 kJ/mol. The leaching of
ulexite was controlled by chemical reaction.
Abstract: Experimental production methods of Chevreul’s salt
being an intermediate stage product in copper recovery were
investigated on this article. Chevreul’s salt, Cu2SO3.CuSO3.2H2O,
being a mixed valence copper sulphite compound, has been obtained
by using different methods and reagents. Chevreul’s salt has an
intense brick-red color. It is highly stable and expensive. The
production of Chevreul’s salt plays a key role in hydrometallurgy.
Thermodynamic tendency on precipitation of Chevreul’s salt is
related to pH and temperature. Besides, SO2 gaseous is a versatile
reagent for precipitating of copper sulphites, Using of SO2 for
selective precipitation can be made by appropriate adjustments of pH
and temperature. Chevreul’s salt does not form in acidic solutions if
those solutions contains considerable amount of sulfurous acid. It is
necessary to maintain between pH 2–4.5, because, solubility of
Chevreul’s salt increases with decreasing of pH values. Also, the
region which Chevreul’s salt is stable can be seen from the potentialpH
diagram.
Abstract: Nanofibers of PVA /nickel nitrate/silica/alumina
izopropoxide/boric acid composite were prepared by using sol-gel
processing and electrospinning technique. By high temperature
calcinations of the above precursor fibers, nanofibers of
NiO/Al2O3/B2O3/SiO2 composite with diameters about 500 nm
could be successfully obtained. The fibers were characterized by
XRD and SEM analyses.
Abstract: Gypsum (CaSO4.2H2O) is a mineral that is found in
large quantities in the Turkey and in the World. In this study, the
dissolution of this mineral in the diammonium hydrogen phosphate
solutions has been studied. The dissolution and dissolution kinetics of
gypsum in diammonium hydrogen phosphate solutions will be useful
for evaluating of solid wastes containing gypsum. Parameters such as
diammonium hydrogen phosphate concentration, temperature and
stirring speed affecting on the dissolution rate of the gypsum in
diammonium hydrogen phosphate solutions were investigated. In
experimental studies have researched effectiveness of the selected
parameters. The dissolution of gypsum were examined in two parts at
low and high temperatures. The experimental results were
successfully correlated by linear regression using Statistica program.
Dissolution curves were evaluated shrinking core models for solidfluid
systems. The activation energy was found to be 34.58 kJ/mol
and 44.45 kJ/mol for the low and the high temperatures. The
dissolution of gypsum was controlled by chemical reaction both low
temperatures and high temperatures.