Abstract: Plastic as an environmental burden is a well-rehearsed topic in the research area. This is due to its global demand and destructive impacts on the environment, which has been a significant concern to the governments. Typically, the use of plastic in the construction industry is seen across low-density, non-structural applications due to its diverse range of benefits including high strength-to-weight ratios, manipulability and durability. It can be said that with the level of plastic consumption experienced in the construction industry, an ongoing responsibility is shown for this sector to continually innovate alternatives for application of recycled plastic waste such as using plastic made replacement from polyethylene, polystyrene, polyvinyl and polypropylene in the concrete mix design. In this study, the impact of partially replaced fine aggregate with polypropylene in the concrete mix design was investigated to evaluate the concrete’s compressive strength by conducting an experimental work which comprises of six concrete mix batches with polypropylene replacements ranging from 0.5 to 3.0%. The results demonstrated a typical decline in the compressive strength with the addition of plastic aggregate, despite this reduction generally mitigated as the level of plastic in the concrete mix increased. Furthermore, two of the six plastic-containing concrete mixes tested in the current study exceeded the ST5 standardised prescribed concrete mix compressive strength requirement at 28-days containing 1.50% and 2.50% plastic aggregates, which demonstrated the potential for use of recycled polypropylene in structural applications, as a partial by mass, fine aggregate replacement in the concrete mix.
Abstract: This paper presents the results of an experimental investigation carried out to evaluate the effects of partial replacement of cement and fine aggregate with industrial waste by-products on concrete strength properties. The Grey Taguchi approach has been used to optimize the mix proportions for desired properties. In this research work, a ternary combination of industrial waste by-products has been used. The experiments have been designed using Taguchi's L9 orthogonal array with four factors having three levels each. The cement was partially replaced by ladle furnace slag (LFS), fly ash (FA) and copper slag (CS) at 10%, 25% and 40% level and fine aggregate (sand) was partially replaced with electric arc furnace slag (EAFS), iron slag (IS) and glass powder (GP) at 20%, 30% and 40% level. Three water to binder ratios, fixed at 0.40, 0.44 and 0.48, were used, and the curing age was fixed at 7, 28 and 90 days. Thus, a series of nine experiments was conducted on the specimens for water to binder ratios of 0.40, 0.44 and 0.48 at 7, 28 and 90 days of the water curing regime. It is evident from the investigations that Grey Taguchi approach for optimization helps in identifying the factors affecting the final outcomes, i.e. compressive strength and split tensile strength of concrete. For the materials and a range of parameters used in this research, the present study has established optimum mixes in terms of strength properties. The best possible levels of mix proportions were determined for maximization through compressive and splitting tensile strength. To verify the results, the optimal mix was produced and tested. The mixture results in higher compressive strength and split tensile strength than other mixes. The compressive strength and split tensile strength of optimal mixtures are also compared with the control concrete mixtures. The results show that compressive strength and split tensile strength of concrete made with partial replacement of cement and fine aggregate is more than control concrete at all ages and w/c ratios. Based on the overall observations, it can be recommended that industrial waste by-products in ternary combinations can effectively be utilized as partial replacements of cement and fine aggregates in all concrete applications.
Abstract: In recent years, waste tyre problem is considered as one of the most crucial environmental pollution problems facing the world. Thus, reusing waste rubber crumb from recycled tyres to develop highly damping concrete is technically feasible and a viable alternative to landfill or incineration. The utilization of waste rubber in concrete generally enhances the ductility, toughness, thermal insulation, and impact resistance. However, the mechanical properties decrease with the amount of rubber used in concrete. The aim of this paper is to develop artificial neural network (ANN) models to predict the compressive strength of rubberised concrete (RuC). A trained and tested ANN was developed using a comprehensive database collected from different sources in the literature. The ANN model developed used 5 input parameters that include: coarse aggregate (CA), fine aggregate (FA), w/c ratio, fine rubber (Fr), and coarse rubber (Cr), whereas the ANN outputs were the corresponding compressive strengths. A parametric study was also conducted to study the trend of various RuC constituents on the compressive strength of RuC.
