Abstract: In this research, waterglass based aerogel powder was
prepared by sol–gel process and ambient pressure drying. Inspired by
limited dust releasing, aerogel powder was introduced to the PET
electrospinning solution in an attempt to create required bulk and
surface structure for the nanofibers to improve their hydrophobic and
insulation properties. The samples evaluation was carried out by
measuring density, porosity, contact angle, heat transfer, FTIR, BET,
and SEM. According to the results, porous silica aerogel powder was
fabricated with mean pore diameter of 24 nm and contact angle of
145.9º. The results indicated the usefulness of the aerogel powder
confined into nanofibers to control surface roughness for
manipulating superhydrophobic nanowebs with water contact angle
of 147º. It can be due to a multi-scale surface roughness which was
created by nanowebs structure itself and nanofibers surface
irregularity in presence of the aerogels while a layer of fluorocarbon
created low surface energy. The wettability of a solid substrate is an
important property that is controlled by both the chemical
composition and geometry of the surface. Also, a decreasing trend in
the heat transfer was observed from 22% for the nanofibers without
any aerogel powder to 8% for the nanofibers with 4% aerogel
powder. The development of thermal insulating materials has become
increasingly more important than ever in view of the fossil energy
depletion and global warming that call for more demanding energysaving
practices.
Abstract: Two types of glass fibers having different lengths
(1/16" and 1/32") were added into rigid PVC foams to enhance the
dimensional stability of extruded rigid Polyvinyl Chloride (PVC)
foam at different concentrations (0-20 phr) using a single screw
profile extruder. PVC foam-glass fiber composites (PVC-GF) were
characterized for their dimensional stability, structural, thermal, and
mechanical properties. Experimental results show that the
dimensional stability, heat resistance, and storage modulus were
enhanced without compromising the tensile and flexural strengths of
the composites. Overall, foam composites which were prepared with
longer glass fibers exhibit better mechanical and thermal properties
than those prepared with shorter glass fibers due to higher
interlocking between the fibers and the foam cells, which result in
better load distribution in the matrix.
Abstract: Two Lithium Disilicate (LD) glass ceramics based on
SiO2-Li2O-K2O-Al2O3 system were prepared through a glass melting
method. The glass rods were then fabricated into dental crowns via a
hot pressing at 900˚C and 850˚C in order to study the effect of the
pressing temperatures on the phase formation and microstructure of
the glasses. Different samples of as cast glass and heat treated
samples (600˚C and 700˚C) were used to press for investigating the
effect of an initial microstructure on the hot pressing technique. Xray
diffraction (XRD) and scanning electron microscopy (SEM) were
performed to determine the phase formation and microstructure of the
samples, respectively. XRD results show that the main crystalline
structure was Li2Si2O5 by having Li3PO4, Li0.6Al0.6Si2O6, Li2SiO3,
Ca5 (PO4)3F and SiO2 as minor phases. Glass compositions with
different heat treatment temperatures exhibited a difference phase
formations but have less effect during pressing. SEM micrographs
showed the microstructure of Li2Si2O5 as lath-like shape in all
glasses. With increasing the initial heat treatment temperature, the
longer the lath-like crystals of lithium disilicate were increased
especially when using glass heat treatment at 700˚C followed by
pressing at 900˚C. This could be suggested that LD1 heat treatment at
700˚C which pressing at 900˚C presented the best formation by the
hot pressing and compiled microstructure.
Abstract: This paper illustrates the effect of nano Magnesium
Hydroxide (MH) loading on the thermal properties of Low Density
Polyethylene (LDPE)/Poly (ethylene-co vinyl acetate) (EVA) nano
composite. Thermal studies were conducted, as it understanding is
vital for preliminary development of new polymeric systems.
Thermal analysis of nanocomposite was conducted using thermo
gravimetric analysis (TGA), and differential scanning calorimetry
(DSC). Major finding of TGA indicated two main stages of
degradation process found at (350 ± 25oC) and (480 ± 25oC)
respectively. Nano metal filler expressed better fire resistance as it
stand over high degree of temperature. Furthermore, DSC analysis
provided a stable glass temperature around 51 (±1oC) and captured
double melting point at 84 (±2oC) and 108 (±2oC). This binary
melting point reflects the modification of nano filler to the polymer
matrix forming melting crystals of folded and extended chain. The
percent crystallinity of the samples grew vividly with increasing filler
content. Overall, increasing the filler loading improved the
degradation temperature and weight loss evidently and a better
process and phase stability was captured in DSC.
