Abstract: Zinc borates are used as a multi-functional flame
retardant additive for its high dehydration temperature. In this study,
the method of ultrasonic mixing was used in the synthesis of zinc
borates. The reactants of zinc oxide (ZnO) and boric acid (H3BO3)
were used at the constant reaction parameters of 90°C reaction
temperature and 55 min of reaction time. Several molar ratios of
ZnO:H3BO3 (1:1, 1:2, 1:3, 1:4 and 1:5) were conducted for the
determination of the optimum reaction ratio. Prior to synthesis the
characterization of the synthesized zinc borates were made by X-Ray
Diffraction (XRD) and Fourier Transform Infrared Spectroscopy
(FT-IR). From the results Zinc Oxide Borate Hydrate
[Zn3B6O12.3.5H2O], were synthesized optimum at the molar ratio of
1:3, with a reaction efficiency of 95.2%.
Abstract: Potassium borates, which are widely used in welding
and metal refining industry, as a lubricating oil additive, cement
additive, fiberglass additive and insulation compound, are one of the
important groups of borate minerals. In this study the production of a
potassium borate mineral via hydrothermal method is aimed. The
potassium source of potassium nitrate (KNO3) was used along with a
sodium source of sodium hydroxide (NaOH) and boron source of
boric acid (H3BO3). The constant parameters of reaction temperature
and reaction time were determined as 80°C and 1 h, respectively. The
molar ratios of 1:1:3 (as KNO3:NaOH:H3BO3), 1:1:4, 1:1:5, 1:1:6
and 1:1:7 were used. Following the synthesis the identifications of
the produced products were conducted by X-Ray Diffraction (XRD),
Fourier Transform Infrared Spectroscopy (FT-IR) and Raman
Spectroscopy. The results of the experiments and analysis showed in
the ratio of 1:1:6, the Santite mineral with powder diffraction file
number (pdf no.) of 01-072-1688, which is known as potassium
pentaborate (KB5O8·4H2O) was synthesized as best.
Abstract: Due to their strong mechanical and thermal properties magnesium borates have a wide usage area such as ceramic industry, detergent production, friction reducing additive and grease production. In this study, microwave synthesis of magnesium borates from MgCl2.6H2O (Magnesium chloride hexahydrate), MgO (Magnesium oxide) and H3BO3 (Boric acid) for different reaction times is researched. X-ray Diffraction (XRD) and Fourier Transform Infrared (FT-IR) Spectroscopy are used to find out how the reaction time sways on the products. The superficial properties are investigated with Scanning Electron Microscopy (SEM). According to XRD analysis, the synthesized compounds are 00-041-1407 pdf coded Shabinite (Mg5(BO3)4Cl2(OH)5.4(H2O)) and 01-073-2158 pdf coded Karlite (Mg7(BO3)3(OH,Cl)5).