Abstract: Climate change, namely precipitation patterns alteration, has led to extreme conditions such as floods and droughts. In turn, excessive construction has led to the waterproofing of the soil, increasing the surface runoff and decreasing the groundwater recharge capacity. The permeable pavements used in areas with low traffic lead to a decrease in the probability of floods peaks occurrence and the sediments reduction and pollutants transport, ensuring rainwater quality improvement. This study aims to evaluate the porous asphalt performance, developed in the laboratory, with addition of cellulosic fibres. One of the main objectives of cellulosic fibres use is to stop binder drainage, preventing its loss during storage and transport. Comparing to the conventional porous asphalt the cellulosic fibres addition improved the porous asphalt performance. The cellulosic fibres allowed the bitumen content increase, enabling retention and better aggregates coating and, consequently, a greater mixture durability. With this solution, it is intended to develop better practices of resilience and adaptation to the extreme climate changes and respond to the sustainability current demands, through the eco-friendly materials use. The mix design was performed for different size aggregates (with fine aggregates – PA1 and with coarse aggregates – PA2). The percentage influence of the fibres to be used was studied. It was observed that overall, the binder drainage decreases as the cellulose fibres percentage increases. It was found that the PA2 mixture obtained most binder drainage relative to PA1 mixture, irrespective of the fibres percentage used. Subsequently, the performance was evaluated through laboratory tests of indirect tensile stiffness modulus, water sensitivity, permeability and permanent deformation. The stiffness modulus for the two mixtures groups (with and without cellulosic fibres) presented very similar values between them. For the water sensitivity test it was observed that porous asphalt containing more fine aggregates are more susceptible to the water presence than mixtures with coarse aggregates. The porous asphalt with coarse aggregates have more air voids which allow water to pass easily leading to ITSR higher values. In the permeability test was observed that asphalt porous without cellulosic fibres presented had lower permeability than asphalt porous with cellulosic fibres. The resistance to permanent deformation results indicates better behaviour of porous asphalt with cellulosic fibres, verifying a bigger rut depth in porous asphalt without cellulosic fibres. In this study, it was observed that porous asphalt with bitumen higher percentages improve the performance to permanent deformation. This fact was only possible due to the bitumen retention by the cellulosic fibres.
Abstract: There need to construct building walls with lightweight masonry bricks/blocks and mortar to reduce the weight and cost of cooling/heating of buildings in hot/cold climates is growing partly due to legislations on energy use and global warming. In this paper, the development of Palm Kernel Shell masonry mortar (PKSMM) prepared with Portland cement and crushed PKS fine aggregate (an agricultural waste) is demonstrated. We show that PKSMM can be used as a lightweight mortar for the construction of lightweight masonry walls with good thermal insulation efficiency than the natural river sand commonly used for masonry mortar production.
Abstract: In this study, the effects of waste marbles as aggregate material on workability and hardened concrete characteristics of self compacting lightweight concrete are investigated. For this purpose, self compacting light weight concrete are produced by waste marble aggregates are replaced with fine aggregate at 5%, 7.5%, and 10% ratios. Fresh concrete properties, slump flow, T50 time, V funnel, compressive strength and ultrasonic pulse velocity of self compacting lightweight concrete are determined. It is concluded from the test results that using waste marbles as aggregate material by replacement with fine aggregate slightly affects fresh and hardened concrete characteristics of self compacting lightweight concretes.
Abstract: In this study, literature related to the replacement of cement with waste marble and the use of waste marble as an aggregate in concrete production was examined. Workability of the concrete decreased when marble powder was used as a substitute for fine aggregate. Marble powder contributed to the compressive strength of concrete because of the CaCO3 and SiO2 present in the chemical structure of the marble. Additionally, the use of marble pieces in place of coarse aggregate revealed that this contributed to the workability and mechanical properties of the concrete. When natural standard sand was replaced with marble dust at a ratio of 15% and 75%, the compressive strength and splitting tensile strength of the concrete increased by 20%-26% and 10%-15%, respectively. However, coarse marble aggregates exhibited the best performance at a 100% replacement ratio. Additionally, there was a greater improvement in the mechanical properties of concrete when waste marble was used in a coarse aggregate form when compared to that of when marble was used in a dust form. If the cement was replaced with marble powder in proportions of 20% or more, then adverse effects were observed on the compressive strength and workability of the concrete. This study indicated that marble dust at a cement-replacement ratio of 5%-10% affected the mechanical properties of concrete by decreasing the global annual CO2 emissions by 12% and also lowering the costs from US$40/m3 to US$33/m3.