Abstract: This paper reports the numerical and experimental
performances of Double Glass Wall are investigated. Two
configurations were considered namely, the Double Clear Glass Wall
(DCGW) and the Double Translucent Glass Wall (DTGW). The
coupled governing equations as well as boundary conditions are
solved using the finite element method (FEM) via COMSOLTM
Multiphysics. Temperature profiles and flow field of the DCGW and
DTGW are reported and discussed. Different constant heat fluxes
were considered as 400 and 800 W.m-2 the corresponding initial
condition temperatures were 30.5 and 38.5ºC respectively. The
results show that the simulation results are in agreement with the
experimental data. Conclusively, the model considered in this study
could reasonable be used simulate the thermal and ventilation
performance of the DCGW and DTGW configurations.
Abstract: This paper contains 2 main parts. In the first part of paper we simulated and studied three types of electrode patterns used in various industries for suspension and handling of the semiconductor and glass and we selected the best pattern by evaluating the electrostatic force, which was comb pattern electrode.
In the second part we investigated the parameters affecting the amount of electrostatic force such as the gap between surface and electrode (g), the electrode width (w), the gap between electrodes (t), the surface permittivity and electrode length and methods of improvement of adhesion force by changing these values.
Abstract: The detection of environmental gases, 12CO2, 13CO2,
and CH4, using near-infrared semiconductor lasers with a short
laser path length is studied by means of wavelength-modulation
spectroscopy. The developed system is compact and has high
sensitivity enough to detect the absorption peaks of isotopic 13CO2
of a 3-% CO2 gas at 2 μm with a path length of 2.4 m, where
its peak size is two orders of magnitude smaller than that of the
ordinary 12CO2 peaks. In addition, the detection of 12CO2 peaks of
a 385-ppm (0.0385-%) CO2 gas in the air is made at 2 μm with a
path length of 1.4 m. Furthermore, in pursuing the detection of an
ancient environmental CH4 gas confined to a bubble in ice at the
polar regions, measurements of the absorption spectrum for a trace
gas of CH4 in a small area are attempted. For a 100-% CH4 gas
trapped in a ∼ 1 mm3 glass container, the absorption peaks of CH4
are obtained at 1.65 μm with a path length of 3 mm, and also the
gas pressure is extrapolated from the measured data.
Abstract: Novel bio-based polymer electrolyte was synthesized
with LiClO4 as the main source of charge carrier. Initially,
polyurethane-LiClO4 polymer electrolytes were synthesized via
prepolymerization method with different NCO/OH ratios and labelled
them as PU1, PU2, PU3 and PU4. Fourier transform infrared (FTIR)
analysis indicates the co-ordination between Li+ ion and polyurethane
in PU1. Differential scanning calorimetry (DSC) analysis indicates
PU1 has the highest glass transition temperature (Tg) corresponds to
the most abundant urethane group which is the hard segment in PU1.
Scanning electron microscopy (SEM) shows the good miscibility
between lithium salt and the polymer. The study found that PU1
possessed the greatest ionic conductivity and the lowest activation
energy, Ea. All the polyurethanes exhibited linear Arrhenius
variations indicating ion transport via simple lithium ion hopping in
polyurethane. This research proves the NCO content in polyurethane
plays an important role in affecting the ionic conductivity of this
polymer electrolyte.
Abstract: In order to efficiently solve the problems created by the deepening energy crisis affecting Europe and the world,
governments cannot neglect the opportunities of using the energy
produced by sun collectors. In many of the EU countries there are sun
collectors producing heat energy, e.g. in 2011 in the area of EU27
(countries which belong to European Union) + Switzerland altogether
37519126 m2 were operated, which are capable of producing 26.3
GWh heat energy. The energy produced by these sun collectors is
utilized at the place of production. In the near future governments
will have to focus more on spreading and using sun collectors.
Among the complex problems of operating sun collectors, this article
deals with determining the optimal tilt angle, directions of sun
collectors. We evaluate the contamination of glass surface of sun
collector to the produced energy. Our theoretically results are confirmed by laboratory measurements. The purpose of our work is to help users and engineers in determination of optimal operation
parameters of sun collectors.
