Abstract: In this study, the Mo-electrode thin films were deposited using two-stepped process and the high purity copper indium selenide-based powder (CuInSe2, CIS) was fabricated by using hydrothermal process by Nanowin Technology Co. Ltd. Because the CIS powder was aggregated into microscale particles, the CIS power was ground into nano-scale particles. 6 wt% CIS particles were mixed and dispersed into isopropyl alcohol (IPA). A new non-vacuum thin-film deposition process, spray coating method (SPM), was investigated to deposit the high-densified CIS absorber layers. 0.1 ml CIS solution was sprayed on the 20 mm×10 mm Mo/glass substrates and then the CuInSe2 thin films were annealed in a selenization furnace using N2 as atmosphere. The annealing temperature and time were set at 550oC and 5 min, and 0.0g~0.6g extra Se content was added in the furnace. The influences of extra Se content on the densification, crystallization, resistivity (ρ), hall mobility (μ), and carrier concentration of the CIS absorber layers were well investigated in this study.
Abstract: In this study, a new criterion for determining the number of classes an image should be segmented is proposed. This criterion is based on discriminant analysis for measuring the separability among the segmented classes of pixels. Based on the new discriminant criterion, two algorithms for recursively segmenting the image into determined number of classes are proposed. The proposed methods can automatically and correctly segment objects with various illuminations into separated images for further processing. Experiments on the extraction of text strings from complex document images demonstrate the effectiveness of the proposed methods.1