Abstract: This article presents the comparison of selected evaluation methods regarding microstructure modification of hardened cement concrete intended for airfield pavements. Basic test results were presented for two pavement quality concrete lots. Analysis included standard concrete used for airfield pavements and modern material solutions based on concrete composite modification. In case of basic grain size distribution of concrete cement CEM I 42,5HSR NA, fine aggregate and coarse aggregate fractions in the form of granite chippings, water and admixtures were considered. In case of grain size distribution of modified concrete, the use of modern modifier as substitute of fine aggregate was suggested. Modification influence on internal concrete structure parameters using scanning electron microscope was defined. Obtained images were compared to the results obtained using computed tomography. Opportunity to use this type of equipment for internal concrete structure diagnostics and an attempt of its parameters evaluation was presented. Obtained test results enabled to reach a conclusion that both methods can be applied for pavement quality concrete diagnostics, with particular purpose of airfield pavements.
Abstract: Fly ash-slag based Geopolymer Cement (GPC) is presenting mechanical properties and environmental advantages that make it the predominant “green” alternative to Portland Cement (PC). Although numerous life-cycle analyses praising its environmental advantages, disposal after the end of its life remains as an issue that has been barely explored. The present study is investigating the recyclability of fly ash-slag GPC as aggregate in mortars. The purpose of the study was to evaluate the effect of GPC fine Recycled Aggregates (RA), at replacement levels of 25% and 50%, on the main mechanical properties of PC and GPC mortar mixes. The results were compared with those obtained by corresponding mixes incorporating natural and PC-RA. The main physical properties of GPC-RA were examined and proven to be comparable to those of PC-RA and slightly inferior to those of natural sand. A negligible effect was observed at 28-day compressive and flexural strength of PC mortars with GPC aggregates having a milder effect than PC. As far as GPC mortars are concerned, the influence of GPC aggregates was enhancing for the investigated mechanical properties. Additionally, a screening test showed that recycled geopolymer aggregates are not prone of inducing alkali silica reaction.
Abstract: This paper reports an experimental work that aimed to investigate the effects of clay brick waste, as part of fine aggregate, on rendering mortar performance. The brick, in crushed form, was from a local brick manufacturer that was rejected due to being of-standard. It was used to replace 33.33 %, 50 %, 66.66 % and 100 % by weight of the quarry sand in mortar. Effects of the brick replacement on the mortar key properties intended for wall plastering were investigated; these are workability, compressive strength, flexural strength, linear shrinkage, water absorption by total immersion and by capillary suction. The results showed that as the brick replacement level increased, the mortar workability reduced. The linear shrinkage increases over time and decreases with the introduction of brick waste. The compressive and flexural strengths decrease with the increase of brick waste because of their great water absorption.
Abstract: This paper discusses the effect of using blast furnace iron slag as a part of fine aggregate on the mechanical performance of hot mix asphalt (HMA). The mechanical performance was evaluated based on various mechanical properties that include; Marshall/stiffness, indirect tensile strength and unconfined compressive strength. The effect of iron slag content on the mechanical properties of the mixtures was also investigated. Four HMA with various iron slag contents, namely; 0%, 5%, 10% and 15% by weight of total mixture were studied. Laboratory testing has revealed an enhancement in the compressive strength of HMA when iron slag was used. Within the tested range of iron slag content, a considerable increase in the compressive strength of the mixtures was observed with the increase of slag content. No significant improvement on Marshall/stiffness and indirect tensile strength of the mixtures was observed when slag was used. Even so, blast furnace iron slag can still be used in asphalt paving for environmental advantages.
Abstract: Mineral product, waste concrete (fine aggregates),
waste in the optical field, industry, and construction employ separators
to separate solids and classify them according to their size. Various
sorting machines are used in the industrial field such as those operating
under electrical properties, centrifugal force, wind power, vibration,
and magnetic force. Study on separators has been carried out to
contribute to the environmental industry. In this study, we perform
CFD analysis for understanding the basic mechanism of the separation
of waste concrete (fine aggregate) particles from air with a machine
built with a rotor with blades. In CFD, we first performed
two-dimensional particle tracking for various particle sizes for the
model with 1 degree, 1.5 degree, and 2 degree angle between each
blade to verify the boundary conditions and the method of rotating
domain method to be used in 3D. Then we developed 3D numerical
model with ANSYS CFX to calculate the air flow and track the
particles. We judged the capability of particle separation for given size
by counting the number of particles escaping from the domain toward
the exit among 10 particles issued at the inlet. We confirm that
particles experience stagnant behavior near the exit of the rotating
blades where the centrifugal force acting on the particles is in balance
with the air drag force. It was also found that the minimum particle
size that can be separated by the machine with the rotor is determined
by its capability to stay at the outlet of the rotor channels.