Abstract: In this study, first thermoplastic composite materials
/plates that have high ballistic impact resistance were produced. For
this purpose, the thermoplastic prepreg and the vacuum bagging
technique were used to produce a composite material. Thermoplastic
prepregs (resin-impregnated fiber) that are supplied ready to be used,
namely high-density polyethylene (HDPE) was chosen as matrix and
unidirectional glass fiber was used as reinforcement. In order to
compare the fiber configuration effect on mechanical properties,
unidirectional and biaxial prepregs were used. Then the
microstructural properties of the composites were investigated with
scanning electron microscopy (SEM) analysis. Impact properties of
the composites were examined by Charpy impact test and tensile
mechanical tests and then the effects of ultraviolet irradiation were
investigated on mechanical performance.
Abstract: Composite materials have important assets compared
to traditional materials. They bring many functional advantages:
lightness, mechanical resistance and chemical, etc. In the present
study we examine the effect of a circular central notch and a precrack
on the tensile fracture of two woven composite materials. The tensile
tests were applied to a standardized specimen, notched and a
precarcked (orientation of the crack 0°, 45° and 90°). These tensile
tests were elaborated according to an experimental planning design of
the type 23.31 requiring 24 experiments with three repetitions. By the
analysis of regression, we obtained a mathematical model describing
the maximum load according to the influential parameters (hole
diameter, precrack length, angle of a precrack orientation). The
specimens precracked at 90° have a better behavior than those having
a precrack at 45° and still better than those having of the precracks
oriented at 0°. In addition the maximum load is inversely
proportional to the notch size.
Abstract: The effect of various humidities on process yields and
degrees of crystallinity for spray-dried powders from spray drying of
lactose with humid air in a straight-through system have been
studied. It has been suggested by Williams–Landel–Ferry kinetics
(WLF) that a higher particle temperature and lower glass-transition
temperature would increase the crystallization rate of the particles
during the spray-drying process. Freshly humidified air produced by
a Buchi-B290 spray dryer as a humidifier attached to the main spray
dryer decreased the particle glass-transition temperature (Tg), while
allowing the particle temperature (Tp) to reach higher values by using
an insulated drying chamber. Differential scanning calorimetry
(DSC) and moisture sorption analysis were used to measure the
degree of crystallinity for the spray-dried lactose powders. The
results showed that higher Tp-Tg, as a result of applying humid air,
improved the process yield from 21 ± 4 to 26 ± 2% and crystallinity
of the particles by decreasing the latent heat of crystallization from
43 ± 1 to 30 ± 11 J/g and the sorption peak height from 7.3 ± 0.7% to
6 ± 0.7%.
Abstract: In this paper, sodium borosilicates glasses were prepared by melting in air. These heat-resistant transparent glasses have subjected subsequently isothermal treatments at different times, which have transformed them at opaque glass (milky white color). Such changes indicate that these glasses showed clearly phase separation (immiscibility). The immiscibility region in a sodium borosilicate ternary system was investigated in this work, i.e. to determine the regions from which some compositions can show phase separation. For this we went through the conditions of thermodynamic equilibrium, which were translated later by mathematical equations to find an approximate solution. The latter has been translated in a simulation which was established thereafter to find the immiscibility regions in this type of special glasses.
Abstract: The design of an optimised horizontal axis 5-meter-long wind turbine rotor blade in according with IEC 61400-2 standard is a research and development project in order to fulfil the requirements of high efficiency of torque from wind production and to optimise the structural components to the lightest and strongest way possible. For this purpose, a research study is presented here by focusing on the structural characteristics of a composite wind turbine blade via finite element modelling and analysis tools. In this work, first, the required data regarding the general geometrical parts are gathered. Then, the airfoil geometries are created at various sections along the span of the blade by using CATIA software to obtain the two surfaces, namely; the suction and the pressure side of the blade in which there is a hat shaped fibre reinforced plastic spar beam, so-called chassis starting at 0.5m from the root of the blade and extends up to 4 m and filled with a foam core. The root part connecting the blade to the main rotor differential metallic hub having twelve hollow threaded studs is then modelled. The materials are assigned as two different types of glass fabrics, polymeric foam core material and the steel-balsa wood combination for the root connection parts. The glass fabrics are applied using hand wet lay-up lamination with epoxy resin as METYX L600E10C-0, is the unidirectional continuous fibres and METYX XL800E10F having a tri-axial architecture with fibres in the 0,+45,-45 degree orientations in a ratio of 2:1:1. Divinycell H45 is used as the polymeric foam. The finite element modelling of the blade is performed via MSC PATRAN software with various meshes created on each structural part considering shell type for all surface geometries, and lumped mass were added to simulate extra adhesive locations. For the static analysis, the boundary conditions are assigned as fixed at the root through aforementioned bolts, where for dynamic analysis both fixed-free and free-free boundary conditions are made. By also taking the mesh independency into account, MSC NASTRAN is used as a solver for both analyses. The static analysis aims the tip deflection of the blade under its own weight and the dynamic analysis comprises normal mode dynamic analysis performed in order to obtain the natural frequencies and corresponding mode shapes focusing the first five in and out-of-plane bending and the torsional modes of the blade. The analyses results of this study are then used as a benchmark prior to modal testing, where the experiments over the produced wind turbine rotor blade has approved the analytical calculations.