Abstract: Response Surface Methods (RSM) provide
statistically validated predictive models that can then be manipulated
for finding optimal process configurations. Variation transmitted to
responses from poorly controlled process factors can be accounted
for by the mathematical technique of propagation of error (POE),
which facilitates ‘finding the flats’ on the surfaces generated by
RSM. The dual response approach to RSM captures the standard
deviation of the output as well as the average. It accounts for
unknown sources of variation. Dual response plus propagation of
error (POE) provides a more useful model of overall response
variation. In our case, we implemented this technique in predicting
compressive strength of concrete of 28 days in age. Since 28 days is
quite time consuming, while it is important to ensure the quality
control process. This paper investigates the potential of using design
of experiments (DOE-RSM) to predict the compressive strength of
concrete at 28th day. Data used for this study was carried out from
experiment schemes at university of Benghazi, civil engineering
department. A total of 114 sets of data were implemented. ACI mix
design method was utilized for the mix design. No admixtures were
used, only the main concrete mix constituents such as cement, coarseaggregate,
fine aggregate and water were utilized in all mixes.
Different mix proportions of the ingredients and different water
cement ratio were used. The proposed mathematical models are
capable of predicting the required concrete compressive strength of
concrete from early ages.
Abstract: Ceramic Waste Aggregates (CWAs) were made from
electric porcelain insulator wastes supplied from an electric power
company, which were crushed and ground to fine aggregate sizes. In
this study, to develop the CWA mortar as an eco–efficient, ground
granulated blast–furnace slag (GGBS) as a Supplementary
Cementitious Material (SCM) was incorporated. The water–to–binder
ratio (W/B) of the CWA mortars was varied at 0.4, 0.5, and 0.6. The
cement of the CWA mortar was replaced by GGBS at 20 and 40% by
volume (at about 18 and 37% by weight). Mechanical properties of
compressive and splitting tensile strengths, and elastic modulus were
evaluated at the age of 7, 28, and 91 days. Moreover, the chloride
ingress test was carried out on the CWA mortars in a 5.0% NaCl
solution for 48 weeks. The chloride diffusion was assessed by using an
electron probe microanalysis (EPMA). To consider the relation of the
apparent chloride diffusion coefficient and the pore size, the pore size
distribution test was also performed using a mercury intrusion
porosimetry at the same time with the EPMA. The compressive
strength of the CWA mortars with the GGBS was higher than that
without the GGBS at the age of 28 and 91 days. The resistance to the
chloride ingress of the CWA mortar was effective in proportion to the
GGBS replacement level.
Abstract: This study investigates the suitability of using plastic,
such as polyethylene terephthalate (PET), as a partial replacement of
natural coarse and fine aggregates (for example, brick chips and
natural sand) to produce lightweight concrete for load bearing
structural members. The plastic coarse aggregate (PCA) and plastic
fine aggregate (PFA) were produced from melted polyethylene
terephthalate (PET) bottles. Tests were conducted using three
different water–cement (w/c) ratios, such as 0.42, 0.48, and 0.57,
where PCA and PFA were used as 50% replacement of coarse and
fine aggregate respectively. Fresh and hardened properties of
concrete have been compared for natural aggregate concrete (NAC),
PCA concrete (PCC) and PFA concrete (PFC). The compressive
strength of concrete at 28 days varied with the water–cement ratio for
both the PCC and PFC. Between PCC and PFC, PFA concrete
showed the highest compressive strength (23.7 MPa) at 0.42 w/c ratio
and also the lowest compressive strength (13.7 MPa) at 0.57 w/c
ratio. Significant reduction in concrete density was mostly observed
for PCC samples, ranging between 1977–1924 kg/m³. With the
increase in water–cement ratio PCC achieved higher workability
compare to both NAC and PFC. It was found that both the PCA and
PFA contained concrete achieved the required compressive strength
to be used for structural purpose as partial replacement of the natural
aggregate; but to obtain the desired lower density as lightweight
concrete the PCA is most suited.
Abstract: This work is focused on the study of valuation of
recycled concrete aggregates, by measuring certain properties of
concrete in the fresh and hardened state. In this study, rheological
tests and physic-mechanical characterization on concretes and
mortars were conducted with recycled concrete whose geometric
properties were identified aggregates. Mortars were elaborated with
recycled fine aggregate (0/5mm) and concretes were manufactured
using recycled coarse aggregates (5/12.5 mm and 12.5/20 mm). First,
a study of the mortars was conducted to determine the effectiveness
of polycarboxylate superplasticizer on the workability of these and
their action deflocculating of the recycled sand. The rheological
behavior of mortars based on fine aggregate recycled was
characterized. The results confirm that the mortars composed of
different fractions of recycled sand (0 /5) have a better mechanical
properties (compressive and flexural strength) compared to normal
mortar. Also, the mechanical strengths of concretes made with
recycled aggregates (5/12.5 mm and 12.5/20 mm), are comparable to
those of conventional concrete with conventional aggregates,
provided that the implementation can be improved by the addition of
a superplasticizer.
Abstract: Construction and Demolition (C&D) wastes contribute the highest percentage of wastes worldwide (75%). Furthermore, ceramic materials contribute the highest percentage of wastes within the C&D wastes (54%). The current option for disposal of ceramic wastes is landfill. This is due to unavailability of standards, avoidance of risk, lack of knowledge and experience in using ceramic wastes in construction. The ability of ceramic wastes to act as a pozzolanic material in the production of cement has been effectively explored. The results proved that temperatures used in the manufacturing of these tiles (about 900⁰C) are sufficient to activate pozzolanic properties of clay. They also showed that, after optimization (11-14% substitution); the cement blend performs better, with no morphological difference between the cement blended with ceramic waste, and that blended with other pozzolanic materials. Sanitary ware and electrical insulator porcelain wastes are some wastes investigated for usage as aggregates in concrete production. When optimized, both produced good results, better than when natural aggregates are used. However, the research on ceramic wastes as partial substitute for fine aggregates or cement has not been overly exploited as the other areas. This review has been concluded with focus on investigating whether ceramic wall tile wastes used as partial substitute for cement and fine aggregates could prove to be beneficial since the two materials are the most high-priced during concrete production.
Abstract: Research on the utilization of fly ash will no longer refer the fly ash as a waste material of thermal power plants. Use of fly ash in concrete making, makes the concrete economical as well as durable. The fly ash is being added to the concrete in three ways namely, as partial replacement to cement, as partial replacement to fine aggregates and as admixture. Addition of fly ash to the concrete in any one of the form mentioned above, makes the concrete more workable and durable than the conventional concrete. Studies on fly ash as partial replacement to cement gained momentum as such replacement makes the concrete economical. In the present study, an attempt has been made to understand the effects of fly ash on the workability characteristics and strength aspects of fly ash concretes. In India major number of thermal power plants is producing low calcium fly ash. Hence in the present investigation low calcium fly ash has been used. Fly ash in concrete was considered for the partial replacement of cement. The percentage replacement of cement by fly ash varied from 0% to 40% at regular intervals of 10%. More over the fine aggregate to coarse aggregate ratio also has been varied as 1:1, 1:2 and 1:3. The workability tests revealed that up to 30% replacement of cement by fly ash in concrete mixes water demand for reduces, beyond 30% replacement of cement by fly ash demanded more water content for constant workability.
Abstract: Pervious concrete is a green alternative to conventional pavements with minimal fine aggregate and a high void content. Pervious concrete allows water to infiltrate through the pavement, thereby reducing the runoff and the requirement for stormwater management systems.
Seashell By-Products (SBP) are produced in an important quantity in France and are considered as waste. This work investigated to use SBP in pervious concrete and produce an even more environmentally friendly product, Pervious Concrete Pavers.
The research methodology involved substituting the coarse aggregate in the previous concrete mix design with 20%, 40% and 60% SBP. The testing showed that pervious concrete containing less than 40% SBP had strengths, permeability and void content which are comparable to the pervious concrete containing with only natural aggregate. The samples that contained 40% SBP or higher had a significant loss in strength and an increase in permeability and a void content from the control mix pervious concrete. On the basis of the results in this research, it was found that the natural aggregate can be substituted by SBP without affecting the delicate balance of a pervious concrete mix. Additional, it is recommended that the optimum replacement percentage for SBP in pervious concrete is 40 % direct replacement of natural coarse aggregate while maintaining the structural performance and drainage capabilities of the pervious concrete.
Abstract: Binder drainage test is widely used to set an upper
limit to the design binder content of porous asphalt. However, the
presence of high amount of fine particles in the drained binder may
affect the accuracy of the test result. This paper presents a study to
characterize the composition and particle size distribution of fine
particles accumulated in the drained binder. Fine aggregates and filler
in the drained binder were extracted using a suitable solvent. Then,
wet and dry sieve analysis was carried out to identify the actual
composition of the extracted fine aggregates and filler. From the
results, almost half of the drained binder consisted of fine aggregates
and this significantly affects the accuracy of the design binder content
of porous asphalt mix. This simple finding highlights the importance
of taking into account the presence of fine aggregates in the
calculation of drained binder.