Abstract: In this study, the Mo-electrode thin films were deposited using two-stepped process and the high purity copper indium selenide-based powder (CuInSe2, CIS) was fabricated by using hydrothermal process by Nanowin Technology Co. Ltd. Because the CIS powder was aggregated into microscale particles, the CIS power was ground into nano-scale particles. 6 wt% CIS particles were mixed and dispersed into isopropyl alcohol (IPA). A new non-vacuum thin-film deposition process, spray coating method (SPM), was investigated to deposit the high-densified CIS absorber layers. 0.1 ml CIS solution was sprayed on the 20 mm×10 mm Mo/glass substrates and then the CuInSe2 thin films were annealed in a selenization furnace using N2 as atmosphere. The annealing temperature and time were set at 550oC and 5 min, and 0.0g~0.6g extra Se content was added in the furnace. The influences of extra Se content on the densification, crystallization, resistivity (ρ), hall mobility (μ), and carrier concentration of the CIS absorber layers were well investigated in this study.
Abstract: The paper reports on the subject of recycling and
further use of secondary raw materials obtained from solar panels,
which is becoming a very up to date topic in recent years. Recycling
these panels is very difficult and complex, and the use of resulting
secondary raw materials is still not fully resolved. Within the
research carried out at the Brno University of Technology, new
polymer materials used for industrial floors are being developed.
Secondary raw materials are incorporated into these polymers as
fillers. One of the tested filler materials was glass obtained from solar
panels. The following text describes procedures and results of the
tests that were performed on these materials, confirming the
possibility of the use of solar panel glass in industrial polymer
flooring systems.
Abstract: When insulation and rehabilitation of structures is important to use quality building materials with high utility value. One potentially interesting and promising groups of construction materials in this area are advanced, thermally insulating plaster silicate based. With the present trend reduction of energy consumption of building structures and reducing CO2 emissions to be developed capillary-active materials that are characterized by their low density, low thermal conductivity while maintaining good mechanical properties.
The paper describes the results of research activities aimed at the development of thermal insulating and rehabilitation material ongoing at the Technical University in Brno, Faculty of Civil Engineering. The achieved results of this development will be the basis for subsequent experimental analysis of the influence of thermal and moisture loads developed on these materials.
Abstract: The work involves develops attended by a numerical
execution of the eXtend Finite Element Method premises a
measurement by the fracture process cracked so many cracked plates
an application will be processed for the calculation of the stress
intensity factor SIF. In the first we give in statically part the
distribution of stress, displacement field and strain of composite plate
in two cases uncrack/edge crack, also in dynamical part the first six
modes shape. Secondly, we calculate Stress Intensity Factor SIF for
different orientation angle θ of central crack with length (2a=0.4mm)
in plan strain condition, KI and KII are obtained for mode I and mode
II respectively using X-FEM method. Finally from crack inclined
involving mixed modes results, the comparison we chose dangerous
inclination and the best crack angle when K is minimal.
Abstract: In this study was performed in situ consolidation of polypropylene matrix/glass reinforced roving by combining heating systems and roll pressing. The commingled roving during hoop winding was winded on a cylindrical mandrel. The work also presents the advances made in the processing of these materials into composites by conventional technique filament winding. Experimental studies were performed with changing parameters – temperature, pressure and speed. Finally, it describes the investigation of the optimal processing conditions that maximize the mechanical properties of the composites. These properties are good enough for composites to be used as engineering materials in many structural applications.
Abstract: Natural plant fibres reinforced polymeric composite materials have been used in many fields of our lives to save the environment. Especially, bamboo fibres due to its environmental sustainability, mechanical properties, and recyclability have been utilized as reinforced polymer matrix composite in construction industries. In this review study bamboo structure and three different methods such as mechanical, chemical and combination of mechanical and chemical to extract fibres from bamboo are summarized. Each extraction method has been done base on the application of bamboo. In addition Bamboo fibre is compared with glass fibre from various aspects and in some parts it has advantages over the glass fibre.